• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.858-868
• /
• 1995

Texture development and martensitic phase transformation, on rolling, are compared in two Hadfield's steels, one having low carbon content(0.65wt% C), the other high carbon content(1.35wt%). In spite of small difference in stacking fault energy(about 2 mJm$^{-2}$ ) between two Hadfield's steels, the differences in texture development are observed. In low carbon steel, the textures developed are similar to those of low stacking fault energy metals in low strain range. However, the abnormal textures such as {111} , {110} <001> are strongly developed at high strain, which are due to the disturbance of u martensite in the development of textures formed at the packets of shear bands or at the grain boundaries. In contrast to low carbon Hadfield's steel( LCHS), the texture development of high carbon Hadfield's steel(HCHS) is simitar to those of low stacking fault energy metals in the whole strain range. This may be due to the fact that the amount of deformation induced martensite was small, as observed by A.C. magnetic susceptibility and iron particle tests.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.47-47
• /
• 2009

용착금속의 미세조직은 크게 Acicular ferrite(AF), Ferrite with aligned second phase(FS), Primary ferrite(=Grain boundary Ferrite) 등으로 나눌 수 있다. 이 중 침상형 페라이트(AF)는 인성과 강도를 동시에 증가시킬 수 있으므로 이를 다량 확보하는 것이 용접산업의 관건이다. 본 연구에서는 침상형 페라이트 발생에 기여한다고 알려진 Ti 함량을 용착금속에서 단계적으로 조절하여 나타나는 미세조직과 특성변화를 관찰하였다. 모재는 HSB-600을 사용하였으며 용접재료는 ER100S-G급의 Ti가 함유되어 있는 것(A)과 미함유된 것(B)을 사용하였다. 모재 성분의 희석을 방지하기 위해 V-Groove 가공 후 Buttering 용접을 실시하였다. 중앙에 가공된 V-그루브에 이들 재료를 적절히 조합하고 용접(입열량 20kJ/cm)하여 Ti함유량을 총 4가지(0.002~0.025% Ti)로 제어하였다. 용접 후 각각의 시편에 대해 미세조직, 충격시험, O/N분석, 성분분석 등의 시험을 진행하였다. 미세조직 관찰결과 Ti함량이 증가할수록 AF는 증가하고 FS는 감소함을 확인할 수 있었으며 충격시험결과 Ti가 많이 함유된 시편일수록 더 낮은 연성취성 천이온도(DBTT)를 나타내었다. EDS와 SEM으로 관찰한 결과 Ti함량 증가에 따라 비금속개재물의 크기는 작아지고 밀도는 높아지는 것을 확인할 수 있었으며 개재물 내에서의 Ti함량도 더 많아지는 것을 확인 할 수 있었다.

• The Korean Journal of Malacology
• /
• v.31 no.2
• /
• pp.137-142
• /
• 2015

This study investigated concentration of trace metals, intersexuality and histopathology of digestive gland in Ruditapes philippinarum. Samples were collected from three areas of Gamak Bay in May, 2010. The concentration of trace metals showed that Al was highest, Zn was second high concentration and the lowest concentration was Cd. The intersexuality was 18.5% and female was higher than the male. Intersex type was observed one type. Destruction of digestive tubule epithelium was highest among other biomarkers in digestive gland. Distribution of basophilic cell was 5.8% and lipofuscin was 1.8%.

• Radiation Oncology Journal
• /
• v.21 no.1
• /
• pp.66-74
• /
• 2003

Purpose : The matrix metalloprotelnases (MMPs) are a family of enzymes whose main function is the degradation of the extracellular matrix. Several studies have revealed that MMPs and TIMPS are related to the wound heating process and in photoaging caused by ultraviolet Irradiation. However, the expressions of MMP and TIMP after irradiation have not, to the best of our knowledge, been studied. This study investigates the expressions of MMP-2 and TIMP-2 in rat Intestinal mucosa following irradiation. Materials and Methods : The entire abdomen of Sprague-Dawley rats was irradiated using a single dose method. The rats were sacrificed on day 1, 2, 3, 5, 7 and 14 following irradiation. Histopathological observations were made using hematoxilin & eosin staining. The expressions of MMP-2 and TIMP-2 were examined using immunohistochemistry, Irnrnunoblotting and ELISA. Results : Radiation induced damage associated with atrophic villi, and infiltration of inflammatory cell was observed from the first postirradiation day, and severe tissue damage was observed on the second and the third postirradiation days. An increase in mitosis and the number of regenerating crypts, as evidence of regeneration, were most noticeable on the fifth postirradiation day. From the immunohistochemlstry, the MMP-2 expression was observed from the first postirradiation day, but was most conspicuous on the third and the fifth postirradiation days. The TIMP-2 expression was most conspicuous on the fifth postirradiation day. From the irnrnunoblotting, the MMP-2 expression was strongly positive on the third postirradlatlon day, and that of TIMP-2 showed a strong positive response on the fifth postirradiation day. In ELISA tests, the expressions of MMP-2 and TIMP-2 were increased in the postirradiation groups compared to those of the normal controls, and showed a maximum increase on the fifth postirradiatlon day. These results were statistically significant. Conclusion : The expressions of MMP-2 and TIMP-2 were increased in the intestinal mucosa of the rats following irradiation, and these results correlated with the histopathological findings, such as tissue damage and regeneration. Therefore, this study suggests that MMP-2 and TIMP-2 play roles in the mechanisms of radiation-induced damage and regeneration of intestinal mucosa of rats.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.226-226
• /
• 2009

일반적으로 알루미늄이나 아연 등과 같은 이온화 경향이 큰 금속들은 그 자체의 활성적인 특성으로 인해 강재와 같은 이온화 경향이 낮은 금속재의 표면에 도금 또는 코팅함으로서 사용 환경 중 자체 내식성 보유와 더불어 손상 결함시 희생양극적인 역할 등의 잇점으로 많이 사용되고 있다. 본 연구에서는 DC 스퍼터링법에 의해 표면조직이 치밀한 여러 가지의 Zn-Mg 합금박막을 제작하였다. 이들 박막은 종래의 Zn도금에 비해 부식환경 중 장기간 갈바닉쌍을 형성하여 모재 금속에 대한 보호막 기능을 우수하게 하는 것으로 나타났다.

• Journal of Korea Foundry Society
• /
• v.6 no.2
• /
• pp.104-115
• /
• 1986

I A쪽과 II A쪽이 Al-Si 합금의 공정조직개량 처리에 효과적인 것은 잘 알려진 사실이나 Na(Sodium)과 Sr(Strontium)만 상업적으로 쓰여지고 있다. 그러나 휘발성과 산화하기 쉬운점때문에 Na 은 그 양을 정확하게 조절하기가 어렵고 특히 온도가 높은 경우 더욱 곤란하나 Sr 은 휘발성이나 산화성은 없으나 micro-또한 macro-porocity의 주 원인으로 보고 되고 있다. 희토류 금속 (예 : Cerium, Lanthanum,etc )도 개량처리 효과가 있다는 논문들(ref. 2, 3, 4, 5) 이 있고, 계속 연구되어 오고 있으나 그 세부사항과 효율성에 관해 정립된 바가 없다. 이런 연유로 Al-Si 합금의 생산을 위한 개량 처리제로서의 희토류 금속의 역할에 대해 구체적이고 세부적인 개량처리기구의 구명을 위해 이 연구가 이루어졌다. Al-Si 합금 356가 채택된 이유는 상업적 Al 주물의 생산을 감안해서 였다.

• Journal of Korea Foundry Society
• /
• v.11 no.6
• /
• pp.491-497
• /
• 1991

Vanadium은 비중이 6.09로써 비교적 무거운 금속에 속하나 Al을 30wt% 이내로 첨가하여 $Ni_3Al$ 및 TiAl와 유사한 비강도가 크며 내열성을 지니는 V-Al합금을 얻을 가능성을 지니고 있다. 본 연구에서는 V-Al합금에 Si, Y, Ti, B등 제3원소를 첨가함에 따르는 미세 응고조직의 거동과 기계적 성질을 조사하였다. 알곤 분위기에서 제조된 V-30%Al합금은 상온에서 고용체와 취성이 큰 금속간 화합물인 $VAl_3$등 2상으로 존재하므로 용체화 처리 과정이 요구되며 24시간 이상 장시간 열처리에 의하여 단일 고용상을 이룰 수 있었다. 규소의 첨가는 금속간 화합물의 형성과 아울러 합금의 경도를 크게 증가시키는 경향을 나타내며 B을 0.3%정도가지 첨가할 때 경도가 낮아지는 현상이 관찰되었다. �c칭된 V-30%Al 합금은 입계면을 따라 decohesive rupture 현상을 나타내며 입자간 파괴 현상도 일부 관찰되었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.2
• /
• pp.298-302
• /
• 2008

This study was carried out to evaluate brazing characteristics of the braze joint between superhard alloy particles and carbon steel. Two types of insert metals that made by mechanical alloying process were selected for this study. One is composed of Cu, Zn and Ag(MIM-1) and the other one is composed of Cu, Zn, Ag and Cd.(MIM-2) The chemical compositions of these insert metals were similar to AWS BAg-20 and BAg-2a system. And the commercial insert metals(CIM-1, CIM-2) were also evaluated for the comparative study. The characterization of the insert metals were conducted by wettability tests, shear tensile test and microstructural analyses. The results indicated that wettability tests displayed that MIM-1 and CIM-1 insert metals had the larger wetting angle than MIM-2 and CIM-2 and the wetting angle of the MIM-1 showed higher value than that of CIM-1. However these values are less than $25^{\circ}$ that is recommended for standard value for usual insert metals. The highest value of shear tensile tests was obtained from the brazed joint that made by MIN-1 and the value was $2.29{\times}10^2MPa$. This value is appeared to be higher or same as the commercial insert metals. The microstructures of the inserts metals were composed of Cu-rich proeutectic structure for matrix and Ag-rich eutectic structure. The braze joint between superhard alloy particles and carbon steel produced by the MIM-1(Ag-Cu-Zn) system showed sound joint showing stable microstructures. However there was also some porosities at the interface.

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.112-115
• /
• 2001

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.121-121
• /
• 2000

반도체 산업의 발달에 따라 소자의 보다 빠른 동작 속도와 큰 집적도를 갖은 ULSI 구조를 얻기 위해, 새로운 금속배선 재료가 요구되고 있다. 기존의 금속 배선인 Al 및 Al 합금은 비교적 낮은 비저항과 박막형성의 용이함으로 인하여 현재까지 금속배선 재료로 사용되고 있으나, 고집적화에 따라 RC Time Delay와 Electromigration의 문제점을 들어내었다. 이러한 문제를 해결할 새로운 배선 재료로 Al보다 낮은 비저항을 가지며, electromigration 저항성을 갖는 Cu 금속배선 재료가 활발히 연구되고 있다. 본 실험에서는 (100) Si 웨이퍼를 기판으로 사용하였으며, 각층은 SiO2/Si3N4/EP Cu/Seed Cu/ TaN/SiO2/Si wafer 상태로 증착하였다. 확산방지막으로 TaN을 사용하였고, seed Cu는 sputtering 으로 증착하였으며, seed Cu 만으로 된 박막과 seed Cu + electro plating Cu로 구성된 박막을 제작하였다. 제작 완료된 박막은 N2 분위기에서 20$0^{\circ}C$ 120 min, 45$0^{\circ}C$ 60min 동안 열처리하여 Cu 박막의 조직 변화를 TEM 및 여러 분석방법을 이용하여 분석하였다. Plan-view TEM결과, 45$0^{\circ}C$, 60min 열처리함에 따라 결정립 성장이 일어난 것을 확인 할 수 있었다. 그러나, 성장후에도 twin boundary, stacking fault, dislocation, small defect 등은 여전히 남아 있음이 관찰된다. 그림 1(a)는 as-deposit 상태이며, 그림 1(b)는 45$0^{\circ}C$, 60min 열처리한 plan-view TEM 사진이다.