• Journal of the Korea Concrete Institute
• /
• v.22 no.5
• /
• pp.703-710
• /
• 2010

Reinforced concrete beams of existing structure often encounter insufficient shear problems for various reasons. Application of steel plates is one of widely used methods for shear strengthening of reinforced concrete beams that are insufficient of shear capacity. This study presents test results on strengthening shear deficient RC beams by external bonding of vertical and diagonal slit type steel plates with anchor bolt. Test parameters are width, interval, angle and length of slits with anchor bolt. The purpose was to evaluate the failure modes and shear capacities for RC beams strengthened by various slit type steel plates with anchor bolt. The results showed that the slit type steel plate specimens strengthened by adhesive bonding and bolting failed in shear fracture modes at maximum load. Flexural crack first occurred on the tension face of beam and then inclined cracks occurred on the shear span. Finally, slit type steel plates strengthened by adhesive bonding and fastening bolts managed to delay abrupt debonding and didn't detach fully from main body of RC beam.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.429-432
• /
• 2000

본 논문의 정수기는 영동산 일라이트를 필터의 주된 재료로 사용하였다. 구조는 여과필터를 교체하여 사용할 수 있도록 된 정수기의 필터 케이스 및 여과 방법에 관한 것으로써, 보다 상세하게는 필터 케이스가 분리, 결합이 간편한 본체와 마개로 구성되어 있다. 이 본체는 1차 여과부와 2차 여과부로 분리되어 물이 1차 여과부의 상부를 통해 인입되어 2차 여과부의 상부로 연결되도록 되어 있어 동일한 크기 내에서 여과구간이 2배로 길어져 여과 효율이 우수한 동시에 물인입구와 물배출구가 동일한 방향에 위치하여 다수 개의 필터 케이스를 연결할 때 필터 케이스의 간격을 좁힐 수 있어 필터 케이스의 설치면적이 좁다. 본체와 마개의 체결방식은 볼트 체결방식으로 되어 있으며, 마개는 플라스틱 재질이어서 본체에 마개를 단단히 체결하면 누수가 방지되도록 되어있다. 즉, 정수기의 필터하우징 성능과 영동산 일라이트가 가지고 있는 기능성을 이용한 필터를 사용함으로써 정수기에서 요구되어지는 정수능력을 가진 정수기를 개발 보고한다.

• Journal of the Korean Geotechnical Society
• /
• v.29 no.6
• /
• pp.33-51
• /
• 2013

This paper introduces the improvement of connection method for segment in tunnel lining system using prestressed steel cable and presents the results of real-scale tests. It conducted a study about the applicability and mechanical behaviour analysis of the new method that connects segment tunnel lining using prestressed steel cable by real-scale test. Through the research, it was found that the new method has stronger connection than conventional assembling methods. Also, the new method can be expected to have integrated behavior and stability increase of shield tunnel lining. It is considered that the new method is much more effective than conventional assembling methods.

• Journal of Korean Society of Steel Construction
• /
• v.9 no.3 s.32
• /
• pp.301-307
• /
• 1997

In field fabrication of steel members, the oversize hole is frequently required due to reaming and mismatching. But, there are no provisions and investigations about oversize hole in the Korean specifications. So, in this study, the tension test of friction type high-tention bolted joints is performed with parameters of bolt hole size, surface treatment and tightening force, and investigate the effect of slip behavior with those parameters. From the results, the enough tightening force is needed to obtain some degree slip load in shot blast treatment case, although tightening force is reduced somewhat, it is no problem to guarantee slip load in zincrich primer case. The slip behavior of joints with oversize hole(26mm) is similar to the slip behavior of joints with hole of nominal size.

• Journal of Aerospace System Engineering
• /
• v.11 no.6
• /
• pp.68-75
• /
• 2017

In this study, the bolt torque calculation method for space industry was compared and verified experimentally. Currently, NASA, European Aerospace Agency, and US National Defense Standards are proposing standards for bolt torque estimation. However, these standards vary slightly and require a high level of comprehension. To address these challenges, we selected typical equations among the widely-used bolt torque calculation methodologies, and the predicted values were verified via clamping force test. In addition, we examined the changes in clamping force associated with handling and refastening.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.10 no.9
• /
• pp.2402-2408
• /
• 2009

This study conducted a static tensile test in order to prevent the lowering of load carrying capacity caused by critical sections made by over bolt holes in the base plate and the cover plate of steel member joints using high-tension bolts. The change of the load carrying capacity of joints was examined by comparison of the maximum load on joint fracture obtained from the tensile test with critical section rate and design strength. According to the results, the rate of decrease in strength was higher when the critical section rate was high, and in particular, decrease in strength was affected much more by critical sections in the base plate than by those in the cover plate. In high-tension bolt joints using over bolt holes for the base plate and the cover plate, load carrying performance was somewhat lower than that in joints using standard bolt holes, but the maximum tensile strength on facture was over 15% higher than design fracture strength. According to the results of this study, the use of over bolt holes in high-tension bolt joints had an insignificant effect on the lowering of load carrying capacity, so the allowance of over bolt holes in the joints of steel members is expected to enhance to the economy and efficiency of the works.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.121-121
• /
• 2009

자동차는 코너 주행 시 In-corner와 Out-corner 의 바퀴 궤적이 달라지므로, 특별한 장치가 없이 좌우 구동 측의 바퀴가 같은 속도로 회전을 하게 되면 정상적인 주행이 불가능하다. 따라서 정상적인 코너 주행이 가능 하려면, 코너 안쪽 바퀴보다 바깥쪽 바퀴가 더 빨리 회전해야 하며 이러한 회전 차를 보상받지 못할 경우 바깥쪽 바퀴가 끌리는 현상이 발생하는데 이를 방지하기 위해 디퍼렌셜 기어가 필요하다. 현재 디퍼렌셜 기어는 디퍼렌셜 케이스와 링기어를 볼트로 체결하는 조립 공법을 통해 생산되고 있다. 하지만 볼트 체결 공법은 조립을 위한 볼트와 볼트 체결을 위한 플랜지와 볼팅을 위한 홀을 가공하는 공정이 필요하기 때문에 재료비 절감 및 생산 효율 향상에 매우 불리하고 볼트체결을 위한 부분 때문에 불필요한 무게가 증가하게 된다. 따라서 본 연구에서는 이러한 기계적 체결 방식을 레이저 용접 방식으로 대체하여 재료비를 절감하고 무게 저감을 통해 주행성능을 향상시키고자 하였다. 링기어의 소재는 침탄처리강(SCM420H)이며 디퍼렌셜 케이스의 소재는 주철(GCD500)을 사용하고 있다. 주철은 용접시 용접부와 열영향부에서 마르텐사이트 조직과 레데브라이트, 시멘타이트 조직이 생성되며 고탄소 모재의 탄소 확산으로 인한 부분 혼합영역에서 탄소 합금이 생성되어 균열이 발생하는 등 용접성이 매우 좋지 않은 것으로 알려져 있다. 이러한 주철의 난용접성을 해결하는 방법으로는 고탄소 모재 용접시 발생하는 탄소의 확산을 억제하거나 예열이나 후열 처리를 통한 냉각 속도의 제어하는 방법과 오스테나이트 안정화 원소를 첨가한 필러와이어를 사용하여 용접시 마르텐사이트와 시멘타이트의 성장을 방해하는 방법 등이 이용되고 있다. 본 연구에서는 예열처리나 후열처리를 통한 주철의 용접법은 대량 생산을 통한 원가절감을 노리는 자동차 업계의 특성에 비추어 볼 때 비용이나 프로세스 구성 면에서 적용하는 것이 어려울 것이라 판단하여 Ni-base filler metal을 통한 주철의 용접법을 선택하였고 그 결과 실차에 적용하기 위한 비틀림 강성 테스트나 내구 테스트는 통과하였으나 NVH 테스트 결과 볼팅 체결 방식에 비하여 소음이 커지는 문제가 발생하고 링기어의 HAZ부가 고경화 되는 문제가 발생하였다. 때문에 용입깊이를 초기 시제품인 5mm에서 4mm로 변경시켜 입열량 감소 및 용접변형을 줄여 소음 문제를 해결하고자 하였으며 링기어의 침탄층을 1mm 절삭하여 링기어 HAZ부의 고경화 문제를 해결하고자 하였다. 이러한 용접 구조 변경이 용접변형 및 강성과 피로에 미치는 영향력을 알아보고자 용접 및 열처리 상용 소프트웨어인 SYSWELD, 구조해석 상용소프트웨어인 NX_NASTRAN, 피로 해석 상용 소프트웨어인 FEMFAT을 이용하여 시뮬레이션 하였고 실제 구조 변경한 용접 시제품과 비교, 분석하였다.

• KEPCO Journal on Electric Power and Energy
• /
• v.7 no.1
• /
• pp.59-62
• /
• 2021

관형지지물은 단일 강관 기둥 형태의 송전탑으로 강관은 상하 여러 개의 프레임으로 분할되어 플랜지부에서 볼트로 체결된다. 신설 송전선로 관형지지물 플랜지 연결부에서 가압전 조립 볼트 절손이 발견됨에 따라 강관도괴방지 대책 수립을 위한 손상원인분석 기술지원을 수행하였다. 본 건에 대해 파손면·균열 분석 기술을 통해 제작과정 상의 문제가 있었음을 확인하였다.

• Composites Research
• /
• v.22 no.5
• /
• pp.30-36
• /
• 2009

The failure strengths and modes in carbon fiber reinforced polymeric composites, with two serial bolt-fastened composite joints, were investigated to evaluate the typical joint configurations of composite components. The parametric studies were performed experimentally at room temperature dry and elevated temperature wet, $82.2^{\circ}C$ on several different laminate configurations. Based on the experimental data presented, two basic load-displacements curves are observed. Each failure mode has the characteristic curve. It is showed that the bearing failure mode occurs in elevated temperature wet condition. It is analysed that the strength of bearing failure mode is not highly depending on the effective modulus of specimen. The failure strength at elevated temperature wet is decreased by the cause of interfacial deterioration between fiber and matrix with moisture absorption.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1469_1470
• /
• 2009

기존의 링크박스는 대부분 직매식으로 수침투 방지를 위해 케이스와 뚜껑 사이에 가스켓을 넣고 볼트로 체결하는 방식으로 사용하여 왔다. 이는 링크박스 유지보수 시 매번 볼트를 체결하고 해체하는 작업이 반복되어 현장 작업성이 떨어졌다. 이에 링크박스를 지상에 설치하며, 볼트의 사용을 최소화함으로써 유지보수 시 작업이 용이한 케비넷형 링크박스를 개발하였으며, 개발된 제품에 대해 전기적, 기계적 성능 시험을 수행하여 그 성능을 검증하였다.