• Magazine of the Korea Concrete Institute
• /
• v.6 no.2
• /
• pp.129-137
• /
• 1994

This study was performed for the purpose of obtaining the fundamental data to establish the criterion of concrete deterioration and presuming steel corrosion of concrete structures under the environment of seawater. Steel embedded concrete specimens were exposed in seawater for 1year. The soluble chloride content in concrete, corrosion potential and steel corrosion were considered. The results show that soluble chloride content in concrete was decreased with lower water-cement ratio and with mineral admixtures. Half-cell potential is reduced with steel corrosion. Corrosion area ratio is correlative with half-cell potential.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.6
• /
• pp.201-211
• /
• 2011

Many reinforced concrete structures have been constructed at the offshore in Korea and those are exposed in environments for long period. Due to that, the reinforcement of the structure faces possibility of corrosion by the salt damage. Such corrosions are effects on the bond performance between concrete and reinforcing bar as well as the performance of the structure. In this study, the performance of RC structure has been investigated when the reinforcing bars are totally bonded and unbonded in the structure. Through the experimental tests and finite element analyses of beam-column joint with bond and unbonded reinforcing bar, the energy dissipation capacity, strength, and crack distribution are compared and discussed.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2012.10a
• /
• pp.285-287
• /
• 2012

염해는 철근 콘크리트 구조물의 주요 열화원인으로서 특히 수해양 부유식 건축물의 상부구조는 비래염분에 의한 피해에 노출되어 있고, 해수에 접하고 있는 함체는 다공질 콘크리트의 모세관으로 염수이온이 침투하므로 상당히 높은 수위의 열화 환경에 노출되어 있다고 분류할 수 있다. 본 연구는 해양에서 유입되는 비래염분량을 정량화하여 철근 콘크리트 구조물 뿐만아니라 강재 건자재의 장수명화를 꾀하는 기초자료를 구축하고자 하였다. 1년간에 걸쳐 측정된 비래염분유입 지역은 기존연구에서 조사된 1km 범위을 상당히 초과하고 있으며 그 량도 강재 발청농도를 탁월하게 상회하는 것으로 분석되었다.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1999.10a
• /
• pp.372.2-372
• /
• 1999

• Journal of the Korea Concrete Institute
• /
• v.13 no.3
• /
• pp.195-205
• /
• 2001

This Paper describes a numerical method to evaluate the flexural strength of reinforced concrete members exposed to fire. An analytical method is developed for the moment-curvature relationship for the cross section which is subjected to high temperature. The method performs heat-transfer analysis for the cross sections and subsequently performs numerical analysis using the stress-strain relationships of concrete and reinforcing steel in various heat conditions. The results of the numerical studies are ; 1) the residual flexural strength exposing at high temperature is affected by the heating time, the depth of concrete cover and reinforcement ratio, 2) the residual flexural strength after exposed at high temperature is recovered of its original strength at minimum ratio of reinforcement, while members having half of maximum ratio and maximum ratio of reinforcement do not recover its original strength, 3) furthermore, the concrete may reach its maximum capacity before reinforcement yields in reinforced concrete members having maximum ratio of reinforcement.

• Journal of the Korea Concrete Institute
• /
• v.19 no.3
• /
• pp.283-292
• /
• 2007

A research projects is currently being conducted to develop a nonlinear finite element analysis methods for predicting the structural behavior of reinforced concrete frame structures, exposed to fire. As part of this, reinforced concrete frames subjected to fire loads were analyzed using the nonlinear finite-element program DIANA. Two numerical steps are incorporated in this program. The first step carries out the nonlinear transient heat flow analysis associated with fire and the second step predicts the structural behavior of reinforced concrete frames subjected to the thermal histories predicted by first step. The complex features of structural behavior in fire conditions, such as thermal expansion, plasticity, cracking or crushing, and material properties changing with temperature are considered. A concrete material model based on nonlinear fracture mechanics to take cracking into account and plasticity models for concrete in compression and reinforcement steel were used. The material and analytical models developed in this paper are verified against the experimental data on simple reinforced concrete beams. The changes in thermal parameters are discussed from the point of view of changes of structure and chemical composition due to the high temperature exposure. Although, this study considers codes standard fire for reinforced concrete frame, any other time-temperature relationship can be easily incorporated.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.22 no.4
• /
• pp.10-18
• /
• 2018

The primary purposes of this study are to understand a fundamental aspect of current uniformity around a reinforcing bar (rebar) in cement mortar, and to develop an accurate monitoring method in a wet-dry cycling process with the alternative current (AC) impedance method. Three cement mortar specimens with two embedded rebars were prepared in the laboratory. As a main variable, the distance between two rebars was designed to be 10, 20 and 30 mm with the same thickness of 20 mm. To simulate the corrosion of rebars in concrete structures in a marine environment, three cement mortar specimens were exposed to 15 wet-drying cycles (24-hour-immersion in seawater and 48-hour-drying in a room temperature) in the laboratory. It was observed that the potential level shifted to a noble value during corrosion potential monitoring, which is attributed to acceleration of dissolved oxygen diffusion at the drying process. AC impedance was measured in a frequency range from 100 kHz to 1 mHz on a wet-drying process. A theoretical model was proposed to explain the interface condition between the rebars and cement mortar by using the equivalent circuit consisting of a solution resistance, a charge transfer resistance and a CPE (constant phase element). It was observed that the diffusion impedance appeared in a low frequency range as corrosion of rebars progresses. At the drying stage of the wet-drying cycles, the currents line for monitoring tended to be non-uniform at the interface of rebar/mortar, being phase shift, ${\theta}$, close to $-45^{\circ}$.

• Journal of the Korea Concrete Institute
• /
• v.15 no.6
• /
• pp.811-819
• /
• 2003

The corrosion of steel reinforcing bar(re-bar) has been the major cause of the reinforced concrete deterioration. FRP(Fiber-reinforced polymer) reinforcing bar has emerged as one of the most promising and affordable solutions to the corrosion problems of steel reinforcement in structural concrete. However, FRP re-bar is pone to deteriorate due to other degradation mechanisms than those for steel. The high alkalinity of concrete, for instance, is a possible degradation source. Other potentially FRP re-bar aggressive environments are sea water, acid solution and fresh water/moisture. In this study long-term durability performance of FRP re-bar were evaluated. The mechanical and durability properties of two type of CFRP-, GFRP re-bar and one type of AFRP re-bar were investigated; the FRP re-bars were subjected to alkaline solution acid solution, salt solution and deionized water. The mechanical and durability properties were investigated by performing tensile, compressive and short beam tests. Experimental results confirmed the desirable resistance of FRP re-bar to aggressive chemical environment.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.549-552
• /
• 2008

Corrosion of reinforcing steel is prohibited under normal condition by the alkalinity of the pore water in the concrete. But the probability of steel corrosion becomes higher when the chloride ions are introduced into the concrete. Steel corrosion is decisive factor for the determination of service life of the marine concrete structures because chloride ions are abundant in the sea. In this paper, chloride penetration analysis for the rectangular pier in the marine environment is performed considering the diffusion movement of chlorides. Result reveals that the chloride concentration in the corner bar is higher than that of in the side bar with rectangular pier. Also the time to the specified accumulation of chloride in the corner bar is much shorter than that in the side bar. Because the corrosion initiation time of corner bar is half as much as that of side bar, service life for the rectangular pier in marine environment should be determined with respect to the coner bar.

• Magazine of the Korea Concrete Institute
• /
• v.8 no.5
• /
• pp.201-209
• /
• 1996

Recently, large scale concrete structures exposed to severe environment are increasingly built in various locations. The corrosion may severely affect the durability and service life of such a concrete structure. It is, therefore, necessary to develop durable concrete to enhance the corrosion resistance. The corrosion resistance of concrete can be identified through accelerated corrosion test. The purpose of the present paper is, therefore, to devise a reasonable and accurate method to predict the amount of corrosion of reinforcing steels. The proposed method which is basically based on the concept of Faraday's Law, determines the corroded amount of a rebar according to accelerated corrosion time. The corrosion is accelerated by employing the potentiometric corrosion test arrangement. The effects of admixtures in concrete including fly ash and silica fume have been also studied to explore the relative corrosion resistance of concrete.