• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.30-39
• /
• 2022

In this study, laboratory test, program analysis, and test construction in the field were performed to utilize Supplementary Cementitious Material (SCM) developed by recycled resources for slope reinforcement as slope improvement material for aging reservoir, and the results were analyzed. As results of the laboratory test, it was analyzed that the mixing ratio of SCM was appropriate by 9 %, and the coef. of permeability was decreased by about 10,000times, indicating a value close to that of the waterproof material applied in Korea. In addition, as a result of program analysis and test construction, it was analyzed that seepage did not occur in the part of reinforced using SCM and showed a higher safety facto r than domestic criteria. Therefore, since it shows sufficient waterproof and reinforcing effects in aging reservoir, it is judged that the slope improvement using SCM can replace the cement for repair and reinforcement method.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.82-93
• /
• 2024

Since the cement industry generates more than 60 % of CO₂ during the clinker production process, supplementary cementitious materials are used worldwide to reduce CO₂ efficiently. Mainly used supplementary cementitious materials such as blast furnace slag and fly ash, which are used in various industries including the cement industry, concrete admixtures, and ground solidification materials. However, since their availability is expected to decrease in the future according to the carbon neutrality strategy of each industry, new supplementary cementitious materials should be used to achieve the cement industry's goal for increasing the additive content of Portland cement. Limestone is a material that already has a large amount in the cement industry and has the advantage of high grinding efficiency, so overseas developed countries established Portland limestone cement standards and succeeded in commercialization. This study was an experimental study conducted to evaluate the possibility of utilizing domestic PLC, the effect of fineness and replacement ratio on the physical properties of cement was investigated, and the environmental impact of cement was evaluated by analyzing CO₂ emissions.

• The magazine of the Korean Society for Advanced Composite Structures
• /
• v.5 no.4
• /
• pp.21-28
• /
• 2014

최근 증가하는 현무암 석분슬러지를 건설재료로 재활용하기 위한 방안으로, 시멘트 몰탈에서 잔골재의 일부를 현무암석분슬러지로 대체한 후, 기능성 마감재로서의 성능을 검증한 결과 다음과 같은 결과를 얻었다. 1. 현무암 석분슬러지를 포함한 몰탈의 휨인장강도와 압축강도는, 대체율 21%에 도달할 때까지 압축 및 휨인장강도는 일반 시벤트몰탈 대비 각각 47%와 35% 증가하였다. 2. 원적외선 방사율에 있어서도 기존몰탈보다 높은 0.933까지 이르렀으며, 이 수치는 기타 기능성 마감재보다 우수한 원적외선 방사율을 나타내는 것이다. 3. 음이온 방사량은 현무암석분의 대체율에 따른 일관된 경향을 보이지는 않았으나, 일반 시멘트몰탈 보다는 5% ~ 12% 증가효과가 나타났다. 4. 기존 시멘트몰탈의 잔골재의 21%를 현무암석분슬러지로 대체할 경우, 시멘트 몰탈보다 물리적 성질이 증가 함과 동시에, 기능성몰탈로서의 원적외선 방사율, 음이온 방사량의 증진효과가 있었다. 또한 새로운 건축자재의 생산을 통한 경제적 이득은 물론, 산업폐기물의 양을 줄일 수 있다.

• Journal of the Korea Concrete Institute
• /
• v.23 no.2
• /
• pp.203-209
• /
• 2011

The cement industry is expected to face a major set-back in the near future due to its large energy consumption and $CO_2$ production, causing global warming. In order to overcome these environmental problems, this research has bee carried out to find a cement substitute material. One possible cement substitute material is Zeolite cement. In this study, the materialistic characteristics of Zeolite cement mortar were evaluated. Natural Zeolite cement mortar was prepared using alkali activation (NaOH) instead of water ($H_2O$) to determine achievable strength and appropriate mixing ratio. Based on the mixing ratio, functional material was added to alkali active agent to harden Zeolite mortar to develop a highly functional construction material. The study result showed that pure Zeolite cement mortar achieved compressive strength of 42 MPa in 7 days depending on the mixing amount of alkaline catalyst and the hardening temperature, showing high efficiency and possibility as a new construction material.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.36 no.6
• /
• pp.415-421
• /
• 2023

In this study, the piezoresistive properties of cementitious composites enhanced with carbon nanotubes for improved electrical conductivity were analyzed using a deep learning-based transformer algorithm. Experimental execution was performed in parallel for acquisition of training data. Previous studies on mixture design, specimen fabrication, chemical composition analysis, and piezoresistive performance testing are also reviewed in this paper. Notably, specimens in which fly ash substituted 50% of the binder material were fabricated and evaluated in this study, in addition to carbon nanotube-infused specimens, thereby exploring the potential enhancement of piezoresistive characteristics in conductive cementitious materials. The experimental results showed more stable piezoresistive responses in specimens with fly-ash substituted binder. The transformer model was trained using 80% of the gathered data, with the remaining 20% employed for validation. The analytical outcomes were generally consistent with empirical measurements, yielding an average absolute error and root mean square error between 0.069 to 0.074 and 0.124 to 0.132, respectively.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.2
• /
• pp.95-103
• /
• 2012

In order to improve the dimensional stability and mechanical performance of cement-based composites, the effect of an expansive admixture based on calcium sulphoaluminate (CSA) on the shrinkage and mechanical properties of strain-hardening cement-based composite (SHCC), which exhibits multiple cracks and pseudo strain-hardening behavior in the direct tension, is investigated. Polyethylene fibers reinforced SHCC mixtures with three levels (30, 70, and 100MPa) of compressive strength were compared through free shrinkage, compressive strength, flexural strength, and direct tensile strength measurements. The SHCC mixtures were cast with and without replacing 10% of Portland cement content with CSA admixture. According to test results, CSA admixture is effective in reducing shrinkage of SHCC material. SHCC mixture with CSA admixture exhibited a little higher strength than companion mixture without CSA admixture.

• Journal of the Korea Concrete Institute
• /
• v.22 no.4
• /
• pp.567-574
• /
• 2010

As a eco-friendly material, Hwangtoh(red clay) has been studied for a partial or complete replacement of portland cement. Most of existing studies focused on the mechanical properties of the Hwangtoh concrete including the compressive strength, drying shrinkage, creep. In the present study, the flexural capacity of the beams made with the Hwangtoh concrete was tested. One of the concrete tested consisted of activated Hwangtoh replacing 20% of the cement. The other consisted 100% activated Hwangtoh replacing all the cement. The simple beams were tested under two point static loading. The flexural strength, cracking moment, deflection, and ductility were compared with those of the beams made with ordinary portland cement concrete.

• Journal of the Korean GEO-environmental Society
• /
• v.9 no.7
• /
• pp.37-43
• /
• 2008

The unconfined compressive strength of soil-cement mixed with red mud, an industrial by-product of alumina production, was investigated in the laboratory. The investigation involved laboratory tests under the various conditions such as red mud content, cement content, fly ash content and ratio of soil replacement with sands. The unconfined compressive strength tests were performed at 7, 14 and 21 days after specimen preparation. Results of the study show that the unconfined compressive strength increased as red mud and fly ash content decreased and cement content increased. Increasing the soil replacement ratio with sands had an insignificant effect on compressive strength because the soil had a similar particle size as the replacement sands.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.4
• /
• pp.57-65
• /
• 2013

The development of the oil refining industry has resulted in an annual 120 million tons of sulphur, which is a by-product of the desulphurization process. To exploit this abundance, the applications of sulphur must be expanded. as excellent durability of reuse of leftover sulphur which has high potential for utilization in construction materials, the study is actively in progress. Meanwhile, there has been active research on semi-rigid pavements that draw on the strengths and overcome the weaknesses of asphalt and concrete pavements. Acrylate is used to prevent cracking but involves a high cost, thus, an alternative material is required. As such, this study presents methods on the reuse of leftover sulphur and examines the engineering performance of grout containing sulfur polymer emulsion (SPE) for use in semi-rigid pavements. Our analysis shows that grout in which 30% of acrylate is replaced with SPE has superior properties in terms of time of flow and strength compared to regular grout. However, performance declined when more than 50% of acrylate was replaced by SPE, indicating that the optimum replacement level is 30%. Through SEM analysis, we found that grout with utra harding cement in this study at three hours had similar hydration properties to that of Type 1 Ordinary Portland Cement (OPC) at seven days, and maintained the properties regardless of grout containing SPE. OPC and grout with a replacement level of 30% displayed similar levels of chloride invasion resistance, whereas grout without SPE was far less resistant. Within the scope of this paper, the optimum replacement level of acrylate with SPE was found to be 30% in consideration of various properties such as time of flow, strength, and chloride invasion resistance.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.685-694
• /
• 2010

As a eco-friendly material, Hwangtoh (red clay) has been studied for complete or partial replacement of portland cement. Most of existing studies focused on the material properties of the Hwangtoh concrete including the compressive strength, drying shringkage, and creep. In the present study, the shear strength of the beams made with the Hwangtoh concrete was tested. Further, bond strength of tension re-bars embedded in the Hwangtoh concrete was tested. One of the concrete tested consisted of activated Hwangtoh replacing 20% of the cement. The other consisted 100% activated. Hwangtoh replacing all the cement. The beam specimens were tested under two point static loading. The test result showed that the shear strength of activated Hwangtoh concrete beams replacing 20% and 100% of cement was equivalent to that of the ordinary portland cement concrete beam. However, the bond strength of activated Hwangtoh concrete replacing 100% of the cement was less than that of the ordinary portland cement concrete.