• Membrane Journal
• /
• v.8 no.2
• /
• pp.77-85
• /
• 1998

To treat effectively EDIR (electrodeposition ion removal) wastewater in terms of CO$_{Mn}$ 1,500~2,000 ppm generated from aluminum painting process, a RO (reverse osmosis) process was designed and installed to recover and reuse the concentrated solvent sent back to the electrocodeposition tank while the permeate reused as rinse water. A RO system in which three polyamide-spiral wound modules ($102\Phi \times 1,016L$ mm) connnected in series had been running to treat 20 m$^3$ in waste volume in 3 days batch operation at the condition of system recovery of 30 %, applied pressure 11.5 $kg_f/cm^2$ and room temperature. During 42 hours continuous operation leading to 5-fold decrease in waste volume, nearly constant permeation flux of 390 l/m$^2$-hr was maintained and the permeate with average CO$_{Mn}$, 300 ppm was obtained which could be used for washing the remaining paint solution in ion-exchange tower instead of demineralized water. Also COD$_{Mn}$ rejection as a function of running time was observed to be in the range of 78~87 % and the observed solvent rejections for ethyl cellusolve, buthyl cellusolve and n-butanol were 79 %, 87 % and 70 %, respectively.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2020.06a
• /
• pp.353-353
• /
• 2020

기후변화에 적응하기 위해 많은 나라들이 수자원 관리 전략을 마련하고 있으며, 대체 수자원 활성화 방안에 관심을 기울이고 있다. 본 연구에서는 대체 수자원 활성화 방안 중 빗물 저류지의 용량 결정 방법을 제시하고자 한다. 빗물 저류지의 용량을 결정하기 위해 메타 휴리스틱 방법 중 하나인 입자 군집 최적화(particle swarm optimization; PSO)를 선정하였다. 이는 기존 실제 설계에 사용되고 있는 시행착오법보다 시간을 단축시킬 수 있다. 최적화 모형은 python의 pyswarm package를 이용해 구성하였다. 모형의 입력자료는 저류지 유입량과 목표 공급량, 목표 보장률이고, 목적함수는 빗물 저류지 용량의 최소화이다. 제약조건은 모의된 보장률이 목표 보장률 이상을 달성하는 것이다. 여기서, 보장률은 전체 모의 기간 중 목표 공급량을 공급한 기간의 비율이다. 제시한 방법론의 적용성을 검토하기 위해 실제 저류지가 설계된 인천의 청라지구 1공구를 선정하여 적용하였다. 최적화 모형의 입력 유입량은 SWMM으로 산정된 1995년부터 2004년까지의 유출량이며, 목표 공급량은 실제 설계에 활용된 용수 목적별 요구 수량이다. 여기서 용수 목적별 요구 수량은 대상지역의 노면 청소수, 화장실 세정수, 호수 유지수 등이다. 산정 결과 계산 시간은 약 30초 소요되며, 목표 보장률을 만족하는 저류지 용량이 결정되었다. 본 연구에 제시한 방법은 제약조건이 추가되어도 기존 시행착오법에 비해 간편함을 확인하였다.

• Journal of Korean Society of Environmental Engineers
• /
• v.31 no.7
• /
• pp.491-498
• /
• 2009

We studied to develop high-efficiency removal system of odor and VOCs(Volatile Organic Compounds) from environmental infrastructure facilities and oil refineries, painting facilities and so on. It can replace RTO and RCO. We tried an removal experiment for VOCs (toluene, xylene, benzene, MEK(methyl ethyl ketone), ethanol, formalin etc. and odor compounds (hydrogen sulfide, etc.). In process, as pre-treatment we used the scrubber with vortex flow (Multi-scrone) to remove the hydrophilic VOCs and as post-treatment, used fibrous bio-filter to remove the hydrophobic VOCs. This hybrid system remove with high efficiency both the hydrophilic VOCs and hydrophobic VOCs. And we tried to make this system to be compact. In experiment using Multi-scrone, contact time is 2~3 seconds and absorption scrubbing water is diaphragm-type electrolysis water. hydrophilic VOCs like ethanol and relatively hydrophilic odor compounds like hydrogen sulfide is excellent, these substances has been removed almost completely, respectively 95~99%, 93~97%. And for MEK, formalin also Showed a high removal efficiency, respectively 78~90%, 72~85%. But in experiment using Multi-scrone, the hydrophobic VOCs like BTX showed a low removal efficiency, respectively 16~22%, 12~18%, 8~16%. In hydrophobic VOCs, toluene removal experiment using fibrous bio-filter, early efficiency was low but after 10days, adaptation period showed high efficiency 85~95%. but in the mixed phase, toluene and MEK efficiency reduced 5~10%. this show microorganism treat first MEK easy to remove. The removal efficiency for MEK using the fibrous biofilter was stable, 80~92%. This hybrid system is also high economical efficiency for RTO. This system reduce more than 50% the cost of equipment and maintenance. As a result, we expect this technology is in the limelight as high efficiency treatment of VOCs in mid-low price.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.33 no.2
• /
• pp.365-372
• /
• 2004

The purpose of this study was to implement HACCP system to foodservice of W and D elementary schools with joint-lunch management system in Kyungsan area. Steamed rice with squid was selected and Control Action, Monitoring Procedure and Control measure were identified based on HACCP flowchart to produce safe and healthy food. It was suggested that frozen squid must be thawed under the cold running city water and kept temperature below 1$0^{\circ}C$ and receiving/thawing procedure has to be done within 30 min. Raw vegetables must be washed under three-tube wash stand and whole prepreparation procedures should be done in 20 minutes. Clean and sanitize all the equipment and utensils before and after handling squid. Knives and cutting boards for vegetable and squid should be classified. Sauce for steamed rice with squid should be heated about 21 minutes to reach the temperature of 94$^{\circ}C$ before serving and internal temperature of food must be kept above 84.4$^{\circ}C$ during serving. The ideal temperature of kitchen should be remained 15∼18$^{\circ}C$. The underground water has to be excluded to minimize the risk of contamination in the foodservice facility and the prepreparation place must be separated with cooking place. Also, Personal hygiene Practice should be check in each stage. Further, additional research needs to be conducted to determine models for HACCP implementation for different menu.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.69-74
• /
• 2015

With difficulties during the cleaning of reflow flux residues due to the decrease of the part size and interconnection pitch in the advanced electronic devices, the need for the no-clean solder paste is increasing. In this study, an epoxy curable solder paste was made with SAC305 solder powder and the curable flux of which the main ingredient is epoxy resin and its reflow solderability, flux residue corrosivity and solder joint mechanical properties was investigated with comparison to the commercial rosin type solder paste. The fillet shape of the cured product around the reflowed solder joint revealed that the curing reaction occurred following the fluxing reaction and solder joint formation. The copper plate solderability test result also revealed that the wettability of the epoxy curable solder paste was comparable to those of the commercial rosin type solder pastes. In the highly accelerated temperature and humidity test, the cured product residue of the curable solder paste showed no corrosion of copper plate. From FT-IR analysis, it was considered to be resulted from the formation of tight bond through epoxy curing reaction. Ball shear, ball pull and die shear tests revealed that the adhesive bonding was formed with the solder surface and the increase of die shear strength of about 15~40% was achieved. It was considered that the epoxy curable solder paste could contribute to the improvement of the package reliability as well as the removal of the flux residue cleaning process.

• Korean Journal of Materials Research
• /
• v.6 no.8
• /
• pp.817-824
• /
• 1996

Removal of Cu impurities on Si substrates using remote H-plasma was investigated. Si substrates were intentionally contaminated by 1ppm ${CuCI}_{2}$, standard chemical solution. To determine the optimal process condition, remote H-plasma cleaning was conducted varying the parameters of rf power, cleaning time and remoteness(the distance between the center of plasma and the surface of Si substrate). After remote H-plasma cleaning was conducted, Si surfaces were analysed by TXRF(total x-ray reflection fluorescence) and AFM(atomic force microscope). The concentration of Cu impurity was reduced by more than a factor of 10 and its RMS roughness was improved by more than 30% after remote H-plasma cleaning. TXRF analysis results show that remote H-plasma cleaning is effective in eliminating Cu impurity on Si surface when it is performed under the optimal process condition. AFM analysis results also verifies that remote H-plasma cleaning makes no damage to the Si surface. The deposition mechanism of Cu impurity may be explained by the redox potential(oxidation-reduction reaction potential) theory. Based on the XPS analysis results we could draw a conclusion that Cu impurities on the Si substrate are removed together with the oxide by a "lift-off" mechanism when the chemical oxide( which forms when Cu ions are adsorbed on the Si surface) is etched off by reactive hydrogen atoms.gen atoms.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.16 no.11
• /
• pp.2525-2531
• /
• 2012

Al-Cu alloy has been used as a circuit material for its low resistance and ease to process for long years at CMOS technology. However, basically metal is very susceptible to corrosion and which has been a long pending trouble in various fields using metal. The defect causes the reliability concerns, so improved methods are necessary to reduce the defect. In the various corrosion parameters, PR strip process conditions after metal etch and optimal cleaning solutions are controllable and increase the process margin to prevent the metal corrosion. This study proposes that chlorine residue after metal etch as the source of metal corrosion, and charges should be removed by optimizing PR strip process condition and cleaning condition.

• Journal of Korea Soil Environment Society
• /
• v.2 no.2
• /
• pp.53-60
• /
• 1997

A series of batch and lab-scale pilot tests were conducted to optimize the design parameters for the application of soil washing techniques to the soil contaminated by heavy metals. Cu, Pb, and Zn were selected as target heavy metals. The concentrations of Cu, Pb, and Zn were 500mg/kg dry soil, 1, 000mg/kg dry soil, and 500mg/kg dry soil, respectively. Citric acid and oxalic acid were used for the extractants. In the batch tests, the extraction efficiencies for Cu, Pb, and Zn were 79%, 72%, 72%, respectively. The proper extractant concentration and dilution ratio(weight/volume) for Cu and Pb were turned to be citric acid 50mM and 1:5, respectively. The extraction efficiencies were enhanced with the addition of 1~2% OA-5 or SDS. From pilot scale tests for Pb, first stage and second stage of soil washing resulted in the extraction efficiency of 59% and 78%, respectively.

• Proceedings of the KAIS Fall Conference
• /
• 2006.05a
• /
• pp.585-586
• /
• 2006

본 연구에서는 고도처리를 위한 BNR 공정에 사용되는 MBR (Membrane Bioreactor)의 막 오염(membrane fouling)을 저감시키기 위해 분리막을 침지시킨 침전조를 상하로 나누어 상부는 폭기조로, 하부는 침전조의 역할을 수행하게 하는 새로운 형태의 막분리 침전조 (aerated settler)의 성능을 평가 하였다. 막분리 침전조는 상하로 구분하기 위해서 baffle을 설치하였다. 파일럿 규모 ($Q=50m^3/d$)의 MBR 공정은 실제 오수를 유입수로 사용하였으며 약 6개월간 운전하였다. 탈질을 위하여 막분리 침전조 하부에서 무산소조로 반송되는 반송수의 DO를 크게 줄어들게 함으로써 무산조에서의 탈질효율이 증가되었다. 처리수의 총 TN 제거율은 75%이었다. 또한 막분리침전조 상 하부의 MLSS 농도 차에 의해 상부에 침지된 막 모듈은 기존의 MBR 공정보다 막 오염 저감 효과가 있어서 세정주기가 증가하였다. 운전 개시 후 4개월째 되는 시점에 TMP가 40cmHg에 도달하여 1회 화학적 약품세정만이 필요하였다.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.1810-1814
• /
• 2008

A small L-type megasonic module for nano-pattern cleaning was designed and manufactured. The impedance graph of the quartz waveguide with a piezoelectric actuator was predicted using finite element method (FEM). The peak value of the piezoelectric actuator alone was 3.373 MHz, which was the same as the experimentally measured value of 3.373 MHz (0.0% error). In addition, the maximum impedance value of the quartz waveguide with the actuator was 3.373 MHz, which agreed well with the measured value of 3.362 MHz (0.3% error). The acoustic pressures of a conventional megasonic system (3 MHz) and the developed system under similar conditions were measured and compared. The results showed that the maximum values and standard deviations of the developed system decreased by 29% and 18%, respectively, compared with the conventional type. This suggests that the small L-type would have higher particle removal efficiency with lower possibilities of pattern damages.