• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.1
• /
• pp.40-44
• /
• 2022

Wet etching of α-Ga₂O₃ epitaxy film was performed using a 35 % hydrochloric (HCl) acid solution. As the temperature of the 35 % HCl solution increased, the α-Ga₂O₃ etch rate increased, and the etch rate of 119.6 nm/min was obtained at 75℃, the highest temperature examined in this work. The activation energy for etch reaction was determined to be 0.776 eV, and this suggests that the wet etching of α-Ga₂O₃ in the 35 % HCl solution was dominated by the reaction-limited mechanism. AFM analysis showed that the surface roughness of the etched surface increased as the temperature of the etchant solution increased.

• KSBB Journal
• /
• v.15 no.3
• /
• pp.285-292
• /
• 2000

Support media for yeast immobilization was prepared from a porous volcanic rock used as a moisturizer in orchid growing. The rock was broken to the size of 2-3 mm and burned at $600^{\circ}C$ in a furnace in order to remove organic materials blocking the pores or treated with HCI solution or NaOH solution to remove the inorganic dirts by dissolving. Even through both the acid and the akali solution were effective the latter was not recommendable because it broke the pore structure by dissolving the elements of the media. This media was mainly consisted of SiO2 with $Al_2O_3$ as a minor component and CaO and K2O as trace elements. It had the finely developed pores of $15-80\mu\textrm{m}$size. Yeast immobilization capacity of this media was about $5{\times108}$ cells/ml bed which is large enough to be used for the practical applications. Yeast immobilization capacities of Alumina and Cordierite were much smaller than that of silica-based media. Scanning electron micrograph of Cordierite and Alumina showed uneven surfaces and small size of pores in contrast to relatively smooth surface and large pores of silica based media which means that smooth surface and large pores are desirable for the good adsorption of microbes on the media.

• Applied Biological Chemistry
• /
• v.20 no.1
• /
• pp.43-57
• /
• 1977

In order to establish methods of potato processing for mixed cooking with rice as main diet, treatment for polyphenol oxidase inactivation in potato tissues, and safety in regard to sanitation were studied. The results were summarized as follows: 1. Cut potato granule which were blanched in boiling water are practical and best in color within $3{\sim}6\;minutes$ dipping. 2. Dipping treatment of potato granules in a saline solution is not pratical because of the resulting color and saline taste. 3. Dipping treatment of potato granules in a boiling saline solution is not practical because of residual salt. 4. Dipping treatment of potato granules in low concentration of hydrochloric acid solution is not effective in color changes but dipping treatment from 0.1N concentration for 4-10 minutes to 0.5N concentration for $1{\sim}10minutes$ shows good effects. 5. Dipping treatment in boiling hydrochloric acid solution of 0.04-0.068N concentration for 3-5 minutes dipping is practical for its resulting color. 6. Dipping treatments in 0.05% of $K_2S_20_5$ solution for $50{\sim}60\;minutes$ and in 0.06% for $40{\sim}60\;minutes$ and 0.065% for $10{\sim}60\;minutes$ shows a small palatability in color but its boiled potato granules shows good color 7. Treatments for any time in $0.01{\sim}0.03%$ of boiling $K_2K_20_5$ solution after predipping in its cold solution for longer time than 30minutes show effective in the color and palatability of the potato granules and their cooked ones. 8. From the view of food sanitation, dipping treatment of the potato granules in the solution of $K_2S_20_5$ is safe because of the few residual amount of $SO_2$. 9. All the methods of treatment that potato granules are dipped for any time at 0.01% of $K_2S_20_5$ solution are safe from the view of fond sanitation. At 0.03% of $K_2S_20_5$ solution, nothing but the methods of treatment that they are dipped within 30 minutes and boiled within 4 minutes are safe.

• Applied Chemistry for Engineering
• /
• v.10 no.6
• /
• pp.895-901
• /
• 1999

The acid characteristics of ${\beta}$-zeolites was modified by the different calcination conditions in order to remove template and the post-treatments such as ammonium ion exchange and HCl treatment. Alkylation of benzene with propene and isopropanol was carried out over the catalysts to investigate the effect of acid characteristics on the selectivity to cumene in this reaction. The $Br{\ddot{o}}nsted$ acidity(IR $3610cm^{-1}$ band) of ${\beta}$-zeolite was significantly reduced by a deep bed calcination compared to that of ${\beta}$-zeolite calcined in a shallow bed. Moreover, extraframework aluminum species which did not show acidity were produced by the framework dealumination on the deep bed calcined ${\beta}$-zeolite. $Br{\ddot{o}}nsted$ acidity of deep bed calcined ${\beta}$-zeolite was significantly recovered by ammonium ion exchange, however, it was partially recovered by a weak HCl treatment. It was found that the framework aluminum as well as the extraframework aluminum were extracted by a strong HCl treatment. The selectivity to cumene was shown to be about 95% on the shallow bed calcined ${\beta}$-zeolite, however, it decreased to 90% on the deep bed calcined one. The post-treatment such as ammonium exchange and weak HCl treatment enhanced the selectivity to cumene up to 93% by the partial recovery of $Br{\ddot{o}}nsted$ acidity. Propene was proved to be a good alkylating agent for the selectivity to cumene compared to isopropanol.

• Clean Technology
• /
• v.26 no.4
• /
• pp.270-278
• /
• 2020

Palladium (Pd) has been widely used in various industrial applications such as jewelry, catalyst, and dental materials despite its limited resources. It has been gaining attention to recover Pd with high purity from the spent materials. This study investigated the optimum conditions for the leaching and recovery of metallic Pd. The leaching parameters are HCl concentration, temperature, time, concentration of oxidants, and pulp density. 97.2% of Pd leaching efficiency was obtained in 3 M HCl with 3 vol% oxidants at 80℃ for 60 min. The ratio of hydrogen peroxide to sodium hypochlorite played a critical role in the leaching efficiency due to the supply of Cl- ions in the leachate. Moreover, the complete recovery of Pd in the leachate was achieved at 80℃ with 0.3 formic acid/leachate after adjusting the pH value of 7. This situation was ascribed to the decomposition of formic acid into hydrogen gas and carbon dioxide at 80℃. ICP-AES and XRD characterized the recovered Pd powder, and the purity of the recovered powder was found to be 99.6%. Consequently, the recovered Pd powder with high purity could be used in circuits, catalyst precursors, and surgical instruments.

• Resources Recycling
• /
• v.21 no.5
• /
• pp.50-57
• /
• 2012

A comparative study has been carried out on the removal of impurities such As, Sb, Bi from the copper sulfate solution by ion exchange resin containing aminophosphosphonic acid as functional group. The various parameters which affect the removal of impurities; such as the reaction temperature, the reaction time, the amount of ion-exchange resins, the concentration of sulfuric acid in electrolyte, were studied. The basic experimental results showed that about 88% of Sb & 94% of Bi can be adsorbed in these chelate resins and removed from the copper sulfate solutions but As was removed below 10% from the solutions. And the selective elution of Bi and Sb from the adsorbed ion exchange resin also can be achieved by $H_2SO_4$ or HCl solutions. The results also showed that 98.1% of Sb and 96.6% of Bi can be adsorbed from the copper sulfate solutions after 2 Bed-volume of continuous ion exchange column test.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.166-170
• /
• 2000

Amorphous calcium carbonate was prepared by wet chemical method and performed the control of their shape using crystalline calcium carbonate that prepared from oyster shell by the $CO_2$ gas blowing method. As a result, amorphous calcium carbonate was obtained by the dissolution process of crystalline calcium carbonate in the dil-HC1 solution, mixing of sodium carbonate solution, precipitation and filtering with high speed. And using the amorphous calcium carbonate of mud type, crystalline calcium carbonates with cubic, needle, spindle, spherical and plate shape were obtained in the temperature rang of 2~$85^{\circ}C$ and reaction time range of 5~60 minute.

• Resources Recycling
• /
• v.19 no.5
• /
• pp.3-12
• /
• 2010

Platinum group metals with high purity are important raw materials for high technology industry. Since there are no domestic ores containing PGMs, it is of importance to develop a separation process by which ultra pure PGMs can be recovered from diverse spent resources. Data on the chemical properties and dissolution behavior of PGMs were obtained from the literature. A method for the thermodynamic analysis of the HCl solution with chlorine gas was introduced. Utilizing the difference in the chemical properties and dissolution behavior of PGMs would lead to an efficient separation process to recover ultra pure PGMs.

• Applied Chemistry for Engineering
• /
• v.5 no.1
• /
• pp.24-29
• /
• 1994

The zeolite X was prepared from the Korean natural clinoptilolite, which contains some mordenite. Thermal treatment removed the clinoptilolite structure from the ore remaining mordenite. The natural clinoptilolites dealuminated with 2N-8N HCI solution and/or thermal treatment were mixed with NaCl, $NaAlO_2$ and NaOH, and reacted to zeolites X at $95^{\circ}C$ for 12~36 hrs. Maximum yield of NaX was obtained for the reactant mixture of 25 gr of natural zeolite acidtreated with 8 N HCI, together with 3.5g NaCl, 8g $NaAlO_2$ and 50 ml of 6N NaOH at $95^{\circ}C$, for 24 hrs.

• Korean Journal of Food Science and Technology
• /
• v.22 no.5
• /
• pp.582-589
• /
• 1990

A method for application of the equivalent time and temperature point for estimating kinetic parameters was proposed. The feasibility of the method was demonstrated with both theoretical and empirical kinetic data. The theoretical kinetic data were obtained from the arbitrarily chosen time-temperature data for three chemical reactions whose kinetics are well established. The experimental kinetic data were obtained for the acid (0.0005 N HCl) catalyzed hydrolysis of sucrose(2%). The activation energy and the frequency factor determined by the proposed method were $104.74{\pm}1.87kJ/mol\;and\;5.62{\times}10^{14}\;hr^{-1}$ respectively and the results agreed well with those obtained by a different method of kinetic parameter estimation, i.e. the linearly increasing temperature method.