• Restorative Dentistry and Endodontics
• /
• v.30 no.3
• /
• pp.204-214
• /
• 2005

This study compared the microtensile bond strength (${\mu}$TBS) and microscopic change of two 2-step and two 1-step self-etching adhesives to dentin according to storage times in distilled water. Occlusal dentin was exposed in 48 human molars. They were divided to four groups by different adhesives: SE Bond group (Clearfil SE Bond), AdheSE group (AdheSE). Adper group (Adper Prompt L-Pop), and Xeno group (Xeno III) . Each group was stored in 37$^{\circ}C$ distilled water for 1, 15, and 30 days. Resin-bonded specimens were sectioned into beams and subjected to ${\mu}$TBS testing with a crosshead speed of 1 mm/minute. For SEM observation, one specimen was selected and sectioned in each group after each stroage time. Resin-dentin interface was observed under FE-SEM. In all storage times, mean ${\mu}$TBS of SE group was significantly higher than those of other groups (p < 0.05). There was no significant difference between mean ${\mu}$TBS of SE group and AdheSE group among all storage times, but significant difference between 1- and 30-day storage in mean y${\mu}$TBS of Adper group and Xeno group (p > 0.05). For 1-and 15-day storage, all groups showed the close adaptation between resin-dentin interfaces. For 30-day storage, resin-dentin interfaces showed wide gap in Adper group and separate pattern in Xeno III group.

• Restorative Dentistry and Endodontics
• /
• v.36 no.6
• /
• pp.490-497
• /
• 2011

Objectives: This study examined the effect of the uncured dentin adhesives on the bond interface between the resin inlay and dentin. Materials and Methods: Dentin surface was exposed in 24 extracted human molars and the teeth were assigned to indirect and direct resin restoration group. For indirect resin groups, exposed dentin surfaces were temporized with provisional resin. The provisional restoration was removed after 1 wk and the teeth were divided further into 4 groups which used dentin adhesives (OptiBond FL, Kerr; One-Step, Bisco) with or without light-curing, respectively (Group OB-C, OB-NC, OS-C and OS-NC). Pre-fabricated resin blocks were cemented on the entire surfaces with resin cement. For the direct resin restoration groups, the dentin surfaces were treated with dentin adhesives (Group OB-D and OS-D), followed by restoring composite resin. After 24 hr, the teeth were assigned to microtensile bond strength (${\mu}TBS$) and confocal laser scanning microscopy (CLSM), respectively. Results: The indirect resin restoration groups showed a lower ${\mu}TBS$ than the direct resin restoration groups. The ${\mu}TBS$ values of the light cured dentin adhesive groups were higher than those of the uncured dentin adhesive groups (p < 0.05). CLSM analysis of the light cured dentin adhesive groups revealed definite and homogenous hybrid layers. However, the uncured dentin adhesive groups showed uncertain or even no hybrid layer. Conclusions: Light-curing of the dentin adhesive prior to the application of the cementing material in luting a resin inlay to dentin resulted in definite, homogenous hybrid layer formation, which may improve the bond strength.

• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.299-308
• /
• 2016

This paper presents an investigation of the mechanical and microstructural properties on hardened samples that were synthesized using blended binder(fly ash(FA) and blast furnace slag cement(BFSC)), alkali activator and sea water or distilled water. Binders were prepared by mixing the FA and BFSC in different blend weight ratios of 6:4, 7:3 and 8:2. Sodium hydroxide and sodium silicate were used 5 wt% of binder, respectively, as an alkaline activator. The compressive strength and absorption were measured at the age of 3, 7 and 28 days, and the XRD, TGA and MIP tests were performed at the age of 28 days. An increase in the content of BFSC leads to an increase in the quantities of ettringite and C-S-H formed, regardless of the type of mixing water. And it also shows higher strength due to the reduction of pores larger than ~50 nm. All hardened samples in this study have common hydration products of C-S-H, $Ca(OH)_2$ and calcite. Hydrocalumite of all reaction products formed was only present in hardened sample mixed with sea water. For each FA/BFSC mixing ratio, the compressive strength of hardened sample mixed with sea water was similar to that mixed with distilled water. It is proposed that the slight increase of strength of samples mixed with sea water is mainly due to the presence of hydrocalumite phase containing chlorine ion, contributing to the change of total porosity and pore size distribution in samples.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2020.06a
• /
• pp.50-50
• /
• 2020

하천, 강어귀 및 해안 지역의 점착성 유사는 흐름 내에 입자의 충돌에 의한 흡탈착으로 인해 다양한 크기의 플록을 형성한다. 이 플록은 오염물과도 군집을 형성하여 하상이 퇴적되는 경우가 많으며 홍수 등과 같은 외부 충격으로 인해 재부 되어 하천 환경 및 생태계에 악영향을 미친다. 군집의 형성은 화학적인 결합과 물리적인 응집으로 분류할 수 있는데, 미세 점착성 유사의 군집형성에 대한 연구는 주로 화학적인 결합에 대한 연구가 활발하다. 반대로 물리적인 결합 혹은 외부 충격에 대한 플록형성 매커니즘에 대한 연구는 미비한 실정이다. 따라서, 본 연구에서는 교반기를 활용한 실험을 통하여 점착성 유사에 대한 물리적인 흡탈착 과정을 분석하였다. 유입된 점착성 유사를 교반기로 외부충격을 주어 흡착과 탈착하는 정도를 탁도와 농도를 통해 정량화하였다. 실험은 원통 수조에서 수행되었으며, 교반기의 RPM을 조절하면서 외부충격의 강도를 조절하였다. 초기 실험을 통해 탁도-농도의 관계를 제시하였고 이를 활용하여 교반강도와 점착성 유사의 농도를 분석하였다. 실험 결과 교반강도가 증가할수록 플록 형성이 활발하게 진행되었으나, 일정 교반강도 이상에서는 다른 흡착 과정을 보였다. 이를 토대로 점착성 유사의 흡탈착의 임계값을 제시하였다. 향후 본 연구결과와 유속 혹은 난류강도 등의 하천특성과 연관성을 분석한다면 하천 내 오염물 관리에 효과적으로 사용될 것으로 기대된다.

• Restorative Dentistry and Endodontics
• /
• v.35 no.3
• /
• pp.211-221
• /
• 2010

Proteoglycan is highly hydrophilic and negatively charged which enable them attract the water. The objective of study was to investigate the effects of Proteoglycan on microtensile bond strength of dentin adhesives and on architecture of dentin collagen matrix of acid etched dentin by removing the chondroitin sulphate attached on Proteoglycan. A flat dentin surface in mid-coronal portion of tooth was prepared. After acid etching, half of the specimens were immersed in 0.1 U/mL chondroitinase ABC (C-ABC) for 48 h at $37^{\circ}C$, while the other half were stored in distilled water. Specimens were bonded with the dentin adhesive using three different bonding techniques (wet, dry and re-wet) followed by microtensile bond strength test. SEM examination was done with debonded specimen, resin-dentin interface and acid-etched dentin surface with/without C-ABC treatment. For the subgroups using wet-bonding or dry-bonding technique, microtensile bond strength showed no significant difference after C-ABC treatment (p > 0.05). Nevertheless, the subgroup using rewetting technique after air dry in the Single Bond 2 group demonstrated a significant decrease of microtensile bond strength after C-ABC treatment. Collagen architecture is loosely packed and some fibrils are aggregated together and relatively collapsed compared with normal acid-etched wet dentin after C-ABC treatment. Further studies are necessary for the contribution to the collagen architecture of noncollagenous protein under the various clinical situations and several dentin conditioners and are also needed about long-term effect on bond strength of dentin adhesive.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.526-536
• /
• 2008

The purpose of this study was to compare the effect of various dentin bonding systems on microtensile bond strength of immediate dentin sealing (IDS) and delayed dentin sealing (DDS). Eighteen extracted permanent molars were used in this study. The teeth for DDS group were restored with a provisional restorations, and immersed in saline solution for 1 week, and divided into 3 subgroups according to various dentin bonding adhesives; SB subgroup (3 step total-etch adhesive), SE subgroup (2 step self-etch adhesive), XE subgroup (1 step self-etch adhesive). In IDS group, the teeth were divided into 3 subgroups, and applied with bonding adhesives as in DDS group. The teeth were restored with provisional restorations, and immersed in saline solution for 1 week. Indirect composite disc was cemented with resin cement, and all specimens were subjected to microtensile bond strength. The data were statistically analyzed with oneway ANOVA and Student t-test. The results were as follows: 1. The IDS group showed significantly higher ${\mu}TBS$ than DDS group in 3 step total-etch and 2 step selfetch adhesive (p < 0.05). 2. In IDS and DDS group, 3 step total-etch adhesive showed the highest ${\mu}TBS$ value, followed by 2 step self-etch, and 1 step self-etch adhesive. In IDS group, the ${\mu}TBS$ value for 1 step self-etch adhesive was significantly different from those of the other subgroups (p < 0.05), and in DDS group, there were statistical differences in all subgroup (p < 0.05). 3. Failure modes of tested dentin bonding adhesives were mostly mixed failure and only 1 step self-etch adhesive showed adhesive failure.

• Restorative Dentistry and Endodontics
• /
• v.31 no.6
• /
• pp.445-451
• /
• 2006

The purposes of this study were to compare the effects of one or two applications of all-in-one adhesives on microtensile bond strengths (${\mu}$TBS) to unground enamel and to investigate the morphological changes in enamel surfaces treated with these adhesives using a scanning electron microscopy (SEM). Twenty-five noncarious, unrestored human mandibular molars were used. The unground enamel surfaces were cleansed with pumice. The following adhesives were applied to lingual, mid-coronal surfaces according to manufacture's directions; Clearfil SE bond in SE group, Adper Prompt L-Pop$^{TM}$1 coat in LP1 group, 2 coats in LP2 group, Xeno$^{\R}$III1 coat in XN1 group, and 2 coats in XN2 group. After application of the adhesives, a hybrid light-activated resin composite was built up on the unground enamel. Each tooth was sectioned to make a cross-sectional area of approximately 1.0 mm$^2$ for each stick. The microtensile bond strength was determined. Each specimen was observed under SEM to examine the morphological changes. Data were analyzed with one-way ANOVA. The results of this study were as follows; 1. The microtensile bond strength values were; SE (19.77 ${\pm}$ 2.44 MPa), LP1 (13.88 ${\pm}$ 3.67 MPa), LP2 (14.50 ${\pm}$ 2.52 MPa), XN1 (14.42 ${\pm}$ 2.51 MPa) and XN2 (15.28 ${\pm}$ 2.79 MPa). SE was significantly higher than the other groups in bond strength (p < 0.05). All groups except SE were not significantly different in bond strength (p < 0.05). 2. All groups were characterized as shallow and irregular etching patterns.

• Restorative Dentistry and Endodontics
• /
• v.35 no.6
• /
• pp.461-472
• /
• 2010

Objectives: This study evaluated microtensile bond strength (${\mu}TBS$) and short-rod fracture toughness to explain fractural behavior of repaired composite restorations according to different surface treatments. Materials and Methods: Thirty composite blocks for ${\mu}TBS$ test and sixty short-rod specimens for fracture toughness test were fabricated and were allocated to 3 groups according to the combination of surface treatment (none-treated, sand blasting, bur roughening). Each group was repaired immediately and 2 weeks later. Twenty-four hours later from repair, ${\mu}TBS$ and fracture toughness test were conducted. Mean values analyzed with two-way ANOVA / Tukey's B test ($\alpha$= 0.05) and correlation analysis was done between ${\mu}TBS$ and fracture toughness. FE-SEM was employed on fractured surface to examine the crack propagation. Results: The fresh composite resin showed higher ${\mu}TBS$ than the aged composite resin (p < 0.001). Mechanically treated groups showed higher bond strength than non-mechanically treated groups except none-treated fresh group in ${\mu}TBS$ (p < 0.05). The fracture toughness value of mechanically treated surface was higher than that of non-mechanically treated surface (p < 0.05). There was no correlation between fracture toughness and microtensile bond strength values. Specimens having high KIC showed toughening mechanism including crack deviation, microcracks and crack bridging in FE-SEM. Conclusions: Surface treatment by mechanical interlock is more important for effective composite repair, and the fracture toughness test could be used as an appropriate tool to examine the fractural behavior of the repaired composite with microtensile bond strength.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.46 no.1
• /
• pp.76-84
• /
• 2019

This study evaluated the microleakage of three restorative materials and three tricalcium silicate-based pulp capping agents. The restorative materials were composite resin (CR), resin-reinforced glass ionomer cement (RMGI), and traditional glass ionomer cement (GIC) and the pulp capping agents were TheraCal $LC^{(R)}$ (TLC), $Biodentine^{(R)}$ (BD), and $ProRoot^{(R)}$ white MTA (WMTA). Additionally, shear bond strengths between the pulp-capping agents and dentine were compared. Class V cavities were made in bovine incisors and classified into nine groups according to the type of pulp-capping agent and final restoration. After immersion in 0.5% fuchsin solution, each specimen was observed with a stereoscopic microscope to score microleakage level. The crowns of the bovine incisors were implanted into acrylic resin, cut horizontally, and divided into three groups. TLC, BD and WMTA blocks were applied on dentine, and the shear bond strengths were measured using a universal testing machine. The microleakage was lowest in TLC + GIC, TLC + RMGI, TLC + CR, and BD + GIC groups and highest in WMTA + RMGI and WMTA + CR groups. The shear bond strength of BD group was the highest and that of WMTA group was significantly lower than the others.

• Restorative Dentistry and Endodontics
• /
• v.33 no.6
• /
• pp.545-552
• /
• 2008

The purpose of this study was to evaluate the influence of sodium ascorbate on microtensile bond strengths of total-etching adhesive system to pulp chamber dentin treated with NaOCl. Pulp chambers of extracted human non-caries permanent molars were treated as follows: group 1, with 0.9% NaCl; group 2, with 5.25% NaOCl; group 3, with 5.25% NaOCl and 10% sodium ascorbate for 1min; group 4, with 5.25% NaOCl and 10% sodium ascorbate for 1 min and 10ml of water; group 5, with 5.25% NaOCl and 10% sodium ascorbate for 5 min; group 6, with 5.25% NaOCl and 10% sodium ascorbate for 5 min and 10ml of water; group 7, with 5.25% NaOCl and 10% sodium ascorbate for 10 min; group 8, with 5.25% NaOCl and 10% sodium ascorbate for 10 min and 10ml of water. Treated specimens were dried, bonded with a total-etching adhesive system (Single bond), restored with a composite resin(Z250) and kept for 24h at 100% humidity to measure the microtensile bond strength. NaOCl-treated group (group 2) demonstrated significantly lower strength than the other groups. No significant difference in microtensile bond strengths was found between NaCl-treated group (group 1) and sodium ascorbatetreated groups (group 3-8). The results of this study indicated that dentin treated with NaOCl reduced the microtensile bond strength of Single bond. Application of 10% sodium ascorbate restored the bond strength of Single bond on NaOCl-treated dentin. Application time of sodium ascorbate did not have a significant effect.