• Economic and Environmental Geology
• /
• v.55 no.3
• /
• pp.281-293
• /
• 2022

We examined degradation characteristics of lead based pigments(white lead, Red lead, Litharge) according to atmospheric environmet condition, for example atmospheric gas(CO₂, NO₂) and soluble salt. Painted samples not changed material compositions but were occured the color change(𝚫E 4~31) after exposed UV irradiation. All sample were not affected by CO₂ gas not only color but chemical composition. However, samples were remakably changed color exposed NO₂ gas and it was formed secondary product like as lead nitrate. Such as red lead and white lead samples' color difference were 𝚫E 2 and 𝚫 10 respectively and became dark, along with litharge became bright and color difference was 𝚫E 5 after react with NO₂ gas. It confirm that NO₂ was influential factor than CO₂ in the case of same concentration. Furthermore salt spray test was taken to figure out soluble salt influence in fine dust. The result showed noticeable color change and secondary product was formed on samples' surface. The glue film peeled off or hole, and color changed around the secondary products. After salt spray, XRD pattern showed decrease peak intensity and lower crystalinity. As a result of salt spray test, white lead was formed new product litharge and litharge was formed litharge and minium. According to the results, influential atmospheric factors for conservation of paint pigments were UV, NO₂, soluble salt, and litharge was most weakness throughout lead base pigments.

• Corrosion Science and Technology
• /
• v.12 no.5
• /
• pp.209-214
• /
• 2013

In the industry, accelerated corrosion test is used for the life time prediction. When anti-corrosion test proceeds in real environments, it is difficult that we predict and evaluate the corrosion life time because of the long test time such as 10 years or more time. Accelerated corrosion test and Salt spray test are able to test corrosion life time of products in the laboratory instead of outdoor corrosion test. Experimental procedure is selected for the corrosion standard specimen, exposure of the specimens, measurements of the mass loss and evaluating the mass loss data. As a result, the acceleration factor of the accelerated corrosion test to the outdoor corrosion test is 414.8. Therefore we can predict the corrosion life time of carbon steel during a short time period.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.22-22
• /
• 2014

아연(Zn)을 대체할 수 있는 물질계 인 알루미늄(Al)과 마그네슘(Mg)을 본 연구에서는 전자빔 증착을 이용하여 냉연 강판 위에 다층으로 코팅하고 열처리를 실시하여 전자현미경 및 글로우방전 분광기를 이용한 코팅층의 특성 분석 및 염수 분무시험을 통해 내식성을 평가하였다.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 1994.04a
• /
• pp.10-15
• /
• 1994

전기도금 공정에서 발생하는 수소취성은 다량의 수소이온이 강제품에 흡수되어 취화되는 현상을 나타내는 것으로 인장강도 200KSI 이상이 요구되는 항공기용 또는 로켓트 추진기관용 초고강도강에서 크게 문제가 되고 있다. 본 내용은 전기 카드뮴도금 작업시에 발생되는 수소취성에 대하여 간략하게 기술하고. 이 수소취성을 제거하는 방법 및 수소취성을 저게 생성시키는 저취성도금인 Cd-Ti 합금도금의 공정개발 결과를 보고한다. 실험결과에 의하면 도금층의 Ti함량은 0.1-0.7%이며 Ti의 공석에 의하여 Cd 도금에 비하여 저취성을 나타냈으며, Cd-Ti합도금의 내식성은 상대평가인 염수분무시험 결과 Cd도금과 비교하여 소재표면의 부식을 일으키는 붉은녹발생까지의 시간이 500시간으로 보다 높은 내식성을 나타내었다. 그리고 Cd-Ti 합금의 공정표준 및 Ti농도의 관리방법 등을 정리하여 보고한다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.121-122
• /
• 2012

합금도금강판의 일시 방청과 기능성 부여 후처리는 크로메이트, 인산염처리 등과 같은 방법을 시행하는 것이 일반적이다. 최근에는 아연합금도금 강판의 사용 및 보관 환경이 가혹해짐에 따라 보다 우수한 일시 방청성과 내식성이 요구되고 있다. 본 연구는 솔젤법을 이용하여 zirconium n-propoxide와 3-glycidoxypropyltrimethoxysilane(GPTS)으로부터 중합된 코팅막과 이에 zirconia nanoparticle입자를 첨가한 코팅막의 공극율(prosity)과 방식효율(protective efficiency)을 분극데이터를 이용하여 비교 평가하였으며, 염수분무시험을 통해 내식성 평가를 진행하였다.

• Journal of Ocean Engineering and Technology
• /
• v.29 no.6
• /
• pp.475-480
• /
• 2015

In this study, we developed a Cr-free organic/inorganic hybrid solution and investigated its coating properties on degraded STS316L. Both the OIBD-1 solution and OIBD-2 solution had excellent corrosion resistance and adhesion ability. However, the solution had some problems in a boiling water environment. In addition, the flexibility was excellent, and the scratch resistance was relatively good.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.105-106
• /
• 2009

AZ31 (3% Al, 1% Zn) Mg 판재의 내식성 향상을 위해 Ti/Zr/Polymer 복합계의 Cr-free 화성처리 방법을 이용하였다. 염수분무시험을 통해 최고 72시간 ($5{\sim}10%$ 발청) 내식성이 나타남을 확인하였다. 화성피막의 내식성은 그 피막이 가진 성분, 균일도, 치밀도, 형상 및 두께에 의해 좌우되는 만큼 TEM, SEM을 통해 화성피막 구조가 내식성과 어떠한 관련이 있는지 조사하였다. 또한, 화성처리 전 단계 공정인 탈지와 산세 및 중화 공정의 변수 조절을 통해 전처리 공정이 최종 화성피막의 물성에 어떠한 영향을 미치는지 조사하였다. 탈지조건을 $35{\sim}40^{\circ}C$, 5분에서 $50{\sim}80^{\circ}C$, $10{\sim}20$분으로 변경 시 좀 더 균일한 외관을 얻을 수 있었고, 적절한 중화제 선택을 통해 화성피막을 균일하게 형성시킬 수 있었다. 투과전자현미경 결과로 미루어 화성피막의 두께보다 균일도와 치밀도가 내식성에 결정적인 영향을 미치는 것을 확인할 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.276-276
• /
• 2012

본 연구에서는 진공증착을 이용하여 제작한 Al-Mg막을 $400^{\circ}C$에서 각각 2, 3, 10분간 열처리를 실시하였다. 합금화 정도는 GDLS와 XRD를 이용하여 표면 및 단면의 조성 분포를 분석하였으며, 염수분무시험을 통하여 내식성과의 연관성을 검토하였다. 열처리를 하지 않은 합금막의 경우 열처리를 한 경우와 비교하여 표면 및 단면에 순수한 Al 또는 Mg이 존재하여 내식성이 상대적으로 우수하였다. 열처리 결과 Al-Mg계 금속간 화합물 $Al_3Mg_2$와 $Al_{12}Mg_{17}$이 관찰되었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.268-268
• /
• 2012

합금도금강판의 일시 방청과 기능성 부여 후처리는 크로메이트, 인산염처리 등과 같은 방법을 시행하는 것이 일반적이다. 그러나, 최근에는 아연합금도금 강판의 사용 및 보관 환경이 가혹해짐에 따라 보다 우수한 일시 방청성과 내식성이 요구되고 있다. 본 연구는 tetraethoxysilane (TEOS), methacryloxypropyltrimethoxysilane (MPTMS) 무기성분과 multifuncitional trimethylolpanetriacrylate(TMPTA) 그리고 1,6-Hexanediol diacrylate(HDODA) 등의 유기성분을 갖는 유무기 하이브리드 솔젤(sol-gel)1)을 제작하여 각 조건에 대하여 표면 관찰 및 염수분무시험을 통한 내식성 평가를 진행하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.163-163
• /
• 2017

철강재는 대량 생산이 가능하여 경제성이 뛰어나고 기계적 성질도 우수하여 다양한 산업 분야에서 널리 사용되고 있다. 그러나 철강재는 부식 환경에 취약하기 때문에 그 용도에 따라 다양한 내식성을 부여하는 표면처리를 적용하고 있다. 이러한 철강재에 대한 내식성 표면처리로는 용융아연도금(HDG)과 용융알루미늄도금(HDA)이 우수한 내식성과 다양한 특성으로 널리 사용되고 있으며 아연과 알루미늄을 접목시킨 갈바륨(GL)도금 또한 우수한 내식성 코팅으로 알려져 있다. 또한 최근에는 기존 용융아연도금에 알루미늄(Al) 과 마그네슘(Mg)을 첨가한 3원계 도금강판이 개발되어 기존 용융도금강판 대비 고내식 코팅으로 알려져 있으며 그 적용은 점차 확대되고 있는 추세이다. 일반적으로 이와 같은 강판소재의 내식성 평가에 대해서는 실제 사용할 환경에 폭로하여 비교-시험 하는 것이 가장 확실하고 신뢰도가 높은 방법이다. 그러나 이러한 방법은 경우에 따라 수년에서 수십년에 이르는 장시간이 소요된다. 그러므로 이 방법을 대체하기 위한 각종 가속적 부식 시험들이 널리 적용되고 있다. 즉, 그 목적이나 용도에 따라 염수분무(SST), 침지(Immersion) 및 전기화학적 분극(Polarization) 등 실내에서 부식 시험 하는 방법이 사용되고 있다. 한편, 이러한 부식 가속 시험들은 실제 외부에서 폭로 시험한 결과와의 상관성이 불명확한 경우가 많아 종종 해석에 어려움을 갖고 있는 실정이다. 또한 이 시험 방법들은 동일 재료를 시험하더라도 시험방법의 차이에 따라 부식요인이나 해석방법이 다르므로 인해 그 내식성 결과가 다르게 나타날 수 있다. 그 중 시험목적에 따라 전기화학적 분극 또는 임피던스 분광법(EIS)과 건조 및 습윤 등의 부식 환경 인자들을 적용한 복합부식시험(CCT) 방법은 근사한 대안으로 주목받고 있다. 하지만 이들 시험 또한 실제 부식 환경과는 여러 환경 및 요인들이 다르기 때문에 그 시험방법에 따라 목적하는 시험 결과가 상이하게 나타날 수 있어 해석-평가 하기에 종종 곤란을 갖는다. 이에 따라 최근에는 재현성이 우수하고 실제 부식 환경을 유사하게 모사할 수 있는 내식성 시험과 해석-평가에 대한 내용이 주요한 과제로 사료되고 있다. 본 연구에서는 다양한 내식성 코팅 강판소재들에 대하여 염수분무(SST), 복합부식(CCT), 갈바닉 시험, EIS 시험을 통하여 부식시험 종류 및 시험 환경, 코팅 소재 별 부식경향을 비교-분석하고자 하였다. 또한 이들 부식 진행과정에서는 미세구조관찰(SEM), 결정구조 분석(XRD) 및 원소조성 분석(EPMA)을 통해 다양한 조건에 따른 강판소재들의 부식경향을 비교-평가하고, 실제 환경과의 상관성 및 가속관계를 도출하고자 하였다.