• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.10
• /
• pp.1243-1248
• /
• 2011

Internal defects are a major concern in the casting process because they have a significant influence on the strength and fatigue life of casting products. In general, they cause stress concentration and can be a starting point of cracks. Therefore, it is important to understand the effects of internal defects on mechanical properties such as fatigue life. In this study, fatigue experiments on tensile specimens with internal defects were performed. The internal defects in the casting product were scanned by an industrial CT scanner, and its shape was simplified by ellipsoidal primitives for the structural and fatigue analysis. The analysis results were compared with experimental results for casting products with internal defects. It was demonstrated that it is possible to consider internal defects of casting products in stress and fatigue analysis. The proposed method provides a tool for the prediction of the fatigue life of casting products and the investigation of the effects of internal defects on mechanical performance.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.29 no.6
• /
• pp.571-575
• /
• 2016

Photo responsive polymer(PRP) is well known for its photo deformation under UV light, and goes back to its original shape in visible light due to the photoisomerization of the azobenzene inside the PRP. In this paper, dynamic study of the vibration in PRP is discussed. In order to predict photo-deformation of the PRP a multiscale modeling is introduced which covers quantum level photo excitation, microscopic morphology, and macroscopic deformation of the PRP. A simple 1D beam model is introduced to model dynamic bending behavior of the PRP. Through fast Fourious transformation analysis, we identify that vibration frequency of the PRP can be controlled by light polarization angle.

• Journal of Distribution Research
• /
• v.5 no.2
• /
• pp.49-68
• /
• 2001

In this chapter, we summarize the results on the optimal location selection and present limitation and direction of research. In order to reach the objective, this study selected and tested the interaction model which obtains the value of co-ordinates on location selection through the optimization technique. This study used the original variables in the model, but the results indicated that there is difference in reality. In order to overcome this difference, this study peformed market survey and found the new variables (first data such as price, quality and assortment of goods, and the second data such as aggregate area, and area of shop, and the number of cars in the parking lot). Then this study determined an optimal variable by empirical analysis which compares an actual value of market share in 1988 with the market share yielded in the model. However, this study found the market share in each variables does not reflect a reality due to an assumption of λ-value in the model. In order to improve this, this study performed a sensitivity analysis which adds the λ value from 1.0 to 2.9 marginally. The analyzed result indicated the highest significance with the market share ratio in 1998 at λ of 1.0. Applying the weighted value to a variable from each of the first data and second data yielded the results that more variables from the first data coincided with the realistic rank on sales. Although this study have some limits and improvements, if a marketer uses this extended model, more significant results will be produced.

• Journal of the Korea Concrete Institute
• /
• v.20 no.2
• /
• pp.249-256
• /
• 2008

With consideration of the ongoing construction of high-rise buildings, it is becoming increasingly important to be able to accurately predict the behavior of them on the stage of design, construction and service. Even though many researchers have developed the analysis method to predict the behavior of high-rise buildings, their studies were based on the two dimensional frame structures composed of line elements such as beams and columns. Recently the high-rise buildings with flat-plate system is widely used because of its advantages. In this study a three dimensional analysis method is developed to analyze the behavior of the high-rise buildings with flat-plate system since it is difficult to model the structural systems reasonably with the existing two dimensional analysis method. The analysis method considered the construction sequence including the temporary work such as installation of form, removal of form, installation of shore, and removal of shore. Line elements were used to describe columns, beams, and shores and plate elements were used to model slabs. The creep and drying shrinkage of concrete were also considered to account for the inelastic behavior of concrete.

• Journal of the Institute of Electronics Engineers of Korea SP
• /
• v.42 no.2 s.302
• /
• pp.131-142
• /
• 2005

The low rate speech coders under 4 kbit/s are based on sinusoidal transform coding (STC) or multiband excitation (MBE). Since the harmonic coders are not efficient to reconstruct the transient segments of speech signals such as onsets, offsets, non-periodic signals, etc, the coders do not provide a natural speech quality. This paper proposes method of a efficient transient model :d a multi-mode low rate coder at 2.4 kbit/s that uses harmonic model for the voiced speech, stochastic model for the unvoiced speech and a model using aperiodic pulse location tracking (APPT) for the transient segments, respectively. The APPT utilizes the harmonic model. The proposed method uses different models depending on the characteristics of LPC residual signals. In addition, it can combine synthesized excitation in CELP coding at time domain with that in harmonic coding at frequency domain efficiently. The proposed coder shows a better speech quality than 2.4 kbit/s version of the mixed excitation linear prediction (MELP) coder that is a U.S. Federal Standard for speech coder.

• Journal of the Korea Concrete Institute
• /
• v.15 no.2
• /
• pp.280-287
• /
• 2003

To evaluate the practical application of oyster shells(OS) as construction materials, an experimental study was performed. More specifically, the long-term mechanical properties and durability of concrete blended with oyster shells were investigated. Test results indicate that long-term strength of concrete blended with 10% oyster shells is almost identical to that of normal concrete. However, the long-term strength of concrete blended with 20% oyster shells is appreciably lower than that of normal concrete. Thereby, concrete with higher oyster shell blend has the possibility of negatively influencing the concrete long-term strength. Elastic modulus of concrete blended with crushed oyster shells decreases as the blending mixture rate increases. Namely, the modulus is reduced to approximately 10∼15% when oyster shells are blended up to 20% as the fine aggregate. The drying shrinkage strain increases with an increasing crushed oyster shells substitution rate. In addition, the existing model code of drying shrinkage and creep do not coincide with the test results of this study. An adequate prediction equation needs to be developed. The utilization of oyster shells as the fine aggregate in concrete has an insignificant effect on fleering and thawing resistance, carbonation and chemical attack of concrete. However, water permeability is considerably improved.

• Applied Chemistry for Engineering
• /
• v.2 no.1
• /
• pp.30-37
• /
• 1991

The production of hydrogen from steam by reduced iron with additives such as CuO, $In_2O_3$, $MoO_3$ and $WO_3$ has been kinetically investigated. It was shown that all additives have a promoting effect on reaction activity in the order of $$MoO_3{\gg}In_2O_3{\sim_=}WO_3{\sim_=}CuO$$. The shrinking core model was applied to predict the complete conversion time and the results were quite comparable with experimental values. The reaction was carried out in a fixed flow reactor packed with reduced iron with 1 wt % of additives under the conditions, $600-750^{\circ}C$, Ar flow rate of 1 L/min and steam partial pressure of 0.085 atm. The apparent activation energies were 14.2, 20.9, 21.3, 22.4 and 27.9 kJ/mol with $MoO_3$, $In_2O_3$, $WO_3$, CuO and without additive, respectively.

• International Journal of Highway Engineering
• /
• v.7 no.4 s.26
• /
• pp.69-77
• /
• 2005

Joint spacing is a potent influence in increasing the long term performance of jointed concrete pavement slabs through the control of tensile stress, sealant failure and Load Transfer Efficiency (LTE). Internal Joint Spacing is an empirical and fixed method therefore this study will present the optimum joint spacing considerations depending on various climactic conditions. Calculating the optimum joint spacing eliminates random cracking due to the effect of the environmental loads such as the early behavior of drying shrinkage and heat hydration. Optimum joint spacing is calculated so as not to cause pavement distress by the deterioration of LTE by long term pavement movement. This study shows that the provisional joint spacing is 6-8m. Pavement Distress Prediction Models show that pavement distress has no effect on joint spacing of 8m.

• Journal of the Korea Concrete Institute
• /
• v.26 no.5
• /
• pp.615-625
• /
• 2014

Excessive long-term slab deflection caused by construction load is a critical issue for the design of concrete slabs, as long span flat plates become popular for tall buildings. In the present study, the effect of construction load causing early slab cracking on the long-term deflection was theoretically studied. On the basis of the result, a numerical analysis method was developed to predict the long-term deflection of flat plates. In the proposed method, immediate deflection due to slab cracking and long-term effect of creep and shrinkage were considered. To verify the construction load effect, long-term slab deflections were measured in actual flat plate buildings under construction. The results showed that the immediate deflection due to the construction load increased significantly the long-term deflection. The proposed method was used to predict the deflections of the buildings. The results were compared with the measurement results. The predictions agree well with the long-term deflections of flat plate affected by construction load.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.11
• /
• pp.5947-5955
• /
• 2013

This study was intended to estimate the axial deformation of joint between pavement modules in the rapid-constructible modular pavement system, and to investigate the applicability of two-phase composites for a joint material, which was composed of cement paste, epoxy, or polyurethane as a matrix and sand as particles. A case which had supports under the pavement module as well as a case which the module was put on roadbed directly were considered in FEM analysis for the axial deformation. The effect of self-weight, live load, thermal change, and drying shrinkage were estimated and the thermal change was found to cause the largest deformation compared to the others. Deformation capacity of two-phase composites was predicted using the modified shear-lag model. In the analytical results for the elastic modulus and maximum tensile strain with different volume fractions of sand, 20~30 % replacement of sand was revealed to satisfy the required strain capacity with economy when if the width of joint was designed to be 15~20 mm.