• Journal of the Korea Concrete Institute
• /
• v.17 no.6 s.90
• /
• pp.931-938
• /
• 2005

When concrete structures are exposed under marine condition for a long time, the steel in concrete is corroded due to the ingression of chlorides in the seawater. Because the damages of corrosion resulting from the chloride ion are very serious, many researches have been performed. Silver nitrate colormetric method that can measure easily penetration depth of chloride ion has been executed, recent)y. However, characteristics of silver nitrate colormetric method were not fully examined. Therefore, the objective of this paper Is to study the applicability of colormetric method. For the purpose of this, effect factors and reaction mechanism of colormetric method were investigated, and the colormetric method is applied for marine concrete structures. According to the results of silver nitrate colored method, two reactions such as white reaction of AgCl and brown reaction of AgOH were shown when $AgNO_3$ was sprayed in splited section. And velocity constant ratio(K) of two reactions appeared that white reaction, AgCl reacts with the fast speed by 3240. When the colormetric method was applied in concrete, it is reasonable that $AgNO_3$ solution more than 0.05N concentration was sprayed. It is confirmed that the colormetric method is useful tool for estimating the chloride of concrete structures in situ. The average chloride amount of colored parts indicates $0.9kg/m^3$ per concrete unit weight.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.553-557
• /
• 2022

The present study evaluate the chloride extracion under electrochemical chloride extraction method. Chloride was penetrated into the concrete from external reservoir using a 4M NaCl solution, and an electrochemical chloride extraction method was applied after the curing period of 1 year. The current density was constantly kept 1000 mA/m² for coulostatic application with the variation in potential difference. The duration of the ECE treatment was 2, 4, 8 weeks, respectively. The residual chloride concentration at all depths decreased, and the chloride concentration decreased as the application period increased. After the application period of 8 weeks, 62.9 to 77.6 % of chloride extracted in the total chloride profile, and 77.7 to 99.5 % of chloride extracted in the free chloride profile. In particular, the concentration of free chloride at a depth of 7 mm or more from the concrete surface was 0.01 % or less by cement. In addition, it was confirmed that the bound chloride could be extracted by the electrochemical chloride extraction.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.5
• /
• pp.189-196
• /
• 2007

The purpose of this study was to analyze steel corrosion resistance of concrete containing copper slag. The specimens were made with normal portland cement and pozzolan materials with various replacement ratio and with W/B ratio ranging from 35% to 55%. Compressive strength, coefficient of chloride diffusion, corrosion area ratio and weight reduction ratio were determinated for the test. The results show that the concrete with pozzolan materials is superior resistant to chloride ions compared to the concrete without pozzolan materials. It was observed that blast furnace slag replacement ratio of 20% gives the best results with respect to chloride ion penetration and corrosion tests and observed that copper slag replacement ratio of 10% gives the seperior resistance compared to normal concrete.

• Journal of the Korea Concrete Institute
• /
• v.16 no.2 s.80
• /
• pp.261-268
• /
• 2004

Corrosion of reinforcement is the main cause of damage and early failure of reinforced concrete structures. The corrosion is mainly progressed by the chloride ingress. In this paper, an experimental study is executed to investigate the effect of concrete properties and testing methods on the coefficients of chloride diffusion. Also, it is surveyed the relationship between total chloride and free chloride in concrete. According to this experiment results, W/C ratio and testing method affect chloride diffusion coefficient of concrete. As W/C ratio is increased, diffusion coefficient in concrete is also increased. Diffusion coefficient obtained by each testing method show the different values, respectively. The model equation of diffusion coefficient with W/C ratio is proposed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.5
• /
• pp.31-38
• /
• 2018

The effects of polymer-binder ratio and metakaolin content on the properties of ultrarapid-hardening polymer-modified concretes using metakaolin are examined. As a result, regardless of the metakaolin content, the flexural, compressive and adhesion in tension strength of the ultrarapid-hardening polymer-modified concretes tend to increase with increasing polymer-binder ratio. Regardless of the polymer-binder ratio, the strengths of the ultrarapid-hardening polymer-modified concretes increase with increasing metakaolin content, and reaches a maximum at metakaolin content of 5%. The water absorption, carbonation depth and resistance of chloride ion penetration of the ultrarapid-hardening polymer-modified concretes decrease with increasing polymer-binder ratio. The resistance of freezing and thawing improvement is attributed to the improved bond between cement hydrates and aggregates because of the incorporation of polymer dispersion.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.505-508
• /
• 2008

Concrete is a type of porous materials and is physically and chemically damaged due to exposure to various environments from the placing to the service life. These reactions affect the corrosionof steel bars applied in concrete and that decreases the durability life and strength of such steel bars. Thus, it is very important to insert rust inhibitors into steel bars in the case of a deterioration element that exceeds the critical amount of corrosion in the location of steel bars. However, it is very difficult to guarantee corrosion resistance at the location of steel bars using conventional technology that applies corrosion inhibitors only on the surface of concrete. This study attempts to develop a method that penetrates corrosion inhibitors up to the location of steel bars and investigate the penetration depth of corrosion inhibitors by verifying moisture migration in concrete under an applied pressure.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.1
• /
• pp.35-44
• /
• 2015

Two main parameters were examined such as CSA content and polymer-binder ratio to find effects on the strength, water absorption, chloride ion penetration depth, carbonation depth, length change and chemical resistance of polymer-modified mortar with CSA and EVA polymer powder (EVAPP). As results, compressive, flexural, tensile, adhesive strengths, and length change of the polymer-modified mortar with CSA and EVAPP increases with increasing CSA content and polymer-binder ratio, although the water absorption, chloride ion penetration depth, and carbonation depth decrease with increasing polymer-binder ratio and CSA content, and also the chemical resistance decreases. Such strength and durability development is attributed to the high tensile strength of EVA polymer and the improved bond between cement hydrates and aggregates because of the addition of EVAPP and CSA.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.5
• /
• pp.16-22
• /
• 2023

In this study, a salt water immersion test was performed on concrete specimens simulating the concrete mix design of the nuclear power plant, and the correlation between the amount of chloride and the XRF component according to the depth of the concrete was analyzed. The amount of chloride on the surface of the nuclear power plant concrete increased slightly with increasing immersion time in salt water, but the amount of chloride in the depth of 5.5 mm or more showed a clear tendency to increase with increasing immersion time in salt water. As a result of analyzing the correlation between the amount of chloride in concrete and the XRF component, the concrete with 20% FA substitution compared with the OPC concrete showed a very high correlation between the composition ratio of Cl ions and the evaluation result of salt damage resistance by XRF component analysis. Accordingly, it was confirmed that chlorine ion analysis and salt damage resistance performance evaluation by XRF component analysis were possible through repeated data accumulation in the nuclear power plant concrete mix with 20% fly ash replacement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.48-55
• /
• 2022

This study uses the recovered water as mixing water and artificial lightweight aggregate pre-wetting water as part of a study to increase the recycling rate and reduce greenhouse gas of the ready-mixed concrete recovered during the concrete transport process, and cement fine powder of blast furnace slag(BFS) and fly ash(FA). The engineering characteristics of the three-component lightweight aggregate mortar used as a substitute were reviewed. For this purpose, the flow, dry unit mass, compressive strength, drying shrinkage, neutralization depth, and chloride ion penetration resistance of the three-component lightweight aggregate mortar were measured. When used together with the formulation, when 15 % of BFS and 5 % of FA were used, it was found to be positive in improving the compressive strength and durability of the mortar.

• Journal of the Korea Concrete Institute
• /
• v.18 no.5 s.95
• /
• pp.667-675
• /
• 2006

Concrete is much more easily damaged by various parameters than by the only one and performance reducing mechanism grows more complicated in that condition. In addition, the factors which really act in concrete structure tend to be activated in turn and the degradation of concrete is very rapidly progressed. The purpose of this study is to evaluate the properties of polymer cement mortars under combined cures. The polymer cement mortars are prepared with various polymer types, polymer-cement ratios and cement-fine aggregate ratio, and tested for compressive and flexural strengths, accelerated carbonation, chloride ion penetration and acid resistance test, and freezing-thawing test. The properties of polymer cement mortars under combined cures is discussed. From the test results, polymer cement mortars have superior strengths compared with plain cement mortar under combined cures. The strengths of polymer cement mortars are markedly increased at curing condition II and V, however strengths are not improved at curing condition I and IV irregardless of polymer types. The carbonation and chloride ion penetration depths of polymer cement mortars tend to decrease in curing conditions, III-C, IV-B, V-A order, and decrease with increasing polymer cement ratios. It is concluded that polymer cement ratio of 10 to 15% are considered optimum for the preparation of such polymer cement mortars.