• Applied Chemistry for Engineering
• /
• v.22 no.6
• /
• pp.623-626
• /
• 2011

Various poly(amic acid)s were synthesized from PMDA/BPDA/p-PDA/ODA with different mole ratios and effectively converted into 4-component polyimide films by thermal imidization. The chemical structures and thermo-mechanical properties of polyimide films were examined using Fourier transform infrared spectroscopy (FT-IR), thermo-gravimetric analyzer (TGA), thermo-mechanical analyzer (TMA), dynamic mechanical analyzer (DMA) and universal tensile machine (UTM). The tensile strength, modulus, and thermal properties of polyimides films increased with the amount of rigid PMDA and p-PDA, while the elongation and moisture absorption of polyimide films increased with the amount of flexible BPDA and ODA. One of 4-component polyimide films exhibited a similar coefficient of thermal expansion (CTE) value to that of copper when it was composed of PMDA : BPDA : p-PDA : ODA with the ratio of 5 : 5 : 4 : 6. Thus, this polyimide film could be useful for a base film for flexible copper clad laminates (FCCL) of flexible printed circuit boards.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.2
• /
• pp.59-64
• /
• 2022

Effects of film stack structure and peeling rate on the peel strength of screen-printed (SP) Ag/polyimide (PI) systems were investigated by a 90° peel test. When PI film was peeled at PI/SP-Ag and PI/SP-Ag/electroplated (EP) Cu structures, the peel strength was nearly constant regardless of the peeling rate. When EP Cu was peeled at EP Cu/SP-Ag/PI structure, the peel strength continuously increased as peeling rate increased. Considering uniaxial tensile test results of EP Cu/SP-Ag film with respect to loading rate, the increase of 90° plastic bending energy and peel strength was attributed to increased flow stress and toughness. On the other hand, viscoelastic PI film showed little variation of flow stress and toughness with respect to loading rate, which was assumed to result in nearly constant 90° plastic bending energy and peel strength.

• Journal of the Microelectronics and Packaging Society
• /
• v.30 no.3
• /
• pp.40-50
• /
• 2023

Recently, the number of components of smartphones increases rapidly, while the PCB size continuously decreases. Therefore, 3D technology with a stacked PCB has been developed to improve component density in smartphone. For the s tacked PCB, it i s very important to obtain solder bonding quality between PCBs. We investigated the effects of the properties, thickness, and number of layers of interposer PCB and sub PCB on warpage of PCB through experimental and numerical analysis to improve the reliability of the stacked PCB. The warpage of the interposer PCB decreased as the thermal expansion coefficient (CTE) of the prepreg decreased, and decreased as the glass transition temperature (Tg) increased. However, if temperature is 240℃ or higher, the reduction of warpage is not large. As FR-5 was applied, the warpage decreased more compared to FR-4, and the higher the number and thickness of the prepreg, the lower the warpage. For sub PCB, the CTE was more important for warpage than Tg of the prepreg, and increase in prepreg thickness was more effective in reducing the warpage. The shear tests indicated that the dummy pad design increased bonding strength. The tumble tests indicated that crack occurrence rate was greatly reduced with the dummy pad.

• Journal of the Microelectronics and Packaging Society
• /
• v.31 no.2
• /
• pp.23-27
• /
• 2024

In this study, the time-dependent warpage behavior caused by the viscoelastic properties of prepreg in a printed circuit board (PCB) was analyzed by finite element method (FEM). The accurate viscoelastic properties of the prepreg were measured by stress relaxation test, which were then incorporated into constructed warpage analysis model. When the PCB was subjected to repeated thermal cycles, the warpage of the PCB was restored to its initial state when only the elastic properties of the prepreg were considered, but when the viscoelastic properties were also considered, the warpage was not restored and permanent warpage change occurred. The warpage analysis for three different types of prepreg was conducted to compare their mechanical reliability, and the results showed that materials with elastic properties dominating over viscoelastic properties experienced less warpage, resulting in better mechanical reliability.

• Clean Technology
• /
• v.17 no.4
• /
• pp.306-313
• /
• 2011

Flux or solder is used in soldering process for manufacturing electronic parts such as printed circuit boards (PCB). After soldering process, residual flux and solder paste on the parts should be removed since their residuals could cause performance degradation or failure of parts due to their corrosion and electric leakage. Ozone depletion substances such as 1,1,1- trichloroethane (TCE) and HCFC-141b have widely been using for removal of residual flux and solder paste after soldering process In manufacturing of electronic parts until now. In this study, non-aqueous cleaning agents without flash point were developed and applied to industrial field for replacement of cleaning agents with ozone depletion. In order to develop non-aqueous cleaning agents without ethers, esters, fluoride- type solvents. And their physical properties and cleaning abilities were evaluated, and they were applied to industrial fields for cleaning of flux and solder on the PCB. And vacuum distillation apparatus were operated to determine their operating conditions and recycling yields for recycling of used cleaning agents formulated in this study. As a result of physical properties measurement of our formulated cleaning agents, they were expected to have good wetting and penetrating power since their surface tensions were relatively low as 18.0~20.4 dyne/$cm^2$ and their wetting indices are relatively large. And some cleaning agents holding fluoride-type solvents as their components did not have any flash point and they seemed to be safe in their handling and storage. The cleaning experimental results showed that some cleaning agents were better in their cleaning of flux and solder paste than 1,1,1-TCE and HCFC-141b. And industrial application results of the formulated cleaning agents for cleaning PCB indicated that they can be applicable to industry due to their good cleaning capability in comparison with HCFC-141b. The recycling experiments of the used formulated cleaning agents through a vacuum distillation apparatus also showed that their 91.9~97.5% could be recycled with its proper operating conditions.

• Korean Journal of Optics and Photonics
• /
• v.18 no.5
• /
• pp.351-361
• /
• 2007

The samples composed of a GST thin film and the protective layers of $ZnS-SiO_2$ or $Al_2O_3$ coated on c-Si substrate were prepared by using the magnetron sputtering method. Samples of three different structures were prepared, that is, i) the GST single film on c-Si substrate, ii) the GST film sandwiched by the protective $ZnS-SiO_2$ layers on c-Si substrate, and iii) the GST film sandwiched by $Al_2O_3$ protective layers on c-Si substrate. The ellipsometric constants in the temperature range from room temperature to $700^{\circ}C$ were obtained by using the in-situ ellipsometer equipped with a conventional heating chamber. The measured ellipsometric constants show strong variations versus temperature. The variation of ellipsometric constants at the temperature region higher than $300^{\circ}C$ shows different behaviors as the ambient medium is changed from in air to in vacuum or the protective layers are changed from $ZnS-SiO_2$ to $Al_2O_3$. Since the long heating time of 1-2 hours is believed to be the origin of the high temperature variation of ellipsometric constants upon the heating environment and the protective layers, a PRAM (Phase-Change Random Access Memory) recorder is introduced to reduce the heating time drastically. By using the PRAM recorder, the GST samples are heated up to $700^{\circ}C$ decomposed preventing its partial evaporation or chemical reactions with adjacent protective layers. The surface image obtained by SEM and the surface micro-roughness verified by AFM also confirmed that samples prepared by the PRAM recorder have smoother surface than the samples prepared by using the conventional heater.