• Journal of Conservation Science
• /
• v.30 no.2
• /
• pp.157-168
• /
• 2014

This study, by selecting 3 kinds(Polish T, H, C) of metal polish being frequently used for silver archival objects treatment at present, a polish having excellent conservative property that minimizes damage of silver surface while effectively removing its yellow discolored layer by each using tool was intended to be discovered by comparing performance of tarnish inhibitor, corrosion inhibitor contained in each polish. As a result of analysis, it was confirmed that specimen that was cleaned with cotton swab and lint-free wipe by using Polish C provides not only uniformed surface expression and minimum damage but also removal function of corrosion layer. In addition, even though tarnish inhibition film should be formed after polish treatment, discolored phenomenon is unable to be prevented but among those polishes, Polish C was represented to be most stable against UV and yellowing and it showed relatively better features than that of Polish H and T in terms of hydrophobic, dispersive property. Through this, it is confirmed that Polish C would show the most excellent performance among polishes being used for conserving silver archival objects.

• Journal of Conservation Science
• /
• v.27 no.4
• /
• pp.415-420
• /
• 2011

Urethane coating agent was made up in order to prevent corrosion on metal relics. This urethane coating agent was designed to solve problems linked to gloss and discoloration caused by existing acrylic coating agent which is mainly applied to metal relics. For the purpose, the urethane coating agent was made up which has lower gloss and slight color change. This coating agent formed thinner coating layer with excellent adhesion compared to the existing agent and has outstanding resistance to the surface oxidization of metal relics and water repellent on the surface. In addition, the agent is considered a stable coating agent replacing current acrylic coating agent with showing easy dissolution in organic solvents such as acetone, toluene and xylene with excellent result in reversible reaction.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.30-30
• /
• 2018

스마트 도금공장을 구축하기 위해서는 도금액 내부의 화학 물질 농도 변화를 측정할 수 있는 화학 센서 기술이 필수적으로 요구된다. 와트욕은 대표적인 고속 니켈 도금액 중 하나로 기본적으로 황산니켈, 염화니켈, 보릭산의 염과 함께 케리어(type-1 광택제), 광택제(type 2-광택제), 응력 제어제 등의 유기 첨가제로 구성되어 있다. 이러한 유기 첨가제는 전차된 니켈층의 두께 균일도, 조도, 미세 구조, 내부 응력 등 다양한 특성을 제어하며, 정밀한 농도 관리가 필수적으로 요구되나, 분석 기술의 부재로 인하여 지금까지도 대부분의 액관리는 할셀법이나 작업자의 경험에 의존하고 있다. Cyclic voltammetry stripping(CVS) 방법은 전기화학 분석 과정에서 나타나는 첨가제의 가속, 감속 특성 등과 여기에 수반되는 stripping peak의 변화를 이용하여 개별 첨가제의 농도를 측정하는 방법이며, 지금까지 인쇄회로기판의 비아필 공정, 전해 동박 제조, 반도체 배선 등 구리도금 산업 전반에 걸쳐 첨가제 관리에 효과적으로 적용되고 있다. 그러나 수소 발생으로 인한 stripping 효율 문제로 인하여 니켈, 주석, 아연 등 표준 환원 전위가 높은 금속 도금액 내부 첨가제 농도 측정은 아직 어려운 상황이다. 본 연구에서는 이 문제를 극복하기 위해 염소를 과량 첨가한 구리 도금액을 CVS 분석의 base 용액으로 이용하여 니켈 도금액 내부 여러 광택제 (polyetylene glycol(PEG) 계열, thiourea 계열, 2-butyne-1,4-diol 등) 농도를 측정하는 법을 제시하였다. 제시된 방법은 CVS 분석 과정에서 구리-염소 사이의 상호 작용으로 인해 생성되는 3가지 stripping peak의 상대적인 크기 변화가 첨가제 농도에 따라 영향을 받는다는 사실에 기반하였다. 본 연구에서는 여기에 관한 원인에 대해 고찰하였으며, 제시된 방법을 통해 광택제 계열 첨가제 농도 측정을 선택적으로 할 수 있다는 것을 증명하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.112-112
• /
• 2016

인체접촉시 니켈도금의 알러지 반응을 억제하기 위한 대체 도금기술인 비 시안계 Cu-Sn 합금도금을 개발함에 있어서, 황산구리5수화물과 황산제일주석을 금속염으로 하여 황산 및 계면활성제, 유화제 등을 포함한 각종 유기첨가제를 포함하였고 특히 은백색조의 외관 색상과 안정적인 Cu-Sn 합금전착을 위해 2종의 착화제인 EDTP($C_{14}H_{32}N_2O_4$)와 TEA(Triethanolamine)를 첨가한 비 시안계 Cu-Sn 합금 도금액을 도출하였다. Cu-Sn 합금도금 피막 조성의 균일화를 도모하기 위해서는 합금 도금액중의 Cu와 Sn 금속이온 농도를 일정하게 유지하는 것이 필요하다. 그러나 합금 도금액중 2가 주석이온($Sn^{2+}$)은 수용액중에서 4가 주석이온($Sn^{4+}$)으로 산화됨으로써 도금액 색상이 백탁이 되고 Stannic Hydroxide($Sn(OH)_4$, $SnO_2{\cdot}2H_2O$)이 생성되어 대량의 침전물이 침강하는 문제점이 발생되는 등 시간 경과에 따른 도금액의 경시 변화가 발생되었다. 상기 침전물은 연속여과에 의해 제거 가능하나 합금 도금액중 $Sn^{2+}$ 농도가 지속적으로 감소하게 된다. 이는 합금 도금액중 금속이온 비율이 변동함으로써 합금도금 피막의 조성비를 일정하게 유지하는 것이 곤란해진다. 이에 $Sn^{4+}$ 침전물 생성을 방지하기 위한 산화방지제를 개발하고 또한 산화방지제의 첨가에 따른 도금 피막 외관에 미치는 영향을 평가하여 외관 개선을 위한 광택제를 개발하고자 한다. 본 연구의 결과를 토대로 니켈도금과 동등 이상의 기능 특성을 갖는 비시안계 Cu-Sn 합금도금액을 개발하여 실용화하는 것을 목적으로 하였다.

• Journal of Conservation Science
• /
• v.33 no.2
• /
• pp.121-130
• /
• 2017

The currently used wax agents for preserving outdoor metal structures, despite their advantages, have disadvantages such as low endurance and reliability. These wax agents are easily damaged by acid rain, dust, moisture in the air, yellow dust, and air pollutants, resulting in corrosion within a short period after the initial conservation treatment. In addition, aged wax can also exhibit changes in the color or gloss, and also give a sense of difference in the surface. Given these existing problems, it is necessary to develop improved materials for metal preservation. Therefore, this study analyzed the characteristics and applications of the existing wax coating agents in order to identify their disadvantages and to develop a better material for metal preservation. In this regard, this study developed a perilla oil based compound wax and conducted experiments to test its endurance. The new compound wax agent was exposed to outdoor and acid rain conditions: it showed four times and 1.5 times the endurance of the existing wax agents in outdoor and acid rain conditions, respectively. In addition, the new agent seems to be more durable and protective as evidenced by the chromaticity, polish maintenance, and contact angle results. Further, although it is 1.3-1.8 times thicker than the existing agents, the new agent shows a more even surface. Based on these findings, it can be concluded that the new compound wax agent based on perilla oil is a better alternative to the existing was coating agents.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.68.2-68.2
• /
• 2017

인체접촉시 니켈도금의 알러지 반응을 억제하기 위한 대체 도금기술인 비 시안계 Cu-Sn 합금도금을 개발함에 있어서, 황산구리5수화물과 황산제일주석을 금속염으로 하여 황산 및 계면활성제, 유화제 등을 포함한 각종 유기첨가제를 포함하였고 특히 은백색조의 외관 색상과 안정적인 Cu-Sn 합금전착을 위해 2종의 착화제인 EDTP (Ethylenediaminetetrapropanol, $C_{14}H_{32}N_2O_4$)와 TEA (Triethanolamine)를 첨가한 비 시안계 Cu-Sn 합금 도금액을 도출하였다. Cu-Sn 합금도금 피막 조성의 균일화를 도모하기 위해서는 합금 도금액중의 Cu와 Sn 금속이온 농도를 일정하게 유지하는 것이 필요하다. 그러나 합금 도금액 중 2가 주석이온($Sn^{2+}$)은 수용액 중에서 4가 주석이온($Sn^{4+}$)으로 산화됨으로써 도금액 색상이 백탁이 되고 Stannic Hydroxide($Sn(OH)_4$, $SnO_2{\cdot}2H_2O$)이 생성되어 대량의 침전물이 침강하는 문제점이 발생되는 등시간 경과에 따른 도금액의 경시 변화가 발생되었다. 상기 침전물은 연속여과에 의해 제거 가능하나 합금 도금액 중 $Sn^{2+}$ 농도가 지속적으로 감소하게 된다. 이는 합금 도금액 중 금속이온 비율이 변동함으로써 합금도금 피막의 조성비를 일정하게 유지하는 것이 곤란해진다. 이에 $Sn^{4+}$ 침전물 생성을 방지하기 위한 산화방지제를 개발하고 또한 산화방지제의 첨가에 따른 도금 피막 외관에 미치는 영향을 평가하여 외관 개선을 위한 광택제를 개발하고자 한다. 본 연구의 결과를 토대로 니켈도금과 동등 이상의 기능 특성을 갖는 비 시안계 Cu-Sn 합금도금액을 개발하여 실용화하는 것을 목적으로 하였다.

• Journal of Conservation Science
• /
• v.26 no.2
• /
• pp.149-156
• /
• 2010

One of resins, V-Flon is useful as a coating material because YK-D80, which is a solvent for V-Flon, is not highly volatile. However, it can not completely harden and can flow out when metal artifacts are joined and restored in the process of the treatment. Therefore, after the impregnation process in order to accelerate the hardening speed of a coating material, usually a dry oven was adopted. This study focused on finding the problems on the dry oven which is employed to increase the speed and investigating the most effective solvent and its composition by checking any change occurred depending on the concentration of solvents. Six different types of solvents were selected and samples were prepared in a manner that they were impregnated with solvents in three concentrations respectively (10%, 20%, 30%). To determine the condition of the samples, the stability evaluation was performed by measuring the change of color and the gloss, the thickness of coated layers, the corrosion after coating, the water resistance by contact angles. Through the comparative experiments between the natural drying and the artificial drying using a dry oven, it was found that when the dry oven is used, some problems are identified on the point of forming a uniform and stable layer because of the unstable data collected from the forced artificial dry. The experiments performed using 3 different concentration rates (10%, 20%, 30%) presented that in the case of 10% V-Flon in Xylene (using as a solvent), its layer was thin as well as it showed the high water-barrier property, which allows it to form the stably coated layer with the lower gloss and color change.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.216-218
• /
• 2014

자동차용 고광택 크롬 도금 박리액에는 질산과 유가금속인 구리 및 니켈이 다량 함유되어 있는 것으로 알려져 있다. 질산($HNO_3$) 및 유가금속은 고가이며 유독하므로 경제적 및 친환경적으로 반드시 회수하여 재활용하여야 한다. 본 연구에서는 도금박리액으로부터 질산과 구리, 니켈을 용매 추출법을 이용하여 분리하였다. 수상에 존재하는 질산의 농도는 0.01 ~ 1N NaOH를 이용하여 적정하여 분석하고, 금속의 농도는 ICP-MS 및 ICP-AES 등을 이용하여 분석하였다. 도금 박리액을 분석한 결과 Cu(76850mg/L), Ni(51990 mg/L)이 함유되어 있음을 알 수 있었다. 용액 내 질산의 양을 NaOH 용액을 이용하여 적정법으로 측정하였을 때, 질산의 양은 대략 1.02 M 임을 알 수 있었다. 50 % Tributylphosphate (TBP)를 이용하여 3단 추출한 유기층의 용액을 증류수를 이용하여 3회의 역추출을 하였을 때, 원액으로부터 48.1 %의 질산을 회수할 수 있음을 알 수 있었으며, 순도는 99.5% 이상이었다. 질산 회수 후 용액 내에 남은 구리와 니켈은 ISE-106로 구리를 추출하여 니켈을 분리한 후 황산을 이용해 역추출 하였다. 회수된 구리는 NaOH를 이용하여 pH를 조절하고 수산화구리 형태로 침전시킨 후 $N_2H_4$를 이용하여 환원시켰고, 온도와 pH 및 환원제를 이용하여 다양한 조건 하에 구리 분말을 제조하였다. 구리를 추출하여 라피네이트 용액으로 분리된 니켈은 $NaBH_4$를 이용하여 환원시켰고, 다양한 조건 하에서 니켈 분말을 제조하였다. 환원 된 분말은 분석결과 99%의 순수한 분말임을 알 수 있었다.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.06a
• /
• pp.223-224
• /
• 2004

고준위폐기물 혹은 사용후 핵연료의 처분용기 재질은 각 국의 처분개념과 처분공의 주위 환경에 따라 달라질 수 있다. 용기의 후보재질로는 탄소강, 스텐레스 강, 구리, 니켈, 티탄 혹은 이들의 합금이 주로 고려되고 있으나, 국내에서는 아직 선정되지 않았다. 국내 처분환경에서 이들 재질의 부식특성을 조사하고자 모의 화강암 지하수를 가해 만든 겔 상태의 경주 벤토나이트에 탄소강, 스텐레스 강, 구리 시편을 넣고, $70^{\circ}C$, 아르곤 분위기에서 530일 경과한 후 시편의 표면 변화 (그림 1) 및 무게 감소를 측정하였다. 철 부식시편은 검정색의 철 화합물 층으로 덮여 있었으며, 구리표면에는 노란색의 부식층이 형성되었는데, 이를 XRD로 분석한 결과 $Cu_2O$로 판명되었다. 그러나 $700^{\circ}C$에서 각각 0, 24, 96시간동안 예민화시킨 스텐레스 강 시편들은 모두 초기상태 그대로 광택을 유지하고 있었으며, XRD에서 다른 화합물의 형성을 발견할 수 없었다 (그림 2). 시편의 무게 감소가 균일부식에 기인한 것으로 가정하여 환산한 결과, 구리와 스텐레스 강 모두 0.3~0.4 $\mu\textrm{m}/yr$의 부식속도를 나타내었다. 그러나 구리는 부식생성물이 표면에 부착되어 있기 때문에 실제 부식두께는 이 값보다 더 클 것으로 생각된다. 용기가 초기 530일간과 같은 속도로 처분용기의 부식이 진행된다면 한국에서 기준처분 개념으로 삼고 있는 50mm 두께의 내부식성 외벽 금속용기는 적어도 만년이상 견딜 수 있을 것으로 추정된다. 한편, 검정색 부식층을 제거한 무게감소로부터 계산한 철의 부식속도는 구리의 약 30배에 해당하였다. 금속 재질의 정확한 부식 거동을 파악하기 위해서는 보다 장기간의 실험이 요구된다. 시험법 선정에 각계(규제기관, 학계, 발전소 현장 및 산업계 등) 전문가로부터 기술자문회의를 통하여 자문 의견을 받기로 하였다. 특히 현재 폐기물 인수 기술기준치가 설정된 국가의 시험법을 심층 있게 검토하기로 하였다.검토하기로 하였다. 혹은 수성주변 환경이 지배하는 산악이나 구릉지에서 흔히 나타나는 침엽수-낙엽활엽수의 혼합림 식생상태를 잘 대변해 주고 있는 것으로 판단된다. 끝으로, 의림지 호저 퇴적층 중에서 인위적인 교란흔적이 없는 암회색 유기질 니층에 대한 탄소연대측정 결과, 제1호공 12번 시료에서 950$\pm$40 years B.P을 얻었으며, 제3-1호공에서도 아래로 내려가면서 8, 10, 11번 시료에 대하여 500$\pm$30 years B.P, 650$\pm$30 years B.P, 800$\pm$40 years B.P의 연대측정 결과를 획득하였다. 이상과 같은 의림지 호저 퇴적층의 형성환경과 형성시기 연구를 통하여 의림지의 제방축조의 최초시기를 해석해 보면, 의림지의 제방은 적어도 과거 약 827년 전에서 866년 전에는 이미 축조되어 있었음을 알 수 있다. 과거 제천 일대에 살았던 옛사람들이 의림지 하류의 곡지중앙과 고기 충적선상지에 대한 관계용 용수조달의 필요성에 부응하여 상류부 곡지하천의 자연입지 환경을 최대한 이용하여 축조한 것으로 판단된다..준비하였다.전류를 구성하는 주요 입자의 에너지 영역(75~l13keV)에서 가장 높은(0.80) 상관계수를 기록했다. 넷째, 회복기 중에 일어나는 입자들의 유입은 자기폭풍의 지속시간을 연장시키는 경향을 보이며 큰 자기폭풍일수록 현저했다. 주상에서 관측된 이러한 특성은 서브스톰 확장기 활동이 자기폭풍의 발달과 밀접한 관계가 있음을 시사한다.se that were all low

• Korean Journal of Heritage: History & Science
• /
• v.46 no.2
• /
• pp.4-25
• /
• 2013

Goli-su is the innovative special kind of the embroidery technique, which combines twining and interlacing skill with metal technology and makes the loops woven to each other with a strand. The loops floating on the space of the ground look like floating veins of sculpture and give people the feeling of the openwork. This kind of characteristic has some similarities with the lacework craft of Western Europe in texture and technique style, but it has its own features different from that of Western Europe. It mainly represents the splendid gloss with metallic materials in the Embroidered cloth, such as gold foil or wire. In the 10th century, early days of Goryo, we can see the basic Goli-su structure form of its initial period in the boy motif embroidery purse unearthed from the first level of Octagonal Nine-storied Pagoda of Woljeong-sa. In the Middle period of Joseon, there are several pieces of Goli-su embroidered relic called "Battle Flag of Goryo", which was taken by the Japanese in 1592 and is now in the Japanese temple. This piece is now converted into altar-table covers. In 18~19th century, two pairs of embroidered pillows in Joseon palace were kept intact, whose time and source are very accurate. The frame of the pillows was embroidered with Goli-su veins, and some gold foil papers were inserted into the inside. The triangle motif with silk was embroidered on the pillow. The stitch in the Needle-Looped embroidery is divided into three kinds according to comprehensive classification: 1. Goli-su ; 2. Goli-Kamgi-su ; 3. Goli-Saegim-su. From the 10th century newly establishing stage to the 13th century, Goli-su has appeared variational stitches and employed 2~3 dimensional color schemes gradually. According to the research of this thesis, we can still see this stitch in the embroidery pillow, which proves that Goli-suwas still kept in Korea in the 19th century. And in terms of the research achievement of this thesis, Archetype technology of Goli-su was restored. Han Sang-soo, Important Intangible Cultural Heritage No. 80 and Master of Embroidery already recreated the Korean relics of Goli-su in Joseon Dynasty. The Needle-Looped embriodery is the overall technological result of ancestral outstanding Metal craft, Twining and Interlacing craft, and Embroidery art. We should inherit, create, and seek the new direction in modern multi-dimensional and international industry societyon the basis of these research results. We can inherit the long history of embroidering, weaving, fiber processing, and expand the applications of other craft industries, and develop new advanced additional values of new dress material, fashion technology, ornament craft and artistic design. Thus, other crafts assist each other and broaden the expressive field to pursue more diversified formative beauty and beautify our life abundantly together.