• Journal of the Korea Concrete Institute
• /
• v.15 no.2
• /
• pp.254-262
• /
• 2003

In this study, the results of applying cold weather concreting mixed with Accelerator for Freeze Protection(AFP) to full scale structures are presented. Since the determination of W/C and amount of AFP significantly have an effect on strength gain and protection of frost damage in early, a full investigation is needed to determine these values at stage of nux design. The flowability of fresh cold weather concreting with AFP was similar to the same W/C. Lower loss of workability and initial slump flow of concrete using superplasticizer of polycarboxylic ester than that of melamine sulphonate showed that polycarboxylic ester was more effective on elapsed time. Temperature histories of specimens located in insulation boxes at the site was similar to that of structures. Thus, it is cleared that simple adiabatic curing method is effective for evaluating in-place concrete strength than specimens cured by sealing method. The investigation results of development of compressive strength of cold weather concreting included AFP with curing methods by logistic curves indicated that AFP can be effective to gain strength at lower temperature than normal curing temperature. In field testing, vinyl sheets were placed over the concrete sections and AFP enabled concrete to gain $5N/{mm}^2$ to protect frost damage in early ages and specified compressive strength of concrete at 28 days under average temperature of $-2^{\circ}C$ (lowest temperature was $-12^{\circ}C$) during site application.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.114-121
• /
• 2010

Portland cement production is under critical review due to high amount of CO2 gas released to the atmosphere. Attempts to increase the utilization of a by-products such as fly ash and ground granulated blast-furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. However, most study deal only with alkali-activated ground granulated blast furnace slag or fly ash, as for the combined use of the both, little information is reported. In this study, we investigated the influence of mixture ratio of fly ash/ blast furnace slag tand curing condition on the flowability and compressive strength of mortar in oder to develop cementless alkali-activated concrete. In view of the results, we found out that the mixture ratio of fly ash/blast furnace slag always results to be significant factors. But the influence of curing temperature in the strength development of mortar is lower than the contribution due to other factors. At the age of 28days, the mixture 50% fly ash and 50% ground granulated blast furnace slag activated with 1:1 the mass ratio of 9M NaOH and sodium silicate, develop compressive strength of about 65 MPa under $20^{\circ}C$ curing.

• Resources Recycling
• /
• v.19 no.4
• /
• pp.19-28
• /
• 2010

Attempts to increase the utilization of a by-products such as fly ash and blast furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. However, most study deal only with alkali-activated blast furnace slag or fly ash, as for the combined use of the both, little information is reported. In this study, we investigated the influence of mixture ratio of fly ash/slag, type of alkaline activator and curing condition on the workability and compressive strength of mortar in oder to develop cementless alkali-activated concrete. In view of the results, we found out that the mixture ratio of fly ash/slag and the type of alkaline activator always results to be significant factors. But the influence of curing temperature in the strength development of mortar is lower than the contribution due to other factors. At the age of 28days, the mixture 50% fly ash and 50% slag activated with 1:1 the mass ratio of 9M NaOH and sodium silicate, develop compressive strength of about 65 MPa under $20^{\circ}C$ curing.

• Journal of the Korea Concrete Institute
• /
• v.26 no.1
• /
• pp.23-34
• /
• 2014

This study investigates the relationship between the performance of fresh and hardened Ultra-High Performance Concrete (UHPC) without heat treatment. The performance of fresh UHPC is determined by the slump flow test related to the fluidity of concrete mixtures, and the air content test. The variables of these tests are the water to binder ratio, superplasticizer dosages and volume fractions of steel fiber. Generally, insufficient fluidity and excessive air contents in concrete mixtures lead to the insufficient packing density related to the performance of harden concrete. The performance of hardened UHPC is determined by the compressive and flexural tensile tests. The results of the fresh UHPC tests show that there is the linear correlation between each variable and the slump flow diameter, and that the slump flow diameter is linearly decreased as the air content ratio increase. Using these results, the formula is developed to predict the fresh performance before mixing UHPC. The results of the hardened UHPC tests show that the hardened performance is not influenced by the air content ratio in the range of 3.2 to 4.2 per cent. However, the flexural tensile strength dominantly influenced by the volume fractions of steel fiber.

• Journal of the Korea Concrete Institute
• /
• v.16 no.1 s.79
• /
• pp.54-60
• /
• 2004

This study deals with the setting behavior of polystyrene mortars using waste expanded polystyrene(EPS) solution-based binders. The binders for polystyrene mortars are made by mixing crosslinking agent with EPS solutions prepared by dissolving EPS in styrene. Polystyrene mortars are prepared with various EPS concentrations of EPS solutions and crosslinking agent contents, subjected to a dry curing, and tested for working life, peak exotherm temperature and 10h-length change. From the test results, He working lives of polystyrene mortars are shortened with raising EPS concentration of EPS solution and crosslinking agent content. Low-shrinkage or non-shrinkage polystyrene mortars could be obtained by adjusting EPS concentration of EPS solution and crosslinking agent content.

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.487-494
• /
• 2011

In this research, the possibility of using bottom ash as a binder for the alkali-activated cement mortar is studied. Several experiments were performed to investigate the variation of the material properties according to the mix proportion. In the experimental program, the flowability and compressive strength were evaluated for various values of water/ash ratio, activator/ash ratio, sodium silicate to sodium hydroxide ratio, curing temperature, and the fineness of bottom ash as the main variables. The experimental results showed that high strength of 40 MPa or greater could be achieved in $60^{\circ}C$ high temperature curing condition with proper flowability. For $20^{\circ}C$ ambient temperature curing, the 28 days compressive strength of approximately 30MPa could be obtained although the early-age strength development was very slow. Based on the results, the range of optimized mix design of bottom-ash based alkali-activated cement mortar was suggested. In addition, using the artificial neural network analysis, the flowability and compressive strength were predicted with the difference in the mix proportion of the bottom-ash based alkali-activated cement mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.4
• /
• pp.585-593
• /
• 2021

This study investigates the compressive strength of high-strength cement composites with 64 mixture designs and 2 curing conditions. The cement composites were designed with varying water-to-binder ratios, silica fume content to cement, and binder content per unit volume of cement composite to explore compressive strength development depending on its mix design. An increase in the water-to-binder ratio decreased the compressive strength of the composites, having consistency with the trend in normal concrete. The compressive strength increased with ages at an ambient curing temperature, but it was not identified at high-temperature curing. The compressive strength development was negligible in case that silica fume content to OPC is 15%~25%, but a decrease in the con ten t below 15% reduced compressive stren gth. It was more obvious in the specimen of low water-to-binder ratio. The specimen with 840kg/m³ of binder content per unit volume had the highest compressive strength in this study, and the decrease in binder content reduced the compressive strength of high strength cement composites in low silica fume content.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.433-436
• /
• 2008

Deterioration in the concrete structure are due to carbonation, chloride ion attack and frost attack. Therefore, concrete structure is needed to surface protection for increase durability using silicate impregnants. Thus, this study is concerned with self-cleaning and durability of silicate hydrophilic impregnants of concrete structure using lithium and potassium silicates. From the experimental test results, lithium and potassium silicates have a good properties as a carbonation resistance. Lithium and potassium silicates make good use of hydrophilic impregnants of concrete structures.

• Resources Recycling
• /
• v.8 no.4
• /
• pp.30-38
• /
• 1999

High 1emperiltur.e propeitles o i cold bonded pellet based on lroll beanng dusts wele invesligaled prim to using as a burden m blasl furnaces, Major conclusions ould be summarized Io llows: the cold bonded pellet needed to bc produced by the characteristic criterion on high lempemhIre prapcrttes as well as a compressive sncnglh. Basicity of cold bonded pellel shruld be linted to be appoxiiniltely 1.7 in order to maintain appropriate softcn~nga nd rnelt~ngp ropcrlies. On thc other hand. basiciq greater than 2.6 showed exce\ulcornersive puessure drop due to powder gelleratlon. Potcntialil], of blast fi~rnaccs lag as binding malerial in m a h g cold ba~~deprel llels !\.us also certified in viewpoinls of high temperature properly.

• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.751-757
• /
• 2004

Artificial lightweight aggregates and solids were manufactured with coal ash(fly ash, bottom ash). In order to apply alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate to concrete, several experimental studies were performed. Thus, it can be noticed the optimal mix proportion, basic characteristies, mechanical properties and environmental safety of alkali-activated coal ash(fly ash, bottom ash) solid and alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate. Also, the freezing-thawing test property of concrete using the alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate was investigated. As a result, the optimal mixing proportion of coal ash(fly ash, bottom ash) solid to make alkali-activated artificial lightweight aggregates was cement $10\%$, water glass $15\%$, NaOH $10\%$, $MnO_2\;5\%$. Alkali-activated coal ash(fly ash, bottom ash) solid can achieve compressive strength of 36.4 MPa, at 7-days, after the paste was cured at air curing after moist curing during 24 hours in $50^{\circ}C$. Alkali-activated coal ash(fly ash, bottom ash) artificial lightweight aggregate that do impregnation to polymer was improved $10\%$ crushing strength $150\%$, and was available to concrete.