• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.3
• /
• pp.115-119
• /
• 2001

Hydroxyapatite-yttria stabilized zirconia bioceramics containing fine zirconia particles were prepared as 3-layered functionally graded materials (FGMs) using a spark plasma sintering (SPS) and hot pressing (HP) apparatuses. The pretreatment of the raw hydroxyapatite promoted the sinterability of hydroxyapatite. The maximum density of pretreated FGM composites could be obtained at lower temperature than that for he untreated FGM samples. No decomposition from hydroxyapatite to three calcium phosphate (TCP) was observed in FGMs of HAp-$ZrO_2$ sintered below $1200^{\circ}C$ for 8 min under 10 MPa by SPS. However, the transformation of the tetragonal zirconia to the cubic modification had occurred in FGMs at this temperature. The presence of zirconia i.e. stress induced transformation of zirconia may be expected to enhance the mechanical properties of HAp-$ZrO_2$ FGM. The SPS is concluded as a better method to fabricated the FGM with dense and high strength compared with HP process.

• Journal of the Korean Ceramic Society
• /
• v.24 no.3
• /
• pp.243-250
• /
• 1987

The effects aging on some properties and thermal-shock behavior of zirconia partially stabilized with 9 mol% MgO (9MZ) were studied. 9MZ specimens were aged over $1200^{\circ}$-$1400^{\circ}C$ for 12hours subsequently, after sintering at $1650^{\circ}C$ for 4 hours. Fracture strength(both before and after thermal-shock test), linear thermal expansion, monoclinic fraction and phase transition by XRD, density, galvanic potential and microstructure were measured. Quantitative chemical analysis around the grain-boundary of the specimen aged at $1350^{\circ}C$ was also conducted by EDX. The aging of 9MZ specimen causes a thermal decomposition of cubic-$ZrO^{2}$ into the formation metastable tetragonal-$ZrO^{2}$ and MgO. The former increases the residual strength after thermal-shock test and the latter improves the thermal-shock resistance due to thermal conduction through the continuous magnesia phase and the formation of monoclinic phase content in matrix were increased with decreasing the aging temperature from $1400^{\circ}C$ to $1200^{\circ}C$. Galvanic potential of the aged specimen exhibited a proper emf characteristic.

• Journal of the Korean Ceramic Society
• /
• v.24 no.2
• /
• pp.186-192
• /
• 1987

ZrO2 powders having high purity were prepared from domestic zircon sand using the caustic fusion method and the soda ash sintering process. In the caustic fusion method, ZrO2 recovery was reached to 96% when 100/140 mesh zircon was reacted with NaOH at the NaOH/Zircon mole ratio 6 and at 650$^{\circ}C$ for 2 hours. And in the soda ash sintering process, ZrO2 was recovered to 88.5% when -325 mesh zircon was reacted with Na2CO3 at the Na2CO3/Zircon mole ratio 1.1 and 1050$^{\circ}C$ for 2 hours. In both cases, Zr component was extracted to ZrOCl2, subsequently crystallized to ZrOCl2$.$8H2O to increase the purity, and converted to ZrO2 by precipitation. And to increase the sinter ability of powder, Cl- ion was removed and strong agglomeration was avoided by methanol distribution of Zr(OH)4 precipitates.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.10
• /
• pp.3234-3242
• /
• 1996

This paper describes experimental results of modified small punch( MSP) test conducted to evaluate the fracure characteristics and mechanical properties of plasma sparayed zirconia ($ZrO_2$ stabilized with 8wt. % $Y_20_3$ : YSZ) NiCrAlY composite. The mixing ratios of YSZ/NiCrAlY were 0/100, 25/75, 50/50, 100/0 v.%. Test temperatures ranged from 293K to 1473K. This study is directed at development of thermal barrrier coating(TBC) system with superior heat resistance and mechanical properties. The microstructure and fracture process of the composite were examined by SEM and AE method. The mechanical properties of 100% YSZ were nearly independent of the temperatures tested in this study. In contrast, the NiCrAlY-containing composites showed a significant decrease of the mechanical properties above 1273K, showing a ductile- brittle transition behavior up to the temperature. Furthermore, it can seen that 25% YSZ/75% NiCrAlY composite gave the highest fracure strength and fracture energy among the mixing ratio tested over the temperature range.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1176-1180
• /
• 1994

The sliding wear behavior of the plasma-sprayed zirconia containing 3 mol% yttria was investigated after the annealing at room temperature to 80$0^{\circ}C$ in various concentrations of humid atmosphere as laboratory, humid, dry argon atmosphere. Both of the friction coefficient and the wear loss increased with increasing temperature up to 80$0^{\circ}C$. Surface morphology of the worn samples changed with annealing temperature. The change of monoclinic/tetragonal (m/t) x-ray peak intensity ratio effected the wear behavior. The m/t ratio had maximum value at 20$0^{\circ}C$ and decreased with increased temperature in laboratory and humid atmosphere. In argon atmosphere the m/t ratio had no maximum value and decreased with increasing temperature. At all the annealing temperature humid atmosphere had more the m/t ratio value than any other atmosphere. The change of toughness was showed the inversed result of m/t ratio change. The results indicated that the resudial stress which was induced by the different amount of phase transformation takes a detrimental role in wear behavior.

• Journal of the Korean Ceramic Society
• /
• v.22 no.4
• /
• pp.40-46
• /
• 1985

Thermal diffusivities of zirconia samples partially or fully stabilized by MgO and $Y_2O_3$ were measured b laser-flash method up to 140$0^{\circ}C$ The values of thermal diffusivity decreased as the contents of MgO and $Y_2O_3$ increased due to the phonon scattering effect of defect structure of cubic phase formed. The temperature dependence of thermal diffusivity showed that the thermal diffusivity values decreased due to phono-phonon scattering as the temperature increased. The difference in thermal diffusivity was observed on cooling after heating up to 140$0^{\circ}C$ for magnesia stabi-lized zirconia samples but not for yttria stabilized zirconia samples.

• Journal of Power System Engineering
• /
• v.9 no.4
• /
• pp.90-95
• /
• 2005

The wire-arc process is a low-cost thermal spray method simply utilizes electrical energy to melt the feedstock wire. It is more userful for field applications, especially to coat large surface area. In this paper, a special Fe-based alloy coatings by using the wire-arc process were developed. Nanoscale composite coatings were achieved either during spraying or through a post heat treatment. As-sprayed Fe-based alloy coatings had been an amorphous matrix structure, after heating to $700^{\circ}C$ for 10 minutes a solid state transformation occurred in the some fraction of amorphous matrix which resulted in the formation of nanostructured recrystallized phase. Scanning electron microscopy (SEM) and field emotional scanning electron microscope(FE-SEM) were applied to analyze the microstructure of the coatings. Additionally hardness and bend resistance of the Fe-based alloy coatings were examined, and these results were compared with those of partially stabilized zirconia(PSZ) coatings by using the plasma spray process.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.2
• /
• pp.74-79
• /
• 2016

The lanthanum oxide nano-rods were grown on the surface of 3 mol% Yttria Partially Stabilized Zirconia ceramic composite which containing Lanthanum-Strontium Manganate, $La_xSr_yMn_zO_3$ for the purpose of endorsing the antistatic property. The diameter and the aspect ratio of the nano-rods were greatly changed according to the growing condition. With the optical microscope observation, the nano-rods shining brightly. It was confirmed that the major components of nano-rods is La, and Sr, Mn, Si are minor components by SEM and TEM analyses.

• Journal of the Korean Ceramic Society
• /
• v.52 no.1
• /
• pp.19-22
• /
• 2015

The joining behavior of YSZ ceramics to the glasses used in the $9Al_2O_3-24ZrO_2-51SiO_2-16R_2O$ and $9Al_2O_3-24ZrO_2-51SiO_2-7La_2O_3-9R_2O$ (wt%) glass systems was investigated. The glass transition and softening temperatures were determined to be $430^{\circ}C$ and $760^{\circ}C$, respectively. The behavior of the contact angle was inversely proportional to an increase in the temperature. The Zr element in YSZ acted as a nucleation agent and contributed to the bonding behavior at the interface.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.3
• /
• pp.631-638
• /
• 1995

In this study, mechanical characteristics test of Functionally Gradient Materia (FGM) was performed by means of Modified Small Punch (MSP) Test with FGM; NiCrAlY-8YSZ and PSZ-Ni. To determine fracture mechanic factor, it was carried out MSP test that has possibility with small specimen (10*10*0.5 mm$^{t}$ ) and AE test to analyze micro fracture mechanism. As a result, fracture behavior became varied from brittle fracture to ductile as the content of Ni(or NiCrAlY) composition was increased and fracture energy was increased too. AE characteristics demonstrated that AE technique can detect the onset of fracture processes and AE energy was suddenly increased in the vicinity of maximum load. Since Young's modulus, fracture stress and fracture toughness was determined by MSP test, it can be known that the composition of NiCrAly 75%/8YSZ25% has the best mechanical property and furthermore this result is supported with fracture surface observation.