• Restorative Dentistry and Endodontics
• /
• 제20권1호
• /
• pp.97-112
• /
• 1995

The purpose of this study was to evaluate the effect of wetting condition made by drying time on bonding of resin cement to dentin. Freshly extracted bovine teeth were grinded to expose flat dentin surfaces. After the exposed dentin surfaces were treated with pretreatment agents and water rinse, each wetting condition of dentin surfaces was made according to drying times and methods including slight blow bry for I-second by air syringe, blow dry for 20-second by air syringe, and 12-hour dry in desiccator respectively. and then, previously made composite resin specimens were bonded onto each conditioned dentin surface of the specimen using Panavia-21(Kuraray Co.), Bistite(Tokuso Co.), and Choice(use with All bond-2, Bisco Inc.) resin cement according as manufacturer's instruction. Bonded specimens were stored in $37^{\circ}C$ distilled water for 24 hours, then the tensile bond strength was measured, cohesive failure rate was calculated, and fractured dentin surfaces and acrylic rod sides were examined under scanning electron microscope. The result were as follows ; In the group of bonding with Panavia-21 resin cement, higher tensile bond strength was seen in 12-hour dry group than in I-second and 20-second dry group(p<0.01). In the group of bonding with Bistite resin cement, higher tensile bond strength was seen in 1-second dry group than in 20-second and 12-hour dry group(p<0.01). In the group of bonding with Choice resin cement, no significant differences of bond strength under given drying time were seen. Cohesive failure rates derived from the groups of bonding with Panavia-21 and Choice resin cement were increased with the increase of tensile bond strength in each drying time. On SEM examination of fractured surface, adhesive failure mode with fractured resin tags was mostly seen in wet condition with I-second drying time in the group of bonding with Panavia-21 resin cement, mixed failure mode with shortened and fractured resin tag was seen in the group of bonding with Bistite resin cement, and regardless of drying time, and cohesive-adhesive mixed failure mode with fracture of 'Hollow' typed resin tags was mainly seen in the group of bonding with Choice resin cement.

• Restorative Dentistry and Endodontics
• /
• 제28권1호
• /
• pp.11-22
• /
• 2003

This study compared the dentin adhesion to composite resin according to air-dry, blot dry, application of rewetting agent on air-dry or blot dry dentin surface by microleakag test and SEM observation. For microleakage test, class V cavity preparations with dentinal margins were prepared on both buccal and lingual surfaces of 40 extracted human molars. For SEM observation, occlusal dentin of 20 extracted human molars were exposed. After etched the dentin, prepared teeth were randomly divided into four groups; D group: air dry for 10-15 sec., B group: blot dry with moist cotton pellet, D-R group: air dry and rewet with Aqua-Prep F for 20 sec., B-R group: blot dry and rewet with Aqua-Prep F for 20 sec. Treated cavities and surfaces were filled or constructed using One-Step adhesives and Aelitefil composite resins. Specimens were stored in distilled water for 24 hours. For microleakage test, the specimens were thermocycled and soaked into 2% methylene blue. The specimens were sectioned longitudinally and evaluated for microleakage under steromicroscope. The data were statistically analysed by Kuskal-Wallis Test, Mann-Whitney and Wilcoxon signed ranked tests. For SEM observation, the specimens were bisectioned mesiodiatally. After decalcified and deproteinized, specimens were observed under SEM. The results of this study were as follows; 1. The microleakges on dentinal margin were the highest in D group compared with B group, D-R group, and B-R group(p<0.05). But there was no significant difference between B group, D-R group and B-R group. 2. D group showed gap and a few resin tags between dentin and composite resin. 3 B group, D-R group, and B-R groups showed close adaptation between dentin and composite resin. It showed that resin rags in B group were numerous and long, in D-R group were few and short, in B-R group were numerous and short or long. 4. Adhesive layer showed in D-R group ($10{\;}\mu\textrm{m}$) and B-R group ($3{\;}\mu\textrm{m}$) In conclusion, use of rewetting agent to dry dentin was efficient to dentin adhesion, also it did not provide reverse effect on blot dry dentin.

• 대한치과보철학회지
• /
• 제51권1호
• /
• pp.20-26
• /
• 2013

연구 목적: 본 연구는 최근 심미수복에 주로 사용되는 CAD/CAM 세라믹 인레이와 각종 레진 시멘트간의 결합강도를 알아보고자 하였다. 연구 재료 및 방법: 원기둥 모양의 세라믹 블록(높이: 5 mm, 직경: 3 mm)을 Cerec3로 제작하고, 총 90개의 우식이 없는 대구치의 상아질 표면에 세 종류의 레진 시멘트(Unicem$^{(R)}$, Biscem$^{(R)}$, Variolink II$^{(R)}$)를 사용하여 각각 제조업체의 지시에 따라 접착했다. 90개의 시편을 레진 시멘트의 종류에 따라 3개의 군으로 나누고, 각 군의 절반은 $5-55^{\circ}C$, 5,000 cycle 조건 하에서 thermocycling을 시행하였고, 다른 절반은 시행하지 않았다. 모든 시편은 결합강도를 측정하기 전에 $37^{\circ}C$ 생리 식염수에 24시간 동안 보관되었다. 전단결합강도는 만능시험기를 이용하여 0.5 mm/min의 cross head speed로 측정하였다. 결과 값은 t-test 및 one-way ANOVA를 사용하여 통계 분석하였다. 결과: Unicem$^{(R)}$ 군의 전단결합강도가 thermocycling 후에 약간 감소했으나 3 개의 군 중 가장 높은 결합 강도를 보였다. Unicem$^{(R)}$ 및 Valiolink II$^{(R)}$ 군의 전단결합강도가 thermocycling에 영향을 받았지만 Biscem$^{(R)}$은 영향을 받지 않았다(P<.05). Thermocyling 전에는 3개의 군 간의 결합강도에 유의한 차이가 없었지만, thermocyling 후에는 Unicem$^{(R)}$과 Valiolink II$^{(R)}$ 군 간에 유의한 차이가 있었다(P<.05). 결론:CAD/CAM 세라믹 인레이 수복물을 치아에 접착할 때, etch-and-rinse 레진 시멘트인 Valiolink II$^{(R)}$ 대신self-adhesive 레진 시멘트인 Unicem$^{(R)}$과 Biscem$^{(R)}$을 사용해도 임상적으로 유용하다.

• 대한소아치과학회지
• /
• 제33권2호
• /
• pp.233-243
• /
• 2006

와동 형성시 C-factor와 충전방법이 복합레진 수복물에서의 수축 응력에 미치는 영향을 평가하고자 발거된 소구치를 대상으로 C-factor가 3.6과 1.0인 와동을 각각 형성한 후 hybrid형 복합레진인 $Z-250^{TM}$(3M ESPE U.S.A.)과 flowable형 복합레진인 $Filtek\;flow^{TM}$(3M ESPE U.S.A.)를 사용하여 layering을 시행하고 광중합하면서 strain gauge법을 이용하여 치질에서의 수축 응력을 측정하였다. 시편을 절단하여 레진과 상아질 사이 계면의 접착상태를 주사전자현미경으로 관찰한 결과 다음과 같은 결과를 얻었다. 1. C-factor에 따른 수축 응력을 측정한 결과 C-factor가 3.7인 제 1군과 제 2군 그리고 제 5군이 900초 후 각각 0.11, 0.07, 0.07 MPa로 C-factor가 1.0인 제 3군과 제 4군의 0.05와 0.04 MPa에 비해 크게 나타났다(P<0.05). 1,800초 후에는 제 1군, 제 5군, 제 2군, 제 3군, 제 4순으로 크게 나타났으나 제 2군과 제 3군 그리고 제 3군과 제 4군 사이에는 유의성이 없었다. 2. 재료에 따른 수축 응력의 차이는 C-factor가 3.7인 와동의 경우 hybrid형 레진인 Filtek $Z-250^{TM}$이 flowable 레진인 $Filtek\;flow^{TM}$에 비해 수축 응력이 크게 나타났으나(P<0.05), C-factor가 1.0인 와동의 경우 재료의 차이에 따른 수축응력의 유의한 차이가 없었다. 3. Layering에 따른 수축 응력은 Filtek $Z-250^{TM}$을 layering 없이 bulk 충전한 제 1군에 비해 flowable 레진을 layering한 제 5군이 전 측정 시간대에 걸쳐 수축 응력이 유의하게 낮게 나타났다(P<0.05). 4. C-factor가 3.7인 제 1군과 제 2군 제 5군은 900초까지 수축 응력이 증가하다 이후 점차 감소하는 경향을 보였다. 5. C-factor가 1.0인 와동의 경우 충전용 레진 종류에 관계없이 레진과 와동벽 사이에 긴밀한 접착 상태를 보였으나 C-factor가 3.7인 와동의 경우 부분적으로 틈이 관찰되었다. 전반적으로 와동저에 비해 와동벽에서 틈이 더 많이 관찰되었다. 이상의 결과를 종합하여 보면 복합레진 수복시 수축응력에 따른 합병증을 예방하기 위해 C-factor를 크지 않게 와동을 설계, 형성하여야 하며 C-factor가 클 경우 flowable 레진을 이장하는 등 재료적인 면에서의 선택과 적용법이 중요할 것으로 사료된다.