Tension-Stiffening and Cracking Behavior of 100 MPa Shrinkage-Compensated Ultra High-Strength Strain-Hardening Cement Composite (UHS-SHCC) Ties (100 MPa급 수축보상 초고강도 변형경화형 시멘트 복합체를 사용한 인장부재의 인장강성 및 균열특성)

  • Song, Young-Jae;Yun, Hyun-Do
    • Journal of the Korea Concrete Institute
    • /
    • v.25 no.4
    • /
    • pp.371-379
    • /
    • 2013
  • This paper investigates the cracking and tension-stiffening behavior of 100 MPa shrinkage-compensated strain-hardening cement composite (SHCC) and conventional concrete tie elements in monotonic and cyclic tension. Strain and surface crack formation of tension ties were monitored with two strain displacement transducers and a photo microscope with a lens of magnification 50 times. Three different cement composites such as conventional concrete, shrinkage-compensated SHCC, and normal SHCC were used in the tie specimens to investigate the influence of the cement composite type on the tension stiffening and cracking behavior. Test results indicated that initial shrinkage of the ultra high-strength cement composites is greatly reduced as the 10% replacement of cement by the shrinkage-compensating admixture based on calcium sulfo-aluminate (CSA). The test results on the SHCC tension ties showed that the first cracking load decreases proportionally to the initial shrinkage strain. Reinforced ultra high-strength SHCC ties with the initial shrinkage compensation exhibited improved tension stiffening and smaller crack spacings, i.e. the reduction in crack width. Cyclic loading did not have a significant effect on tension stiffening and cracking behavior of tension ties with normal concrete and SHCC materials.

A Field Application of the Self-Compaction Concrete for Shrinkage Compensation (수축보상을 위한 자기충전 콘크리트의 현장적용)

  • Lee, Sang-Soo;Won, Cheol;Park, Sang-Joon;Kim, Dong-Seok
    • Proceedings of the Korean Institute of Building Construction Conference
    • /
    • 2002.05a
    • /
    • pp.7-12
    • /
    • 2002
  • The purpose of this study is to design and to apply the self-compaction concrete mixture to field, having not only high strength but also compensation for shrinkage without thermal crack under 4 sides outer restraint of the member. In the experimental mix, replacement ratio of limestone Powder, CSA expansive additives, and unit water were selected as parameters, using portland blast-furnace slag cement. And, bleeding test, expansibility test, hydration heat analysis were performed. As a results, when Cement is replaced with 35% limestone Powder, 6% CSA expansive additives at unit water 175kg/$m^3$, demanded performances of fresh and hardened self-compaction concrete are accomplished in the field application.

  • PDF

A Study on the Plastic Shrinkage Properties of Cement Mortars (시멘트 모르터의 소성수축 특성에 관한 연구)

  • 이의학;김범수;송영진;송명신;이경희;박한수
    • Journal of the Korean Ceramic Society
    • /
    • v.38 no.8
    • /
    • pp.716-723
    • /
    • 2001
  • 시멘트 모르터의 소성수축에 의한 균열을 방지하기 위해 소성수축 특성에 관한 연구를 수행하였다. 우리나라 봄철의 대표적인 기후인 온도 20$\pm$3$^{\circ}C$, 상대습도 55%, 풍속 3.5m/s의 기후조건으로 하였으며, 모르터의 물 시멘트 비, 시멘트 골재 비, 팽창재 사용, 플라이 애쉬 치환, 수분증발을 억제하기 위한 중점제 등을 사용하여 소성수축의 특성을 검토하였다. 연구 결과 소성수축 변형은 응결시간과 밀접한 관계가 있으며 응결시간이 빠를수록 변형은 크게 나타났다. 또한 물시멘트 비에 의해서도 소성수축 변형은 큰 것으로 나타났다. 모르터에서의 골재 비율이 작거나, 플라이 애쉬의 치환율이 클수록 소성수축 변형은 매우 크게 나타났다. 중점제의 사용은 소성수축 변형을 줄이는데 효과가 있었으며, 건조수축 보상용 팽창재의 사용은 소성수축 변형율을 크게 하는데 이는 ettringite 생성에 의한 물 시멘트 비의 감소효과를 가져오기 때문이다.

  • PDF

Tunable dispersion compensator based on chirped fiber bragg gratings with a mechanical rotator (회전기와 첩 광섬유 격자를 이용한 가변 분산 보상기)

  • 김준희;배준기;한영근;김상혁;이상배;정제명
    • Korean Journal of Optics and Photonics
    • /
    • v.15 no.2
    • /
    • pp.100-103
    • /
    • 2004
  • A systematic method for tunable dispersion compensation based on chirped fiber Bragg gratings without a center wavelength shift is proposed. The specially designed mechanical rotator can flexibly control the chirping ratio along the fiber grating and the corresponding dispersion value. The group delay can be linearly controllable since the proposed method can induce a linear strain gradient with the rotation angle change. The dispersion value could be controlled from 228.04 ㎰/nm to 1430.7 ㎰/nm with small center wavelength shift, which was less than 0.03 nm.

Modeling of Void growth in partial Frame Process (PFP성형공정의 기포성장에 관한 모델링)

  • 안경현
    • The Korean Journal of Rheology
    • /
    • v.8 no.3_4
    • /
    • pp.207-214
    • /
    • 1996
  • 사출성형은 많은 장점과 유용성에도 불구하고 싱크마크나 휨과 같은 변형문제를 피 하기 어렵다. 이것은 성형품의 부위별 온도분포 및 냉각속도 차이에 의한 잔류응력에 기인 하는 것으로 구조가 복잡하거나 크기가 쿤 경우에 더욱 더 문제가 되기 쉽다. 이와 같은 문 제를 해결하기 위하여 성형품의 내부에 기포를 형성시켜 수지의 수축분을 기포의 성장으로 보상하여 주는 가스사출성형이 개발되어 많이 활용되고 있는 실정이다. 한편 일반 가스성형 과 달리 수지를 완전히 채운후 저압의 공기를 이용하여 기포를 발생시켜 수지의 체적수축분 을 보상해주는 PFP성형기술은 가스사출의 나점인 공기의 유동조절문제를 해결하고 비용이 저렴한 등의 잇점을 가지고 있다. 이 과정은 가스성형공정의 2차 침투과정과 매우 유사하나 아직까지 이에대한 이해나 연구는 매우 부족한 실정이다 본 연구는 기포의 성장이 수지의 체적수축에 의한 것이라는 가정에 근거하여 기포성장길이에 관한 모델링을 수행한 것이다. 실험결과와의 비교를 통하여 기본 가정에 대한 타당성을 검증하고 여러 인자들의 영향을 살 펴보았다. 본 연구는 PFP성형공정에 대한 이해를 증진시켜 금형설계 및 성형조건 설정에 대한 가이드라인을 제시하며 아울러 PFP공정에 대한 보다 체계적인 이해 및 일반가스성형 의 2차 침투과정 등의 관련 현상에 대한 이해 및 연구에 도움이 될것으로 기대된다.

  • PDF

Fundamental Properties of Cement Composites Containing Lightly Burnt MgO Powders (저온 소성한 MgO 분말을 혼입한 시멘트 복합체의 기초 물성)

  • Jang, Bong-Seok;Kwon, Yong-Gil;Choi, Seul-Woo;Lee, Kwang-Myong
    • Journal of the Korea Concrete Institute
    • /
    • v.23 no.2
    • /
    • pp.225-233
    • /
    • 2011
  • The volume change in concrete takes place with changes in temperature and water content immediately after concrete casting. In the early age stage, the thermal and drying shrinkages can cause cracks that are very crucial to the durability of concrete. It was reported that when the cement with lightly-burnt MgO powder was used, the shrinkage of concrete can be reduced. This study investigates fundamental properties of cement composites with lightly burnt MgO powder by performing various experiments. The stability test results verified that MgO powder in cement composites does not cause any abnormal expansion. Also, the hydrate product analysis results obtained from MgO cement paste showed that MgO powder reduces the shrinkage at the longterm ages. In addition, the cement composites containing the proper amount of MgO powder could improve compressive strength. Finally, the shrinkage reduction from using MgO powder can be optimized by increasing MgO replacement level and curing temperature.

Autogeneous Shrinkage Characteristics of Ultra High Performance Concrete (초고성능 콘크리트의 자기수축 특성)

  • Kim, Sung-Wook;Choi, Sung;Lee, Kwang-Myong;Park, Jung-Jun
    • Journal of the Korea Concrete Institute
    • /
    • v.23 no.3
    • /
    • pp.295-301
    • /
    • 2011
  • Recently, the use of UHPC made of superplasticizers, silica fume, and steel fibers has been increasing worldwide. Although UHPC has a very high strength as well as an excellent durability performance due to its dense microstructures, earlyage cracks may occur due to the high heat of hydration and autogenous shrinkage caused by low W/B and high unit cement content. The early-age shrinkage cracking of UHPC can be controlled by using the shrinkage reducers and expansive admixtures having autogenous shrinkage compensation effect. In this paper, ultrasonic pulse velocity of UHPC containing shrinkage reducers and expansive agents was measured to predict its stiffness change. Also, the effect of shrinkage reducers and expansive agents on the autogenous shinkage of UHPC was investigated through the shrinkage test of UHPC specimens. Furthermore, the material coefficients of autogenous shrinkage prediction model were determined using the autogenous shrinkage values of UHPC with age. Consequently, the test results showed that, by adding shrinkage reducers and expansive agents, the stiffness of UHPC was rapidly developed at early-ages and the autogenous shrinkage was considerably reduced.

A Study on the Properties of High Performance Concrete Using CSA Expansive Additives and Inorganic Admixtures (CSA계 팽창재 및 무기질 혼화재를 이용한 고성능 콘크리트의 특성에 관한 연구)

  • Han, Cheon-Goo;Bahn, Ho-Yong;Jun, Byung-Chea;Hong, Sang-Hee
    • Magazine of the Korea Concrete Institute
    • /
    • v.11 no.1
    • /
    • pp.141-148
    • /
    • 1999
  • Recently, high performance concrete developed has a good quality at fresh and hardened state, but high binder contents results in spending much money on manufacturing and many cracks by drying and autogenous shrinkage, Therefore, in this paper, not only prevention of cracks caused by drying and autogenous shrinkage, but improvement of quality and accomplishment of economy by applying F.A(fly ash), S.F(silica fume) and CSA(calcium sulfa aluminate) expansive additives as an inorganic admixtures in W/B 35% are discussed. According to the experimental results, when 5% of CSA expansive additives and 15:5(F.A:S.F)are replaced at unit cement content, high performance concrete with both good fluidity at fresh state and high compressive strength, compensation of drying and autogenous shrinkage at hardened state are accomplished.

A Study on the Hydration Reaction Model of Expansive Additive of Ettringite-Gypsum Type (에트링가이트-석탄 복합계 팽장재의 수화반응 모델에 관한 연구)

  • Park Sun Gyu;Takahumi Noguchi;Kim Moo-Han
    • Journal of the Korea Concrete Institute
    • /
    • v.17 no.4 s.88
    • /
    • pp.581-586
    • /
    • 2005
  • High-performance concrete (HPC), which is particularly sensitive to self-desiccation, is required to be durable even in severe environmental conditions, i.e. costal area, cold district, etc. However, in recent years, some attention was particularly given to cracking sensitivity of high performance concrete at early age. It has been argued and demonstrated experimentally that such concrete undergoes autogenous shrinkage due to self-desiccation at early age under restrained condition, nd, as a result, internal tensile stress may develop, leading to micro cracking and macro cracking. This shrinkage-introduced crack produces a major serviceability problem for concrete structures. One possible method to reduce cracking due to autogenous shrinkage is the addition of expansive additive. Tests conducted by many researches have shown the beneficial effects of addition of expansive additive for reducing the risk of autogenous shrinkage-introduced cracking. However, the research on hydration model of expansion additive has been hardly researched up to now. This paper presents a study of the hydration model of Ettringite-Gypsum type expansive additive. As a result of comparing forecast values with experiment value, proposed model is shown to expressible of hydration of expansive additive.

A Study on the Mix Design of the Self-Compaction Concrete for the LNG Tank (LNG Tank용 자기충전 콘크리트의 배합설계에 관한 연구)

  • Kim, Dong-Seok;Park, Sang-Joon;Won, Cheol;Lee, Sang-Soo
    • Journal of the Korea Institute of Building Construction
    • /
    • v.3 no.4
    • /
    • pp.135-138
    • /
    • 2003
  • The purpose of this study was to design the self-compaction concrete mixture, having not only high strength but also compensation of shrinkage without thermal crack under 4 sides outer restraint of the member. In the experimental mix, replacement ratio of limestone Powder, CSA expansive additives, and unit water were selected as parameters, using portland blast-furnace slag cement. And, bleeding test, expansibility test, hydration heat analysis were performed. As a results, when 35% of limestone Powder, 6% CSA expansive additives are replaced at unit water 175kg/$\textrm{m}^3$, demanded performances of fresh and hardened self-compaction concrete are accomplished.