• Journal of Korean Society of Environmental Engineers
• /
• v.32 no.7
• /
• pp.649-655
• /
• 2010

This study investigated the degradation of phenol using sonication and/or UV-C. The effects of frequency, temperature, pH in solution, argon purging, with UV intensity were estimated in sonication-only, UV-only, and the combined reaction of sonication with UV. The optimum condition for degrading phenol in the sonication-only reaction was 35 kHz, $5^{\circ}C$, and pH 4. As this condition approximately 30% degradation of phenol was achieved within 360 min. However, phenol in the UV-only at $19.3\;mw/cm^2$ under the same condition was completely degraded within 60 min. In the combined system of sonication with UV, the degradation of phenol was well fitted to first-order rate model, and phenol was completely degraded within 360 min and 45 min at UV intensity of $7.6\;mW/cm^2$($17.3{\times}10^{-3}\;min^{-1}$) and $19.3\;mW/cm^2$($138.1{\times}10^{-3}\;min^{-1}$), respectively. Adding methanol, as a radical scavenger, in the phenol degradation in the sonication reaction indicates that OH radical is a major factor in the degradation of phenol. The order of degradation efficiencies of phenol was in the order of as follows; combined reaction of sonication with UV > UV-only > sonication-only.

• Korean Chemical Engineering Research
• /
• v.50 no.6
• /
• pp.952-959
• /
• 2012

The photocatalytic reactor was designed to have improved efficiency by enhancing a light intensity of photocatalytic reactor using a reflector coated on the surface at the outer radius of annular shaped photocatalytic reactor. The improved photocatalytic reactor performed to treat waste air containing malodor and VOC with the enhanced light intensity, of which the effect on their removal efficiency was investigated. The intensities of illumination of the improved photocatalytic reactor filled with porous silica-based media and nonporous glass bead media carrying photocatalyst were observed to increase by 28.5% and 30.1%, respectively, compared to those of photocatalytic reactor without any reflector. Using the improved photocatalytic reactor filled with porous silica-based media and nonporous glass bead media carrying photocatalyst, the removal efficiencies were enhanced by 2~3% and insignificantly, respectively. The removal efficiencies of the optimized photocatalytic reactor with reflectors, filled with porous silica-based media carrying photocatalyst, were observed to increase by 26% and 60%, compared to those of photocatalytic reactor (i.e., 19% and 53%), without any reflector, filled with nonporous glass bead media carrying photocatalyst, for hydrogen sulfide and toluene, respectively. The roughness of used reflector surface was measured to be ca. four times as big as that of a commercial mirror. However, their removal efficiencies are expected to be enhanced by increasing an light intensity resulting from lowering the roughness of used reflector coated on the improved photocatalytic reactor in the future.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.39 no.8
• /
• pp.1-11
• /
• 2002

A multi-section DFB-LD shows optical bistability subject to externally injected light signal, then it has potential applications such as wavelength conversion and optical logic gates. In this paper, we have studied the optical bistability in multi-section DFB-LD using split-step time-domain model. It is confirmed that the multi-section DFB-LD, which is excited inhomogeneously, shows bistability. The optical bistable characteristics are investigated when input light is injected into a absorptive region. Simulation results show that multi-section DFB-LD works as a flip-flop depending on the set-reset optical pulse which has a few ns in switching time and a few pj in switching energy, so that it can act as a optical logic device. Besides, if we change the carrier lifetime and the differential gain coefficient, it is expected that the response time of optical output signal can be reduced.

• KSBB Journal
• /
• v.15 no.3
• /
• pp.254-261
• /
• 2000

A bacterial leaching was conducted for pyrite with Thiobacillus ferrooxidans(ATcC 19859) and Thiobacillus KY isolated from acid mine water around Kwangyang area to characterize the surface of substrate as reaction progress at the optimum condition under 9K medium for 3- days. It was found that the surface crystallinity changes referred to hkl plane was observed for 20 days leached by T. ferrooxidans similar changes also observed for 10 days leached pyrite by Thiobacillus KY. Based on he results of SEM-EDS the atomic ratios of Fe, S and Si on the surface were changed to sulfur rich phase but exposed Si ratio decreased from 16.94% to 4.85% during 30days mainly due to reprecipitating of Fe and S as a mixed compound.

• Journal of Korean Society of Environmental Engineers
• /
• v.33 no.8
• /
• pp.591-597
• /
• 2011

The purpose of this study was to determine optimum conditions for the cultivation of Chlorella sp. FC-21 using light emitting diodes (LEDs). Specific growth rate and cell concentration were measured for the reactors at the illuminations of different wavelengths of LEDs. Among various types of LEDs, red LEDs were the most effective light source, and also greatest increases of specific growth rate and cell concentrations were obtained when light intensity of red LEDs increased. The specific growth rate decreased when initial cell concentration increased due to the shading effect of each cell in the reactor. To determine beneficial effect of aeration to cell cultivation, micro-air bubbles were aerated at 0.35 vvm in the reactor at the illumination of red LEDs. Two and ten times greater specific growth rate and cell concentration were obtained when aeration was applied. From this study, we found that red LEDs with aeration were the most appropriate light source for the cultivation of Chlorella sp. FC-21.

• Korean Journal of Materials Research
• /
• v.7 no.1
• /
• pp.21-26
• /
• 1997

고주파 마그네트론 반응성 스퍼터링(rf magnetron reactive sputtering)으로 티타늄산화물 박막을 제조하여 산소비율에 따른 반응성 스퍼터링의 증착기구를 조사하고 산소비율 및 기판온도에 따른 산화물 조성의 변화, 미세조직, 광학적 특성의 변화를 연구하였다. 기존의 진공기상증착법으로 증착만 박막에 비해, 금속타겟을 사용하여 높은 증착속도를 얻을 수 있는 반응성 마그네트론 스퍼터링으로 성막한 티타늄산화물 박막은 치밀도가 우수하여 높은 굴절률(2.06)과 높은 광투과율을 보였다. 상온에서 성막된 티타늄 산화물박막의 경우, 산소비율이 낮은 조건에서는 다결정형의조직을 보였으나 산소비율이 높은 경우에는 비정질조직을 나타냈으며, 기판온도가 30$0^{\circ}C$ 이상에서는 산소비율에 상관없이 다결정형의 조직을 나타냈다. 하지만 산소비율이 임계값이상에서는 박막의 조성, 증착속도 등이 거의 변하지 않는 안정된 증착조건을 보였다. 30% 이상의 산소비율의 반응성 스퍼터링의 조건에서는 TiO$_{2}$의 조성의 박막으로 성장하여 약 3.82-3.87 eV의 band gap을 나타냈으며 기판온도의 증가에 따라 비정질 TiO$_{2}$에서 다결정 TiO$_{2}$으로 조직의 변화를 보여 광투과도도 약간 증가하는 경향을 나타냈다.

• Elastomers and Composites
• /
• v.34 no.1
• /
• pp.3-10
• /
• 1999

Kinetics of solution photopolymerization of acrylonitrile(AN) with sensitizer, such as $NaSCN,\;KSCN,\;Ba(SCN)_2,\;NH_4SCN,\;ZnCl_2$ and $Na_2SeO_3$, were studied using UV crosslinker at various monomer concentrations($1.8{\sim}7.58mo1/1$), sensitizer concentrations($10{\sim}60%$), reaction temperature($10{\sim}70^{\circ}C$), energy intensities($1,000{\sim}9,900{\mu}J/cm^2$) at isothermal condition under nitrogen atmosphere. Under the irradiation of high pressure mercury lamp(${\lambda}=365nm$). High conversion and uniform molecular weight were obtained compare to thermal polymerization at reaction temperature of $50^{\circ}C$, reaction time of 3hr and 50% NaSCN without any initiator. Their kinetic model was as follows : $R_p=0.0142[M]^{0.82}[I]^{0.49}[S]^{0.52}$ exp(-1.33/RT).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.24-24
• /
• 2010

Chalcopyrite $Cu(In,Ga)Se_2$ (CIGS) 화합물 반도체는 고효율 박막태양전지의 광 흡수층으로 사용되는 물질 중 가장 우수한 효율 (19.9%, NREL 2008)을 보유하고 있다. CIGS는 직접천이형 에너지밴드갭 (direct bandgap)을 가지고 있고, 광흡수계수가 $1{\times}10^5\;cm^{-1}$로서 반도체 중 서 가장 흡수율이 높은 재료에 속하여 두께 $1{\sim}2\;{\mu}m$의 박막으로도 고효율의 태양전지 제조가 가능하고, 또한 장기적으로 전기광학적 안정성이 매우 우수한 특성을 지니고 있다. 현재 고효율 CIGS 셀생성을 위해 널리 사용되고 있는 CIGS 흡수층 성장공정은 "co-evaporation(동시증발법)"과 2-step 공정이라 불리는 "sputter-selenization(스퍼터-셀렌화)" 방법이다. 동시증발법은 개별원소 Cu, In, Ga, Se 들을 고진공 분위기에서 고온 ($550{\sim}600^{\circ}C$)기판위에 증착하는 방법으로 소면적에서 가장 좋은 효율(~20%)을 보이는 공정이다. 하지만, 고온, 고진공 공정조건과 대면적 증착시 온도 및 조성 불균일 등의 문제점 등으로 상용화에 어려움이 있다. 스퍼터-셀렌화 공정은 1단계에서 스퍼터링 방식으로 CuGaIn 전구체를 증착하고, 2단계에서 고온($550{\sim}600^{\circ}C$)하에 $H_2Se$ 혹은 Se vapor와 반응시켜 CIGS를 생성한다. 일본의 Showa Shell와 Honda Soltec 등에 의해 이미 상업화 되었듯이, 저비용 대면적으로 상업화 가능성이 높은 공정으로 평가되고 있다. 하지만, 2단계에서 사용되는 $H_2Se$ 및 Se vapor의 유독성, 기상 Se과 금속전구체 간의 느린 셀렌화 반응속도, 셀렌화반응 후 생성된 CIGS 박막 두께방향으로의 Ga 불균일분포, 생성된 CIGS/Mo 계면 접착력 저하등의 문제점들이 해결되어야만 상업화에 성공할 수 있을 것이다. 본 Tutorial에서는 CIGS 물질의 열역학 상평형과 반응메카니즘에 대해 설명하고, 다양한 생성 공정들을 소개할 것이다.

• Korean Journal of Weed Science
• /
• v.7 no.2
• /
• pp.130-138
• /
• 1987

The effects of light and storage conditions on the germination of Oenothera lamarckiana were investigated. Germination was induced by red light, but inhibited by green, blue or infrared. No germination occurred in the dark. Radicle was more photosensitive than other parts of the seed. The rate of germination was proportional to increase in Light intensity ranging from 10 to 3000 Lux. Photosensitivity occurred 6 hrs after water imbibition of air-dried seeds. Maximum photosensitivity was detected 1-2 days after seeding under the light condition at 300 Lux. Germination was almost completed 3 days after seeding. When seeds stored in the chilling and wetting condition were kept at constant temperature in the dark, they germinated well. Air-dried seeds, however, didn't germinate. Whereas, the seeds which kept at alternating temperature had the tendency that seeds stored at room temperature (25$^{\circ}C$) germinated better than those stored at low temperature (4$^{\circ}C$).

• Applied Chemistry for Engineering
• /
• v.21 no.4
• /
• pp.445-451
• /
• 2010

$TiO_2$ shows considerably efficient photoreaction activity under the ultraviolet range but it has disadvantage that there is no activity in the visible light range. In this study, it was tried to find a solution for the problem of this kind of photocatalyst by utilizing transition metal, which can show electronic transition with $TiO_2$ in the visible light area. Photocatalyst was prepared, which can have photocatalytic activity in the wide wavelength range, not only ultraviolet region but also visible light area and prevent the combination of electron and hole hindering the photoreaction. For this purpose, by using the ion exchange method, $TiO_2$ precursor and transition metal precursor were dipped into H typed strong acid ion-exchange resin. And two kind photocatalysts (Ti-M-SCM) in which transition metal and titanium dioxide coexist through the carbonization/activation process was prepared. Moreover, photolytic reaction under the wavelength 254 nm and 365 nm was performed for humic acid (HA) in the continuous reactor in order to estimate the efficiency of produced Ti-M-SCM.