• Journal of the Korean Applied Science and Technology
• /
• v.32 no.2
• /
• pp.188-193
• /
• 2015

Blast Furnace Slag is good for enhancing the qualities of concrete such as reducing hydration heat increasing fluidity, long-term strength and durability, but it has some problems: construction time is increased or the rotation rate of form is decreased due to low development of early strength. In this study, an aqueous alkali solution for alkali activated reaction was obtained by the electrolysis using concentrated water discharged from seawater desalination process. Prepared aqueous alkali solution was applied to produce mortars using blast furnace slag. The results can be summarized as follows : For the mortar, compressive strength was decreased below 2% of NaOH and increased below 6% of NaOH. And compressive strength was increased gradually with increasing NaOCl contents. However, NaCl contents of mortars caused a decrease of 28days strength above early strength.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.613-616
• /
• 2008

Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. Instead, the source of material such as fly ash and blast slag, that are rich in Silicon(Si) and Aluminium(Al), are activated by alkaline liquids to produce the binder. Hence concrete with no cement is effect reduction of CO$_2$ gas. In this study, we investigated the influence of the workability and compressive strength of mortar on water reducing agent, alkaline activator and curing method in oder to develop cementless blast slag based alkali-activated mortar. In view of the results, we found out that the flowability of mortar was lowered as increasing to mole concentration of NaOH, but not large the loss of flowability to 9M NaOH, most of water reducing agent was not effect. The compressive strength was improved as increasing to mole concentration of NaOH, was the most effect in 9M NaOH. The curing temperature and curing conditions on compressive strength of blast slag based alkali-activated mortar didn't influence.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2015.07a
• /
• pp.216-217
• /
• 2015

This study consist of research on the strength development properties of alkali activated slag(AAS) by differential combination of activators, initial protecting and curing conditions. 3 type of binders cured in the atmosphere, underwater and sealed were estimated compressive strength of 3, 7 and 28 days. Test results showed that strength development properties of binders varied with initial protecting and curing conditions because of ionized anions in pore water.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.63-71
• /
• 2011

Portland cement production is under critical review due to high amount of $CO_2$ gas released to the atmosphere. Attempts to increase the utilization of a by-products such as fly ash and ground granulated blast-furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. In this study, we investigated the influence of alkali activator and superplasticizer on the flowability and compressive strength of the alkali-activated mortar in oder to develop cementless alkali-activated concrete using blast furnace slag. In view of the results, we found out that the type and mixture ratio of alkali activator, the type and adding order of superplasticizer results to be significant factors. When cementless alkali-activated mortar using blast furnace slag manufactured with 1:1 the mass ratio of 9M NaOH and sodium silicate, and added superplasticizer before alkali activator in the mixer, we can be secured workability with 180 mm of flow during 1 hours and compressive strength of about 50 MPa under $20^{\circ}C$ curing condition at age of 28days.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.315-316
• /
• 2010

The purpose of this study is to observe the effect of mixture ratio of alkali-activator on workability and compressive strength of alkali-activated mortar that using fly ash and blast furnace slag.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.2
• /
• pp.63-69
• /
• 2012

Recently, the cement industries brought very severe environment problems such as resource depletion and global warming with massive carbon dioxide during its production. The number of cases using industrial by-products such as the ground granulated blast furnace slag (GGBFS) in concrete mixtures is increasing to resolve the environmental issue. GGBFS is mainly used in the range between 20 to 50% to replace cement, but nowadays lots of researches are carried out to develop the alkali-activated slag (AAS) concrete with no cement. In this study, the early age properties of alkali activated slag (AAS) mortar are investigated to obtain the fundamental data for AAS concrete application to structural members. The experimental variables were the water-binder ratios of 0.3, 0.4, and 0.5 and NaOH as the alkali activator of 4%, 8%, and 12% by the mass of GGBFS, and compressive strength, flow, setting time, and ultrasonic pulse velocity of AAS mortars were measured and analyzed. It is found from the test results that as the normal concrete the lower W/B, the higher compressive strength. However, superplasticizer has to be used for producing high strength AAS concrete because the workability of AAS mortar are significantly lowered.

• Journal of the Korea Concrete Institute
• /
• v.25 no.3
• /
• pp.305-312
• /
• 2013

This paper reports the results of an investigation into the effects of silica fume on strength properties of alkali-activated slag cement (AASC) with water-binder (W/B) ratio and replacement ratio of silica fume content. The W/B ratio varied between 0.50 and 0.60 at a constant increment of 0.05. The silica fume content varied from 0% to 50% by weight of slag. The activators was used sodium hydroxide (NaOH) and the dosage of activator was 3M. The strength development with W/B ratio has been studied at different ages of 1, 3, 7 and 28 days. For mixes of AASC mortars with varying silica fume content, the flow values were lower than the control mixes (without silica fume). The flow value was decrease as the content of silica fume increase. This is because the higher surface areas of silica fume particles increase the water requirement. The analysis of these results indicates that, increasing the silica fume content in AASC mortar also increased the compressive strength. Moreover, the strength decreases with the W/B ratios increases. This is because the particle sizes of silica fume are smaller than slag. The high compressive strength of blended slag-silica fume mortars was due to both the filler effect and the activated reaction of silica fume evidently giving the mortar matrix a denser microstructure, thereby resulting in a significant gain in strength.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.05a
• /
• pp.240-241
• /
• 2018

In this paper, we tried to find the proper ratio of industrial byproducts which can express mechanical characteristics similar to ordinary portland cement by varying the ratio of industrial byproducts. as a result, the activated slag binder produced by the industrial byproduct in this study increased in compressive strength as the ratio of blast furnace slag increased and the fly ash ratio decreased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.2
• /
• pp.94-101
• /
• 2016

This paper presents an investigation into the durability alkali-activated materials(AAM) mortar and paste samples manufactured using fly-ash(FA) and ground granulated blast furnace slag(GGBFS) exposed to a sulfate environment with different GGBFS replace ratios(0, 30, 50 and 100%), sodium silicate modules($Ms[SiO_2/Na_2O]$ 1.0, 1.5 and 2.0) and initial curing temperatures($23^{\circ}C$ and $70^{\circ}C$). The tests involved immersions for a period of 6 months into 10% solutions of sodium sulfate and magnesium sulfate. The evolution of compressive strength, weight, length expansion and microstructural observation such as x-ray diffraction were studied. As a results, as higher GGBFS replace ratio or Ms shown higher compressive strengths on 28 days. In case of immersed in 10% sodium sulfate solution, the samples shows increase in long-term strength. However, for samples immersed in magnesium sulfate solutions, the general observation was that the compressive strength decreased after immersion. The most drastic reduction of compressive strength and expansion of weight and length occurred when GGBFS or Ms ratios were higher. Also, the XRD analysis of samples immersed in magnesium sulfate indicated that expansion of AAM caused by gypsum($CaSO_4{\cdot}2H_2O$); the gypsum increased up to 6 months continuously.

• Journal of Korean Society of Water and Wastewater
• /
• v.30 no.3
• /
• pp.293-297
• /
• 2016

This study was performed in order to obtain the effect of the compressive strength of the cured product with manufacturing conditions (amounts of fine aggregate and different types of alkali activator). Material which is the basis of the cured product was used for the blast furnace slag, which has a latent hydraulic activity. Consequently, when using sodium hydroxide as the alkali activator, it is possible to obtain a higher compressive strength than using the calcium hydroxide. And also, it can be added a 10% of fine aggregate with blast furnace slag to improve the compressive strength.