• Journal of the Korean Ceramic Society
• /
• v.38 no.2
• /
• pp.112-116
• /
• 2001

고상반응법에 의한 제조한 ZnGa$_2$O$_4$형광체에 Li 및 Tm 원소를 도핑함에 따른 발광특성을 조사하였다. 254nm 여기 하에서, 환원 처리된 ZnGa$_2$O$_4$형광체는 245nm에서 흡수피크와 380nm에서 발광피크를 나타내며, 이는 스피넬 구조에서 Ga$^{3+}$ 이온의 $^4$T$_2$$\longrightarrow$$^4$A$_2$천이에 기인한다. ZnGa$_2$O$_4$형광체에 있어서 Li 및 Tm을 도핑했을 경우가 도핑하지 않은 시료에 비해 발광강도 및 색순도가 개선되었으며, Li 및 Tm을 각각 0.1 mol, 0.01 mol 첨가했을 때 가장 우수한 발광강도 및 색순도 특성을 보였다.

• Journal of the Korean Ceramic Society
• /
• v.40 no.7
• /
• pp.652-656
• /
• 2003

The green emitting phosphor, BnGa$_2$O$_4$:Mn thin films with spinel structure were deposited by rf magnetron sputtering at various Ar/O$_2$ ratios. Thin film phosphors were heat-treated in air and $N_2$+vacuum atmosphere, respectively. Effects of Ar/O$_2$ ratios and annealing conditions on the structural and photoluminescence (PL) and cathodeluminescence (CL) properties were investigated. Luminous properties were more improved by inhibiting the films from contacting with oxygen during heat treatment.

• Journal of Korean Ophthalmic Optics Society
• /
• v.7 no.1
• /
• pp.35-38
• /
• 2002

Ferrite thin film with glass substrate was prepared by ferrite plating method in order to make sunglass which cut off ultraviolet and electromagnetic field. It has single phase of polycrystalline spinel structure and has gloss like as mirror and has hardness without scratch by scraping with nail. The transmittance of ferrite thin film is lowered near 400nm manifestly, which shows that the ferrite thin film was cut off ultraviolet successfully. Therefore, the sunglass with ferrite plating is use of cut of ultraviolet and electromagnetic field.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.333-333
• /
• 2012

$Co_3O_4$ 계열 스피넬(spinel) 전이금속 산화물 $TCo_2O_4$ (T = 3d 전이금속)는 화학적 촉매, 센서, 이차전지, 연료전지 등으로의 응용성에 기인하여 최근 주목을 받고 있으며, 특정 응용분야와 관련하여 그 박막 시료 제작 및 물리적, 화학적 성질들에 대한 세밀한 연구의 필요성이 제기되고 있다. 본 연구에서는 졸-겔 방법을 이용하여 $TCo_2O_4$ 박막이 $Al_2O_3$ (0001) 기판 위에 균일한 두께로 제작될 수 있는 최적 조건을 찾고자 하였으며, 후열처리 조건 변화에 따르는 박막의 구조적 성질 변화를 조사하였다. 후열처리는 공기 중에서 이루어졌으며 온도 ${\sim}800^{\circ}C$에서 최적 결정성을 갖는 다결정 박막이 얻어졌다. 또한, 박막에 작은 시간(~10 min) 동안의 전자선(electron beam) 조사를 통한 다결정 박막의 형성도 관측되었다. $TCo_2O_4$ 박막들에 대한 X-ray diffraction, X-ray photoelectron spectroscopy, spectroscopic ellipsometry 측정들을 수행하여 그 구조적, 광학적 성질을 조사 하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2012.05a
• /
• pp.86.2-86.2
• /
• 2012

산화금속은 높은 결정성, quantum size effect, 높은 투과도, 대기중의 안정도 등과 같은 탁월한 성질들로 인하여 오늘날 실리콘의 대체물로서 많은 연구가 보고되고 있다. 이러한 금속산화물의 크기와 모양을 조절하며 대량 생산하기 위한 합성방법으로 가수분해, 금속양이온 응축법과 같은 다양한 수용액상 방법이 연구되고 있다. 하지만 2차원 단일 층에 나노물질을 정렬하고 전기적 접합을 형성하는 것이 매우 어렵다는 점 때문에 나노물질을 기판 위에 자유롭게 성장시키는 방법에 대해서는 아직 많이 보고 되어있지 않다. 본 연구에서 저온의 수용액에서 1차원의 나노막대가 2차원의 스피넬 구조 위에 heteroepotaxial 접합을 이루며 성장시키는 방법을 이용하였다. P-n접합 형성을 위하여 (0001)방향으로 배향된 n-type ZnO 나노막대를 (111)방향의 p-type Co3O4 나노플레이트 위에 성장시킨 구조를 제작하였으며 이를 바탕으로 다이오드소자를 제작하여 ideal factor, turn-on voltage, rectifying ratio등의 전기적 특성을 평가하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.8
• /
• pp.652-657
• /
• 1998

We have performed spin-spray ferrite plating of $Fe{_3}{-X}-Ni_XO_4$(X=0.17~0.26) films in the temperature region $T=80~95[^{\circ}C]$. A reaction solution and an oxidizing solution were supplied to a reaction chamber by supply pump. The solubility limit of Ni increases as the substrate temperature increase, from X=0.17 at $80[^{\circ}C]$ to X=0.26 at $95[^{\circ}C]$. All the films are polycrystalline with no preferential orientation, and the magnetization exhibits no definite anisotropy. Grain size in the films increases as X increases, reaching $0.87[\mu{m}]$ at X=0.26.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.7
• /
• pp.546-551
• /
• 1998

$Mn{1-X}Fe{2+X}O_4, Mg_{1-X}Fe_{2+X}O_4$ (x=0.0, 0.025, 0.1, 0.2) for negative temperature coefficient (NTC) thermistor was prepared by calcination at $800^{\circ}C$ and sintering at form 1100 to $1250^{\circ}C$ with $50^{\circ}C$ intervals. The best linear property was obtained in the Mn-based sample sintered at $1200^{\circ}C$ with x=0.0 composition. Temperature coefficient of resistance, $\alpha$, was $-5.6%/^{\circ}C$ in the Mn-based sample, $-5.2%/^{\circ}C$ in the MM-based sample, and $-1.6%/^{\circ}C$ in the Mg-based sample. thermistor parameter, B, was in the range of 2665~7780 K. The results show the possibility that Mn-Ni-Co based thermistor could be substituted by the composition used in this study.

• Journal of the Korean Magnetics Society
• /
• v.2 no.2
• /
• pp.105-113
• /
• 1992

조성이 Mn$_{x}$Zn$_{1-x}$ Fe$_{2}$O$_{4}$ 훼라이트(x=0.75, 0.52)를 pusher type 연속 전기로를 이용하여 질소 분위기하에서 1360 .deg. C 로 3시간 동안 소결하여 얻어냈다. 본 연구에서는 스피넬 구조인 Mn-Zn 훼라이트의 FMR(Ferrimagnetic Resonance) 스펙트럼 특징과 초기투자율과의 상관성을 조사하고자 EPR X-band 스펙 트로미터를 이용 9.50 GHz의 microwave frequency에서 FMR 실험을 수행하였다. FMR 공명흡수선은 주 자기공명 흡 수선외에 낮은 자기장에서 약한 subsidiary 공명흡수선을 나타내는데 온도변화에 따른 주 자기공명 흡수선과 sub- sidiary 공명흡수선(제2, 제3 공명흡수선)의 세기, 공명선폭, g값 등의 온도 의존성을 연구함으로써 제2 공명흡수 선이 나타나는 원인을 분석하였으며, 자기공명 흡수선의 g값, 자기공명선 세기, 그리고 공명선폭과 초기투자율의 상관성을 연구하였다. 실험 결과 주 자기공명 흡수선의 g값, 자기공명선 세기, 공명선폭은 초기투자율 값과 밀접 한 관련이 있음을 확인할 수 있었다.었다.

• Journal of the Korean Ceramic Society
• /
• v.33 no.7
• /
• pp.779-784
• /
• 1996

The spinel/cubic stabilized zirconia composites were fabricated via, The reaction sintering of monoclinic zirco-nia(baddeleyite) added with MgAl powder. During heating Mg and Al were oxidizedfirst and subsequently the oxides formed spinel (MgAl2O4) and finally remained MgO stabilized the zirconia, Because the oxides formed during the oxidation process would have very fine grain size (order of submicron) mainly due to the effects of attrition milling the reaction sintering was more effective in densification and improvement of strength and fracture toughness than conventional sintering with direct addition of MgO. The sintering behavior phase transformation during firing and mechanical properties of sintered body were investigated with emphasis on the relations between spinel formation due to MgAl addition and sintering and mechanical properties.

• Journal of the Korean Ceramic Society
• /
• v.29 no.2
• /
• pp.101-106
• /
• 1992

Sintering behavior, distribution of dopant oxides and electrical properties in the ZnO-Bi2O3-CoO-Sb2O3 and ZnO-Bi2O3-CoO-Sb2O3-Cr2O3 systems were studied. The linear shrinkage of ZnO varistors from 850 to 950$^{\circ}C$ was related to the decomposition reaction (py\longrightarrowsp+Bi2O3) of the pyrochlore phase. In the distribution of the dopant oxides (CoO, Sb2O3, Cr2O3), Co distribute uniformly throughout the sample, the distribution of Sb coincided with small particles (spinel phase, Zn7Sb2O12), and Cr distributed very consistently with Sb. The increase in breakdown voltage, due to the addition of Cr2O3, was not only attributed to the decrease in the ZnO grain size but also to the solution of Cr2O3 in the spinel phase. The leakage current (80% V60 ${\mu}\textrm{A}$) was increased by the addition of Cr2O3.