• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.11a
• /
• pp.87-90
• /
• 2006

This study investigates the temperature history of slab mock-up specimens for hot weather concreting applying various surface insulating methods, in order to improve concrete quality at hot weather condition. Test showed that the use of insulating blanket or a bubble sheet on upper section of slab prevented from abrupt increase of temperature and vaporization of moisture during early curing at hot weather circumstance. In addition, it secured higher strength at early age. Therefore it is concluded that concrete construction insulating with the bubble sheet will reduce the plastic and drying shrinkage as well as improve strength at early age, thus securing concrete duality.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.173-174
• /
• 2017

Although the application period of hot weather concrete in our country is two months of July~August which is relatively short, many problems in various aspects such as generation of plastic/dry contraction cracks and cold joints can be caused unless proper quality control measures are established at this time. Therefore, this study compared the temperature history of the placed concrete by applying a mono white and aluminum-deposited bubble sheet developed with surface coating curing materials for surface exposure and summer to an actually constructed apartment slab. The analysis result showed that the mono white bubble sheet is the best method.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.175-176
• /
• 2017

Many problems in various aspects such as generation of plastic/dry contraction cracks and cold joints can be caused unless proper quality control measures are established in hot weather circumstances. Therefore, this study aimed to compare the crack patterns of concrete by applying a change in 3 surface curing methods such as a mono aluminum-deposited bubble sheet developed to reduce the temperature and cracks through reflection of heat in summer and a PE film and a surface exposure used generally to an actually constructed apartment slab. The study result confirmed that the best concrete crack reduction effect can be obtained with a mono aluminum-deposited bubble sheet.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.6
• /
• pp.189-196
• /
• 2020

When concrete member become large like in high rise buildings, hydration heat makes temperature difference inside and outside and cause cracks. The method of using latent heat material as heat reducer could be more accessible, usable and efficient than other methods. Therefore, many studies using PCM as heat reducer are being conducted. Since heat reducer have different reacting temperature, they may be affected by environmental factors like ambient and concrete mixing temperature but studies issuing this are insignificant. Therefore, this paper attempt to evaluate the hydration heat characteristics and quality of concrete using strontium-based PCM under hot weather conditions. As a result, when the strontium-based hydration heat reducer was mixed 3wt.% and 5wt.% in hot weather condition, hydration heat speed and heating rate could be reduced by 8%, 21%, and 75, 85 minutes compared to OPC, respectively. This is considered to be the phase change reaction is relatively promoted when the temperature is high and cause improve performance than room condition result. Later, comparing the efficiency of other types of P.C.M in hot weather condition, and conduct detailed reviews on the strength development in long-term age.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.34 no.5
• /
• pp.27-34
• /
• 2018

Concrete placed under hot weather condition suffers from larger slump loss, rapid moisture evaporation due to high air temperature. Proper measures for material, transportation and curing should be taken to prevent the quality deterioration of the concrete under hot weather condition. In Korea, Although the period of hot weather concrete in Korea occupies only 2 months, there are a lot of quality problems including plastic, drying shrinkage and cold joint. Therefore, the objective of this paper is to investigate and compare the temperature history and crack occurrence of the concrete, which was placed in the actual apartment house construction field under hot weather condition, in response to the application of surface covered curing blankets including PE film, single layer clear bubble sheet, white colored bubble sheet and aluminum metalized bubble sheet. Test results indicated that the application of white colored bubble sheet and aluminum metalized bubble sheet showed most favorable results in terms of reduction in temperature rise and crack occurrence as well as easiness in handling. But, due to light reflection by aluminum metalized bubble sheet, it is believed that white colored bubble sheet is preferable.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.251-257
• /
• 2018

There are various quality deteriorations of concrete such as plastic, drying shrinkage due to abrupt moisture evaporation, slump loss and cold joint under hot weather condition. To protect from above deteriorations, several kinds of modified bubble sheets have been applied to secure heat insulation performance. But, there is not enough application cases of bubble sheets at job site under hot weather condition. The objective of the paper is to investigate the temperature profile and crack occurrence of the concrete covered with five different kinds of surface curing sheets, which is placed under hot weather condition. Single layer transparent bubble sheet, white colored bubble sheet, aluminum metalizing bubble sheet and PE film are adopted for surface curing sheets. Test results indicated that application of aluminum metalizing bubble sheet had most favorable effect on the reduction of on temperature rise and on the crack reduction of concrete. But due to larger reflection of light by aluminum, it brings about visual pollution to the workers. Hence, the application of white colored bubble sheet can be the most desirable alternative to protect the concrete from hot weather in the field.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.6A
• /
• pp.881-891
• /
• 2008

The purpose of the present study is to investigate the influence of seasonal temperature variation on the thermal stresses in roller compacted concrete dam(RCD) structures. Using the finite element code, DIANA performs 2-D transient temperature and resultant stress analysis for RCD. Time variability of the mesh geometry is considered in order to simulate successive phases of the structure's construction. The main analysis variables are construction sequence, concrete temperature and ambient temperature. The results show principal tensile stress of hot-weathering concrete is higher than that of cold-weathering concrete. In some case the index of thermal cracking excesses 1.0, RCD also needs thermal management on placing temperature according to weather condition.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.11a
• /
• pp.56-57
• /
• 2013

In this study, in regard to concrete considering variety of admixture content rate, we evaluated property of adiabatic temperature rise. By setting up high temperature history, we evaluated effect to compression strength property of high strength concrete by early high temperature history. As a result, early high temperature history accelerated Hydration reaction of cement and contribute early strength development but it didn't accomplish performance objective in long-term aged.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2012.11a
• /
• pp.11-12
• /
• 2012

This study investigates the temperature rise of reinforcement bars located in the middle of the form (for reinforcement concrete) during hot weather condition. The temperature was measured for three consecutive days before placing concrete. Test results showed that the temperature started to increase at 7:00 AM before sun rised, and peaked at around 2:00 PM. It was found that the thinner the diameter of a reinforcement bar, the higher is the speed of temperature rise and drop of the bar. The peak level of temperature for D13, D19, D25 and D32 was 54.4℃, 55.2℃, 56.4℃ and 60.2℃, respectively.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2008.11a
• /
• pp.53-56
• /
• 2008

This paper is to investigate the change of the period of hot weather concrete with elapse of age based on climate data. Climate data for 30 years and 5 years are used respectively. Determination of the period of hot weather concreting on architectural execution in Korea according to the specifications of AIJ, KSCE, and ACI are discussed. According to the research, the period of hot weather concreting with each specification in most regions lasts over 35 days. Compared with the period of cold weather concreting in hillside and inland area, coastal areas have shorter period in the same latitude. The period of hot weather concreting tends to decrease with high latitude. As expected, with the elapse of age, the period of hot weather concrete exhibited to decrease, especially, big city like Seoul, Busan etc had remarkably increased period by as much as a week. This is due to the global warming and industrialization effect with the elapse of age.