In this paper, We deposited the BST thin-film on p-type (100)Si, (100)MgO and MgO/Si substrates respectively using RF magnetron sputtering method. After the BST thin-fil m was deposited, we performed RTA(rapid thermal anneal) at $600^{\circ}C$, oxygen atmosphere and 1 min. In the XRD measurement, we observed the (110) $Ba_{0.5}Sr_{0.5}TiO_3$ main peak in all samples and the peak intensity increased after post annealing. Then we manufactured a capacitor using Al Electrode and measured I-V, C-V. In C-V measurement result values for each substrate, dielectric constant was calculated 120 (bare Si), 305(MgO/Si), 310(MgO) respectively. A leakage current density was present less than 1 $\mu\textrm{A/cm}^2$ at applied fields below 0.3 MV/cm. In conclusion we confirmed that MgO/Si substrates give good results for BST thin-film deposition.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.159-160
• /
• 2012

지난 30년 동안 플래시 메모리의 주류 역할을 하였던 부유 게이트 플래시 메모리는 40 nm 기술 노드 이하에서 셀간 간섭, 터널 산화막의 누설전류 등에 의한 오동작으로 기술적 한계를 맞게 되었다. 또한 기존의 비휘발성 메모리는 동작 시 높은 전압을 요구하므로 전력소비 측면에서도 취약한 단점이 있다. 그러나 이러한 문제점들을 기존의 Si기반의 소자기술이 아닌 새로운 재료나 공정을 통해서 해결하려는 연구가 최근 활발하게 진행되고 있다. 특히, 플래시 메모리의 중요한 구성요소의 하나인 터널 산화막은 메모리 소자의 크기가 줄어듦에 따라서 SiO2단층 구조로서는 7 nm 이하에서 stress induced leakage current (SILC), 직접 터널링 전류의 증가와 같은 많은 문제점들이 발생한다. 한편, 기존의 부유 게이트 타입의 메모리를 대신할 것으로 기대되는 전하 포획형 메모리는 쓰기/지우기 속도를 향상시킬 수 있으며 소자의 축소화에도 셀간 간섭이 일어나지 않으므로 부유 게이트 플래시 메모리를 대체할 수 있는 기술로 주목받고 있다. 특히, TBM (tunnel barrier engineered memory) 소자는 유전율이 큰 절연막을 적층하여 전계에 대한 터널 산화막의 민감도를 증가시키고, 적층된 물리적 두께의 증가에 의해 메모리의 데이터 유지 특성을 크게 개선시킬 수 있는 기술로 관심이 증가하고 있다. 본 연구에서는 Si3N4/Ta2O5를 적층시킨 staggered구조의 tunnel barrier를 제안하였고, Si기판 위에 tunnel layer로 Si3N4를 Low Pressure Chemical Vapor Deposition (LPCVD) 방법과 Ta2O5를 RF Sputtering 방법으로 각각 3/3 nm 증착한 후 e-beam evaporation을 이용하여 게이트 전극으로 Al을 150 nm 증착하여 MIS- capacitor구조의 메모리 소자를 제작하여 동작 특성을 평가하였다. 또한, Si3N4/Ta2O5 staggered tunnel barrier 형성 후의 후속 열처리에 따른 전기적 특성의 개선효과를 확인하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.177-177
• /
• 2011

Complementary metal-insulator-metal capacitor에서 $SiO_2$는 절연체로 널리 사용되고 있었으나, 반도체 소자의 고직접화로 인한 선폭의 감소로 터널링 효과에 의해 누설전류가 증가하여, 대체 물질에 대한 연구가 활발히 진행되고 있다. 그 중 $ZrO_2$는 고유전율, wide bandgap, 열안정성의 특징을 가지고 있어 대체 물질로 주목 받고 있다. $ZrO_2$ 박막 제작에는 sputter, atomic layer deposition 등의 진공증착을 이용한 방법과 용액을 이용한 sol-gel 법이 있다. 화학용액을 이용한 sol-gel 법은 소자의 패턴을 프린트 할 수 있는 장점과 상대적으로 값싼 공정으로 인해 최근 주목 받고 있지만, 진공증착법에 비해서 연구가 전무한 실정이다. 본 연구에서는 sol-gel 법에 의해 프린트된 $ZrO_2$ 박막의 광특성을 분광타원편광분석법으로 연구하였다. Si 기판위에 0.1 M의 $ZrO_2$ sol을 입힌 뒤에 $300{\sim}700^{\circ}C$의 온도에서 열처리 하였다. 분광타원 편광분석기로 1.12~6.52 eV 에너지 영역에서 측정하였고, $ZrO_2$ 박막의 광특성 분석을 위해서 Tauc-Lorentz 모델을 이용하였다. 그 결과 고온에서의 열처리로 인해 효율이 높아서 소자로 이용할 수 있는 tetragonal 구조를 가진 $ZrO_2$ 박막이 형성됨을 분석할 수 있었다. 본 연구는 sol-gel법으로 제작된 $ZrO_2$ 박막의 고직접, 고속 소자응용성과 비파괴적인 광특성 분석법을 제시하고 있다.

• Journal of Sensor Science and Technology
• /
• v.9 no.1
• /
• pp.83-89
• /
• 2000

BST thin films were deposited on the ITO coated glass for using TFELD insulating layer by rf magnetron sputtering method. $O_2/(Ar+O_2)$ mixing ratio was 10%, substrate temperature was changed from R.T. to $500^{\circ}C$, and working pressure was changed from 5 mTorr to 30 mTorr. BST thin films deposited with various conditions were investigated electrical, optical, structural properties, and stoichiometry. The result of investigation was achieved good fabrication condition that substrate temperature of $400^{\circ}C$, and working pressure of 30 mTorr. Relative dielectric constant of 254 at 1 kHz, leakage current density was below $3.3{\times}10^{-7\;}A/cm^2$ at 5\;MV/cm applied electric field, and transmittance was over 82% at visible range.

• Fire Science and Engineering
• /
• v.33 no.4
• /
• pp.105-111
• /
• 2019

In South Korea, smoke control systems are designed according to the fire safety standards NFSC501 and NFSC 501A. However, there is a problem in that the design values are incompatible when measuring the performance of the system after the design construction for calculating the leakage crack area described in the standards. Therefore, we compared the standards for smoke control systems from South Korea, Japan, and the United Kingdom. In South Korea, designs are conducted uniformly according to the NFSC 501A Manual, but in Japan and the United Kingdom, designs consider smoke temperature, duct loss, and fire floor air supply. Furthermore, they use larger values than in South Korea.

• The Transactions of the Korean Institute of Power Electronics
• /
• v.8 no.6
• /
• pp.504-511
• /
• 2003

In this paper, inverter type neon power supply using a piezoelectric transformer is fabricated and its characteristic is investigated. Developed neon power supply is composed of basic circuit and blocks, such as rectifier part, frequency oscillation part and piezoelectric transformer and resonant half bridge inverters. In this paper for complement the low power limitation, piezoelectric transformer at parallel connected driving by inverter is studied for noon tubes system of high power. When piezoelectric transformer is connected with parallel, LC filter connection method with parallel and selection of inductance L and capacitor C of primary side is suggested for reduce unbalanced current at the terminal of each transformer. Piezoelectric transformers use piezoelectric ceramic devices. Thus it is wireless therefore it has high power density, high Isolation level, low loss, more light, and miniaturization. In addition, high voltage transfer ratio is expected because there is no leakage inductance. Also, it has economic merit that the electrical loss Is low because structure is simple, small and tighter weight.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.22 no.9
• /
• pp.103-110
• /
• 2008

In terms of electrical safety, environmental impact assessment and revision of domestic regulation are needed for the electric facilities. In this paper, risk of electric facilities is assessed by the spot measures and analysis in dust generation area. Adhesion dust in a surface of insulated materials cause electrical accidents. In a mechanism of these accidents, when the dust lie on electric facilities, a leakage current is flowed and the surface of insulated material is carbonized. Hereafter, electrical fire is generated due to Joule's heat. As the results, dusts are found in protection devices or panel board and sampled dusts vary in sampled amounts and conductivity severally. For the most part, sodium is detected but zinc and calcium are detected in case of reclaimed rubber factory by the ICP-AES(Inductively Coupled Plasma-Atomic Emission Spectroscopy). In a sewerage, the ingredients such as sodium, magnesium, iron, calcium, aluminium, etc are detected uniformly. So that, results of the spot measures and analysis of dusts are become the important data for the assessment of electrical hazard in dust generation area.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.342-342
• /
• 2007

원자층 증착(Atomic Layer Deposition: ALD) 방법은 반응물질들을 펄스형태로 챔버에 공급하여 기판 표면에 반응물질의 표면 포화반응에 의한 화학적 흡착과 탈착을 이용한 박막증착기술이다. ALD법은 박막의 조성 정밀제어가 쉽고, 파티클 발생이 없으며, 대면적의 박막 증착시 균일성이 우수하고, 박막 두께의 정밀 조절이 용이한 장점이 있다. 원자층 증착 공정에서 짧은 시간 안에 소스를 충분히 공급하기 위한 방법으로는 소스 온도를 증가시켜 전구체의 증기압을 높여 반응기로의 유입량을 증가시키는 방법, 전구체의 공급시간을 늘리는 방법 등을 들 수 있다. 그러나 전구체 온도를 상승시키는 경우, 공정 조건의 변화가 요구되며 전구체의 변질에 의하여 형성된 막이 의도하는 막 특성을 만족시키지 못하게 되는 문제점이 발생될 우려가 있다. 그리고 전구체를 충분히 공급하기 위하여 전구체의 공급시간을 늘이는 방법을 사용하면, 원하는 두께의 막을 형성하기 위하여 소요되는 공정시간이 증가된다. 이를 해결하기 위해 수송가스를 이용한 버블러 형태의 전구체 공급 장치를 사용하지만 이 또한 전구체의 수명을 단축시키는 단점을 가지고 있다. 본 논문에서는 위의 문제점을 극복할 수 있는 새로운 개념의 수송가스 도움 전구체 공급 장치를 소개한다. 본 연구에서 사용된 수송가스 도움 전구체 공급 장치를 가지는 ALD 장비는 Lucida-D200 (NCD Technology사)이며 기판으로는 8인치 실리콘 웨이퍼를 사용하였으며 (TEMA)Zr을 사용하여 ZrO2 박막을 성장하였다. 수송가스 도움 전구체 공급 장치를 사용한 경우, 그렇지 않은 경우 보다 $30^{\circ}C$ 이상 전구체 온도를 낮출 수 있으며, 또한 증착 속도를 약 2배정도 증가시킬 수 있었다. 이들 박막들은 XRD, XPS, AFM 등을 이용하여 결정구조, 결합에너지, 표면 거칠기 등의 특성을 관찰하였다. 그리고 C-V, I-V 측정을 이용해 정전용량, 유전율, 누설전류 등의 전기적 특성을 평가하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.218-218
• /
• 2010

기존의 비휘발성 메모리 소자는 터널 절연막으로 $SiO_2$ 단일 절연막을 이용하였다. 그러나 소자의 축소화와 함께 비휘발성 메모리 소자의 동작 전압을 낮추기 위해서 $SiO_2$ 단일 절연막의 두께도 감소 시켜야만 하였다. 하지만 $SiO_2$ 단일 절연막의 두께 감소에 따라, 메모리의 동작 횟수와 데이터 보존 시간의 감소등의 문제점들로 인해 기술적인 한계점에 이르렀다. 이러한 문제점들을 해결하기 위한 연구가 활발히 진행되고 있는 가운데, 최근 high-k 물질을 기반으로 하는 Tunnel Barrier Engineered (TEB) 기술이 주목 받고 있다. TBE 기술이란, 터널 절연막을 위해 서로 다른 유전율을 갖는 유전체를 적층함으로써 쓰기/지우기 속도의 향상과 함께, 물리적인 두께 증가로 인한 데이터 보존 시간을 향상 시킬 수 있는 기술이다. 따라서, 본 연구에서는 적층된 터널 절연막에 이용되는 $HfO_2$를 FGA (Forming Gas Annealing)와 RTA (Rapid Thermal Annealing) 공정에 의한 열처리 효과를 알아보기 위해, 온도에 따른 전기적인 특성을 MIS-Capacitor 제작을 통하여 분석하였다. 이를 위해 먼저 Si 기판 위에 $SiO_2$를 약 3 nm 성장시킨 후, $HfO_2$를 Atomic Layer Deposition (ALD) 방법으로 약 8 nm를 증착 하였고, Aluminum을 약 150 nm 증착 하여 게이트 전극으로 이용하였다. 이를 C-V와 I-V 특성을 이용하여 분석함으로 써, 열처리 공정을 통한 $HfO_2$의 터널 절연막 특성이 향상됨을 확인 하였다. 특히, $450^{\circ}C$ $H_2/N_2$(98%/2%) 분위기에서 진행한 FGA 공정은 $HfO_2$의 전하 트랩핑 현상을 줄일 뿐 만 아니라, 낮은 전계에서는 낮은 누설 전류를, 높은 전계에서는 높은 터널링 전류가 흐르는 것을 확인 하였다. 이와 같은 전압에 대한 터널링 전류의 민감도의 향상은 비휘발성 메모리 소자의 쓰기/지우기 특성을 개선할 수 있음을 의미한다. 반면 $N_2$ 분위기에서 실시한 RTA 공정에서는, 전하 트랩핑 현상은 감소 하였지만 FGA 공정 후 보다는 전하 트랩핑 현상이 더 크게 나타났다. 따라서, 적층된 터널 절연막은 적절한 열처리 공정을 통하여 비휘발성 메모리 소자의 성능을 향상 시킬 수 있음이 기대된다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.423-423
• /
• 2010

유기발광소자의 제작 기술이 빠르게 발전함에 따라 디스플레이와 조명 분야에서 많은 응용 가능성을 보여주고 있다. 유기발광소자의 발광효율은 발광층내에서 전자와 정공의 비와 밀접한 관계가 있기 때문에 전자 수송층과 정공 수송층내에서 전하의 이동도를 제어하는 구조에 대한 연구는 매우 중요하다. 본 연구에서는 전자 수송층으로 tris(8-hydroxyquinoline)aluminum ($Alq_3$)와 4,7-diphenyl-1,10-phenanthroline (BPhen)의 다중 이종구조를 사용하여 제작된 녹색 유기발광소자의 전기적 성질과 광학적 성질을 연구하였다. $Alq_3$와 BPhen 다중 이종구조의 위치와 이종구조 개수의 변화에 따라 전자의 변하는 전송특성으로 인하여 변화되는 발광특성을 체계적으로 조사하였다. 유기발광소자의 구동전압은 $Alq_3$/BPhen 이종구조의 수가 증가할수록 증가하는 경향을 보인다. $Alq_3$와 BPhen 내에서 전자의 이동도가 다르기 때문에 $Alq_3$/BPhen 이종계면에 전자가 축적되어 공간전하를 형성하므로 계면에서 내부전계가 형성되어 구동전압이 약간 증가하는 경향을 보인다. 또한 $Alq_3$/BPhen 이종계면에서 축적된 전자들로 인하여 형성된 내부 전계로 인해 저전압에서 누설 정공의 수가 증가하였다. 그러나 다중 이종구조로 된 전자 수송층을 포함한 유기발광소자의 발광 효율은 구동전압이 증가할수록 안정화 되었다. 이는 이종계면의 수가 증가함에 따라 각각의 이종계면에서 축적되는 전자의 양이 감소하기 때문에 고전압에서 효율감소율이 작아졌다. $Alq_3$/BPhen 다중 이종구조를 가진 전자 수송층내에서 전자의 전송 메카니즘에 대한 이해는 유기발광소자의 발광효율이 안정화된 구조를 설계하는데 중요한 실험적 결과를 제공한다.