• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.855-858
• /
• 2008

A compression lap splice can be calculated longer than a tension lap splice in high strength concrete according to current design codes. Including effects of transverse reinforcement, a compression splice becomes much longer than a tension splice. Effects of transverse reinforcement on strength and behavior of compression lap splice, which always exist in actual structures, have been investigated through experimental study of column tests with concrete strength of 40 and 60 MPa. Confined specimens have twice of calculated strengths by current design codes. New design equations for the compression lap splice including the effects of transverse reinforcement are required for practical purpose of ultra-high strength concrete. End bearing is enhanced by transverse reinforcement placed at ends of splice not by transverse reinforcement within splice length. As more transverse reinforcement are placed, the stresses developed by bond linearly increase. The transverse reinforcements at ends of splice a little improve the strength by bond.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.87-98
• /
• 2011

Crack formations are inevitable in reinforced concrete structures. To estimate crack widths, empirical formulae are used widely and indirect crack controling methods of limiting bar spacing and bar diameter are also used due to their simplicity. In EC2, the characteristic crack width is calculated by multiplying maximum crack spacing and average strain. In this study, limit values of maximum bar spacing and bar diameter are examined as the material characteristics are varied. Two models of tension stiffening effect and maximum crack spacing and their effects are evaluated. The obtained results are compared with the values obtained using KCI method. The results showed that a significant difference is found when two tension stiffening effect are employed, and an under-estimation is found when 2nd order tension stiffening effect and maximum crack spacing limit from Part II were implemented. Therefore, a rational indirect crack control method attained using the tension stiffening effect of 2nd order form is needed. Also, a consistency in serviceabiliy analysis in flexural members needs to be secured. In order to achieve these goals, two crack controling models are suggested.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.13-16
• /
• 2008

In a tension-controlled section, all steel tension reinforcement is assumed to yield at ultimate when using the strength design method to calculate the nominal flexural strength of members with steel reinforcement arranged in multiple layers. Therefore, the tension force is assumed to act at the centroid of the reinforcement with a magnitude equal to the area of tension reinforcement times the yield strength of steel. Because FRP materials have no plastic region, the stress in each reinforcement layer will vary depending on its distance from the neutral axis. Similarly, if different types of FRP bars are used to reinforce the same member, the stress level in each bar type will vary, and the member will show different behavior from our expectation. In this study, six high-strength concrete beam specimens reinforced with conventional steels, CFRP bars, and GFRP bars as flexural reinforcements were constructed and tested. The members reinforced with hybrid reinforcements showed higher stiffness, smaller crack width, and better ductility than the members reinforced with single type of FRP bars.

• Journal of Industrial Technology
• /
• v.26 no.B
• /
• pp.127-134
• /
• 2006

As material needs have been increasing with recent economic growth, it is a current tendency that the magnitude of load applied to structure has been rising. With improved technique of product materials, steel and concrete have been stranger than ever so the danger of fatigue damage increases as permanent action of repeated loads. In case of deformed steel bars widely used in reinforced concrete structure, when they are product in factory, there will exist same parts connecting the steels. Such connections are easy to be weakened by permanent action of repeated loads. It is a real condition in Korea that there is lack of research of it. As a result of estimating fatigue characteristic of Pressure Welded joints with the steels that are oftenly used and producted in domestic it is showed that there are no remarkable difference in fatigue strength. Because there is no detail which is refered in Civil Specification, this paper will be the basic data being added in later Specification.

• Journal of Korean Society of Steel Construction
• /
• v.24 no.5
• /
• pp.605-612
• /
• 2012

A tension member that has a high-strength bolt fastened to a standard bolt hole increases structural resistance but causes problems from workability or economic perspectives. In this research, a total of 28 samples that have standard and over bolt holes as the tension member's high-strength bolted connection were made and a tension test was conducted. The change of strength of the connection has been confirmed by comparing the tension load of standard and over bolt hole samples obtained from the test results with the design strength due to net section and end distance. Samples made with over bolt holes had a lighter tension load than that of samples made with standard bolt holes, exceeded the design strength of present design standards, and although decrease in strength was inevitable due to the over bolt hole, their safety was satisfactory.

• Journal of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.239-248
• /
• 2002

A constitutive model unifying plasticity and crack damage mode)s was developed to address the cyclic behavior of reinforced concrete planar members. The stress of concrete in tension-compression was conceptually defined by the sum of the compressive stress developed by the strut-action of concrete and the tensile stresses developed by tensile cracking. The plasticity model with multiple failure criteria was used to describe the isotropic damage of compressive crushing affected by the anisotropic damage of tensile cracking. The concepts of the multiple fixed crack damage model and the plastic flow model of tensile cracking were used to describe the tensile stress-strain relationship of multi-directional cracks. This unified model can describe the behavioral characteristics of reinforced concrete in cyclic tension-compression conditions, i.e. multiple tensile crack orientations, progressively rotating crack damage, and compressive crushing of concrete. The proposed constitutive model was implemented to finite element analysis, and it was verified by comparison with existing experimental results from reinforced concrete shear panels and walls under cyclic load conditions.

• Journal of the Korea Concrete Institute
• /
• v.29 no.1
• /
• pp.53-64
• /
• 2017

Ultra-high performance fiber-reinforced concrete (UHPFRC) is characterized by a post-cracking residual tensile strength with a large tensile strain as well as a high compressive strength. To determine a material tensile strength of UHPFRC, three-point loading test on notched prism and direct tensile test on doubly notched plate were compared and then the design tensile strength is decided. Shear tests on nine I-shaped beams with varied types of fiber volume ratio, shear span ratio and size effect were conducted to investigate shear behavior in web. From the test results, the stress redistribution ability represented as diagonal cracked zone was quantified by inclination of principal stress in web. The test results shows that the specimens were capable of resistance to shear loading without stirrup in a range of large deformation and the strength increase with post-cracking behavior is stable. However at the ultimate state all test specimens failed as a crack localization in the damaged zone and the shear strength of specimens is affected by shear span ratio and effective depth. Strength predictions show that the existing recommendations should be modified considering shear span ratio and effective depth as design parameters.

• 건축구조
• /
• v.13 no.3
• /
• pp.86-87
• /
• 2006

대공간구조물의 계획을 위하여 장스팬 구조물의 계획을 실시하였다. 보나 슬래브 부재는 상부에 압축력과 하부에 인장력을 받는다. 일반구조체로 120M 의 장스팬을 감당할 수 없으므로 케이블의 인장력을 이용한 대공간구조물을 계획하였다.

• Journal of the Korea Concrete Institute
• /
• v.23 no.2
• /
• pp.169-176
• /
• 2011

In this study, the flexural test for reinforced high performance fiber reinforced cementitious composites (R/HPFRCC) members has been conducted in order to investigate the flexural behavior including the effect of an ordinary tensile reinforcing bar. Through the test, it was observed that the flexural strength increased due to the stable tensile stress transfer of HPFRCC, even up to the ultimate state. In addition, no localized crack appeared until the yielding of the reinforcement. From the layered section analysis of the tested members, it was found that the analysis with the tensile model obtained from the tension stiffening test showed better agreement with the flexural test results, whereas the analysis with direct tension test results overestimated the flexural capacity. Through the experimental and analytical studies, two flexural failure modes have been defined in this paper; concrete crushing at the top compression layer or tensile failure at the bottom tensile layer of the beam section. Based on these two flexural failure modes, a simple formula that estimates the ultimate flexural strength of the member has been proposed in this paper. The proposed equations can be useful in a design and an analysis of R/HPFRCC members.

• Magazine of the Korea Concrete Institute
• /
• v.7 no.5
• /
• pp.145-154
• /
• 1995

Concrete has two different failure mechanisms : compressive crushing and tensile cracking. Concrete models should use the two different failure criteria to analyze the inelastic behavior of concrete including multiaxial crushing and tensile cracking. Concrete models used in this study are based on plasticity with multiple failure criteria of compressive crushing and tensile cracking. For tensile cracking behavior, two different plasticity models are investigated. The* ,e are rotating-crack and fixed-crack plasticity models, classified according to idealization of crack 0rientat:ions. The material models simplify inelastic behavior of concrete for plane stress problenls. The material models are used for the finite element anlaysis. Analytical results are compared with several experiments of reinforced concrete member. The advantages and disadva.ntages of rotating-crack and fixed -crack plasticity models are discussed.