• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05c
• /
• pp.114-117
• /
• 2001

$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$(x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their structural and dielectric properties were investigated with variation of composition ratio and sintering temperature. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around $1020^{\circ}C$ due to the formation of the polycrystalline perovskite phase. BSCT(50/40/10) specimen sintered at $1500^{\circ}C$ showed the highest average grain size(18.25$[{\mu}m]$). Curie temperature and dielectric constant at room temperature decreased with increasing amount of Ca. BSCT(50/40/10) specimen sintered at $1450^{\circ}C$ showed a good dielectric constant, K, (=4324) and dielectric loss, $tan{\delta}$, (=0.972%) properties at 1[KHz].

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1573-1576
• /
• 1997

Thin films of $BaTiO_3$ system were prepared by radio frequency (rf)/dc magnetron sputtering method. We have investigated crystal structure, surface morphology and PTCR(positive-temperature coefficient of resistance) characteristics of the specimen depending on second heat - treatment temperatures. Scanning electron microscope(SEM) image of $BaTiO_3$ thin films shows that the specimen heat treated in between 900 and 1100[$^{\circ}C$] shows a grain growth. At 1100[$^{\circ}C$], the specimen stops grain-growing and becomes a crystal. A resistivity-temperature characteristics of the specimen depends on the doping concentrations of Mn.

• Korean Journal of Materials Research
• /
• v.16 no.8
• /
• pp.466-472
• /
• 2006

The electrical, dielectric properties, and its stability of ZPCCL-based varistors were investigated for different sintering temperatures in the range of $1230{\sim}1300^{\circ}C$. As the sintering temperatures increased, the varistor voltage decreased in the range of $777.9{\sim}108$ V/mm, the nonlinear coefficient decreased in the range of $77.9{\sim}7.1$, and the leakage current increased in the range of $0.3{\sim}50.6\;{\mu}A$. The stability of electrical and dielectric characteristics was obtained from sintering temperature of $1260^{\circ}C$. the varistors sintered at $1260^{\circ}C$ marked the high electrical and dielectric stability, with $%{\Delta}{V_{1mA}=+1.9%,\;%{\Delta}{\alpha}=-10.6%,\;%{\Delta}I_L=+20%\;and\;%{\Delta}tan\;{\delta}=+9.9%$ for DC accelerated aging stress state of $0.95V_{1mA}/150^{\circ}C$/24 h.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1487-1489
• /
• 1994

$(Zr_{0.65}Sn_{0.35})Ti_{1.04}O_4$ system which has a dielectric constant, low dielectric loss and temperature coefficient was investigated. Temperature coefficient varied from positive to negative with increasing of NiO. For the NiO content 1.0wt%. i.e $(Zr_{0.65}Sn_{0.35})Ti_{1.04}O_4$, the ceramic showed very good dielectric properties such as ${\epsilon}$=37.8, $Q{\times}f_o=49.000$ and ${\tau}_r= 4{\pm}1ppm/^{\circ}C$.

• Journal of Powder Materials
• /
• v.11 no.5
• /
• pp.363-368
• /
• 2004

In the present study, the focus is on the analysis of the effect of the mold dimensions on the temperature distribution of a die during plasma activated sintering. The temperature distribution of a cylindrical mold with various dimensions was measured using K-type thermocouples. The temperature homogeneity of the die was studied based on the direction and dimensions of the die. A temperature gradient existed in the radial direction of the die during the plasma activated sintering. Also, the magnitude of the temperature gradient was increased with increasing sintering temperature. In the longitudinal direction, however, there was no temperature gradient. The temperature gradient of the die in the radial direction strongly depended on a ratio of die volume to punch area.

• Journal of the Korean Ceramic Society
• /
• v.17 no.2
• /
• pp.89-95
• /
• 1980

The effect of non-stoichimetry and sintering temperature on the magnetic properties of materials in the system $Ni_{0.39}Zn_{0.61}Fe_{2.0+x}O_4$ have been investigated. The value of x used in initial weighing of oxides were varied from -0.04 to -0.12. The value of x, however, appears to be from +0.04 to -0.04 after ferrite powder preparation due to iron pick up during ball mill mixing and grinding. The densities of specimens which were deficientinrion were higher than those with excess ion. Specimens with near stoichiometric composition showed maximum initial permeability an dminimum coercivity whereas high values of quality factor (Q) were observed in iron deficient specimens. The quality factor decreased monotonically with increasing sintering temperature, but the permeability showed maxima with increasing sintering temperature. Thus highest value of figure of merit $\mu$Q was obtained in composition $Ni_{0.39}Zn_{0.61}Fe_{1.98O4}$ sintered at 100$0^{\circ}C$ for 3 hrs. in an air atmosphere.

• Journal of the Korean Ceramic Society
• /
• v.43 no.9 s.292
• /
• pp.558-563
• /
• 2006

The electrical and dielectric properties of $ZnO-Pr_6O_{11}CoO-Cr_2O_3La_2O_3-based$ nonlinear resistors were investigated at different sintering temperatures in the range of $1230{\sim}1300^{|circ}C$. As the sintering temperature increased, the breakdown voltage decreased from 777.9 to 108.0V/mm, the nonlinear coefficient greatly decreased from 77.0 to 7.1, and the leakage current increased from $0.4{\mu}A\;to\;50.6{\mu}A$. On the other hand, the donor density from $0.90{\times}10^{18}\;to\;2.59{\times}10^{18}/cm^3$ and the barrier height decreased from 1.89 to 0.69 eV with increasing temperature. The dielectric dissipation factor increased from 0.0879 to 0.2839 for the increase of sintering temperature.

• 한국기계연구소 소보
• /
• s.20
• /
• pp.65-70
• /
• 1990

The $Y_2 BaCuO_5$ phase was synthesized under various calcination temperatures and sintered. The $Y_2 BaCuO_5$ phase strarted to form at $850^{\circ}C$ for 6hours calcination time and, at $1000^{\circ}C$, all the X-ray diffraction peaks corresponded to $Y_2 BaCuO_5$. The sintered density of $Y_2 BaCuO_5$ was increased to 97 % of its theoretical density by the control of calcination temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.242-245
• /
• 2000

The electrical properties of ZPCCE (ZnO-Pr$_{6}$O$_{11}$-CoO-Cr$_2$O$_3$-Er$_2$O$_3$) based varistors were investigated with sintering temperature in range of 1335 to 135$0^{\circ}C$ for 1h. As the sintering temperature increases, the nonlinear exponent decreased, but was high beyond 40 except for 1.0 mol% Er$_2$O$_3$. Among all ZPCCE varistors, the varistor having the highest nonlinear exponent was obtained by sintering at 1335$^{\circ}C$, containing 2.0 mol% Er$_2$O$_3$ and then the nonlinear exponent was 78.05, and the varistors with 0.5 mol% Er$_2$O$_3$ exhibited the lowest leakage current of 1.92 $\mu$A.A.A.

• Proceedings of the KIEE Conference
• /
• 2006.07c
• /
• pp.1703-1704
• /
• 2006

In this paper, PZT(20/80) thick films were fabricated by the screen-printing method. And the PZT(80/20) coating solution was synthesized by the sol-gel method. PZT(20/80) thick films were screen-printed on the alumina substrates. PZT(80/20) thin film was spin-coated on the PZT(20/80) thick films to obtain densification. And the structural and electrical properties of PZT thick films were investigated with variation of sintering temperature. The PZT specimen sintered at $650^{\circ}C$ showed good relative dielectric constant of 219 and dielectric loss of 2.45%. Also the remanent polarization and the coercive field were $16.48{\mu}C/cm^2$ and 35.48kV/cm, respectively.