• Journal of the Korea Concrete Institute
• /
• v.24 no.5
• /
• pp.525-533
• /
• 2012

In this study, bending tests were performed on beam specimens made of UHPCC with the fiber content range of 0~5 vol% to investigate the contribution of fiber content to first cracking strength and flexural tensile strength. Also, four-point bending tests for unnotched beam as well as three-point bending test for notched beam were performed to estimate the effect of the presence of notch on the strengths. The experiment result showed that the increase in fiber content made linear improvement in the flexural tensile strength; whereas first cracking strength was enhanced only when at least 1 vol% of fibers was incorporated. Comparison of the bending test results with and without notch showed that the notch effect varied with the fiber content. The increase in fiber content diminished the effect of stress concentration on the notch tip, reducing the difference in the strengths. With much higher fiber content, the effect of stress concentration almost disappeared and the defection on cracking plane or the size effect dominated the strengths, consequently resulting in higher strengths in the notched beams than the unnotched ones.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.67-75
• /
• 2011

The effect of steel-fiber contents on the compressive behavior of ultra high performance cementitious composites (UHPCC) was studied to propose a compressive behavior model for UHPCC. The experiments considered fiber contents of 0~5 vol.% and the results indicated that compressive strength and corresponding strain as well as elastic modulus were improved as the fiber contents increased. Compared to the previous study results obtained from concrete with compressive strength of 100MPa or less, the reinforcement effect on strength showed similar tendency, while the effect on the strain and elastic modulus were much less. Strength, strain, and elastic modulus according to the fiber contents were presented as a linear function of fiber reinforcement index (RI). Fiber reinforcement in UHPCC had no influence on the shape of compressive behavioral curve. Considering its effect on compressive strength, strain, and elastic modulus, a compressive stress-strain relation for UHPCC was proposed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.4
• /
• pp.109-115
• /
• 2015

High performance fiber reinforced cementitious composite (HPFRCC) can provide high fracture energy absorption as well as high strength with high fiber volume fraction. The increased fracture energy helps resisting high frequency loadings, such as earthquake, impact or blast. This study investigates the flexural performance of slurry infiltrated fiber concrete (SIFCON), one of the important HPFRCC, with respect to varying fiber volume fraction. The maximum fiber volume fraction was 8.0 % and reduced to 6.0% by 0.5% and the maximum volume fraction is obtained by packing fibers with simple tapping by hands. The used fiber was a steel fiber with the length 30 mm and the diameter of 0.5 mm. The flexural strengths were 48.7 MPa at 8.0 % and 22.8 MPa at 6.0 %. The measured flexural strength is much higher compared to other cememtitious composite materials but decreased proportional to the fractions. This result implies that for SIFCON considered herein the reduced amount of steel fibers may affect its flexural performance in a negatively way. The flexural toughness, an index to represent the fracture energy absorption, also decreased with the reduced fiber amount.

• Journal of the Korea Concrete Institute
• /
• v.18 no.6 s.96
• /
• pp.743-748
• /
• 2006

This paper presents results of an experimental study conducted to investigate the effect of volume fraction of fibers on the mechanical properties of a fiber-reinforced, lightweight aggregate concrete(FRLAC) that was produced without an autoclave process. The FRLAC enhanced the strength of lightweight, cellular concrete by adding polypropylene fibers and lightweight aggregates. To investigate the effect of volume fraction of fibers on the mechanical behavior of FRLAC and to determine the optimal volume fraction of fibers, a series of compression and flexural strength tests on FRLAC specimens with various fiber volume fractions(0%, 0.10%, 0.25%, 0.50%) were conducted. It was observed from the tests that a 0.25% volume fraction of fibers maximized the increase in the strength of FRLAC and the fibers controlled cracking in FRLAC.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.537-538
• /
• 2009

To estimate the effect of fiber volume fraction on first cracking strength and flexural tensile strength of UHPC, flexrual tensile tests were carried out within 5 vol.% fiber reinforcement. The test results informed that both first cracking strength and flexural tensile strength improved linearly as fiber volume fraction increased.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.2A
• /
• pp.105-113
• /
• 2011

This study evaluated the effects of fibers on the mechanical properties and chemical solution resistance of porous concrete with fiber type (jute, pulp, PVA and nylon fiber) and fiber volume fraction (0.0%, 0.1%, 0.2%, 0.3%). The tests that were carried out to analysis the properties of porous concrete included compressive strength, void ratio, pH value, and chemical solution exposure with varying type and volume fraction of fiber were conducted. The type and volume fraction of fiber also affected the void ratio, compressive strength, flexural strength and chemical solution exposure. Increased volume fractions of fiber resulted in improved properties of the compressive strength, flexural strength and void ratio. However, the difference between the measured pH value and chemical resistance of porous concrete with fiber type and volume fraction was not significant.

• Journal of the Korea Concrete Institute
• /
• v.27 no.3
• /
• pp.229-236
• /
• 2015

This paper describes the effect of aggregate size on compressive behavior of high-strength steel fiber reinforced concrete. The Specified compression strength is 60 MPa and the range of fiber volume fraction is 0~2%. The main variable is the aggregate size, which was used for the aggregate size of 8 and 20 mm. So, ten concrete mixtures were prepared and tested to evaluate the fresh and hardened properties of SFRC at curing ages (7, 14, 28, 56 and 91 days), respectively. Items estimated in this study are the fresh properties (air contents, slump), hardened properties (compressive strength, modulus of elasticity, post-peak response and compressive toughness). As a result, the aggregate size has little effect on the compressive strength and modulus of elasticity. On the other hand, the ductile behavior was shown after post peak and the compressive toughness was increasing as decreasing the aggregate size. These effects are clearly represented in the fiber volume fraction 2%, which are the point appeared fiber ball. It is considered that the decreasing the aggregate size has effect on the fiber dispersibility.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.34 no.6
• /
• pp.1677-1685
• /
• 2014

Short discrete fibers compounded with concrete can enhance the tensile resistance and ductility of concrete. Recently, the effectiveness of the reinforcement has increased according to the increasing length of steel fiber. However, the lengthening of steel fiber requires reducing the ratio of the fiber content to remain the workability and quality of concrete. Thus, the present study evaluated the flexural performance of fiber reinforced concrete with less than l.0% fiber volume ratios of steel fiber, 30mm and 60mm long, and polypropylene fiber, being evaluated as a good reinforcing material with chemical stability, long-term durability, and cost effectiveness. Concrete with more than 0.25% steel and 0.5% polypropylene fibers improved the brittle failure of concrete after reaching cracking strength. Concrete reinforced with polypropylene exhibited deflection-softening behavior, but that with more than 0.5% polypropylene delayed stress reduction and recovered flexural strength by 60 to 80% after cracking strength. In conclusion, concrete reinforced with more than 0.75% polypropylene could improve structural flexural performance. In particular, energy absorption capacity of reinforced concrete with 1.0% polypropylene fiber was similar to that with 0.5% and 0.7% steel fibers.

• The Journal of the Korea Contents Association
• /
• v.15 no.3
• /
• pp.427-437
• /
• 2015

Concrete, as a construction material, needs suitable reinforcement for tensile region due to weak tensile strength. Many researches on cement reduction have been attempted for $CO_2$ emissions during cement clinker production. In this paper engineering properties of concrete enhanced with polypropylene fiber (PPF) and rice husk ash (RHA) are evaluated. Fiber volume ratios of 0.125~0.375 and RHA replacement ratio of 0~20% are considered for concrete mixture. Lots of test including compressive, split, flexural and the related crack width, impact energy, and pull out test are performed and the results are evaluated considering the fiber ratios, fiber length and RHA replacement. Fiber and RHA ratios have dominant effects on tensile and compressive characteristics respectively, and the concrete with 0.125% of PPF and 10% of RHA shows the most effective enhancement for engineering properties. Appropriate addition of RHA and PPF are very effective both for engineering property enhancement and clean technology.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.421-424
• /
• 2008

Ultra high strength steel fiber-reinforced concrete is characterized with high tensile strength and ductility. This paper revealed the influence of fiber volume fraction on the tensile softening behaviour of ultra high strength steel fiber-reinforced concrete and developed tensile softening model to predict the deformation capacity by finite element method analysis with experimental results. The initial stiffness of ultra high strength steel fiber-reinforced concrete was constant irrespective of fiber volume fraction. The increase of fiber volume fraction improved the flexural tensile strength and caused more brittle softening behaviour. Finite element method analysis proposed by Uchida et al. was introduced to obtain the tensile softening curve from three point notched beam test results and we proposed the tensile softening model as a function of fiber volume fraction and critical crack width.