• Journal of the Korean Magnetics Society
• /
• v.1 no.1
• /
• pp.25-29
• /
• 1991

It has been found that the as-quenched ribbons of $Sm_{x}Fe_{100-x-y}Ti_{y}(3.8{\leq}x{\leq}11.5,\;3.8{\leq}y{\leq}19.2)$ are composed of metastable $TbCu_{7}-type$ structure, ${\alpha}-(Fe,\;Ti),\;Fe_{2}Ti$ and an unknown phase accompanying strong diffraction line at $d=2.14{\AA}$. The metastable $TbCu_{7}-type$ phase, which was formed by rapid quenching, did not transform fully to the stable phases after annealing at $850^{\circ}C$ for 45 minutes except the one existed in $SmFe_{11}Ti$ melt-spun ribbon. The $SmFe_{11}Ti$ melt-spun ribbon, annealed at $850^{\circ}C$ for 45 minutes in vacuum, was found to be composed of $ThMn_{12}$. $\alpha$-(Fe, Ti) and $Fe_{2}Ti$ phases. The formation of $\alpha$-(Fe, Ti) and $Fe_{2}Ti$ phases in this melt-spun ribbon was due to the evaporation of Sm atoms during the high temperature annealing. The atomic ratios for the surface and the inside of $SmFe_{11}Ti$ melt-spun ribbon annealed in vacuum were $SmFe_{25.8}Ti_{2.6}$ and $SmFe_{11.7}Ti_{1.0}$ respectively. It is thought to be that much of $\alpha$-(Fe, Ti) and $Fe_{2}Ti$ phases exist on the surface of ribbon.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1999.04a
• /
• pp.66-67
• /
• 1999

• Proceedings of the Korean Magnestics Society Conference
• /
• 1996.10a
• /
• pp.62-63
• /
• 1996

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1999.10a
• /
• pp.30-30
• /
• 1999

• Korean Journal of Materials Research
• /
• v.7 no.1
• /
• pp.50-56
• /
• 1997

급냉응고법을 이용하여 고용한도 이상으로 Mn량을 첨가할 때 Mn량에 따른 인장특성의 변화와 시효특성을 조사하였다. 원심분무법으로 AI-4.7%Zn-2.5%Mg-0.2%Zr합금에 Mn량을 각기 달리 첨가한 급냉응고 분말을 제조 하였다. 이 분말을 냉간압축, 진공 탈가스처리를 한 후 15:1로 압출하여 봉상 시편을 만들었다. 분말의 미세조직은 $\alpha$-AI수지상과 수지상간 편석부로 이루어져 있으며 Mn첨가에 따라 조직의 변화는 관찰되지 않았다. 빠른 냉각속도로 인하여 2.0%Mn을 첨가한 경우에도 초정 Mn상을 발견할 수 없었다. 압출재의 미세조직은 아결정립으로 이루어져 있으며 약간의 제2상들이 관찰되었다. 대부분의 Mn 분산상은 압출후 용체화처리 과정에서 형성되었으며 시효경화량은 Mn양에 관계없이 일정하였다. 46$0^{\circ}C$에서 1시간 용체화처리하고 12$0^{\circ}C$에서 24시간 시효처리한 경우 최대의 시효경도값을 나타내었다. 인장강도는 Mn첨가량에 따라 증가 하였는데 이것은 Mn분산상의 밀도증가에 의한 것으로 확인되었다. 2.0%Mn을 첨가한 합금의 시효후 인장강도는 590MPa, 연산율은 4%를 보였다.

• Korean Journal of Materials Research
• /
• v.4 no.6
• /
• pp.644-650
• /
• 1994

The submicron powders of high-purity silicon have been produced by Electrohydrodynamic Atomization. Field-emission scanning transmission electron microscopy(STEM) is used to determine the microstructure and solidification phase. .Then it is found that the droplets less than 60nm diameter are solidified as the amorphous phase. A useful and accessible characterization of atomic arrangements in amorphous solids can be given in terms of a radial distribution function. According to experimental determinations of the radial distribution function for amorphous silicon, its similarity to the crystalline structure at small radial distances indicates that the basic tetrahedral arrangement found in the diamond cubic structure of silicon must be maintained in the amorphous structure.

• Journal of Korea Foundry Society
• /
• v.11 no.5
• /
• pp.348-353
• /
• 1991

• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.415-418
• /
• 1998

• 기계와재료
• /
• v.6 no.2 s.20
• /
• pp.38-45
• /
• 1994

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1993.04a
• /
• pp.54-58
• /
• 1993

Cu, Si, Mg, Ca, Cd, Sn, Pb등이 첨가되는 Al계 bearing 합금은 베어링 특성이 우수하여 최근 자동차드의 엔진 부품용 베어링소재로 많이 사용되어지고 있다. 합금원소 Si는 합금의 경도를 향상시키며 Si-rich한 경한 입자를 생성시켜 소착저항력(antiseizure)을 향상시키며 또한 합금의 주조성도 향상시켜 내마모성이 요구되는 Al계 베어링 합금에 주합금원소로 첨가된다. 본 연구에서는 강제죠반법과 급냉응고법을 이용하여 Al-Pb-Gu계와 Al-Si-Gu-Pb계 베어링합금을 제조하였다. 베어링합금이 급냉응고법으로 제조되었기 때문에 합금의 기지에는 Cu가 과포된 상태로 존재하여 석출경화에 앞서 행하여지는 용체화처리와 같은 효과가 얻어졌다. 본 실험에서는 Cu가 과포화된 기지를 갖는 주조상태의 시료를 시효열처리하여 석출경화된 베어링합금을 얻어서 석출경화에 의한 기지강화가 베어링합금의 내마모성질에 어떠한 효과를 가져오는지 규명하였다.