• Journal of Conservation Science
• /
• v.26 no.1
• /
• pp.61-67
• /
• 2010

After selecting five types of adhesive epoxy resin for metallic cultural assets such as $Araldite^{(R)}$ rapid type, $Devcon^{(R)}$, $Araldite^{(R)}$ SV427+HV427, $CDK^{(R)}$520, $Araldite^{(R)}$ AW106+HV953 which had already been studied, this paper approached more closely the problem of yellowing and the signal of aging with time passing by connecting the problems with the safety of metallic cultural assets. The change of physical properties according to the change of state of epoxy adhesives was investigated through the change of flexural strength and the change of surface hardness by artificially providing the possible environmental change factors such as ultra-violet ray, and acid base, and how the epoxy chemically changes in its ingredients by the environment was analyzed through FT-IR. As a result of the experiment, for the most part of adhesives brought about the physical change of flexural strength, the change of surface hardness, and the chemical change of chemical ingredients as the product of alcohol, which were respectively different according to the time of ultraviolet irradiation, and acid base change. Under most of the conditions, SV427+HV427 and $CDK^{(R)}$520 were fairly stabilized under each condition of weatherability, but it seems that they should be refrained from being applied in case that the area to restore is thin and wide because the degree of flexural strength of themselves is low. Also, it is found that the preservation environment is very important not only for artifacts but also for the preservation of resins sused for preservation treatment.

• Journal of Conservation Science
• /
• v.17 s.17
• /
• pp.57-64
• /
• 2005

In the course of examining the micro structure of Iron chisel and Iron arrowhead, a relics of the 16th or 17th of Chosun Dynasty unearthed at near Gangsun-tower, Chengpyeong temple. Collected un-eroded samples from the relics were looked into the metallic structure through optical metallography. Non-metallic inclusions were-analysed by SEM and EDS. The micro structure examination and SEM-SDS analysis revealed that Iron chisel and Iron arrowhead had been produced from the sponge iron close to pure iron made by low temperature reducing in a solid and then the surface carbon content was increased by carburizing treatment. It was also found that Iron chisel had been hardened through the repetitive processes of quench hardening and heat treatment, after increasing carbon content to a certain level. Up to now, there have been a number of studies in the domestic academia which were studied mainly on the structure of metallic relics in the period of the Three Kingdoms or before. Although this research was limited in type and number of the relics, it turned out to be interesting in that it revealed the 16th or 17th century way of processing iron, even in fragments. It is thought to be fruitful that iron had been made even in the Chosun Dynasty from the sponge iron.

• Journal of Conservation Science
• /
• v.37 no.2
• /
• pp.144-153
• /
• 2021

Gwanghwadang-Wonsam was designated as National Folklore Cultural Heritage No. 52 in 1979, it is in good condition. However, a problem is the attached a phoenix insignia badge that did not exist when it was designated recently. As it became known as the only purple Wonsam artifact with "phoenix insignia", raising the need for its conservation. In this regard, scientific analysis was required to correct misinformation about designated cultural assets and restore the original designated state by analyzing the history of the Gwanghwadang-Wonsam, other relics of the phoenix insignia and its making design patterns. An X-ray fluorescence analysis was used to confirm that the Phoenix insignia's metal threads were titanium-plated silver. Phoenix insignia using titanium-plated gold thread was not identified in Gwanghwadang-Wonsam photographs in 1986, and the TiN-type membrane plating method was used in various industries in the 1990s, which can be estimated to be attached in the early and mid-1990s. Especially, the scientific analysis results from the X-ray fluorescence analysis in this study provide key evidence for conservation processing. This study demonstrates the importance of investigating relics and similar artifacts in the conservation process of inherited relics and as a precedent for restoration that corrects misinformation about designated cultural properties.

• Proceedings of the Korea Information Processing Society Conference
• /
• 2017.04a
• /
• pp.514-516
• /
• 2017

금속탐지 센서는 공항, 유물 탐지, 지뢰 탐지 등 여러 분야에서 유용하게 사용하고 있다. 하지만 기존의 금속 탐지기의 경우 탐지되어진 물체를 구분할 수 없어 사람이 직접 그 물체가 어떤 것인지 확인을 해야 한다. 만약 이 과정을 컴퓨터를 통해 처리할 수 있다면 물체가 무엇인지 확인하는 검사시간을 줄일 수 있으며, 인적자원의 낭비를 줄일 수 있다. 이 연구에서는 AMR 자기 스위치 센서를 이용하여 금속을 탐지하고, 데이터를 분석하여 탐지된 물체의 철의 함유량을 파악, 어떠한 물체인지 유추하는 것을 목표로 하였다. 이를 위해 금속 함유량이 다른 여러 물체의 데이터, 센서를 지나가는 속도에 다른 데이터, 센서와의 거리에 다른 데이터등을 측정하였고, 이를 통해 철의 함량을 구하기 위한 요소를 파악하였다.

• Journal of Conservation Science
• /
• v.26 no.2
• /
• pp.149-156
• /
• 2010

One of resins, V-Flon is useful as a coating material because YK-D80, which is a solvent for V-Flon, is not highly volatile. However, it can not completely harden and can flow out when metal artifacts are joined and restored in the process of the treatment. Therefore, after the impregnation process in order to accelerate the hardening speed of a coating material, usually a dry oven was adopted. This study focused on finding the problems on the dry oven which is employed to increase the speed and investigating the most effective solvent and its composition by checking any change occurred depending on the concentration of solvents. Six different types of solvents were selected and samples were prepared in a manner that they were impregnated with solvents in three concentrations respectively (10%, 20%, 30%). To determine the condition of the samples, the stability evaluation was performed by measuring the change of color and the gloss, the thickness of coated layers, the corrosion after coating, the water resistance by contact angles. Through the comparative experiments between the natural drying and the artificial drying using a dry oven, it was found that when the dry oven is used, some problems are identified on the point of forming a uniform and stable layer because of the unstable data collected from the forced artificial dry. The experiments performed using 3 different concentration rates (10%, 20%, 30%) presented that in the case of 10% V-Flon in Xylene (using as a solvent), its layer was thin as well as it showed the high water-barrier property, which allows it to form the stably coated layer with the lower gloss and color change.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.11a
• /
• pp.60-60
• /
• 1994

• 보존과학연구
• /
• s.6
• /
• pp.48-57
• /
• 1985

This report described the corrosion structure of excavated iron artifacts in terms of simple model based on the knowledge of the corrosion process. (Fig.1)(Table 1,2)In storing the objects, there are basically three ways in which they either break in wedges, flakes and dish-shaped flakes. Completely mineralized objects or those with only a small iron core tend to break into wedges and more solid objects either split small dish-shaped flakes or large flat ones.(Fig. 2,3,4)There are two ways, therefore, to prevent this from happening. One is to keep the artifacts rigorously dried in Silica-gel, never allowing the relative humidity to rise. This is feasible which the artifacts are in store but causes great difficulty if they are wanted for museum display. Because they still contain $ FeCl _2$ they are always at risk ; they contain the seeds of their own destruction. The other alternative is to use of washing process to dissolve out the $ FeCl _2$. In this connection, many different methods to stabilize the artifact have been employed; boiling iron in frequent changes of water, soaking in Na-sesquicarbonate solution, soaking in alkaline Na-sulphite solution. In this report, introduced the alkaline sulphite method by the N.A. North and C.Pearson.Finally, Let me extend my thanks to Ancient Monument Lab., Museum of London Conservation Lab., British Museum Conservation Div. and National Maritime Museum Conservation Lab. who have helped me and made many valuable suggestions.

• Korean Journal of Heritage: History & Science
• /
• v.46 no.3
• /
• pp.4-15
• /
• 2013

The study of corrosion products generated by archaeological bronzes that have been buried for a long time can provide certain evidence that enables us to understand the natural corrosion process of bronze and helps us develop conservation and preservation methods. In the present study, the specimens taken from two bronze mirrors and three bronze swords were used to study the corrosion morphology and the related phenomena such as selective corrosion of ${\alpha}$ or ${\alpha}+{\delta}$ phases, decuprification, destannification, and secondary copper. Furthermore, corrosion development was discussed based on the ions distributed throughout the corrosion layers.

• Journal of Conservation Science
• /
• v.27 no.4
• /
• pp.345-356
• /
• 2011

To remove metal stains of the ceramics, chemical cleaning is essential case by case. This study investigated the removal characteristics of iron stains by oxalic acid and citric acid including their application methods of soaking and poultice. The soaking method in cleaning agents showed removal process by color difference and released iron contents from iron stains on ceramics. Iron stains were removed successfully from ceramics, which soaked in oxalic acid for 60 hours. However, it is recommendable to soak in 0.25M oxalic acid for one to three hours because most iron stains were disappeared in 3 hours soaking. Citric acid is less effective than oxalic acid in removing iron stains because of heavy molecular weight and low acidity. Poultices (bentonite, sepiolite, activated carbon fiber and celite) with oxalic acid were applied on contaminated ceramics. After ten hours, iron stains on ceramics were removed successfully by poultice. Among them, bentonite and sepiolite have better application. Therefore, sepiolite with 0.25M oxalic acid was applied on the iron stains of whiteware and celadon from Ma Island, and then stains were removed. However, it is judged that the application methods can be varied according to the form and depth of contaminant. In addition, the residues of poultice on the ceramics will be considered for preventing contamination.

• Conservation Science in Museum
• /
• v.21
• /
• pp.53-66
• /
• 2019

This study describes the processes undertaken for the conservation treatment of metal artifacts excavated in Hasong-ri, Yeongwol, Gangwon-do and the results of the related surface composition analysis. X-ray fluorescence analysis (XRF) was applied to analyze the surface composition of a small gilt-bronze wind chime, two clappers, and a small gourd-shaped bronze bottle. The gourd-shaped bronze bottle was investigated using radiography to examine its internal structure. The wind chime and clappers were excavated from the same location. A gilt layer was identified on the wind chime, but surface corrosion made it difficult to identify any such layers on the clappers. The element analysis revealed that the wind chime was made of bronze in a Cu-Sn-Pb ternary system and was gilt-plated using mercury amalgam. The clappers were made from copper with a small amount of gold detected, but did not show any evidence of mercury. Since a thick corrosion layer was affixed to the surface of each clapper, it was impossible to identify the surface composition and determine if the clappers had been gilded. It is possible that the gold detected from the clappers was a foreign substance or had detached from the giltbronze wind chime buried alongside them. The small gourd-shaped bronze bottle was investigated through surface element analysis and radiography to verify if it was a type of silver bottle used as currency during the Goryeo dynasty. The radiography photography identified that a small hole in the middle of the base had been stopped up. The general surface analysis did not detect silver, which suggests that the bottle was made of bronze instead and was not one of the silver bottles used as a means of currency.