In this paper, in order to develop Pb-free piezoelectric ceramics, $[Li_{0.04}(Na_{0.44}K_{0.52})-(Nb_{0.86}Ta_{0.10}Sb_{0.04})]O_3$ ceramic was fabricated with the variation of ZnO addition. Piezoelectric properties of the ceramic were varied with the amount of ZnO addition and showed the maximum kp value at 0.2 wt% ZnO addition. Qm of ZnO added ceramics showed lower values than the non-added ceramics, however, the kp was increased by the addition of ZnO up to 0.2 wt%. At the sintering temperature of 1110$^{\circ}C$ and the calcination temperature of 850$^{\circ}C$, the optimal values of density=473g/$cm^3$, kp=0.473, $\varepsilon_r$=1403 were obtained.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.216-217
• /
• 2005

In this paper, in order to develop Pb-free piezoelectric ceramics, $(Li_{0.05}Na_{0.57}K_{0.38})NbO_3$ ceramic was fabricated with the variation of $Bi_2O_3$ addition. Piezoelectric properties of the ceramic were varied with the amount of $Bi_2O_3$ addition and showed the maximum kp value at.0.2 wt% $Bi_2O_3$ addition. Qm of $Bi_2O_3$ added ceramics showed lower values than the non-added ceramics, however, the kp was increased by the addition of $Bi_2O_3$ up to 0.2 wt%. At the sintering temperature of 1110$^{\circ}C$ and the calcination temperature of 850$^{\circ}C$, the optimal values of density=4.52g/$cm^3$, kp=0.47, $\varepsilon_r$=400 were obtained.

• Proceedings of the KIEE Conference
• /
• 2000.11c
• /
• pp.413-415
• /
• 2000

Piezoelectric ceramics of PZT have been developed to apply for transformers in notebook. Use of piezoelectric ceramics in applications like piezoelectric transformers was made possible by the development of new materials with high electromechanical coupling coefficients and high mechanical quality factor. "Hard" ferroelectiric ceramics of complex composition based on lead zirconate titanate with Mn additive have been prepared. The perovskitic phase reaction of the oxides. The crucial role played by the intermediate mixing and grinding procedures in the assessment of the final properties of the material was investigated. Densification up to approximately the theoretical density value was achieved. The polarization was obtained by subjecting the samples at $30kVcm^{-1}$ poling electric field, in a silicon oil bath heated at $110^{\circ}C$. Their microstructural and morphological properties were checked by X-ray diffraction analysis and scanning electron microscopy. The optimized samples presented very high qualify and electromechanical coupling factors, together with small dielectric loss.

• Journal of the Korean Solar Energy Society
• /
• v.28 no.3
• /
• pp.53-59
• /
• 2008

This paper reports an experimental investigation to design a tree-shaped wind power system using piezo-electric materials. The proposed system is to produce power if wind is strong enough to produce any bending motions in the energy converting elements, i.e., piezo-electric materials. Two different kinds of piezoelectric materials are used in the present study to produce power by scavenging energy from the wind. The soft flexible one made the leaf element while the hard one was applied to the trunk portion of the tree requiring rather strong winds to generate any power. Although small, each leaf deems to play the role of a power producer and currents are continuously trickling down to the storage battery installed at the bottom of the system.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.3
• /
• pp.220-226
• /
• 2000

The piezoelectric material for piezoelectric transformer needs the high electromechanical coupling factor( $k_{p}$) the piezoelectric constant( $d_{33}$) and the mechanical quality factor( $Q_{m}$)in order to obtain high voltage step-up ratio and low temperature rising. In this study the piezoelectric transformers were fabricated using Pb［$Zr_{0.45}$/ $Ti_{0}$48//L $u_{0.02}$(M $n_{1}$3//S $b_{2}$3/)$_{0.05}$］ $O_3$(PMS-PZT) and Pb［Z $r_{0.25}$/ $Ti_{0.375}$(M $g_{1}$3//N $b_{2}$3/)$_{0.375}$］ $O_3$+0.5wt%Mn $O_2$(PMN-PZT) ceramics. The piezoelectric properties of PMS-PZT and PMN-PZT were measured. The voltage set-up ratios of the piezoelectric transformers using PMS-PZT and PMN-PZT were the value of 15, 20 respectively under 100$_{KΩ}$ in Rosen type transformer.r.ormer.r.r.r.r.r.r.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.277-278
• /
• 2007

In this study, in order to develop multilayer piezo-actuator, PMN-PNN-PZT ceramics were fabricated using $Li_2CO_3,\;Na_2CO_3$, ZnO as sintering aids and their piezoelectric and dielectric properties were investigated according to the Bi substitution. Bi substitution enhanced electromechanical coupling factor$(k_p)$ and dielectric constant$({\varepsilon}_r)$. However, mechanical quality factor was deteriorated. At the sintering temperature of $870^{\circ}C$ and Bi substitution of 1mol%, density, electromechanical coupling factor$(k_p)$, mechanical quality factor$(Q_m)$, Dielectric constant$({\varepsilon}_r)$ and piezoelectric constant$(d_{33})$ of specimen showed the optimum value of $7.878g/cm^3$, 0.608, 835, 1603 and 397pC/N, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.305-306
• /
• 2005

In this paper, in order to develop Pb-free piezoelectric ceramics, $(Li_{0.04}Na_{0.44}K_{0.52})(Nb_{0.86}Ta_{0.10}Sb_{0.04})O_3$ ceramics were fabricated with the variation of calcination temperature and sintering temperature. Specimens couldn't be sintered below $111^{\circ}C$ and showed the largest density at calcination temperature of $800^{\circ}C$. Specimens manufactured with the variation of calcination temperature showed pseudo-tetragonal phase, and showed the optimal values of kp=0.45, ${\varepsilon}r$=1336 and $d_{33}$=254 at calcination temperature of $800^{\circ}C$ and sintering temperature of $1110^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.344-345
• /
• 2006

In this study, in order to develop low temperature sintering piezoelectric transformer, $(Pb_{0.99-x}Ca_xSr_{0.01})Ti_{0.96}(Mn_{1/3}Sb_{2/3})_{0.04}O_3$ ceramic systems were fabricated using $Na_2CO_3-Li_2CO_3$ as sintering aids and investigated with the amount of Ca substitution. The piezoelectric transformer requires high electromechanical coupling factor $k_t$ and high mechanical quality factor $Q_{mt}$ for generating high output power At the ($PbCaSr)Ti(MnSb)O_3$ ceramics with 24mol% Ca substitution sintered at $900^{\circ}C$, electromechanical coupling factor $k_t$ and mechanical quality factor $Q_{mt}$ showed the optimal values of 0.504 and 1655 respectively, for thickness vibration mode multilayer piezoelectric transformer application.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.8 no.5
• /
• pp.995-999
• /
• 2007

The lead zirconate titanate (PZT) powders were synthesized to make the piezoelectric ceramics in low temperature as low as $900^{\circ}C$. To investigate the influence of additives on sintering of PZT, two kinds of sintering aids were made as follows; $wB_2O_3-xBi_2O_3-zCuO$and LiBiO2-CuO. The sintering aid, $1{\sim}3$ wt.% $LiBiO_2-CuO$, was added into these PZT powders and the specimens were fired at temperature in the range of $800{\sim}1200^{\circ}C$. The highest density was shown in the specimen with 1 wt.% $LiBiO_2-CuO$ as additive at temperature of $900^{\circ}C$. The sintered specimen were analyzed by X-ray diffraction(XRD) and scanning electron microscopy (SEM) was utilized to observe the microstructure, especially the densified morphology of specimens. In the XRD pattern, the well-crystallized PZT phase could be obtained in consequence of firing at $900^{\circ}C$. The scanning electron microscopy(SEM) was utilized to observe the structure of specimens after firing at $900^{\circ}C$. The densified perovskite structure of $PbZrTiO_3$ could be obtained by sintering at temperature as low as $900^{\circ}C$. The high sinterability of PZT ceramics was attributed to the low formation temperature of the liquid phase of additives.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.36 no.4
• /
• pp.341-350
• /
• 2023

The templated grain growth (TGG) method has gained significant attention for its ability to produce highly textured piezoelectric ceramics with significantly enhanced performance, making it a promising method for transducer and actuator applications. However, the texturing process using the TGG method requires the optimization of multiple steps, which can be challenging for beginners in this field. Therefore, in this tutorial, we provide an overview of the TGG method mainly based on our previous published works, including its various processing steps such as synthesizing anisotropic-shaped templates with size and size distribution control using the molten salt synthesis technique, tape casting, and identifying key factors for proper alignment of the templates in the target matrix system. Our goal is to provide a resource that can serve as a basic reference for researchers and engineers looking to improve their understanding and utilization of the TGG method for producing textured piezoelectric ceramics.