• Polymer(Korea)
• /
• v.27 no.4
• /
• pp.275-284
• /
• 2003

The positive temperature coefficient (PTC) effects of high density polyethylene (HDPE)/carbon black composite materials were investigated by enhancing adhesive characteristics of electrodes and controlling HDPE chemical crosslinking. When the silver paste was used as an electrode for the same 45 wt% HDPE/carbon composites, the resistance was over 1 $\Omega$, which should be compared with the resistance of 0.2 $\Omega$ for the dendritic copper electrode. In general, the silver-paste electrode exhibited higher electrical resistance than cupper electrode due to the interfacial resistance between the electrode and PTC composites. The HDPE/carbon composite exhibited typical PTC characteristics maintaining a constant resistance up to vicat point and showing a maximum at the melting point of HDPE. The crosslinked HDPE significantly decreased the negative temperature coefficient (NTC) phenomena, and desirably showed a constant or slightly increasing feature of electrical resistance in the high temperature region.

• Proceedings of the Korean Institute of IIIuminating and Electrical Installation Engineers Conference
• /
• 2009.05a
• /
• pp.293-296
• /
• 2009

In order to protect the electrical fire, AFCI(Arc Fault Cirruit Interrupter) was obligated to adopted in United States of America since 2002. AFCI using by line resistor of neutral trace needs to compensate the resistance variation of the line resistor by temperature variation. In this paper, the ASIC including the temperature compensation circuit is implemented. The successful implementation is verified by showing the effectiveness of an electric and a temperature characteristics for ARC signals by simulation results.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.187-188
• /
• 2012

magnetron-sputtering법을 사용하여 $Cr_{1-x}Al_xN$ 박막을 증착함에 있어 Al 함량의 변화를 주었다. 그 후 열처리를 통하여 thermal inkjet 방식 print head의 heater resistor 소재로서의 특성 향상을 도모하였다. Al의 함량이 증가할수록 결정구조는 NaCl에서 wurtzite HCP 구조로 변화하였으며 전기적 특성 또한 다르게 나타났다. 비열처리 시 Al 함량이 클수록 결정성은 떨어진다는 것을 확인하였고, 열처리 시 Al 함량이 적을 수 록 더 안정한 온도 저항 계수를 나타내는 것을 확인하였다.

• Journal of Bio-Environment Control
• /
• v.1 no.2
• /
• pp.187-191
• /
• 1992

온도의 계측에는 열팽창(Thermal expansion), 열전기(thermoelectricity), 전기저항(resistance)등의 원리를 이용하고 있다. (1) 열팽창식 온도계 물체의 열팽창 원리를 이용하는 온도계에는 두 금속의 열팽창 계수의 차이를 이용하는 바이멜탈 온도계, 액체의 팽창을 이용하는 유리 온도계, 기체 압력이 온도에 비례하는 것을 이용하는 압력식 온도계 등이 있으나, 이중에서 유리 온도계가 가장 널리 사용되고 있다.(중략)

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.6
• /
• pp.1205-1215
• /
• 1992

The solidification rate is of special importance in determining the casting structures and properties. The heat transfer characteristics at the interface between the mold and the casting is one of the major factors that control the solidification rate. The thermal resistance exists due to the air-gap formation at the mold/casting interface during the freezing process. In this study two-dimensional Stefan problem with air-gap resistance in the rectangular mold is considered and the heat transfer characteristics is numerically examined by using the enthalpy method. The effects of the major parameters, such as mold geometry, thermal conductivity, heat transfer coefficient, and initial temperature of casting, on the thermal characteristics are investigated.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.134-134
• /
• 2009

원자층 증착법을 이용하여 platinum group metal(Ru, Ir, Pt). metal nitride(TaN, TiN, AlN), 그리고 metal oxide($Al_2O_3$, $TiO_2$)을 증착하고, 미세구조와 공정 변수가 내산화성, 내부식성, 저항 및 온도저항계수에 미치는 영향을 연구하였다. proto-type의 전자저항막 제조를 통해 종래의 TaN 전자저항막에 비해 우수한 내부식성 및 내산화성을 가짐을 확인하였다.

• International Journal of Highway Engineering
• /
• v.3 no.3 s.9
• /
• pp.111-118
• /
• 2001

Since the advent of turbojet aircraft with their greater weight and high landing speed breaking performance on runway surface has become un critical. Under certain weather conditions(wet weather, winter) hydroplaning or unacceptable loss of traction can occur, resulting in poor braking performance and possible loss of directional control. To address this concern a number of research project me conducted by NASA, FAA, USAF. The various method which was reported the advantage of the increasing the friction and decreasing the hydroplaning effect. A-2 section of inchon international airport was grooved using drying grooving method. In order to evaluate the effectiveness of the dry grooving method the surface was spray with water and measured the fiction factor and the depth of the water using Mu meter and water depth measuring device. The field test results shooed that the fiction factor nos increased and the depth of the water decreased. The dry grooving method illustrated the reduction of hydroplaning and also, no distress on the runway.

• Proceedings of the KIEE Conference
• /
• 2002.07c
• /
• pp.1470-1472
• /
• 2002

3원계 51wt%Ni-4lwt%Cr-8wt%Si 합금 타겟을 가지고 DC/RF 마그네트론 스퍼터를 이용하여 박막저항을 제조하였고, 낮은 저항온도계수(TCR)를 가지는 박막을 만들기 위해 제조공정의 변화에 따른 박막의 미세구조와 전기적인 특성을 조사하였다. 스퍼터링 제조공정 변수로써 DC/RF Power, 반응압력, 기판온도를 변화시켰고, 제조된 박막은 공기중에서 $400[^{\circ}C]$까지 열처리 하였다. 반응압력을 감소시킴에 따라 TCR값은 감소하였고, 기판온도 및 열처리 온도의 증가에 따라 TCR값도 증가하였다. 또한, 비저항은 DC Power에서 $172[{\mu}{\Omega}cm]$, RF인 경우에는 $209[{\mu}{\Omega}cm]$을 나타내었고, 각각 +52, $-25[ppm/^{\circ}C]$의 TCR값을 나타냈다. 이와 같은 결과로부터 제조공정을 변화시킴에 따라 면저항 및 저항온도계수의 제어가 가능함을 알 수 있었다.

• Electrical & Electronic Materials
• /
• v.9 no.9
• /
• pp.911-917
• /
• 1996

Platinum thin films were deposited on Si-wafer by DC rnagnetron sputtering for RTD (resistance thermometer devices). We investigated the physical and electrical characteristics of these films under various conditions, the input power, working vacuum, temperature of substrate and also after annealing these films. The deposition rate was increased with increasing the input power but decreased with increasing Ar gas pressure. The resistivity and sheet resistivity were decreased with increasing the temperature of substrate and the annealing time at 1000.deg. C. At substrate temperature of >$300^{\circ}C$, input power of 7 w/cm$^{2}$, working vacuum of 5 mtorr and annealing conditions of 1000.deg. C and 240 min, we obtained 10.65.mu..ohm..cm, resistivity of Pt thin films and 3800-3900 ppm/.deg. C, TCR(temperature coefficient of resistance). These values are close to the bulk value. These results indicate that the Pt thin films deposited by DC magnetron sputtering have potentiality for the development of Pt RTD temperature sensor.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.9-9
• /
• 2008

일반적으로 섬광법으로 열전도율을 구하기 위해서는 섬광법으로 열확산계수를 측정하고, 시차주사열량계(Differential Scanning Calorimetry, DSC)로 비열측정을 하며 아르키메데스의 원리를 이용한 용적밀도를 구하여 이들 각각의 값을 사용하여 열전도율을 얻는다. 따라서 열전도율을 정밀하게 측정하기 위해서는 이 세 가지 물성치를 측정할 때 수반되는 오차요인을 종합적으로 검토하여 개선하는 것이 매우 중요하다. 섬광법으로 열확산계수를 측정할 때 시료의 전면에 조사되는 빛의 흡수율을 향상시키고 배면에서의 온도상승의 감지를 증대할 목적으로 시료 양면에 흑연코팅을 하게 된다. 이때 코팅된 흑연이 시료에 부가적으로 열저항을 증가시켜서 열확산계수를 측정하는데 가장 큰 오차요인이 되고 있다. 한편 비열은 대부분 DSC로 측정하는데, 시료와 용기의 열접촉 정도에 따라 큰 오차요인이 되기도 한다. 본 연구에서는 열확산계수를 정밀하게 측정하기 위해서 시료에 부가적인 열저항으로 작용하는 흑연코팅의 두께와 시료배면에서의 온도상승곡선 간의 상관관계를 실험식으로 도출하였으며 이방법은 열확산계수를 정밀하게 측정하는데 매우 유효한 방법임이 입증되었다. 또한 DSC의 접촉에서의 문제점을 해결하기 위해서 시료배면에서의 무차원 시간축(t/$t_{max}$)을 도입하였으며. 무차원 시간축에 따른 온도상승 곡선에서 표준시료와 측정시료의 half time($t_{1/2}$)의 0.5 배와 1.5배 사이 구간을 적분한 뒤 비교하여 열량계산으로부터 비열을 구하는 방법을 새롭게 개발하였으며 기존의 DSC에 비하여 정밀도를 향상시킬 수 있었다. 결론적으로 새롭게 제안된 측정기법들은 열확산계수 및 비열 혹정 시의 근본적인 오차요인을 혁신적으로 해결함으로써 정밀하고 신뢰성 있는 열전도율을 측정할 수 있음을 입증할 수 있었다.