• 한국재료학회지
• /
• 제14권10호
• /
• pp.731-736
• /
• 2004

Herein, we report on the co-firing of a low-K wiring substrate and a middle-K functional substrate in LTCC. Firstly, we researched the sintering behavior and dielectric properties of the low-k wiring substrate comprised by alumina and glass frit with ${\varepsilon}_r$, of $\sim7$ and the middle-k functional substrate comprised by $Ba_{5}Nb_{4}O_{15}$ and glass frit with ${\varepsilon}_r$, of $20\sim30$. The warpage and delamination between the hetero layers of the low-K and the middle-K composition were also studied. In particular, physical matching of the hetero layers could be possible by adjusting of the sintering properties of the composition. We observed that an introduction of the glass frit to the low- and middle-K substrate gives rise to a minimization of an effect given by separation of the hetero layers, and modification of the fraction of the glass frit accompanied by a variation of the composition could control the sintering behavior and its beginning temperature. In the case of co-firing of the L03 as the low-K wiring substrate composition and the M03 as the middle-K functional substrate composition at $875^{\circ}C$, we could fabricate a desirable structure of hetero layers without any kinds of structural defects such as separation, warpage, delamination, pore trap, etc. We suppose that the co-firing techniques described in this study would provide a helpful method to fabricate a LTCC multi-functional for the next generation.

• 한국세라믹학회지
• /
• 제39권6호
• /
• pp.598-603
• /
• 2002

(M $g_{0.93}$C $a_{0.07}$)Ti $O_3$마이크로파 유전체 세라믹스에 alumine borosilicate계 유리를 5~30wt% 첨가하여 저온소결 특성과 마이크로파 유전 특성을 조사하였다. (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$에 alumine borosilicate계 유리를 첨가함으로서 소결온도를 135$0^{\circ}C$에서 95$0^{\circ}C$로 낮추었으며, 유리의 첨가량이 증가함에 따라 소결밀도의 증가 및 입성장이 뚜렷이 나타났고 20~30wt%의 유리가 첨가된 영역에서는 95%의 상대밀도를 갖는 소결체를 얻을 수 있었다. (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$에 20wt%의 alumino boiosilicate계 유리를 첨가함으로서 95$0^{\circ}C$에서 유전율($\varepsilon$$_{r}$)은 15~16, 품질계수(Q$\times$f)는 8000이었으며, 이때 공진주파수의 온도 계수($ au$$_{cf}$ )는 -45 ppm/$^{\circ}C$을 나타내었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.611-614
• /
• 2004

[ $Ba(Zn_{1/3}Nb_{2/3})O_3$ ] (BZN) 세라믹스의 소결 온도는 약 $1350^{\circ}C$ 이다. 그러나 $B_2O_3$가 첨가된 경우, BZN 세라믹스는 $900^{\circ}C$에서 소결되었다. $BaB_4O_7$, $BaB_2O_4$ 그리고 $BaNb_2O_6$ 이차상이 $B_2O_3$가 첨가된 BZN 세라믹스에서 관찰되었다. $BaB_4O_7$과 $BaB_2O_4$ 이차상은 약 $900^{\circ}C$에서 공정 온도를 가지기 때문에 $B_2O_3$를 첨가한 BZN 세라믹스론 $900^{\circ}C$에서 소결하는 동안 액상으로 존재할 것으로 여겨지며, 그것이 BZN 세라믹스의 소결온도를 낮출 것으로 생각된다. 소결 온도의 증가에 따라 유전 상수 ($\varepsilon_r$)와 품질 계수 ($Q{\times}f$)의 값은 증가하였는데, 이는 밀도의 증가에 기인한다. 그러나 $B_2O_3$의 첨가량이 많은 경우 Q 값은 감소하는데, 이는 이차상의 존재가 품질계수의 저하를 초래한다고 생각된다. 2.0 mol% $B_2O_3$가 첨가된 BZN 세라믹스를 $950^{\circ}C$에서 2시간 동안 소결하는 경우, $Q{\times}f$=13.600 GHz, $\varepsilon_r$=37.6 그리고 공진 주파수 온도계수 ($\tau_f$) = 19 ppm/$^{\circ}C$의 유전특성을 얻을 수 있었다.

• 한국세라믹학회지
• /
• 제40권2호
• /
• pp.172-177
• /
• 2003

저온동시소성 기능성 기판용 소재로 활용하기 위하여 Ba $Ti_4$ $O_{9}$계 마이크로파 유전체에 저융점의 유리 프리트를 첨가하여 저온소성 거동 및 마이크로파 유전특성을 고찰하였다. 유리 프리트의 첨가량이 증가할수록 소결 하한 온도가 낮아졌으며, l0wt%의 유리 프리트를 첨가하였을 때 875$^{\circ}C$의 소성온도에서 상대밀도 98% 이상을 나타내는 충분한 소결이 이루어졌다. 이 때 소결체의 마이크로파 유전특성은 유전율 32, 품질계수 9000 GHz, 공진주파수 온도계수 10 ppm/$^{\circ}C$으로 평가되었다. 유리의 첨가량이 증가하면서 소결 과정에서 주상인 Ba $Ti_4$ $O_{9}$가 Ba $Ti_{5}$ $O_{11}$상과 $Ba_4$ $Ti_{13}$ $O_{30}$상으로의 변화하는 현상도 관찰되었다.

• 한국전기전자재료학회논문지
• /
• 제25권7호
• /
• pp.511-515
• /
• 2012

A road energy harvester was designed and fabricated to convert mechanical energy from the vehicle load to electrical energy. The road energy harvester is composed of 24 piezoelectric cantilevers and a vehicle load transfer mechanism. Applying a vehicle load transfer mechanism rather than directly installing energy harvesters under roads decreases the area of road construction and allows more energy harvesters to be installed on the side of the road. The power generation amount with respect to the vehicular velocity change was assessed by installing the vehicle load transfer mechanism and the energy harvester in the form of speed bumps and underground. The energy harvester installed in a speed bump form generated power of 7.61 mW at the vehicular velocity of 20 km/h. Also, power generation of the energy harvester installed in the underground form was 63.9 mW at the vehicular velocity of 28 km/h. Although the number of piezoelectric cantilevers was reduced by 1/3 to 24 in comparison to the previous research results with 72 piezoelectric cantilevers, similar power generation characteristic value was obtained within the vehicular velocity of 20 km/h by altering the vehicle load transfer mechanism and cantilever vibration method.

• 한국결정성장학회지
• /
• 제29권6호
• /
• pp.345-351
• /
• 2019

디지털 잉크젯 프린팅 기술은 고해상도, 빠른 인쇄 속도, 높은 잉크 효율과 같은 장점과 함께 다양한 소재 적용이 용이하여 반도체, 디스플레이, 세라믹 타일 등의 산업 분야에서 주목을 받고 있다. 최근에는 전통적인 잉크 소재에서 벗어나 우수한 내열성, 내광성, 내화학성 등을 보이는 기능성 소재도 잉크젯 프린팅 공정에 적용하려는 시도가 활발히 진행되고 있다. 특히 2차원 인쇄뿐만 아니라 3차원 적층인쇄에 관한 연구도 시작되고 있으며 이를 위해서는 토출되는 잉크의 유변학적 물성과 프린트되는 기판과의 상호작용를 제어하는 것이 필수적이다. 본 연구에서는 나노 실리카 입자가 포함된 광경화성 세라믹 잉크를 합성하고 잉크의 물성과 프린팅 기판의 표면특성을 제어하였다. 나노 실리카 입자가 포함된 광경화성 세라믹 잉크의 퍼짐현상을 억제하고 기판과의 접촉각 특성을 개선함으로써 결과적으로 프린팅 해상도 및 적층성을 향상시켰으며 잉크젯 프린팅을 이용한 광경화 나노 실리카 잉크의 3D 프린팅에 대한 가능성을 확인하였다.

• 한국결정성장학회지
• /
• 제29권6호
• /
• pp.352-358
• /
• 2019

최근 인쇄용지는 단순히 정보 전달의 기능을 넘어서 미적, 예술적 가치가 부가면서 고품질의 인쇄가 가능한 도공지(coated paper)에 대한 시장의 수요가 증가하고 있다. 특히 실사급 고품질의 인쇄가 가능한 잉크젯 프린팅의 도공지는 잉크의 인쇄적성을 향상시키기 위하여 표면에 젖음성(wettability)과 다공성 구조(porous structure)를 갖는 도공층의 역할이 매우 중요하다. 본 연구에서는 나노 실리카 졸 입자에 실란 커플링제로 표면처리하고 수용성 결합제인 폴리비닐알콜(PVA)와 혼합하여 도공액(coating color)를 제조하고 원지(base paper)에 코팅하여 도공층을 제조하였다. 실란 커플링제로 표면처리한 나노 실리카 도공층은 표면처리하지 않은 도공층과 비교하여 균일한 기공 분포 및 평탄한 표면 거칠기를 가지며, 판매용 고급 인화지와 유사한 광택도를 갖는 것을 확인하였다. 특히 잉크의 망점(dot)에 대한 진원도로 평가하는 인쇄적성 평가 결과 실란 커플링제로 표면처리한 도공지는 다층 구조의 도공층을 갖는 판매용 고급 인화지보다 더 우수한 결과를 얻을 수 있었다. 이러한 결과는 실란 커플링제 표면처리를 통하여 나노 실리카 입자의 분산성이 향상되어 우수한 젖음성과 균일한 기공 분포를 갖는 도공층 형성이 가능하였기 때문으로 확인되었다.

• 한국세라믹학회지
• /
• 제42권2호
• /
• pp.81-87
• /
• 2005

[ $BaTiO_3$ ]계 유전체 모재료에 대하여 $Al_{2}O_{3}$와 CaO 조성이 소량 포함된 lithium-borosilicate계 유리 프릿을 $5\~15wt\%$ 적용함으로써 LTCC용 내장 캐패시터로 적용 가능한 조성을 개발하였다. 이를 위하여 먼저, 화학적으로 안정하고 저온소성효과가 탁월한 유리 프릿 조성물을 설계하고 이를 유전체 모재료에 적용하여 저온소성특성 및 유전특성을 평가하였다. $BaTiO_3$ 세라믹스를 모재료로 하는 경우 유리 프릿을 5wt$\%$ 첨가하였을 때 $925^{\circ}C$에서 $95\%$ 정도의 상대밀도 값을 나타내었으며, 이 경우 유전율 990, 유전손실 $3.1\%$의 유전특성을 나타내었다. $(Ba,Ca)(Ti,Zr)O_3$ 세라믹스를 모재료로 하여 유리프릿을 10 wt$\%$ 첨가한 경우는 $875^{\circ}C$의 소결온도에서 상대밀도가 $95\%$ 이상이며 기공율 $0.5\%$ 이하인 소결특성을 나타내었고, 700 이상의 유전율 및 $2\%$ 내외의 유전손실 값을 가지는 것으로 측정되었다.

• 한국세라믹학회지
• /
• 제38권2호
• /
• pp.117-121
• /
• 2001

본 연구에서는 Zr $O_2$첨가가 Ba(Zn$_{1}$3/Ta$_{2}$3/) $O_3$(BZT)세라믹의 구조와 고주파 유전특성에 미치는 영향을 조사하였다. 모든 시료에서 $Ba_{5}$Ta$_4$ $O_{15}$ 이차상이 발견되었으며 Zr $O_2$의 첨가량이 증가하면 $Ba_{5}$Ta$_4$ $O_{15}$ 상의 양은 감소하였다. 반면에 Zr $O_2$의 첨가량이 1.5 mol% 이상인 시료에서는 $Ba_{0.5}$Ta $O_3$상이 발견되었다. BZT의 입자 크기는 약 1$mu extrm{m}$ 정도였지만, Zr $O_2$를 첨가하면 입자 크기가 증가하였다. SEM 및 TEM 분석에 의하여 Zr $O_2$가 첨가되면 액상이 존재하는 것을 알 수 있었으며, 이로 인하여 입자가 성장되는 것이 발견되었다. 시편의 밀도는 소량의 Zr $O_2$를 첨가하면 증가하지만 Zr $O_2$첨가량이 증가하면 감소하였다. 유전율은 모든 시료가 27에서 30 사이의 값을 가지고 있었다. 공진주파수 온도계수는 소량의 Zr $O_2$을 첨가하였을 때는 변화하지 않았지만 첨가량이 2.5 mol% 이상에서는 증가하였다. Q$\times$f 값은 Zr $O_2$을 첨가하면 증가하였고, 입자 성장이 완료되는 조성에서 최대 값을 보였다. 본 연구에서는 Zr $O_2$를 2.0 mol% 첨가하고 15$50^{\circ}C$에서 10시간 소결한 시료에서 최대의 Q$\times$f 값(164,000)을 얻을 수 있었다.다.다.

• The Korean Journal of Ecology
• /
• 제23권1호
• /
• pp.65-70
• /
• 2000

본 조사는 매미나방 개체군의 전이단계에 따른 질적 그리고 수량적 특성을 구명하기 위하여, 1987∼1997까지 중부지방 및 제주도에서 발생 했던 일부 개체군을 대상으로 유충밀도, 난괴 밀도, 산란량, 식물피해 정도 등을 조사 분석하였으며, 합성 페로몬인（＋）disparlure와 우유 용기형 트랩(USDA-Milk carton trap)을 설치하여 수컷의 우화 패턴, 포획량과 난괴 밀도와의 상관관계를 조사하였다. 유충의 밀도는 난괴의 밀도와 식물 피해정도 등과 일치하여 매미나방의 유충의 분산이 주로 산란 지역 내에서 이루어지는 것으로 나타났다, 한국에서 매미나방 발생으로 인한 피해기간은 비교적 짧았으며 개체군 증가 이후 무해기까지의 경과기간은 2∼3년으로 나타났다. 산란량은 개체군 단계별 특성을 보였는데 폭발 단계를 경험한 개체군은 평균 산란수가 336.3 ± 161로 폭발 단계를 거치지 않은 개체군의 산란 수(537∼601) 보다 상당히 낮았다. 최근 개체군 전이단계를 경험한 개체군에서는 산란량의 변이 폭이 큰 것으로 나타났고 특히 여러 해 동안 개체군의 변화로 인한 피해가 없었던 남산에서의 매미나방 산란량은 537±24 로 난괴간의 변이가 작은 것으로 조사되었다. 페로몬 트랩에 의한 포획성적(우화 최성기의 평균 포획 수컷 수/일)은 대부분의 지역에서 다음 세대의 난괴 밀도와 양의 상관관계를 보였다 (r²=0.93).