• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.05a
• /
• pp.367-368
• /
• 2006

Today, the Artificial Intervertebral Disc (AID) is being developed by increasing the oblique of the endplate gradually. In other words, Ultra-high Molecular Weight Polyethylene (UHMWPE) which is apply to the sliding core of the AID, does not change the shape but alters the oblique of endplate. However, the unreasonable increase of degree of freedom (DOF) can result in the aggravation of the bone fusion and the initial stability and it can also lead to the increase of the concentrated force in core. For these reasons, it is necessary to develop the advanced techniques, which choose the most adequate DOF. In this study, the new optimized modeling of the sliding core and the endplate, the fatigue characteristics, the crack propagation and the formation mechanism of wearing debris was studied and the minimizing technique will be derived from this research.

• Journal of the Society of Naval Architects of Korea
• /
• v.34 no.3
• /
• pp.61-69
• /
• 1997

A simple and relatively new experimental method is proposed to estimate the plane stress fracture toughness by using compact tension (CT) specimen. The anti-buckling plates (fabricated to prevent the buckling caused by the 45 plastic yielding around crack tip under the plane stress condition) help to determine the relatively accurate plane stress fracture toughness of two stainless steels (SS304 and SS316). The fatigue crack propagation behavior of two stainless steels under two different loading conditions such as 10Hz and 5Hz frequency fatigue loadings was investigated by using image analysis technique (IAT) which renders several technical advantages over various conventional measuring methods. It was found that the IAT could be used to estimate fatigue crack lengths more effectively. Furthermore, it was suggested that we might control the measuring time interval for fatigue crack propagation by nearly automatically controlled technical process with the help of IAT.

• Journal of Ocean Engineering and Technology
• /
• v.2 no.2
• /
• pp.61-70
• /
• 1988

In order to consider the concept of the fitness for purpose'in fatigue design of offshore structure, fracture mechanics is applied to evaluate initial or weld defects. Generally, linear elastic fracture mechanics has been applied to tstimate initial fatigue crack propagation rate as well as long fatigue crack propagation rate. But, initial fatigue crack propagation rate in elasto-plastic notch field may not be characterized by application of stress intensity factor range .DELTA. K, because plastic effect due to stress concentration of notch may contribute to initial crack propagation. Therefore, to introduce the plastic effect into fatigue crack driving force, in this studty, the evaluating method of J-integral range .DELTA. J, was developed by willson was modified for application to notch field. In calculation of .DELTA. J obtained from the modified J-integral, stress gradient and crack closure behavior in the notch field were considered. The initial crack propagation rates in the notch fields of mild steels and high tensile strength steels were correlated to .DELTA. J. As the result, it was cleared that the present .DELTA. J is applicable to charachterize the fatigue crack propagation rates in both the elastic and elasto-plastic notch fields.

• Journal of the Korean Society for Precision Engineering
• /
• v.14 no.11
• /
• pp.69-76
• /
• 1997

The rotating bending fatigue tests were performed using the specimens taken from Cr-Mo-V steel, widely sued in thermal power plant turbines, at various temperatures such as room temperature, 300 .deg. C, 425 .deg. C and 550 .deg. C. The characteristics of fatigue crack propagation were examined and analyzed by using fracture mechanics parameter. The plastic replica method was also applied in order to measure the crack length on the basis of serial observation of fatigue crack propagation behavior on the defected specimen surface. The fatigue crack propagation behavior of Cr-Mo-V steel was investigated within the frame work of elastic-plastic fracture mechanics. The propagation law of fatigue crack is obtained uniquely by using the term .sigma. $^{n}$ sub a/where .sigma. $_{a}$ is the service stress, a is the crack length and n is a constant. The values of constant n are nearly equal to 2.48, 2.60 and 8.61 at room temperature, 300 .deg. C and 425 .deg. C.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.7
• /
• pp.1217-1226
• /
• 2003

The purpose of this paper is to investigate fatigue crack behavior under shear(Mode II) loading. Various specimens and devices have been used in order to produce Mode II loading in fatigue experiments for shear crack propagation. But, there is not sufficient comparisons of experimental results between Mode II and others loading modes, because of characteristics of applied loads and specimens. So, compact tension shear(CTS) specimens were used in this paper to investigate the propagation behavior of Mode II by comparing the experimental results between loading modes. We firstly observed the characteristics which was showed in Mode II experiment using CTS specimens. The experimental results under Mode II loading were compared with fatigue crack behavior under Mode I and Mixed-mode I＋II loading. The characteristics for initiation and propagation behavior under Mode II loading was investigated by such comparisons.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.5
• /
• pp.901-910
• /
• 1989

Corrosion fatigue crack propagation behavior of duplex stainless steel weldments in substitute ocean water was investigated to evalulate effects of micro-structural change and residual stresses. Fatigue crack propagation rate was found influenced markedly .alpha./.gamma. phase ratio but little by residual stresses. Fatigue crack propagation rate is higher in the corrosive environment than in room atmosphere. The crack propagation rate estimated by the measurement of striation spacing was higher than that, obtained by crack length measurement in low .DELTK.K region. At hight .DELTK.K region, however, both crack propagation rates were found to be identical.

• Journal of the Korean GEO-environmental Society
• /
• v.7 no.2
• /
• pp.43-53
• /
• 2006

Hydraulic fracturing is an important and abundant process in both industrial applications and natural environments. The formation of hydraulic fractures includes nucleation, growth, and termination in numerous rock types and stress regimes, at scales ranging from microns to many kilometers. As a result, fracture segmentation, commonly observed at all scales and in all geo-materials, contributes to this complexity in many ways. In particular, the mechanical interaction of fracture segments strongly affect almost all hydraulic fracturing processes. In this paper, the segmented fracture opening deformation in rock by hydraulic fracturing is quantified using boundary collocation method and is compared with non-interacting single fracture.

• Korean Journal of Materials Research
• /
• v.3 no.6
• /
• pp.575-584
• /
• 1993

The effects of atmosphere on the creep rupture properties of Ni-base superalloy Ren6 80 were investigated. Creep rupture tests were performed at $760^{\circ}C$, 657MPa and 982%, 157MPa under Ar gas atmospheres. Creep rupture mode and rupture properties (rupture life and elongation) were similar in two different atmospheres under the condition of $760^{\circ}C$, 657MPa. However, the results at $982^{\circ}C$, 157MPa showed different creep rupture mode and life between air and Ar gas atmospheres. In air, it was shown that creep cracks were initiated at surface-exposed grain boundaries and propagated along grain boundaries. In Ar gas atmosphere, the cracks were initiated at inner grain boundaries and coalesced to surface cracks which cause cup-and-cone type fracture. Due to protective oxide layer formation, air test showed longer rupture life than Ar test.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.56-56
• /
• 2009

AISI 316L 스테인리스강에 새롭게 디자인한 서로 다른 3가지 응고모드를 가진 와이어로 FCAW(Flux Cored Arc Welding)을 하였다. 각각의 3가지 와이어는 Pseudobinary phase diagram에 따라 AF, FA, F모드를 가졌다. 미세조직은 $Cr_{eq}/Ni_{eq}$이 증가할수록 델타 페라이트 함량이 증가하였으며, 초정 상의 경우 초정 오스테나이트에서 초정 페라이트로 변태하였고, 연성저하균열의 민감도가 감소하였다. 연성저하균열은 이동결정립계의 형상에 따라 좌우되며, 미량의 페라이트를 함유한 오스테나이트에서는 페라이트가 핀(Pin) 역할을 제대로 하지 못하여 직선형태의 이동 결정립계 따라 입계 미끄러짐의 메커니즘을 통해 전파되었으며, 곡선형태의 이동 결정립계에서는 델타 페라이트가 핀 역할을 하여 역할을 하여 구속 상태에서 응력집중을 막고 응력을 분산시켜 균열이 전파되는 것을 방해하여 균열이 발생되지 않았다.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.18 no.5
• /
• pp.29-34
• /
• 2014

Particulate reinforced composite is composed of hard particles and polymer matrix. This material has been widely applied for engineering industry such as automobile, construction and aerospace. For the safe application, it is important to assess crack resistance behavior. Especially in aerospace industry, crack could cause significant problem when the material is used for solid rocket fuel. Therefore, it is inevitable to estimate the characteristics of the crack propagation. In this study, crack propagation tests were conducted using particulate reinforced composite under crosshead rate 2.54 mm/min in the range of temperature $-60^{\circ}C$ to $60^{\circ}C$. The strain contour of surface for specimen was generated using digital image correlation method.