• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.32 no.3D
• /
• pp.223-229
• /
• 2012

Skid resistance is defined as the friction between pavement surfaces and vehicle tires. Lower skid resistances were observed as the vehicle speeds the water film thicknesses were increased according to the analysis results using computer modeling. The lift force is calculated from the analysis results and depends on vehicle speeds and the water film thickness. A modified IFI(international friction index) skid resistance prediction model was developed to reduce the differences between the IFI resistance prediction model and the actual skid resistance. The correlation analysis results between the IFI prediction model and the actual skid resistance revealed that the $R^2$ using the modified IFI prediction model was 0.64 whereas the $R^2$ using the conventional IFI prediction model was 0.49. This presents the modified prediction model is better than the conventional one. An improved precise prediction model is to be obtained if water film thicknesses are considered in the modified prediction model.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.7
• /
• pp.681-686
• /
• 2015

The onset characteristics of friction-induced noise for a steel plate and 4 metallic pins (Cu, Ni, Al, Mg) were studied through the pin-on-disk machine and the reciprocating testing machine. The results showed that the negative slope of the friction curve was related to the onset time of friction noise. Particularly, Cu was found to be the best metallic material for preventing squeak noise in terms of the onset time and the negative friction slope.

• Tribology and Lubricants
• /
• v.29 no.6
• /
• pp.372-377
• /
• 2013

This study investigated the interface temperatures for the sliding friction of three types of pins fabricated with thermocouple wires by the suction casting method. Optical microscopy was used to examine the surrounding material state at the bonding interface with the thermocouple wires. Friction tests were performed under dry sliding conditions against stainless steel 304 at nominal stresses of 1.42-4.25 MPa and sliding speeds of 0.5-1.25 m/s. Tribological data were collected using a custom-made pin-on-disk apparatus that measured the interface temperature and corresponding friction coefficient. Static tests were performed to demonstrate the functionality and reliability of the thermocouple wires-combined temperature sensor (TCTS). Each TCTS showed good linearity and sensitivity and very similar response times for the thermocouple and critical temperature during sliding friction.

• Journal of the Korean Society for Railway
• /
• v.10 no.6
• /
• pp.772-778
• /
• 2007

For the wear characteristics assessment of Saemaul train passing through curves, an analysis model for multi-car system has been developed. By using this model and ADAMS/Rail, sensitivity analyses have been conducted for the wear characteristics by changing the related parameters. At low speed, the wear number and the sliding mean of right wheel showed higher than left wheel, while those of left wheel showed higher than right wheel at high speed. According to the decrease of curve radius, the wear number and the sliding mean were increased. When the length of transition curve was increased, the wear number and the sliding mean was increased. And according to increase of cant, the wear number and the sliding mean were increased.

• Journal of the Institute of Electronics Engineers of Korea SP
• /
• v.47 no.4
• /
• pp.28-34
• /
• 2010

In this paper, we proposed an algorithm for utilizing visual information for non-contact predicting method of friction coefficient. Coefficient of friction is very important in driving on road and traversing over obstacle. Our algorithm is based on terrain classification for visual image. The proposed method, non-contacting approach, has advantage over other methods that extract material characteristic of road by sensors contacting road surface. This method is composed of learning group(experiment, grouping material) and predicting friction coefficient group(Bayesian classification prediction function). Every group include previous work of vision. Advantage of our algorithm before entering such terrain can be very useful for avoiding slippery areas. We make experiment on measurement of friction coefficient of terrain. This result is utilized real friction coefficient as prediction method. We show error between real friction coefficient and predicted friction coefficient for performance evaluation of our algorithm.

• Tribology and Lubricants
• /
• v.25 no.1
• /
• pp.25-30
• /
• 2009

본 연구에서는 pin-on-disk 마찰 시험기를 통하여 Hexagonal 배열 $40{\mu}m$ Dimple 패턴의 효과를 실험하였다. 마찰 실험은 미끄럼 속도가 $0.06{\sim}0.34m/s$로 하였으며 마찰하중은 $20{\sim}100\;N$의 범위로 하였고, Dimple의 밀도는 $10{\sim}25%$의 범위로 제작하여 실험을 행하였다. 일반적으로 속도가 증가하고 하중이 감소할수록 마찰계수는 감소하는 경향을 나타내었으며, Dimple에 의한 마찰저감 효과는 속도가 $0.14{\sim}0.26m/s$의 범위에서 나타났다. $40{\mu}m$ Hexagonal 배열 Dimple 패턴의 마찰 특성에서는 밀도가 12.5%에서 가장 좋은 경향을 나타내었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.28-28
• /
• 2003

고온가압소결(Hot Pressing) 된 다이아몬드 공구용 Co-Fe, Co-Ni계 금속본드의 상온 건식 미끄럼 마멸시험을 행하고, 조성에 따른 각 본드의 마멸 특성을 비교하고 마멸 기구를 규명하였다. 미끄럼 마멸시험은 pin-on-disk 형태의 마멸시험기를 사용하여 각 조성의 성분, 적용하중 그리고 마멸상대재를 변수로 상온, 대기 중에서 실시되었다. 마멸속도는 마멸시험 전후의 시편의 무게 감량을 이론밀도와 거리로 나누어 계산되었다. 마멸기구의 규명을 위하여 시험된 시편의 마멸면과 마멸단면을 SEM과 EDS를 이용하여 분석하였다. 시험 결과 Co-Fe system의 경우 그 마멸속도는 마멸상대재의 영향보다는 Fe 첨가에 따른 시편의 미세조직과 기계적 성질의 차이에 따라 크게 변화하였다. 그러나 Co-Ni system의 마멸속도는 마멸 상대재에 따라 크게 변화하는 것이 관찰되었다. $Al_2$O$_3$를 상대재로 마멸된 경우에는 마멸속도가 시편/상대재 접촉면에서 형성되는 산화층의 영향을 크게 받았고, glass bead(83% SiO$_2$)를 상대재로 한 경우에는 시편의 경도와 마멸속도는 서로 반비례하였다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.10 no.10
• /
• pp.2831-2836
• /
• 2009

If a design load exceeding the frictional force of the contact surface is applied to the connection of steel members using a high-tension bolt friction joint, sliding occurs and the connection of the steel members bears the design load through the shear strength and bearing strength of the bolt and the base plate. The sliding distance can be determined by the tensile force of the bolt, the friction coefficient of the contact surface, and the position of the bolt in the base plate hole. This study measured and analyzed sliding according to standard bolt hole and oversize bolt hole when pure bending moment and tensile force were applied to high-tension bolt joints with different sizes of bolt holes made in the base plate and the cover plate. In a high-tension bolt joint receiving pure bending moment and tensile force, the load causing sliding in an oversize bolt hole was $74\sim94%$ of that in a standard bolt hole. In a member receiving tensile force, the sliding load ratio was lower when the size of oversize bolt holes in the base plate and the cover plate was large. In addition, the size of the oversize bolt hole in the base plate was more closely correlated with the change of sliding loadthan the size of the oversize bolt hole in the base plate.

• Journal of the korean Society of Automotive Engineers
• /
• v.5 no.3
• /
• pp.56-63
• /
• 1983

강성체로된 견인물체가 탄성무한경면으로 지지된 점탄성층 위를 미끄러져 갈 때 접촉구간에서의 압력분포와 마찰 특성을 고찰하였다. 즉, 접촉구간에서의 강성체의 모양과 압력분포에 관한 적분 방정식을 구하고, 점탄성층의 두께가 접촉구간에 비하여 충분히 두꺼울 때 압력분포와 마찰계 수의 근사해를 구하였다. 압력분포의 모양은 점탄성층의 물성을 표시하는 지수값, 즉 .alpha.<1/2, .alpha.=1/2, .alpha.>1/2에 따라서 크게 다르다. 한편, 수치해석에 의하면 마찰 계수에 대한 근 사해는 강성체의 미끄럼 속도, 점탄성 층의 두께, 탄성체의 영율 (E$_{o}$ )과 점탄성층의 시효 성탄성계수 (E$_{v}$ )의 차, 즉 E$_{o}$ /E$_{v}$ 에 따라 변화함을 알 수 있다. 즉, 탄성체가 점탄성층에 비하여 딱딱하면 할수록, 또 강성체 속도가 느리면 느릴수록 마찰계수는 작아진다. 그리고 불성의 지수(.alpha.)가 커지면 커질수록 근사해의 수렵 속도는 느려지게 되고 지 수(.alpha.)가 1에 가까워지면 점탄성층의 탄성효과는 점성효과에 비하여 거의 무시할 수 있으며 근사해는 의미가 없어지게 된다.

• Tribology and Lubricants
• /
• v.9 no.1
• /
• pp.9-15
• /
• 1993

Tribology는 미끄럼 혹은 구름베어링, 피스톤링, 기어, 공구, 그밖의 상대적 움직임하에 있는 부품의 설계 및 제조와 관련된 학문이다. 또한 tribology는 서로 접촉하는 재료의 적절한 사용, 윤활유와의 상호작용 이해 및 적절한 선택을 통해 마모와 마찰의 감소 혹은 최적의 마찰(브레이크, 벨트 등의 경우)을 위해 연구되는 분야이다. 부품의 내마모성을 향상시키고 적절한 마찰계수를 얻기 위해서는 기계 설계, 윤활유 선택 및 개발, 재료의 선택 및 개발 등 여러 분야의 기여가 모두 필요하다. 지금까지는 전통적으로 사용되어 오던 재료, 특히 금속재료를 중심으로 하여 기계 및 윤활제 개발 등에 치중하여 왔다. 그러나 산업이 발전되고 복잡화됨에 따라 극한 분위기 즉 고온, 고진공하에서의 장시간 사용과 고효율 등을 요구하여 최근의 tribology 분야에 사용되는 부품들의 신소재로의 대체를 요구하고 있다. 한 예로 지금의 엔진보다 더 고온에서 작동되는 고효율의 경량의 첨단 열엔진의 개발을 들 수 있다. 이러한 열 엔진의 사용목적을 달성하기 위해서는 기존의 금속재료로는 고온에서 작동괴기에는 너무 약하고 무겁기 때문에 구조용 세라믹스가 고려되고 있는 것이다. 신소재 분야중 세라믹스는 고기능성 부품과 이미 산업화된 분야의 부품의 대체 재료로 주목을 받고 있다.