• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.2
• /
• pp.86-93
• /
• 2020

Shotcrete concrete is generally used in the form of ready-mixed concrete products using type I ordinary portland cement(hereinafter referred to as OPC) and about 5% of accelerator mixed separately in the field. In this study, we tested the effect of addition of slag powder(SP) and limestone powder(LSP) on a penetration resistance, compressive strength of binder for shotcrete using calcium aluminate type accerlerator. And we analysed hydrates and pore structure effects on mortar performance. In the future, it is expected to be useful for manufacturing optimized composite cement as a binder for shotcrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.2
• /
• pp.78-85
• /
• 2020

Shotcrete concrete is generally used in the form of ready-mixed concrete products using type I ordinary portland cement(hereinafter referred to as OPC) and about 5% of accelerator mixed separately in the field. In this study, we tested the effect of OPC fineness and SO₃ content on a penetration resistance, compressive strength of binder for shotcrete using calcium aluminate type accerlerator. And we analysed hydrates and pore structure effects on mortar performance. In the future, it is expected to be useful for manufacturing optimized OPC as a binder for shotcrete.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.12 no.4
• /
• pp.285-294
• /
• 2010

As there are increasing number of tunneling works these days, shotcrete is used as primary supports in order to secure the stability of tunnels. The quality of shotcrete has a direct influence on tunnels, because it is a primary support which secures the stability of completed tunnels as well as the stability of tunnels under excavation. Especially in case that ordinary shotcrete is used under weak rock conditions or at water gushing sections, more shotcrete is needed and rebound ratio increases. As a result, it is hard to keep economic feasibility. In addition to it, in subway construction, there are cases of separated excavation and it may have a bad influence on construction period or quality. Therefore, in this study, we are going to evaluate the early strength of powder type accelerator.

• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.633-640
• /
• 2010

This study was performed to get basic information about properties of high blaine cement for shotcrete use. Particle size distribution, setting time and compressive strength test, analysis like as SEM, DSC thermal analysis, XRD was carried out to investigate principle properties of high blaine cement. Setting time of high blaine cement was shorter and compressive strength was higher than those of ordinary portland cement (OPC). Results of analysis showed early hydration products of high blaine cement is smaller and spread widely due to increased specific surface. From the SEM observation and analysis of DSC and XRD results, it was seen that the aluminates accelerators promoted calcium aluminium hydrates while the alkali free accelerators increased ettringite and monosulfates formation. Strength and setting time measurement of cement paste with aluminate accelerator is more effective than the alkali free accelerator in reducing the setting time and increasing early strength while alkali free accelerator is more effective in increasing the strength after 7 days.

• Magazine of the Korea Concrete Institute
• /
• v.15 no.4
• /
• pp.36-40
• /
• 2003

• Magazine of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.49-51
• /
• 2015

• Resources Recycling
• /
• v.18 no.1
• /
• pp.38-43
• /
• 2009

In this study, binderless consolidation processes of ultra foe Si powder, by-products of making high purity poly-Si in the current method, were systematically investigated for use as economical solar-grade feedstock. The average diameter of the silicon powder was $7.8{\mu}m$. The main contaminants of the fine silicon powder were $SiO_2$ type oxide and humidity. The chemical pretreatment using the HF solution was observed to be effective for the improvement of the compactability of the silicon powder and the density ratio and the strength of the silicon powder compacts. The yield of the binder-free consolidation process increased by 20% under a vacuum condition. In as-received state, the silicon powder were not pure enough to be used as solar grade feed-stock material. After the dry chemical treatments, a sufficiently high purity above solar-grade was able to be achieved.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.5
• /
• pp.389-396
• /
• 2014

The set accelerator used for shotcrete at high pH environment often causes the dusting problem in practice. In this research, a slurry-type set accelerator was developed to avoid this problem and its effectiveness was investigated by applying it to shotcrete mortars. Set time, stiffening, compressive strength, and chloride ion penetration resistance were examined with different amounts of slag, used as partial replacement of cement. According to the experimental results, it was found that the earlier responses such as set time, stiffening, and 1-day compressive strength were probably affected by the amount of ettringite, formulated by the hydration between C12A7 and calcium sulfate polymorphs present in blast furnace slag. Whereas, it is believed that the result of compressive strength after 3 days was attributed to the hydration of tricalcium silicates. As for the results of a chloride ion penetration test, the partial replacement of cement with slag significantly reduced the total charge passed through the shotcrete mortar.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.555-558
• /
• 2005

The purpose of this study is to evaluate the chemical resistance of polymer powder-modified mortars with special accelerator component. Polymer powder-modified mortars with the accelerator are prepared with various polymer-binder ratios, and tested for flexural and compressive strengths and mass change. Chemicals resistance was tested by dealing with $10\%$ HCl and $5\%\;H_2SO_4$ aqueous solution. As a result, the weight reduction ratio of the mortars decreased with increasing polymer-binder ratio. However, in the viewpoint of strength reduction by chemical attacks, the maximum chemical resistance of the mortars was shown at a polymer-binder ratio of $5\%$.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.559-562
• /
• 2005

The purpose of this study is to evaluate the durability and bond strength of polymer powder-modified mortars with special accelerator components. The mortars were prepared with various polymer-binder ratios and applied to the concrete substrate as a repair material. Bond strength, flexural and compressive strengths, freeze-thaw resistance and carbonation resistance were measured for the test. As a result, bond strength of the mortars was increased with an increase in the polymer-cement ratio, and freeze-thaw resistance and carbonation resistance were significantly improved with increasing polymer-cement ratio also.