• Resources Recycling
• /
• v.23 no.3
• /
• pp.13-20
• /
• 2014

Nowadays, due to the development of industrial and civil engineering technology, enlargement and diversification of concrete structures are being tried. At the same time, the hydration heat generated during the construction of large structures lead to thermal crack, which is occurs causing a problem that durability degradation. In this paper, in order to study the durability and reducing hydration heat of concrete according to the types of cement, that is ordinary portland cement, fly ash cement mixed with a two-component, ternary blend cement mixed with fly ash and blast furnace slag and low heat cement concrete are produced, and compare and analyze the results using property, durability and hydration characteristics, ternary blend cement is appeared to be the most excellent in durability and reduction of hydration heat, and it was determined suitable for construction of mass concrete and requiring durability.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.545-548
• /
• 2008

As the corrosion of reinforcing bar in concrete structures exposed to chloride attack is one of main factors to determine the remaining service life, marine concrete structures have to be designed to protect the chloride penetration. Among the durability design methods such as deterministic method and probabilistic method, design method based on the probabilistic theory has been widely studied. However, the most essential material, data of the material properties related to chloride diffusion, are still insufficient. In this paper, the probabilistic distribution of chloride diffusion coefficients and aging coefficients are derived by the experiment and analysis for the chloride coefficients of concrete containing pozzolans, which are generally used in marine structures.

• Journal of the Korea Institute of Building Construction
• /
• v.5 no.1 s.15
• /
• pp.81-88
• /
• 2005

As a part of efforts for conformity of demand to high quality of concrete and for solution of economic problem, blast-furnace slag has been utilized by means of cement replacement. With utilization of blast-furnace slag, superior performance can be ensured, environmental pollution can be prevented and economical advantage can be obtained. But blast-furnace slag has a lot of disadvantages like retardation of strength manifestation etc. in field construction, so properties examination of concrete using blast-furnace slag instead of cement is necessary. For upper necessity, it is planed that basic data for utilization and performance management of blast-furnace slag by means of cement replacement is presented with experimental comparison and investigation of engineering properties of concrete according to the replacement ratio and fineness of blast-furnace slag.

• Journal of the Korea Concrete Institute
• /
• v.20 no.6
• /
• pp.773-784
• /
• 2008

Even if the exploitation of copper slag produced during the smelting process of copper as aggregate for construction purpose has been permitted since 2004 in Korea, the lack of sufficient data enabling to evaluate its long-term stability that is its durability has to date impeded its application. This study intends to investigate experimentally the durability characteristics of 18 and 27 MPa-class commercial concretes in which natural sand (fine aggregates) has been partially replaced by copper slag through accelerated and exposure tests so as to provide bases promoting the application of copper slag concrete. The experimental results revealed insignificant difference of the durability characteristics in most of the mix proportions in which 30% of natural sand was replaced by copper slag. In the case where crushed sand was adopted, tests verified similar characteristics for replacement ratio of 50%. Particularly, the results of the exposure test conducted during 8 years demonstrated that equivalent level of durability was secured compared to the case using natural sand. In the case of 18MPa-class lower grade concrete, exposure test verified also that the physical lifetime similar to 50 years could be secured until carbonation reaches cover depth of 20 mm.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.466-473
• /
• 2017

RC (Reinforced Concrete) member has varying service life due to varying diffusion characteristics with loading conditions even if it is exposed to constant exterior conditions. In the paper, quantitative parameters are obtained through adopting the previous results for effects of compressive, tensile, and cold joint on chloride diffusion in OPC (Ordinary Portland Cement) and GGBFS (Ground Granulated Blast Furnace Slag) concrete. Service life is evaluated in RC simple beam with 10.0m of span through increasing loading from self weight (2.5kN/m) to the loading to cracking moment (5.5kN/m). In OPC concrete without cold joint, service life changes to 89.4% for tensile region and 101% for compressive region with loadings while GGBFS concrete has 80.0% and 106%, respectively. For cold joint area, GGBFS concrete shows much reduced service life to 82~80% in compressive region and 69~61% in tensile region, which is caused by the lower diffusion in normal condition but relatively higher increasing cold joint effect than OPC concrete.

• Proceedings of the Korean Geotechical Society Conference
• /
• 2002.11b
• /
• pp.18-30
• /
• 2002

이암 및 셰일은 점토를 함유하고 있어 풍화작용을 받을 경우 공학적 성질이 급격히 변화하여 강도 저하, 내구성저하현상 및 토사와 유사한 거동을 보이는 등 토목공사에 위험한 요소가 되고 있다. 풍화된 시료엔 대한 실험용 시료 가공이 어렵고 적용 가능한 실험법이 적어 공학적 특성이나 거동을 정량적으로 파악하는 기법이 다른 암종에 비해 극히 제한된다. 현재까지 강도측정과 같은 일반적인 물성의 단순측정보다는 내구성을 분석하는 슬레이킹 내구성 시험 (Slake durability test), Modified Jar test, 팽창율 측정시험 (Swelling test) 등의 정량화 시험법이 주로 사용되고 있으며 국내 현장에서도 적용을 권장할 수 있다. 이러한 실험치의 해석에서 단일 실험치 (예: 팽창율)만으로 지질공학적 특성을 파악하는 경우 잘못된 판단을 할 수도 있으므로, X선 회절분석시험 (XRD: X-Ray Diffraction Test), TG-DTA분석, 주사전자현미경 (SEM: Scanning Electron Microscope) 이미지 분석, 투수계수 측정실험 등도 함께 수행하여 실험결과를 종합적으로 해석하는 것이 바람직하다.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.285-286
• /
• 2009

In this study, chloride ions permeability test of regulated set cement concrete using ground granulated blast-furnace slag was carried out. The purpose of the present study is to develop pavement materials with high performance with respect to resisance to chloride penetration.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.443-444
• /
• 2009

This study investigated the development of high durability concrete under an oceanic region through the examination and comparison of the fundamental property and diffusion of chloride ion to apply a high durability admixture on the mortar.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2013.10a
• /
• pp.261-263
• /
• 2013

해양환경에서의 아연코팅철근 콘크리트 보의 휨 성능 및 균열 특성 실험을 수행하였다. 또한, 보에서 발생하는 균열 및 파괴양상을 파악하였다. 그 결과, 해양환경에서의 콘크리트 부재의 피복두께를 기존 설계기준보다 작게 적용시켜도 부재에 발생하는 염해에 대한 내구성을 확보할 수 있으며, 아연코팅 철근의 적용은 일반철근 콘크리트 보다 내구성 측면에서 유리하다고 판단된다.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.10 no.1
• /
• pp.15-22
• /
• 2010

Chloride-induced corrosion of steel bars in concrete exposed to marine environments has become one of the major causes of deterioration in many important facilities made of reinforced concrete. A study on chloride penetration in concrete has developed through long period exposure test along seawater, assesment of chloride ion diffusion by electrochemical techniques and so on. However, reasonable and exclusive chloride penetration model considering concrete material properties with mixture, degree of hydration, binding capacity has not been established. Therefore, in this paper, chloride penetration analysis of non-steady state is accomplished with material properties of concrete. Comparing with the results of analysis and chloride ponding test, we could accept the effect of binding capacity on chloride penetration in concrete and these results could be applied to a service life prediction of R.C. structures submerged in seawater. Therefore, there are 20~40% differences of service life to SHRP prediction.