• Journal of Ocean Engineering and Technology
• /
• v.17 no.2
• /
• pp.40-46
• /
• 2003

The corrosion resistance of super duplex stainless steel on both its fibrous and dispersed phase was investigated. These structures consist of various volume fraction and distribution of austenite structure, which were obtained by changing the heat treatment temperature and cycle. The fibrous phase had higher austenite volume fraction than that of the dispersed phase at the same temperature. Corrosion resistance of super duplex stainless steel was evaluated through an immersion test and an impingement test, using 35% HCI and sea water, respectively. Super duplex stainless steel was compared with STS316L and STS304. The corrosion resistance of super duplex stainless steel was superior to ST316L and STS304. The dispersed phase of super duplex stainless steel was more stabilized than the fibrous phase in corrosion. The magnitude of corrosion rate was in order STS304, STS316L, fibrous phase of super duplex stainless steel and dispersed phase of super duplex stainless steel.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.10a
• /
• pp.20-25
• /
• 2000

lh deleterious Cr, Mo rich -$\sigma$phase is a hard embrittling precipitate, which forms between MU)-900 $^{\circ}C$, often associated with a reduction in both impact properties and corrosion reshame. On this study, After aging at MU) "C, fatigue crack propagation induced by a phase precipitation was evaluated and time-frequency analysis of acoustic emission was conducted It was possible to find fracture mechanism by a phase precipitation due to time-frequency anulysis of acoustic emission signals.nals.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.2
• /
• pp.65-69
• /
• 2000

This study is to investigate the characteristics of fatigue crack propagation in rolled super duplex stainless steel that was changed austenite-ferrite volume fraction by heat treatment. It was used two kinds of specimen the rolling and the transverse directions δ-phase fraction affected sound velocity hardness and Young's modulus. Characteristics of fatigue crack propagation was affected by anisotropy and (δ+γ) phase volume fractions.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.5
• /
• pp.79-84
• /
• 2009

Super duplex stainless steel has long life in severe environments by showing the enough strength and corrosion resistance. Therefore, the fracture mechanics approach needs to support the structural strength integrity for the used material. In this study, fatigue crack propagation behavior was investigated to super duplex stainless steel with 0.2% nitrogen. The various volume fraction and distribution of austenite structure for applied specimen in test were obtained by changing the heat treatment temperature and cycle. From test results, fatigue crack propagation rate showed two kinds of tendency between da/dN and ${\Delta}K$ according to distribution of austenite structure and structure anisotropy.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.73-78
• /
• 2000

On this study, the fatigue crack propagation of super duplex stainless steel is investigated in conditions of various volume fraction of austenite phase by changing heat treatment temperature. And we analysed acoustic emission signals during the fatigue test by time-frequency analysis methods. As the temperature of heat treatment increased, volume fraction of austenite decreased and coarse grain was obtained. The specimen heat treated at $1200^{\circ}C$ had longer fatigue life and slower rate of crack growth. As a result of time-frequency analyze of acoustic emission signals during fatigue test, main frequency was $200{\sim}300kHz$ having no correlation with heat treatment and crack length, and 500kHz was obtained by dimple and separate of inclusion

• Journal of Ocean Engineering and Technology
• /
• v.22 no.4
• /
• pp.46-50
• /
• 2008

Super duplex stainless steel has along life in severe environments because of its strength and corrosion resistance. If 0.2$\sim$0.3% Nitrogen in aninterstitial solid solution is added, the austenite structure is reinforced. This improves the solid solution hardening and the anticorrosionability. In this study, the mechanical properties and structures of the super duplex stainless steel with the 0.2% N additive were investigated to determine the effect of various volume fractions on the austenite phase. The various volume fractions and distributions of the austenite structure in the applied test specimens were obtained by changing the heat treatment temperature and cycle. The characteristics by amounts of the $\sigma$ phase obtained from the precipitation heat treatment were alsoinvestigated. From the results, when the austenite volume fraction increases, the tensile strength decreases and elongation increases. And the $\sigma$ phase was rapidly increased by increasing the heat treatment time. When the volume fraction of the $\sigma$ phase increased, tensile strength increased.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.5
• /
• pp.85-91
• /
• 2009

A stainless steel that contains aggressive negative ion was known to decrease the corrosion resistance. Stainless steel with super corrosion resistance was developed for improvement of corrosion resistance. Super duplex stainless steel is widely used under sever environment because of good mechanical properties and corrosion resistance. Also, Super duplex stainless steel has long life in severe environments by showing the enough strength and corrosion resistance. But duplex stainless steel is not stabilized compared to austenite stainless steel in corrosion resistance. In this study, corrosion characteristic were investigated to super duplex stainless steel with additive 0.2% nitrogen with $SiO_2$ thin films coated or no coated by sol-gel method in 3.5% NaCl. From test results, corrosion current density in the heat-treated specimen for ${\sigma}$ phase precipitation was higher than that of different heat-treated specimen. Also, $SiO_2$ colloidal-coated specimen had not occurred almost corrosion.

• Journal of the Korean Society for Heat Treatment
• /
• v.14 no.4
• /
• pp.205-211
• /
• 2001

The characteristics of super duplex stainless steel were investigated on its fibrous structure and dispersed structure. These structures consist of various volume fractions and distributions of the austenite phase that were obtained by changing the heat treatment temperature and cycle. The fibrous structure had higher austenite volume fraction than dispersed structure on the same temperature. As the austenite volume fraction increased in both structures, tensile strength and elongation increased, but hardness decreased. Fatigue life of fibrous structure parallel to rolling direction was shorter than that of perpendicular to rolling direction. Fatigue life of dispersed structure was longer than parallel fibrous structure, and shorter than perpendicular fibrous structure. Fatigue crack propagation rate of fibrous structure was faster than that of dispersed structure.

• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.2
• /
• pp.74-79
• /
• 2012

This study has been carried out to investigate the precipitation behavior of ${\chi}$ phase and effect of ${\chi}$ phase precipitation on the impact toughness of 25%Cr-7%Ni-4%Mo super duplex stainless steel. It was proved that the ${\chi}$ phase was a intermetallic compound, which represented the higher chromium and molybdenum concentration than the matrix phases, and also showed the higher molybdenum concentration than the ${\sigma}$ phase. The ${\chi}$ phase was precipitated at the interface between ferrite and austenite or inside the ferrite matrix in the early stage of aging. The number of ${\chi}$ phase precipitates increased with increasing aging time, however, after showing the maximum value, the number was decreased due to the gradual transformation of ${\chi}$ phase into ${\sigma}$-phase. Aging ferrite phase was decomposed by the $r^2$ phase and ${\sigma}$-phase. Impact toughness rapidly decreased with time in the initial stage of aging at ${\chi}$ phase start to precipitate. Thus, the impact toughness was greatly influence for the precipitation of ${\chi}$ phase.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.1
• /
• pp.30-39
• /
• 1997

After changing the heat treating atmosphere of nitrogen gas, argon gas and vacuum, the nitrogen contents, microstructural changes, hardness and corrosion resistance of 0.25wt.%N alloyed super duplex stainless steel have been investigated in the temperature range from $1050^{\circ}C$ to $1350^{\circ}C$. The nitrogen content showed to be increased up to 0.36wt.% after heat treating the specimen in nitrogen gas at $1200^{\circ}C$, while the decrement of nitrogen content in vacuum atmosphere was shown down to 0.03wt.% at $1350^{\circ}C$. After heat treating in the mixed gas atmosphere of argon and nitrogen at $1250^{\circ}C$, the surface ${\gamma}$ phase existed as ${\alpha}+{\gamma}$ phase increased with increasing nitrogen gas content. The ${\gamma}$ single phase appeared at the surface above $80%N_2$ gas, while the surface ${\alpha}$ single phase was shown below $20%N_2$ gas. When heat treating the specimen in nitrogen gas at $1050^{\circ}C$, the hardness of austenite phases increased above Hv 40 at the surface layer compared to the hardness of the core parts, while decrement of denitriding effect caused to the hardness nearly unchanged between surface and the core parts after heat treating in vacuum atmosphere. The surface ${\gamma}$ single phase specimen showed superior corrosion resistance than the surface ${\alpha}$ single phase specimen. The surface ${\alpha}$ phase existed in the ${\alpha}+{\gamma}$ microstructure showed higher corrosion resistance after heat treating in the nitrogen gas atmosphere than the ${\alpha}$ phase heat treated in the argon gas and vacuum atmosphere.