• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.309-316
• /
• 2016

In this study, performance of hardening accelerator types which promote setting and hardening of cement has been reviewed in order to develop early age strength of concrete with compressive strength of 21~27 MPa after examination of strength development of the concrete at early age according to curing temperature and unit cement(binder) content. As results, soluble mineral salt showed better hardening acceleration effect than organic salt in the scope of this study. Also, hydration reaction accelerating effect of $C_3S$ by Soluble mineral salt is effective on development of early age compressive strength and it was shown that the Pt's hydration reaction accelerating effect was the best. Construction duration reduction can be expected by securing compressive strength for prevention of early aged freezing damage in 25hour-curing time under curing temperature at $15^{\circ}C$. Also, it was shown that compressive strength of specimen cured at $5^{\circ}C$ was similar with plain specimen cured at $10^{\circ}C$. Therefore, it is expected that fuel costs and carbon dioxide can be reduced when the same construction duration is considered.

• International Journal of Highway Engineering
• /
• v.13 no.2
• /
• pp.103-114
• /
• 2011

Usage of bicycle has been supported the universal reduction of energy consumption and $CO_2$. For the same purpose, new constructions for long length bike roads are planned in Korea. Recently, laboratory tests of physical properties and resistance against environmental loading about optimum mix design of roller compacted concrete, that have advantages of high structural performance by cement hydration and aggregate interlocking, simple construction procedure and low construction cost, are performed for the effective construction of new bike roads. However, properties of roller compacted concrete had different results between laboratory and field tests since it had different compaction method. Also, construction method of roller compacted concrete are not defined for the application of bike roads since it had different demand performance such as thin pavement thickness, low strength and etc with road pavements. Thus, in this experimental research was launched to evaluate the core properties, visual inspection, compaction ratio, water content, thickness reduction rate of roller compaction, skid resistance and roughness by experimental construction about variable mix proportion and compaction method based on laboratory test results. And construction method of roller compacted concrete pavement were suggested for the application of bike roads.

• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.769-774
• /
• 2005

Fluosilicic acid(H2SiF6) is recovered as an aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded H3PO4 or HF. Generally, fluosilicates are the salts produced by the reaction of H2SiF6 and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. This study was performed to know mechanical properties and watertightness using fluosilicates based composite made from fluosilicates and other compounds. Mix proportions for experiments were modulated at 0.45 of water to cement ratio and $0.0-2.0\%$ of adding ratio of fluosilicates based composite. Evaluation for mechanical properties of concrete was conducted to know fresh state of concrete, hardening state of concrete, and watertightness. Evaluation for watertightness of concrete was carried out permeability, absorption test and porosity analysis. In addition. Scanning Electron Microscopy(SEM) and Energy Dispersive X-Ray(EDX) used for investigating micro-structure and atomic component distributed in hardened concrete. It is ascertained that characteristics of mechanical properties and watertightness was more improved than non-added because of packing role of fluosilicates based composite and pozzolanic reaction of soluble $SiO_2$. Also, concrete added fluosilicates based composite had a tendency to delay setting time and only $0.5\%$ addition of fluosilicates based composite delayed 150 minutes compared with non-added.

• Korean Journal of Construction Engineering and Management
• /
• v.7 no.2 s.30
• /
• pp.71-80
• /
• 2006

It is required to study systematical on the concrete quality management to extend structure life because rebuilding effect is reducing under present condition of large sized and high stories structure. Concrete, which shows its intensity by hydrating action and a big change in quality according to hot weather and temperature, produces a lot of quality problem under hot and cold weather. Because of each specification and construction plan which does not have basic standard on site, concrete's quality is irregular and makes some defect. As a result, Dae-gu is fumed out to be the longest area after investigating application period and days focused on 8 cities weather information about t relationship between hot weather circumstance and construction environment. Therefore, we first surveyed the curing construction processing in the region and found out the problem of quality management. Then figure out the way of solution. Moreover, we integrated curing quality management, which is applied differently to each site, to have equal quality and to reduce defect from construction site. And then, based on various test of construction condition and analysis of quality management item, we suggest effective concrete quality management to make curing construction standard guide and plan under hot weather.

• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.347-352
• /
• 2011

When concrete is worked in cold weather, the methods of using hot air, water and aggregate heating, accelerators are used to prevent early frosting and to improve early strength. But these methods raise problems such as implementation difficulty, high cost, and energy losses. Among the available cold weathering methods, accelerator method is the most economical but with the drawbacks of rapid setting and insufficient workability in the initial hydration stage. Therefore, the tablet method usually used for pharmaceutical field was applied to the accelerator method to compare the controlled reaction time of the new and old accelerator method. Based on the test results, physical and mechanical properties of concrete were tested and the possibility of delaying initial reactions to increase the total reaction time was evaluated. The results showed that when both accelerators and tablet were used, setting-time decreased. Physical properties of concrete were optimal for tablet 0.5% and 1.0%. Also, accelerator 0.5%, tablet 0.5% and 1.0% showed good early strengths.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.5
• /
• pp.104-111
• /
• 2015

This study shows the mechanical properties of alkali-activated slag cement (AASC) synthesized using sulfate with NaOH solution. The used sulfates were calcium sulfate ($CaSO_4$, denoted CS) and sodium sulfate ($Na_2SO_4$, denoted SS). The replacement ratio of sulfates was 2.5, 5.0, 7.5 and 10.0% by weight of slag. NaOH solution of 2M and 4M concentration was used. A sample was activated with sulfate and activated with blended activator (blending NaOH solution with sulfate) respectively. 24 mix ratios were used and the water-binder weight ratio for the test was set 0.5. This research carried out the compressive strength, flexural strength, ultrasonic pulse velocity (UPV), absorption and X-ray diffraction (XRD). In the case of samples with CS, sample with 7.5% CS, sample with 2M NaOH+5.0% CS and sample with 4M NaOH+5.0% CS showed the good performance in the strength development. In the case of samples with SS, sample with 10.0% SS, sample with 2M NaOH+7.5% SS and sample with 4M NaOH+2.5% SS obtained good performance in strength. The results of UPV and water absorption showed a similar tendency to the strength properties. The XRD analysis of samples indicated that the hydration products formed in samples were ettringite, CSH and silicate phases. In this study, it is indicated that when compared to the use of sulfate only, the use of both sulfate and NaOH solution makes mechanical properties of AASC better.