The development of an insulated coating which can be used for amorphous alloys is extremely important from the practical point of view. This importance may be enhanced by the influence of the coating on the magnetic properties. The purpose of this study is to show how new developed insulating coating materials and method influence the magnetic properties of amorphous Fe/sub 87/Zr/sub 7/B/sub 5/Ag/sub 1/(at%) ribbon.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.175-175
• /
• 2005

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.172-172
• /
• 2005

• Journal of the Korean Magnetics Society
• /
• v.10 no.2
• /
• pp.49-52
• /
• 2000

The changes of magnetic properties in neutron irradiated F $e_{81}$ $B_{13.5}$S $i_{3.5}$ $C_2$ amorphous ribbon were studied by X-ray diffraction, hysteresis loop, temperature dependence of magnetization and complex permeability. The fluences of thermal ( $n_{th}$) and fast ( $n_{f}$) neutron were 6.95$\times$10$^{18}$ $n_{th}$ c $m^{-2}$ and 4.56$\times$10$^{16}$ $n_{f}$c $m^{-2}$ , respectively. The changes of XRD Profiles were not observable at the neutron irradiated sample. The complex permeability spectra showed that the permeability from domain wall motion decreased due to the increase of pinning force against domain motion by the neutron irradiation, and the relaxation frequency of rotational magnetization moved to higher frequency region. The measurement of hysteresis loop showed the increase of magnetic softness, related to rotational magnetization, but saturation magnetization was decreased in neutron irradiation sample. The Curie temperature was decreased in the neutron irradiated sample.e.e.e.

• Journal of the Korean Magnetics Society
• /
• v.2 no.2
• /
• pp.91-98
• /
• 1992

In a $Co_{67}Fe_{4.5}Nb_{2}Si_{10}B_{15}$ amorphous alloy ribbon the effect to two-step annealing on the soft magnetic properties has been studied. By two-step annealing method which the second annealing at low temperature of $310^{\circ}C$ for 2 hours is undertaken after the primary annealing at high temperature above $480^{\circ}C$ for 20 minutes at the vacuum state, the coercive force and the squareness are not changed nearly but the initial permeability at d.c. and the effective permeability at a.c. are remark-ably increased compared with the one-step annealing. The maxima of the initial permeability and the effective permeability at 1 kHz after the two-step annealing are 290,000 and 41,000, respectively, which are 30% higher than those of the one-step annealing. The change of magnetic properties with annealing temperature is discussed in terms of the residual stress, the domain size, the cluster and the crystalline phase.

• Journal of the Korean Magnetics Society
• /
• v.8 no.5
• /
• pp.255-260
• /
• 1998

Fabrication condition and magnetic properties of ultrathin Co-based amorphous alloy have been investigated. When the ejection gas pressure was lower than 0.05 kgf/$\textrm{cm}^2$ at the roll speed of 55 m/s, ultrathin ribbons with the thickness less than 10 ${\mu}{\textrm}{m}$ were successfully obtained. The ribbon thickness decreased linearly with the decrease in ejection pressure. Moreover the significant decrease in ribbon width was accompanied with the decrease of thickness in the range of ejection pressure to form an ultrathin ribbon. This behavior was attributed to the decrease of effective ejection pressure in the both end-sides of rectangular nozzle due to the larger friction between molten metal and nozzle wall. The effective permeability at low frequency (1 kHz) decreased largely with the decrease in ribbon thickness, while the coercive force increased with the thickness decrease. It was considered that these behaviors were due to the enhancement of surface effect leading to the suppression of wall motion. However effective permeability at high frequency (1 MHz) increased with the decrease in ribbon thickness, and this was ascribed to the easier magnetization rotation owing to the reduction of eddy current.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.847-854
• /
• 1994

An amorphous single phase and coexistent amorphous and hcp-Mg phases in Mg-Zn-Ce system were found to form in the composition ranges of 20 to 40% Zn, 0 to 10% Ce and 5 to 20% Zn, 0 to 5% Ce, respectively. A $Mg_{85}Zn_{12}Ce_{3}$ amorphous alloy containing nanoscale hcp-Mg particles was found to form either by melt spinning or by heat treatment of melt -spun ribbon. The particle size of the hcp-Mg phase can be controlled in the range of 4 to 20 nm. The mixed phase alloy prepared thus has a good bending ductility and exhibits high ultimate tensile strength($\sigma_{B}$) ranging from 670 to 930 MPa and fracture elongation($\varepsilon_{f}$) of 5.2 to 2.0%. The highest specific strength($\sigma_{B}$/density =$\sigma_{s}$)$3.6 \times 10^5N \cdot m/kg$. It should be noted that the highest values of flB, US and ？1 are considerably higher than those (690MPa,$2.5 \times 10^5N \cdot m/kg$and 2.5%) for amorphous Mg-Zn-Ce alloys. The increase of the mechanical strengths by the formation of the mixed phase structure is presumably due to a dispersion hardening of the hcp supersaturated solution which has the hardness higher than that of the amorphous phase with the same composition.

• Journal of the Korean Magnetics Society
• /
• v.1 no.2
• /
• pp.55-59
• /
• 1991

The temperature-dependent magnetization curves of amorphous Fe-Co-(Nd, Sm, Gd, Tb)-B alloys were measured using a vibrating sample magnetometer from 77 K up to 900 K. The spin wave stiffness constants and the range of the exchange interaction were calculated from the saturation magnetization values at 0 K. Curie temperatures and the Bloch coefficients estimated from the saturation magnetization curves. The low temperature dependence of magnetization is in good agreement with Bloch relation, $M_{s}(T)=M_{s}(O)(1-BT^{3/2}-CT^{5/2})$. The spin wave stiffness constant and the range of exchange interaction are decreased by substitution of heavy rare earth (Tb, Gd).

• Journal of the Korean Magnetics Society
• /
• v.4 no.2
• /
• pp.150-153
• /
• 1994

Magnetic field annealing method has been used to obtain proper hysteresis loop shapes which are useful to a device using amorphous ribbon. In this study, two pairs of Helmhotz coils were used to apply longitudinal and transverse magnetic field during annealing. For the measurement of coercive field strength noise which depends on magnetic field annealing, Co-based amorphous alloy ribbon $VITROVAC^{\circledR}$ 6030 was used. For the sample which was annealed under dc transverse and dc longitudinal magnetic field, coercive field strength noise was nearly independent of magnetizing frequency ranging from 1 to 100 kHz, but dc transverse and ac longitudinal magnetic fields annealed samples show that the coercive field strength noise decreased in power of magnetizing frequency. When magnetic domain nucleation occurred, the coercive field strength noise increased remarkably and decreased in power of magnetizing frequency.

• Journal of Korea Foundry Society
• /
• v.36 no.1
• /
• pp.18-23
• /
• 2016

Iron based amorphous ribbons with the nominal compositions of $(Fe_{79}C_{11}B_8Si_2)_{100-X}Cr_X$ (X = 0,2,4,6,8 at%) have been developed as reinforcements that can be applied to the concrete materials. Mechanical properties and glass forming ability of the ribbons can be enhanced by the optimum amounts of Cr additions that can also improve corrosion properties of the ribbons. Vein patterns typical of the fractured surface morphology of amorphous alloys have been observed on the surfaces of ribbons after tensile tests. It is inferred from the EDS analysis results of vein patterns that carbon segregations occur within the narrow shear band regions.