• Applied Chemistry for Engineering
• /
• v.10 no.2
• /
• pp.212-217
• /
• 1999

Porous alumina membrane with asymmetrical structure was prepared by anodic oxidation under constant DC current mode in aqueous solution of sulfuric acid. In order to produce membrane with improved properties, the aluminium plate was pre-treated with thermal oxidation, chemical polishing and electrochemical polishing before anodic oxidation. The thickness and pore diameter of the membrane were controlled by current density and charge density, respectively. The upper layer of 20 nm under of pore diameter was produced under very low current density while the lower layer of 36 nm pore diameter was produced under higher current density. The thickness of the membrane was about $80{\sim}90{\mu}m$ and that of the upper layer was $6{\mu}m$. We found that the mechanism of gas permeation through the membrane depended on Knudsen diffusion.

• Polymer(Korea)
• /
• v.37 no.5
• /
• pp.592-599
• /
• 2013

In this study, polyacrylonitrile (PAN)-based porous carbon nanofibers were prepared from PAN polymer solution by electrospinning and KOH activation with various concentrations, and the characterization of pore structures and carbon dioxide adsorption was investigated. Manufactured PAN-based activated carbon nanofibers tend to decrease diameter and increase surface oxygen functional groups depending on the increasing concentration of KOH solution. In addition, according to the results of nitrogen adsorption for pore properties analysis, it indicated increase of the specific surface area in conformity with increasing concentration of KOH solution. Micropore volume of treated activated carbon nanofibers (ANCF) by 4 M KOH was the largest compared with other samples and mesopore volume of treated ANCF by 8 M KOH was the largest volume, respectively. The concentration of KOH effects textural and surface properties, as represented by BET and XPS, which enhance carbon dioxide adsorption capacity at 0 and $25^{\circ}C$.

• Journal of Adhesion and Interface
• /
• v.24 no.4
• /
• pp.136-142
• /
• 2023

In this study, TEOS was used as a silica source, and a triblock copolymer (P123) was used as a template to produce mesoporous silica with a well-ordered hexagonal mesopore array through a self-assembly method and hydrothermal process under acidic condition. (Surfactant-extracted SBA-15). Surfactant-extracted SBA-15 showed the particle shape of a short rod with a size of approximately 980 nm. The surface area and pore diameter were 730 m²g^-1 and 70.8 Å, respectively. Meanwhile, aminosilane (3-aminopropyltriethoxysilane, APTES) was grafted into the mesopores using a post-synthesis method. Mesoporous silica (APTES-SBA-15) modified with aminosilane had a well-ordered pore structure (p6mm) and well-maintained the particle shape of short rods. The surface area and pore diameter of APTES-SBA-15 decreased to 350 m²g^-1 and 60.7 Å, respectively. APTES-modified mesoporous silica was treated with a solution of rare earth metal ions (Eu³⁺, Tb³⁺) to synthesize a mesoporous silica material in which rare earth metal complexes were introduced into the mesopores. (Eu/APTES-SBA-15, Tb/APTES-SBA-15) These materials exhibited characteristic photoluminescence spectra by λ_ex=250 nm. (⁵D₄→⁷F₅ (543.5 nm), ⁵D₄→⁷F₄ (583.5 nm), ⁵D₄→⁷F₃ (620.2 nm) transitions for Tb/APTES-SBA-15; ⁵D₀→⁷F₀ (577.7 nm), ⁵D₀→⁷F₁ (592.0 nm), ⁵D₀→⁷F₂ (614.9 nm), ⁵D₀→⁷F₃ (650.3 nm) and ⁵D₀→⁷F₄ (698.5 nm) transitions for Eu/APTES-SBA-15)

• Journal of Korean Society of Environmental Engineers
• /
• v.22 no.7
• /
• pp.1319-1330
• /
• 2000

Activated carbons prepared by chemical activation of organic waste sludges with $ZnCl_2$ and $K_2S$ have been studied in terms of their pore development and adsorptivity. Pore development of the carbons prepared from organic waste sludges was characterized by the nitrogen adsorption at 77K. The $ZnCl_2$-activated carbon produced by chemical activation with zinc chloride exhibited type I isotherm characteristics according to the BDDT classification, suggesting the presence of micropores formed by activation process. The isotherms of the commercial powdered activated carbon and $K_2S$-activated carbon reveal a hysteresis similar to that of type IV in BDDT classification, indicating the formation of mesopores. This result implies that the major pores of $K_2S$-activated carbon are composed of meso and micropores, and a macropores are minor. The adsorptive capacities of metal on the $K_2S$-activated carbon prepared from organic waste sludges were found to be superior to those on a commercial granular activated carbon. The Langmuir and Freundlich isotherms yield a fairly good fit to the adsorption data, indicating a monolayer adsorption of metals onto $K_2S$-activated carbon. The adsorptive capacity of the $K_2S$-activated carbon was superior to $ZnCl_2$-activated carbon for $PO_4$-P, and vice versa for $NO_3$-N. From the results of the studies reported here, it can be concluded that activated carbons with adsorptivity superior to commercial granular activated carbons can be produced from organic waste sludge using a two-step carbonization/activation procedure with zinc chloride or potassium sulfide as the activating agents.

• Applied Chemistry for Engineering
• /
• v.29 no.2
• /
• pp.237-243
• /
• 2018

The surface chemistry of WCK-AC, WCN-AC and WCZ-AC which are activated carbons prepared from waste citrus peel using KOH, NaOH, and $ZnCl_2$ as activating chemicals were investigated. Also the relationships between the adsorption capacities of the target gases such as acetone, benzene and methyl mercaptan (MM) by the prepared activated carbons and the pore characteristics of each activated carbon were examined. According to XPS analysis of the prepared activated carbons, graphite and phenolic were the main surface functional groups of C1, and the sum of phenol, carbonyl and carboxyl groups increased in the order of WCK-AC > WCN-AC > WCZ-AC. The breakthrough curves obtained from the adsorption experiments for the three target gases in the fixed bed adsorption reactor were well simulated by the empirical equations proposed by Yoon and Nelson. The adsorption capacity for acetone, benzene and MM was larger for activated carbons with the larger sum of surface functional groups. The larger the specific surface area and the pore volume of activated carbons and the smaller the pore size, the better the adsorption performance. In particular, the specific surface area was the best criterion for the adsorption performance of activated carbons used in this study.

• Applied Chemistry for Engineering
• /
• v.27 no.4
• /
• pp.449-454
• /
• 2016

In this study, highly monodispersed porous carbon microcapsules with a hollow core were synthesized using polystyrene (PS) beads as a hard template. The surface of PS was first modified with polyvinylpyrollidone (PVP) for the easy attachment of inorganic silica sol. After coating the surface of PVP modified PS microspheres with SBA-16 sol, the carbon microcapsules with a hollow macroporous core were fabricated through reverse replication method by filling carbon sources in the mesopores of silica mold. The hollow carbons having a mesoporous shell structure and narrow particle size distribution could be obtained after the carbonization of carbon source and the dissolution of silica mold by HF solution. The mesoporous characteristics and electrochemical properties of hollow carbon microcapsules were characterized by XRD, SEM, TEM, $N_2$ adsorption/desorption analysis and cyclic voltammetry. They showed the high electric conductivity and capability for use as efficient electro-materials such as a supercapacitor.

• Applied Chemistry for Engineering
• /
• v.8 no.6
• /
• pp.1048-1053
• /
• 1997

Modified mordenites by HF treatement, which have different $SiO_2/Al_2O_3$ ratio, and those mixed with $\gamma$-alumina are prepared and used for catalytic cracking of triphenylmethane(TPM) in micro-activity tester(MAT). Dealumination of mordenites decreased the acid content but developed secondary mesopores. The conversion and the selectivity of benzene over modified mordenites with the mesopores were increased. However, for the further dealuminated mordenites, they decreased due to the destruction of pore structure and low acid amount. Accordingly, the maximum cracking activity and the maximum selectivity of benzene were obtained about 17 $SiO_2/Al_2O_3$ ratio of modified mordenites. The modified mordenites mixed with alumina enhanced the cracking activity of TPM compared with the pure mordenites. It can be explained that TPM is cracked at active sites with in large pores of alumina firstly and further cracked into small molecules in zeolite pores as step mechanism of catalytic cracking.

• Elastomers and Composites
• /
• v.33 no.3
• /
• pp.185-192
• /
• 1998

This study was investigated on the physical properties of synthetic rubber compounds containing silica and silane copuled silica. Surface area and pore volume of silane copuled silica appeared to be low compared with those of pure silica because silane coupling agent blocks the pore of silica surface during silanization reaction. Silica with large surface area and high structure showed the short scorch time$(t_5)$ and rapid cure rate. The silane coupled silica showed the shorter scorch time and more rapid cure rate than pure silica because of the of effect of sulfur in the silane coupling agent(Si 69), The high value of $N_2SA$ minus CTAB com-pared with surface area and structure of silica showed the high 300% modulus. Also, the surface area and structure of silica did not affected the amount of PICO loss that indicate the abrasion resistance but affected the amount of cut and chip loss.

• 한국전자현미경학회:학술대회논문집
• /
• 2004.11a
• /
• pp.95-99
• /
• 2004

• Proceedings of the Membrane Society of Korea Conference
• /
• 1993.06a
• /
• pp.1-29
• /
• 1993

막 분리는 막의 물리화학적 특성, 분리대상 물질의 물리화학적 특성, 그리고 물질의 이동현상을 조절하는 압력차, 농도차 및 전위차 등의 추진력, 이 세가지 요소의 조합에 의해 행해진다. 막은 막을 구성하고 있는 물질의 물성, 구조, 막의 응용분야 및 역할 등에 의하여 세공막(Macroporous membranes), 미세공막(Microporous membranes), 비공성막(Nonporous membranes)등으로 분류된다.