Abstract
It has been found that the as-quenched ribbons of $Sm_{x}Fe_{100-x-y}Ti_{y}(3.8{\leq}x{\leq}11.5,\;3.8{\leq}y{\leq}19.2)$ are composed of metastable $TbCu_{7}-type$ structure, ${\alpha}-(Fe,\;Ti),\;Fe_{2}Ti$ and an unknown phase accompanying strong diffraction line at $d=2.14{\AA}$. The metastable $TbCu_{7}-type$ phase, which was formed by rapid quenching, did not transform fully to the stable phases after annealing at $850^{\circ}C$ for 45 minutes except the one existed in $SmFe_{11}Ti$ melt-spun ribbon. The $SmFe_{11}Ti$ melt-spun ribbon, annealed at $850^{\circ}C$ for 45 minutes in vacuum, was found to be composed of $ThMn_{12}$. $\alpha$-(Fe, Ti) and $Fe_{2}Ti$ phases. The formation of $\alpha$-(Fe, Ti) and $Fe_{2}Ti$ phases in this melt-spun ribbon was due to the evaporation of Sm atoms during the high temperature annealing. The atomic ratios for the surface and the inside of $SmFe_{11}Ti$ melt-spun ribbon annealed in vacuum were $SmFe_{25.8}Ti_{2.6}$ and $SmFe_{11.7}Ti_{1.0}$ respectively. It is thought to be that much of $\alpha$-(Fe, Ti) and $Fe_{2}Ti$ phases exist on the surface of ribbon.
단롤법 급냉응고장치를 이용하여 디스크 표면속도 40m/s로 Sm-Fe-Ti 리본시편을 제작하하고 이의 결정구조 및 자기특성을 조사하였다. 급낸응고상태에서 $Sm_{x}Fe_{100-x-y}Ti_{y}(3.8{\leq}x{\leq}11.5,\;3.8{\leq}y{\leq}19.2)$ 합금은 전 조성에 걸쳐 $TbCu_{7}-type$ 구조의 준안정상이 형성되고 조성에 따라 ${\alpha}-(Fe,\;Ti),\;Fe_{2}Ti$. 비정질 및 $d=2.14{\AA}$에 강한 회절선을 나타내는 미지의 상 등이 존재함을 알 수 있었다. 한편, 급냉응고에 의하여 생성된 이들 $TbCu_{7}-type$ 구조의 준안정상은 $850^{\circ}C$에서 45분간 열처리한 후에도 완전하게 안전상으로 변태되지 않았으나 $SmFe_{11}Ti$ 조성에서는 거의 완전한 변태가 이루어짐을 알 수 있었다. 최적조건($850^{\circ}C{\times}45분$)으로 열처리한 $SmFe_{11}Ti$ 급냉응고리본은 주상인 $ThMn_{12}$ 구조의 경자성상과 연자성상인 $\alpha$-(Fe, Ti) 및 반강자성 $Fe_{2}Ti$ 등으로 구성되어 있었으며, $\alpha$-(Fe, Ti) 및 $Fe_{2}Ti$의 생성은 열처리시 Sm 원자의 증발에 기인한 것으로 판명되었다. 최적조건으로 열처리한 $SmFe_{11}Ti$ 급냉응고리본의 표면 및 내부 조성에 대한 원자비율은 각각 $SmFe_{25.8}Ti_{2.6}$ 및 $SmFe_{11.7}Ti_{1.0}$이었으며, $\alpha$-(Fe, Ti) 및 $Fe_{2}Ti$의 대부분은 리본의 표면층에 존재하는 것으로 관찰되었다.