• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2005.05a
• /
• pp.97-102
• /
• 2005

본 연구에서는 국내 재생 알루미늄업체에서 발생된 알루미늄 폐드로스를 수산화나트륨 용액으로 침출하여 폐드로스 중의 잔류 알루미늄을 용액 상으로 침출, 분리시키고, 침출용액 중에서 알루미늄 성분을 수산화알루미늄으로 회수하였으며 침출이 안 된 폐드로스 잔사는 수세, 건조, 배소 과정을 거쳐 알루미나질 내화물 원료로 재활용하는 연구를 수행하였다. 그리고, 1일 4톤의 알루미늄 폐드로스를 처리할 수 있는 규모의 파일롯트 플랜트를 건설, 시운전함으로써 연구결과의 상용화 가능성을 제시하였다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.10
• /
• pp.4672-4678
• /
• 2013

Aluminum dross is formation at the surface of the molten metal as the latter reacts with the furnace atmosphere and it was an unavoidable by-product of the aluminum production process. However aluminum dross was usually landfilled or disposed without treatment, causing much environmental damage. The purpose of this study is to investigate the possibility of ceramic catalyst support using recycled Al dross. The recycled Al dross was made into SCR catalyst by mixing with $WO_3$, $V_2O_5$ and $TiO_2$. The $V_2O_5-WO_3/TiO_2-Al_2O_3$ SCR catalyst was observed with XRF, XRD and BET. $V_2O_5-WO_3/TiO_2-Al_2O_3$ SCR strength was measured by Universal Testing Machine(UTM). As the added $Al_2O_3$, streagth is increased. And the NOx removal activity was observed by MR(Micro-Reactor). The temperatures ranging from $350^{\circ}C$ and $400^{\circ}C$, $V_2O_5-WO_3/TiO_2-Al_2O_3$ SCR catalyst De-NOx performance result of showed excellent activity over 90% at application condition.

• Ceramist
• /
• v.12 no.2
• /
• pp.13-19
• /
• 2009

• Resources Recycling
• /
• v.28 no.4
• /
• pp.44-50
• /
• 2019

In the electric arc furnace process, the chemical energy such as the heat of oxidation reaction and the heat of carbon combustion etc. is consumed as 30% of the total input energy. In order to reduce $CO_2$ emission in EAF, it is necessary to decrease the use of electric power energy during scrap melting stage and increase the use of chemical energy. In general, when the carbon materials is individually charged into the molten steel, the carbon materials floated to the slag layer due to low density before it is dissolved in molten steel. When the concentration of carbon in the molten steel is high, the combustion energy of carbon by oxygen injection can lower the electric power energy and improve the chemical energy consumption. Therefore, an efficient charging methods of carbon material is required to increase the efficiency of carbon combustion heat. On the other hand, Al-dross, which is known as a by-product after Al smelting, includes over 25 mass% of metallic Al, and the oxidation heats of Al is lager than that of carbon. However, the recycling ratio fo Al-dross was very low and is almost landfilled. In order to effectively utilize the heats of oxidation of Al in Al-dross, it is necessary to study the application of Al-dross in the steel process. In this study, the dissolution efficiency of carbon and aluminum in molten steel was investigated by varying the reaction temperature and the mixing ratios of coke and Al-dross.

• Resources Recycling
• /
• v.26 no.6
• /
• pp.58-64
• /
• 2017

Leaching of black dross with HCl solution was conducted to find a suitable process to recover valauble materials. In this work, the leaching behavior of the components was compared between black dross and the residues after water treatment. All the components except $TiO_2$ in the black dross were dissolved by HCl solution in the experimental ranges. Treatment of the black dross with water to recover the salts has negative effect on the leaching of $Al_2O_3$, MgO and $SiO_2$. The reactions occuring during the leaching were discussed. At an optimum leaching condition of 3 M HCl and $90^{\circ}C$, the leaching percentage of $Al_2O_3$, MgO and $SiO_2$ was 85, 100 and 40%, respectively.

• Resources Recycling
• /
• v.29 no.6
• /
• pp.65-72
• /
• 2020

Black dross is a dark gray dross generated during the aluminum recycling process that uses flux, and contains NaCl, KCl, Al2O3, MgO, etc. Black dross is separated into soluble substances (NaCl, KCl) and insoluble substances (Al2O4, MgO) through the dissolution process. Soluble materials can be reused as salt flux, and Al2O3 and MgO can be upcycled to various ceramic materials through the synthesis process. In this study, Mayenite was synthesized using Al2O3 and MgO recovered from black dross, and the synthesis was performed according to the mixing ratio and reaction temperature. It was confirmed that when Mayenite was synthesized using black dross (spinel) and CaCO3, precursors were changed to Mg0.4Al2.4O4 and CaO at 700 ℃, and to Ca12Al14O33 (Mayenite) after 800 ℃. In the mixing conditions experiment, it was confirmed that the Mayenite XRD peak increased with increase of the CaCO3 content, and the Mg0.4Al2.4O4 XRD peak decreased. As a result of the BET analysis of the synthesized powder, the surface area decreased as the fine particles were grown and agglomerated in the process of generating mayenite.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 1993.03a
• /
• pp.8-8
• /
• 1993

• Resources Recycling
• /
• v.14 no.2
• /
• pp.19-27
• /
• 2005

The recycling possibility of aluminum waste dross(AWD) as a ceramic raw material of porous light-weight material was examined. A aluminum waste dross was washed 4-7 consecutive times and roasted at 900$^{\circ}% for 1hour as pre-treatments. The properties of the pre-treatment of aluminum waste dross was investigated. It was conformed by XRD result that the spinel crystalline was grown in AWD, after roasting. After the roasted AWD was ground in aqueous state, the sodium hexaphosphate(SHP) as a dispersant which is used for stabilizing the concentrated slurry was added to the AWD slurry. The porous material was prepared by slurry foaming method with surfactant at room temperature. The foamed slurry volumes were 2 and 3 times of the original slurry volume. The properties of porous material with extended volume of 3 times was following: the porosity was about 84%, bulk density was 0.59 g/cm$^3$, the range of pore was from 50 ${\mu}m$ to 500 ${\mu}m$ and mean pore size was about 200 ${\mu}m$. AWD porous material was sintered at 1150$^{\circ}C-1250$^{\circ}C. It was colcluded that AWD was sintered well at 1200$^{\circ}C from material surface observation by SEM.

• Resources Recycling
• /
• v.28 no.4
• /
• pp.23-29
• /
• 2019

In order to recover pure alumina from balck dross, precipiatation experiments were done to the NaOH leaching solution of mechanically activated black dross. In this work, hydrogen peroxide was added to the synthic solution as a precipitating agent. Among some variables, the concentration of $H_2O_2$ and the volume ratio of $H_2O_2$ to solution showed a remarkable effect on the precipitation of aluminum hydroxide. At the optimum conditions, most of the aluminate was precipitated. Calcination of the aluminum hydroxide at $1200^{\circ}C$ led to the formation of ${\theta}$ and ${\alpha}$-alumina. The charactistics of the synthesized activated alumina was measured by XRD and EDS. The average particles size of the alumina was $3.73{\mu}m$.

• Resources Recycling
• /
• v.28 no.2
• /
• pp.54-61
• /
• 2019

In order to recover pure alumina from black dross, leaching of mechanically activated black dross with NaOH solution resulted in an aluminate solution containing a small amount of Si(IV). Selective adsorption of Si(IV) onto hydrotalcite was investigated from 5 M NaOH solution where the concentration of Al(III) and Si(IV) was 13000 and 150 mg/L, respectively. Only Si(IV) was selectively loaded onto hydrotalcite, while Al(III) remained in the solution. Effect of the calcination treatment of hydrotalcite and concentration of calcined hydrotalcite and NaOH on the loading of Si(IV) was investigated. Although the loading percentage of Si(IV) was low from 5 M NaOH solution, most of the Si(IV) was removed by adjusting the concentration of NaOH by 48 times dilution with water when the concentration of calcined hydrotalcite was higher than 4.5 g/L. The loading of Si(IV) onto calcined hydrotalcite followed Freundlich adsorption isotherm.