Using a surface modification technique, ion beam assisted deposition (IBAD) of Ti thin film it becomes possible to prepare an active ceramic surface to braze $Al_2O_3$-STS304 with conventional Ag-Cu eutectic composition filler metal. Researches on bonding formations at interfaces of ceramic joints were mainly related on the development of filler metals to ceramic, the process parameters, and clarifications of reaction products. From the results, the reactive brazing is a very convenient technique compared to the conventional Mn-Mo method. However melting point of reactive filler is still higher than that of Ag-Cu eutectic and it forms the brittle inter metallic compound. Recently several new approaches are introduced to overcome the main shortcomings of the reactive metal brazing in ceramic-metal, metal vapor vacuum arc ion source was introduced to implant the reactive element directly into the ceramics surface, and sputter deposition with sputter etching for the deposition of active material.

• Korean Journal of Materials Research
• /
• v.10 no.10
• /
• pp.703-708
• /
• 2000

As the engine design changes to get high efficiency and performance of commercial diesel engine, surface w wear of the earn follower becomes an important issue as applied load increasing at the contact face between cam follower and cam. We developed the ceramic cam follower made of sili$\infty$n nitride ceramic which was more wear resistant than the cast iron or sintered metal cam follower. Ceramic cam follower was made by direct brazing of thin ceramic disk to steel body using an active brazing alloy without the interlayer. In-situ crowning(R), resulted from the difference of thermal expansion coefficient between ceramic and carbon steel after direct brazing without any stress-relieving inter]ayer, could be controlled. When a earbon steel was heated above $A_{c1}$ point and then c$\infty$led, the expansion curve represented a hysteresis. Appropriate crowning was achieved below the $A_{c1}$ point(about $723^{\circ}C$) and crowning increased with brazing temperature exponentially above the $A_{c1}$ point. Optimum brazing temperature range was from 700 to $720^{\circ}C$. We developed successfully the ceramic cam follower having appropriate crowning and being inexpensive. Also we could successfully control the crowning of ceramic earn follower by hysteresis behavior of thermal expansion of earbon steel during direct brazing process.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.1000-1007
• /
• 2001

In an evacuated tube solar collector, the stable sealing of the heat pipe to the glass tube is important for the collector to use for a long period of time. The sealing of copper tube to the glass is quite difficult because of the large differences in the physical and chemical properties of the two materials. In this study, therefore, a proper copper oxide layer was induced to improve the chemical bonding of the two materials, and the oxidation state of copper and the interface between copper and glass were examined by XRD, SEM and EDS. Its bonding strength was also measured. Cu$_2$O was formed when the bare copper was heat-treated under 600$^{\circ}C$, while CuO oxide layer was formed above that temperature. The bonding state of CuO to the copper was very poor. The borate treatment of the copper, however, extend the stable forming of Cu$_2$O layer to 800$^{\circ}C$. Borosilicate glass tube was sealed to a copper tube by Housekeeper method only when the sealing part was covered with Cu$_2$O layer. The bonding strength at the interface was measured 354.4N, its thermal shock resistance was acceptable.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.3
• /
• pp.223-233
• /
• 2011

A ceramic monolithic catalyst is a honeycomb structure that consists of two layers. The honeycomb structure is regarded as a continuum in structure and heat-flow analysis. The equivalent mechanical properties of the honeycomb structure were determined by performing finite element analysis (FEA) for a test specimen. Bending strength experiments and FEA of the test specimen used in ASTM C1674-08 standard test were performed individually. The bonding coefficient between the cordierite ceramic layer and the washcoat layer was almost zero. The FEA test specimen was modeled on the basis of the bonding coefficient. The elastic modulus, Poisson's ratio, and the thermal properties of the ceramic monolithic substrate were determined by performing the FEA of the test specimen.

• Journal of the Korean Ceramic Society
• /
• v.37 no.10
• /
• pp.994-1000
• /
• 2000

Mn-Ni-Co계 스피넬을 모재로 선택하여 상업용 페라이트 등 다양한 종류의 Fe-스피넬과 동시 소결 가능성을 검토할 목적으로 각 소재의 소결 거동, 서미스터와의 계면 반응이나, 2차상의 형성 등에 대해 알아보았다. 대부분의 페라이트 조성이 Mn 스피넬과 새로운 2차상을 형성하지는 않는 것을 알 수 있었다. 상업용 페라이트의 경우 115$0^{\circ}C$ 소결 온도에서 접합이 가능한 조성은 다량의 액상이 존재하며 접합계면의 폭이 상대적으로 넓으므로 서미스터 특성에도 좋지 않은 영향을 줄 수 있을 것으로 생각된다. 반면에 MFN1과 MFN2 조성은 접합계면에서 새로운 2차상이 형성되지 않고 원소의 상호확산도 작아 NTC 서미스터의 동시소결용 보호재로서의 가능성이 높은 것으로 확인되었다.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.654-660
• /
• 1991

Stabilized Zirconia (3 mol % Yttria, 3Y-TZP) was joined with intermetallic compound NiTi which has similar thermal expansion coefficient. The optimum bonding condition was determined by the Taguchi Method. Under the optimum bonding condition, the 4-point bending strength was as high as 400 MPa. bonding interfaces were examined by optical microscope, SEM, and TEM; reaction products were identified by XRD and TEM, The relationship between products and strength was examined.

• Proceedings of the KWS Conference
• /
• 1990.11a
• /
• pp.145-147
• /
• 1990

• Korean Journal of Materials Research
• /
• v.6 no.9
• /
• pp.963-971
• /
• 1996

세라믹 강화 복합 재료의 모재로서 사용되는 무정형 PEEK가 보여주는 self-bonding 현상의 주 기구인 PEEK체인들의 확산(interdiffusion)과 뒤엉킴(entanglement)이 일어나기 위하여 PEEK의 접합 면에서 반드시 선행되어 일어나야 하는 젖음성의 정도에 미치는 접합 공정 변수의 영향을 C-mode acoustic microscopy를 이용하여 고찰하였다. 또한 self-bonding 된 PEEK시편들의 전단 변형시 전단 하중의 증가에 따라 일어나는 접합 면에서의 debonding 정도를 측정함으로써 접합 면에서 일어나는 파괴 거동을 관찰하였다. 각각의 접합 조건에서의 젖음성의 정도는 시간과 압력의 증가에 따라 다소 증가함을 보여 주었으나, 접합 온도와는 거의 무관함을 보여 주었다. 또한 전단 파괴 시험시 각각의 접합 조건 하에서 개발된 self-bonding강도의 80%-90%이상의 전단 하중이 가해진 후부터 debonding이 시작되어, 이 후 하중이 증가함에 따라 급속도로 진행되어 파괴가 일어남을 알 수 있었다.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.189.2-189
• /
• 2003

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.140.2-140
• /
• 2003