• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.4
• /
• pp.596-605
• /
• 2016

In previous years, practice hand grenades were composed of non-degradable plastics and caused environmental pollution. Therefore, this study applied PLA(Polylactic acid) to practice hand grenades that would biodegradable within a short time. High expectations are being placed on PLA as a substitute for plastics because it can decompose to water and carbon dioxide. The aim of this study was to confirm that the PLA material of a practice hand grenade has biodegradability in a pilot-scale composting unit and estimate the applicability for other items. A composting test was progressed according to ISO 16929(2013). The test process was found to be valid. At the end of the composting test (after 12 weeks), the entire content of the test bin with the test sheet was sieved, sorted and analyzed. A disintegration percentage of 99.2% was obtained after 12 weeks of composting. Therefore, the 90% pass level required by ISO 17088(2013), EN 13432(2000), and ASTM D 6400-12 was easily reached. On the other hand, more research will be needed to determine additional applications of PLA material for consumables.

• Journal of Adhesion and Interface
• /
• v.10 no.2
• /
• pp.106-112
• /
• 2009

In the present work, novel biocomposites made with biodegradable Lyocell woven fabrics and poly (butylene succinate) were successfully fabricated for the first time. Lyocell/poly(butylene succinate) biocomposites with different fiber loadings of 0, 30, 40, 50 and 60 wt% were prepared by compression molding with a sheet interleaving manner. The effect of Lyocell fabric loading on the interlaminar shear strength, tensile and flexural properties, heat deflection temperature, thermal expansion behavior, and thermal stability of the biocomposites was investigated. The properties strongly depended on the fabric loading and the results were consistent with each other. It was demonstrated that the Lyocell fabrics played a remarkable role in improving the properties of poly(butylene succinate) resin by incorporating the fabrics into the resin. The greatest inter-laminar, tensile, flexural and thermal properties of the biocomposites were obtained with Lyocell fabrics of 50% by weight.

• Composites Research
• /
• v.24 no.4
• /
• pp.5-10
• /
• 2011

As environmental pollution getting worse, biodegradable materials have been drawn more attention than ever. In this study, polylactic acid (PLA)/carbon nanotubc (CNT) nanocomposites were manufactured via extrusion molding and injection molding, In order to change the crystallinity, annealing treatment was done for different time span, Crystallization kinetics of PLA was analyzed by differential scanning calorimeter (DSC), and it was confirmed that a proper amount of CNT can increase the crystallization rate of PLA. In addition, the presence of CNT significantly accelerates the hydrolytic degradation rate of PLA, however, it decreases with the increase of crystallinity. The reason is that degradation may occur in the PLA/CNT interface easily, and the molecular structure of the composite becomes dense with the increase of crystallinity.

• Korean Chemical Engineering Research
• /
• v.49 no.2
• /
• pp.206-210
• /
• 2011

We fabricated rod-like poly(lactic acid)(PLA) specimens through applying various methods of equal-channel angular extrusion(ECAE) process and investigated the change of thermal and mechanical properties of specimens before and after each ECAE process. Combining three re-injection routes(A, BC, and C) and three pass counts(1, 2 and 4) allowed us to fabricate 7 different PLA specimens. Thermal properties of each specimen were measured by both differential scanning calorimeter and thermo-gravimetric analyzer. Shear strains of each specimen with respect to applied loads were measured by indentation hardness tester. Field emmision scanning electron microscopy was used to observe internal microstructure of cross-section of each specimen. The observed microstructures qualitatively supported the explanation of hardness test results. Among 7 specimens, PLA-P2A showed the biggest shear strain probably due to its dense microstructure.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.11
• /
• pp.6023-6028
• /
• 2013

Recently, biodegradable polymers are gaining more and more attention due to international environmental issues. Succinic acid is synthesised by chemical process of hydrogenation. Succinic acid synthesized has certain amount water content. To remove the water contained in succinic acid is used generally by hot air drying process. But recently, microwave drying process having the advantage of shortening the drying time and uniform drying of product are gaining more attention. In this study, hot air drying and microwave drying efficiency were compared at drying process. In addition, we confirmed commercial applicability in microwave drying process of succinic acid. Microwave drying process has higher efficiency than 70% compared with hot air drying process at thickness of 1cm. Economic efficiency were compared through examination of power consumption for complete drying of succinic acid at microwave and hot air dyring.

• Applied Chemistry for Engineering
• /
• v.4 no.2
• /
• pp.324-334
• /
• 1993

Chitin, the natural polymer has been known as harmless and innoxious material to human and has been also known to be biodegradable. Chitosan which was prepared by the deacetylation of chitin, was propionylated to obtain porous bead shaped propionyl chitosan and its possibility as a water-absorbant polymer was investigated. Propionyl chitosan porous bead was synthesized by acylation reaction using emulsion method of acetic acid solution and propionyl chitosan was partially crosslinked using ethyleneglycol diglycidyl ether. Through the experiment varying the moles of propionic anhydride, reaction time and reaction temperature, best results for water-absorption ability was obtained at reaction condition of 5 moles of propionic anhydride, 10 hours of reaction time and $22^{\circ}C$ of reaction temperature. The absorption ability to the distilled water, various salt solutions, artificial urine and artificial blood, absorption time and retention of water of synthesized porous bead were investigated and also mechanical strength after crosslinking was determined.

• Clean Technology
• /
• v.23 no.2
• /
• pp.133-139
• /
• 2017

Bio-based plastics containing the biomass content higher than 25 wt% have been considered as environment-friendly materials due to their effects on the reduction in the $CO_2$ emission and petroleum consumption as well as biodegradability after use. In this study, poly vinyl chloride, plant-derived plasticizers, by adding a biodegradable catalyst was observed a change in the biodegradability and physical properties. To produce the oxidative decomposition transparent bio film, which is broken down in the initial percent elongation and physical properties such as tensile strength, it was to test the safety of the product as a food packaging material. Poly vinyl chloride, primary plasticizer, secondary plasticizer, anti fogging agent, the combined stabilizer were mixed in a high speed mixer, then extruded using an extrusion molding machine, after cooling, winding, to produce a oxidative decomposition transparent bio film and the control film, with a thickness of $12{\mu}m$ through winder role. Mechanical properties tensile strength, elongation, and the maximum load elongation and biodegradation test. Transparent bio film produced by biodegradation catalyst is compared with the control film. Tensile strength and elongation of films were found to be no significant difference. Further, as a result of the biodegradation test for 45 days based on the ASTM D6954-04 method, biodegrability of film is 61.4%.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.7
• /
• pp.4081-4086
• /
• 2014

Cellulose acetate butyrate (CAB) is a biodegradable resin with excellent optical properties, but it is difficult to apply film process. In this study, an attempt was made to improve the processability of CAB using polyactic acid and the mechanical properties using an impact modifier. Polylacitc acid (PLA)/Cellulose acetate butyrate (CAB) blends with an impact modifier were prepared using a twin screw extruder. The temperature range was $140^{\circ}C$ to $200^{\circ}C$, and the screw speed was fixed to 200 rpm. To evaluate the miscibility of impact modified CAB/PLA, the glass transition behavior and morphology were observed by DSC and FE-SEM. The mechanical properties were investigated by dynamic mechanical analysis (DMA) and a Universal Testing Machine (UTM). In addition, the effect of an impact modifier in the polymer matrix was determined using a notched Izod impact strength tester. Finally, the PLA/CAB/impact modifier 75/25/10 ratio was found to be a compatible system. In the 10wt.% impact modifier, the sample had a 4 times higher izod impact strength than the non-toughening composition.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.43 no.4
• /
• pp.281-290
• /
• 2007

This study was aimed not only to develop the gill net and trap made of biodegradable monofilaments in order to prevent a ghost fishing and to protect marine ecosystem, but also to analyze their spinning process and physical properties. Results showed that the spinning speed of biodegradable polybutylene succinate(PBS) monofilament was estimated to be approximately 100m/min when spinning temperature and cooling water temperature were adjusted at $180^{\circ}C$ and $3^{\circ}C$, respectively. The breaking loads of PBS monofilaments were estimated to be $35.3kg/mm^2$ at ${\phi}0.2mm$, $46.5kg/mm^2$ at ${\phi}0.3mm$, and $49.7kg/mm^2$ at ${\phi}0.4mm$ in the dry condition, respectively. However, its breaking loads in the wet condition were reduced by 2.4-5.5%, compared to those in the dry condition. The knotted strength of PBS monofilament at ${\phi}0.2mm$ was estimated to be 98.6% of PE in the dry condition. The breaking load of PBS monofilament at ${\phi}0.3mm$ was evaluated to be 81.8% of PA, and its softness showed 3 times less than that of PA in the wet condition. The breaking load of PBS monofilament at ${\phi}0.4mm$ was 95.3% of PA, and its softness showed 1.6 times less than that of PA in the wet state. However, the load elastic elongations of two kinds of monofilaments were estimated to be 1% higher than that of PA.

• KOREAN JOURNAL OF PACKAGING SCIENCE & TECHNOLOGY
• /
• v.28 no.2
• /
• pp.105-113
• /
• 2022

Mulching film was produced by LDPE and LLDPE adding biomass byproducts and MA(maleic anhydride), talc/clay/CaO/CaCO₃. And also surveyed to tensile strength, elongation, TGA and DSC according to the UV irradiation time. The tensile strength and elongation showed 20 N/cm² and 5% after UV irradiation 100 hours, and those was nearly 0 N/cm² and 0% after 200 hours, respectively. TGA of film was showed to peak of polymer itself, and DSC was slightly higher than that of initial value. At the pilot scale test, we were able to see the differentiate of degradation between control and developed film after 12 weeks, and also torn off at several part of mulching film. The degradation of mulching film after growing corn showed similar to a pilot scale test. Above the results, the developed mulching film adding biomass will be to used for agricultural farming.