• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.1
• /
• pp.84-92
• /
• 2014

The purpose of study is to analyze mechanism with early high portland cement and hardening accelerator. As the result, it was concluded that hardening accelerator makes accelerates appearance of $Ca(OH)_2$ through experiment using TG-DTA when it hydrates with cement. On the result of compressive strength, as increasing the amount of hardening accelerator used, early compressive strength was improved. Also, as a result of hydration heat, hardening accelerator accelerates hydration of $C_3S$ that is cement's component. On the result of XRD's analyzation, hydration product for each age could be check and it was shown that as increasing the amount of hardening accelerator used, peak point of hydration product was recorded high. As the result of SEM, appearance of C-S-H was shown as the amount of $Ca(OH)_2$'s appearance and each age according to additive contents of hardening accelerator. Therefore hardening accelerator used on this study is effective on getting early compressive strength.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.05a
• /
• pp.195-196
• /
• 2012

In this study, it was investigated early age strength generation of low cement concrete with type and addition ratio of hydration accelerator obtaining fundamental data for the application in construction field.

• Journal of the Korea Institute of Building Construction
• /
• v.13 no.4
• /
• pp.407-415
• /
• 2013

The purpose of this research is to verify the performance of hardening accelerator in cement paste through mechanical performance evaluation and micro structure analysis on hardening accelerator for development of super high early strength concrete. The research results showed that hardening accelerator produced $Ca(OH)_2$ when hydrated with cement, enhancing the degree of saturation of Ca ion by using differential thermal analysis. Moreover, porosity was reduced rapidly as capillary pores were filled by hydration products of $C_3S$. According to the experiment using hydration measurement testing, when 1% and 3% of accelerator were mixed, hydration rate increased toward the second peak point compared to high early strength cement, before the first peak point disappeared. It turned out that adding accelerator accelerated the hydration rate of cement, especially $C_3S$. The shape of C-S-H is shown depending on the amounts of accelerator added and the production and age of $Ca(OH)_2$ by using SEM to observes hydration products. Therefore, it's evident that hardening accelerator used in this research increases amounts of $Ca(OH)_2$ and accelerates $C_3S$, it is effective for the strength development on early age.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.2
• /
• pp.135-142
• /
• 2014

The heat of hydration can be reduced through the use of retarding agents. Typical retarding agents include sugar and glucose. However, these significantly delay the setting of cement paste. For the efficient use of sugar and glucose for mass concrete construction, it is necessary to develop a technique that can provide a setting behavior equivalent to that of plain concrete. In this work, the temperature rise of cement paste was monitored with the addition of various retarders including sugar and glucose. Hydrated cement powder was made with a water to cement ratio of 5 in order to accelerate the retarded cement pastes. It was found that the addition of hydrated cement powder in retarded pastes reduced the maximum temperature of cement paste. The use of hydrated cement powder could also successfully reduce the time to reach the maximum temperature.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.1
• /
• pp.25-33
• /
• 2015

In this study, initial crack index was evaluated by FEM analysis to find the crack propagation from hydration heat in precast concrete. As results, as the usage of hardening accelerator increased, initial compressive strength increased and setting time was shortened. Additionally, as amounts of hardening accelerators increased, the central temperature of concrete increased and the time to reach the highest temperature was shortened. It was demonstrated that the hardening accelerators accelerated the hydration reaction of cement, and caused the increase of hydration heat within the short period of time. Furthermore, the crack index for evaluating the heat level was performed by FEM. As results, there was no problem about the cracks, despite of the growth of initial high hydration heat. This is because of the increased tensile strength that is large enough to sustain the thermally induced-stress.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.2
• /
• pp.153-160
• /
• 2023

In this study, nano-sized C-S-H crystals were synthesized using the liquid phase reaction method and their properties were investigated. The synthesized C-S-H crystals were added to the cement composite in suspension form to determine their effect on the hydration properties of the cement. The amount of chemical admixture was varied to obtain nano-sized C-S-H crystals with optimal agglomerated morphology, and SEM photographs were analyzed. A cleaning process was added to remove harmful substances other than the synthesiz ed C-S-H crystals. It was found that the concentration of harmful substances was reduced in the case of C-S-H crystals subjected to the cleaning process. The synthesized C-S-H suspensions were prepared with and without the cleaning process, and cement composites were prepared with the cement weight content as the main variable. The effect of C-S-H crystals on the initial hydration properties of the cement was confirmed by microhydration heat analysis. In addition, mortar specimens were prepared to measure the compressive strength over time. The test results showed that the nano-sized C-S-H crystals act as nucleation sites in the cement paste to promote the early hydration of the cement and increase the early compressive strength.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.1-10
• /
• 2013

In this study utilize industry product for OPC(ordinary portland cement) and BFS(blast furnace slag) mixing concrete early age compressive strength elevation and executed study for high strength binder. Association ratio of industry product for high strength binder manufacture is Titanogypsum (4) : Limestone (3) : Waterworks Sludge by ratio of (3) as it is proper move. high strength binder mixing rate appeared that (7~9) % are proper via preliminary test. Could confirm that display high compressive strength incidence rate in early age than plain harmony according as mix high strength binder mixing concrete compressive strength high strength binder. Also, high strength binder generality that give function than high strength binder used in existing displayed more excellent intensity, and compressive strength displayed result that multiply single breadth according as high strength binder substitute that give function increases.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.5
• /
• pp.405-412
• /
• 2016

In order to examine the possibility of practical use of concrete at low-temperature environment using high early strength cement with cold resistance admixture, an experimental study on workability, freezing temperature and compressive strength of the mortar with different types of anti-freezer, water reducing agent and accelerator for freeze protection at low-temperature were evaluated. Compressive strength was increased in use of anti-freezer, especially SN anti-freezer was higher than CN anti-freezer. 0min flow was increased, the 20min flow was decreased. And 20min flow was improved in use of FR, RT water reducing agent. CF, LS accelerator for freeze protection, regardless of the type of water reducing agent, compressive strength was increased.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.3
• /
• pp.265-271
• /
• 2015

This study is intended to produce a PC (Precast Concrete) member without a steam curing process in developing the high early strength concrete satisfying the condition of 10MPa in compressive strength at the age of 6 hours, and is intended to ensure economic feasibility by increasing the turnover rate of concrete form. Hence, high early strength cement with high $C_3S$ content and the hardening accelerator of powder type accelerating the hydration of $C_3S$ was used. And the properties of concrete were evaluated according to the hardening accelerator mixing ratio (0, 1.2, 1.6, 2.0). No big difference was found from the tests of both slump and air content. When 1.6 % or higher amounts of the hardening accelerator were mixed, the compressive strength of 10MPa was achieved at the age of 6 hours. From the test results of autogenous (drying) shrinkage and plastic shrinkage, it can be seen that there was a difference according to hydration reaction rate due to the addition of the hardening accelerator. However, it was shown that no problem arose with crack and durability. And it was shown that resistance to freezing-thawing, carbonation, and penetration were excellent.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.2
• /
• pp.156-162
• /
• 2014

This study aims to develop a rapidly hardening type of concrete to achieve the removal of form intensity (more than 10MPa) using the method of curing at room temperature in order to solve some economic environmental problems by omitting the steam curing process involved in producing PC (Precast Concrete). Therefore, this study evaluated a rapidly hardening cement containing a high amunt of C3S, which is very responsive in expressing early intensity, and a rapidly hardening type of concrete which uses some hardening accelerator to increase thehydration reaction of $C_3S$. The results of the experiment on concrete using some hardening accelerator are asfollows. In the slump flow experiment for identifying the liquidity and the air test, the desired values were met. The compression strength showed rapid expression response by 12 hours, and met the desired value within 6~9 hours. Its drying shrinkage value and Autogenous shrinkage value were measured as below ($-754.5{\times}10^{-6}$),and satisfied the requirements. In addition, in the Semi-Adiabatic Temperature Test, it was found that the concrete rose to its peak temperature within 24 hours and then its temperature dropped.