• Journal of Ocean Engineering and Technology
• /
• v.6 no.2
• /
• pp.85-93
• /
• 1992

The only hardness of 2nd phase of martensite in dual phase steel which was composed of the martensite and ferrite was changed. Fatigue test was conducted by cantilever type of self-made rotated bending fatigue testing machine. The corrosion fatigue fracture behaviors of dual phase steel were investigated in 3% NaCl solution at $N_f$ = $1.5\times$$10^5$ $N_f$=1.0 $\times$ $10^6$ cycles. The fatigue strength was increased with increasing the hardness of 2nd phase. The size and number of corrsion pits were influenced by the 2nd phase hardness and pits remain constant in size just after they were transited into cracks. The life of crack initiation was effected by stress level. The shape of relation of $\Delta$K and da/dn has smaller scattering in it in 3% NaCl solution than that in air. The higher the 2nd phase hardness is, the higher the corrosion fatigue life becomes. Corrosion fatigue fracture behavior was effected by mechanics in case of $N_f$=1.5$\times$10$^5$$N_f$=1.5$\times$10$^6$ cycles.

• Journal of Welding and Joining
• /
• v.14 no.2
• /
• pp.36-45
• /
• 1996

Fatigue strength of the spot welded lap joint is considerably influenced by corrosive environments. Particularly, the chloride and the sulfide are most injurious to strength of the spot welded lap joint. Therefore, there is a need to evaluate its effect to corrosion fatigue strength for safe life design of spot welded structures. In order to evaluate their corrosion fatigue strength, corrosion fatigue tests on the spot welded lap joints of the uncoated and the coated high strength steel sheets were conducted in air and in 10% NaCl solution. Corrosion fatigue strength of the uncoated specimens were entirely lower than the coated one in NaCl solution, but those of the coated specimens in NaCl solution were lower than in air. And stress distribution in single spon welded lap joint subjected to tension-shear load was investigated by the finite element method. Using these results, we tried to evaluate corrosion fatgue strength of the various spot welded lap joints with maximum stress $\sigma_{max}$ at edge on loading side of the spot welded lap joint. We could find that corrosion fatigue strength could be quantitatively and systematically rearranged by $\sigma_{max}$.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.22.1-22.1
• /
• 2011

산업의 발달과 더불어 수송기기를 포함한 각종 구조물의 경량화에 따라 피로파괴에 대한 관심이 높아지고 있다. 과거에는 피로균열생성과 피로균열전파를 구분하지 않는 S-N (stress-cycles to failure) 피로 개념을 이용하여 구조재의 피로 거동을 이해하고자 하였다. 그러나 최근에는 모든 구조물에는 균열이 존재한다는 가정에서 시작된 파괴역학(fracture mechanics)에 기초한 피로균열성장 개념을 이용하여 피로에 대한 저항성이 큰 구조재를 개발하고 있으며, 구조물의 피로수명을 예측하고 있다. 본 발표에서는 미세조직, 인장특성, 용접이나 부식 환경 등이 금속의 피로 및 피로균열성장(fatigue crack propagation)에 미치는 영향에 대한 논하고자 한다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.3 s.174
• /
• pp.603-612
• /
• 2000

Corrosion characteristics on the 12Cr alloy steel of turbine blade was electro-chemically investigated in 3.5wt% NaCI and 12.7wt% Na2S04 solution, respectively. Electro-chemical polarization test, Huey test and Oxalic acid etching test were previously conducted to estimate corrosion susceptibility of the material. And, using the horizontal corrosion fatigue tester, corrosion fatigue characteristics of 12Cr alloy steel in distilled water, 3.5wt% NaCI solution, and 12.7wt%(1M) Na2S04 solution were also fracture-mechanically estimated and compared their results. Parameter considered was room temperature, 60'C and 90'C. Corrosion fatigue crack length was measured by DC potential difference method.Obtained results are as follows,1) 12Cr alloy steel showed high corrosion rate in 3.5wt% NaCI solution and Na2S04 solution at high tempratue.2) Intergranular corrosion sensitivity of 12 Cr alloy was smaller than austenitic stainless steel.3) Corrosion fatigue crack growth rate in 3.5wt% NaCI and 12.7wt%(IM) Na2S04 solution is entirely higher than in the distilled water, and also increased with the temperature increase.

• Proceedings of the KWS Conference
• /
• 1992.04a
• /
• pp.78-80
• /
• 1992

• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.24 no.2
• /
• pp.142-146
• /
• 2012

In the geothermal power, the geothermal fluid such as water or steam is moved from the ground to turbine a pipeline. Because the geothermal fluid with high temperature contains Cl-and SO4-, It cause to diminish the system lifetime due to the increase in the corrosion of pipeline. In the present work, the characteristics of corrosion and its fatigue of the sus316 which is used in the pipeline are evaluated experimentally. From this study, the following results can be obtained; for the case of the corrosion environment, it is found that the corrosion rate is faster than that of the steam environment by 10 to 30 times, and the corrosion fatigue limit is underestimated compared to that of steam state.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.2
• /
• pp.57-69
• /
• 1997

The objetive of this study is to compare the mechanical proprties of 6000 series Al-Mg-Si aluminum alloy (AC120) with 5000 series Al-Mg aluminum alloy (TG25), and to investigate the influence of corrosion solution for fatigue life. Comparing of TG25 and AC120 alloy sheets, TG25 alloy sheets showing higher plastic ratio and total elongation have better formability than AC120 alloy sheets. The hardness of nugget area was a little higher than that of base metal area. Also, grain coarsening was observed in HAZ(Heat Affected Zone). In a corrosion fatigue experiment, the fatigue life decreased as concentration increased, when a dipping time was constant. The life decreased as dippling time increased, when a concentration was constant.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2004.04a
• /
• pp.77-82
• /
• 2004

This study presents reliability assessment of merchant ships with focus on hull girder ultimate limit state, taking into account the time-dependent effects of corrosion, fatigue cracking and local denting. Some considerations for establishing a reliability-based repair and maintenance scheme are also made so as to keep a ship's hull girder strength reliability at an acceptable level even later in life.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.39.1-39.1
• /
• 2011

가압경수로의 압력경계기기는 약 $300^{\circ}C$, 150기압의 고온고압수환경에서 가동되고 있다. 특히 가압기 밀림관은 고온수와, 저온수가 교차하는 부분으로 열성층 형성으로 열적, 기계적 피로 및 수화학환경이 더해진 부식피로 등에 의하여 손상을 받는다. PWR 원전에서 수화학환경은 대표적으로 용존산소(DO) 5ppb, pH 6~8, 용존수소(DH) <30 cc/kg, 온도 $316^{\circ}C$의 환경을 유지하게 된다. 가압기 밀림관에는 오스테나이트계 스테인리스강이 사용되는데, 오스테나이트계 스테인리스강은 고온 수화학환경에 민감한 것으로 알려져 있다. 따라서 오스테나이트계 스테인리강을 공기중에서의 기계적특성 및 피로특성을 향상시키기 위하여 질소를 첨가한 스테인리스강을 제조하여 PWR 원전환경에서의 피로균열성장특성을 평가하였다. 실험에 사용된 재료는 PWR 원전 가압기 밀림관 소재인 Type 347 스테인리스강에 0.0005 wt%가 첨가된 상용재와 0.11 wt% 질소가 첨가된 재료이다. 사용된 시편형상은 두께 5 mm, 폭 25.4 mm의 CT 시편이다. 수화학환경은 150기압, 온도 $316^{\circ}C$, 용존산소(DO) 5ppb, 용존수소(DH) 30 cc/Kg, pH는 약 7로 유지 하였으며, 응력비 0.1, 하중 반복속도 10Hz의 기계적 조건에서 하중제어로 시험을 진행하였다. 균열길이는 직류전위차법(Direct Current Potential Drop: DCPD)을 이용하여 측정하였다. 질소함량이 증가할수록 동일 사이클에서 균열길이가 늦게 성장하였고, 피로균열성장속도도 약간 늦어지는 것으로 나타났다. 각 스테인리스강의 피로파면 관찰결과 상용재는 약 1 ${\mu}m$의 산화물들이 생성되는 반면 질소첨가 스테인리스강은 약 0.1 ${\mu}m$정도 산화물이 생성되었다. 산화막의 두께도 질소가 첨가됨으로써 상용재에 비해 얇게 생성되었다. 따라서 질소가 첨가됨으로써 부식환경에서 내산화성이 향상되었으며, 이는 피로균열성장특성에 영향을 미치는 것으로 판단된다.

• Journal of Advanced Marine Engineering and Technology
• /
• v.40 no.1
• /
• pp.10-16
• /
• 2016

Fatigue analysis for life extension of a ship is different from that of a newly constructed ship since the current corrosion margin and voyage routes of the past and future must be considered, thereby complicating the life extension procedure. This research introduces the fatigue analysis case for the life extension project of a moss LNG carrier using full spectral fatigue analysis, which has been previously used for newly constructed ships. It is expected that the fatigue analysis methodologies and full spectral fatigue analysis program used in this study will be applicable to other life extension projects.