• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.142-147
• /
• 2010

Nano-sized $BaNd_2Ti_5O_{14}$ powders were prepared by the spray pyrolysis process. Sucrose used as the organic additive enabled the formation of nano-sized $BaNd_2Ti_5O_{14}$ powders. The powders prepared from the spray solution without sucrose had a spherical shape, dense structure and micron size before and after calcination. However, the precursor powders prepared from the spray solution with sucrose had a large size, and hollow and porous morphology. The precursor powders had an amorphous crystal structure because of the short residence time of the powders inside the hot wall reactor. The complete decomposition of sucrose did not occur inside the hot wall reactor. Therefore, the precursor powders obtained from the spray solution with sucrose of 0.5M had a carbon content of 39.2wt.%. The powders obtained from the spray solution with sucrose of 0.5M had a slightly aggregated structure of nano-sized primary powders of $BaNd_2Ti_5O_{14}$ crystalline phase after calcination at $1000^{\circ}C$. The calcined powders turned into nano-sized $BaNd_2Ti_5O_{14}$ powders after milling. The mean size of the $BaNd_2Ti_5O_{14}$ powders was 125 nm.

• Korean Journal of Materials Research
• /
• v.18 no.2
• /
• pp.92-97
• /
• 2008

In spray pyrolysis, the effects of the preparation temperature, flow rate of the carrier gas and concentration of the spray solution on characteristics such as the morphology, size, and emission intensity of $Ca_8Mg(SiO_4)_4Cl_2:Eu^{2+}$ phosphor powders under long-wavelength ultraviolet light were investigated. The phosphor powders obtained post-treatment had a range of micron sizes with regular morphologies. However, the composition, crystal structure and photoluminescence intensity of the phosphor powders were affected by the preparation conditions of the precursor powders. The $Ca_8Mg(SiO_4)_4Cl_2:Eu^{2+}$ phosphor powders prepared at temperatures that were lower and higher than $700^{\circ}C$ had low photoluminescence intensities due to deficiencies related to the of Cl component. The phosphor powders with the deficient Cl component had impurity peaks of $Ca_2SiO_4$. The optimum flow rates of the carrier gas in the preparation of the $Ca_8Mg(SiO_4)_4Cl_2:Eu^{2+}$ phosphor powders with high photoluminescence intensities and regular morphologies were between 40 and 60 l/minute. Phosphor powders prepared from a spray solution above 0.5 M had regular morphologies and high photoluminescence intensities.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.4
• /
• pp.247-255
• /
• 2005

Although heat treatment is a process of great technological importance in order to obtain desired mechanical properties such as hardness, the process was required a tedious and expensive experimentation to specify the process parameters. Consequently, the availability of reliable and efficient numerical simulation program would enable easy specification of process parameters to achieve desired microstructure and mechanical properties without defects like crack and distortion. In present work, the developed numerical simulation program could predict distributions of microstructure and thermal stress in steels under different cooling conditions. The computer program is based on the finite difference method for temperature analysis and microstructural changes and the finite element method for thermal stress analysis. Multi-phase decomposition model was used for description of diffusional austenite decompositions in low alloy steels during cooling after austenitization. The model predicts the progress of ferrite, pearlite, and bainite transformations simultaneously during quenching and estimates the amount of martensite also by using Koistinen and Marburger equation. To verify the developed program, the calculated results are compared with experimental ones of casting product. Based on these results, newly designed heat treatment process is proposed and it was proved to be effective for industry.

• Fire Science and Engineering
• /
• v.31 no.5
• /
• pp.1-6
• /
• 2017

The fire and explosion properties of combustible materials are necessary for the safe handling, storage, transportation and disposal. Typical combustion characteristics for process safety include auto ignition temperature(AIT). The AIT is an important index for the safe handling of combustible liquids. The AIT is the lowest temperature at which the material will spontaneously ignite. In this study, the AITs and ignition delay times of n-pentanol and p-xylene mixture were measured by using ASTM E659 apparatus. The AITs of n-pentanol and p-xylene which constituted binary system were $285^{\circ}C$ and $557^{\circ}C$, respectively. The experimental AITs and ignition delay times of n-pentanol and p-xylene mixture were a good agreement with the calculated AITs and ignition delay times by the proposed equations with a few A.A.D. (average absolute deviation). Therefore, it is possible to estimate the AITs and ignition delay times in other compositions of n-pentanol and p-xylene mixture by using the predictive equations which presented in this study.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.3
• /
• pp.615-620
• /
• 2008

We fabriacted thermal evaporated $10nm-Ni_{1-x}Co_x$(x=0.2, 0.6, and 0.7) films on 70 nm-thick polysilicon substrate with $0.5{\mu}m$ line width. NiCo composite silicide layers were formed by rapid thermal annealing (RTA) at the temperatures of $700^{\circ}C$ and $1000^{\circ}C$. Then, we checked the microstructure evaluation of silicide patterns. A FIB (focused ion beam) was used to micro-mill the interconnect patterns with low energy condition (30kV-10pA-2 sec). We investigated the possibility of selective removal of silicide layers. It was possible to remove low resistance silicide layer selectively with the given FIB condition for our proposed NiCo composite silicides. However, the silicides formed from $Ni_{40}Co_{60}$ and $Ni_{30}Co_{70}$ composition showed void defects in interconnect patterns. Those void defects hinder the selective milling for the NiCo composite silicides.

• Resources Recycling
• /
• v.9 no.6
• /
• pp.23-30
• /
• 2000

Since most of the waste plastics are incinerated and landfilled for the plastic treatment, the environmental friendly processes must be introduced. The plastic utilization of plastic to the blast furnace as a substitutional fuel was developed as a useful recycling method of waste plastics, and commercialized in several ironmaking company in Europe and Japan. Present study was carried out to understand the effect of plastic injection on blast furnace process continuously by using the foundry blast furnace in POSCO. The coke replacement ratio turned out to be 0.98 with the waste plastic injection up to 13.8 kg/thm of injection rate, and there were no significant effect of the kinds of injection plastics on the replacement ratio in this test operation. The permeability in the furnace became worse and the heat load in the lower part of blast furnace was increased with increasing the injection rate of waste plastics. As the rate of plastic injection were increased, the top gas utilization and shaft efficiency were also decreased from the Rist diagram analysis.

• Resources Recycling
• /
• v.26 no.5
• /
• pp.61-66
• /
• 2017

Vanadium Dioxide has been investigated for use as a "spectrally-selective" window coating to block infrared transmission and reduce the loss of building interior heat through windows. The preparation of thermochromic $VO_2$ powder by the reductive reaction with hydrogen was studied. The reductive reaction method has many advantages of easy and mass production of $VO_2$ powder according to controlled reaction without semi-conductor equipments like sputter and beam evaporator. The reaction temperature, time, concentration of reductive gas, post-annealing condition and W addition as dopant would affect the characterization of $VO_2$ powder and its thermochromism. Many applications for electrical device and energy-saving technologies is expected.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.209-209
• /
• 2010

금(Au) 또는 은(Ag) 금속 나노입자의 모양, 크기, 분포 상태를 조절하여 가시광선과 적외선, 자외선 영역에서 강한 표면 플라즈몬 효과을 이용할 수 있는데, 최근 이러한 금속 나노입자의 표면플라즈몬 효과를 이용하여 태양광 소자의 성능을 향상시키는 연구가 매우 활발하게 이루어지고 있다. 그 중, 높은 효율과 낮은 제작비용 그리고 간단한 공정과정의 장점을 갖고 있어서 크게 주목 받고 있는 염료감응태양전지에서도 금(Au) 또는 은(Ag) 금속 나노입자을 이용하기 위한 많은 연구가 진행되고 있다. 그 예로, Au가 코팅된 $TiO_2$ 기반의 염료감응태양전지구조를 제작하여, 입사된 빛이 표면플라즈몬 효과를 통해, Au에서 여기된 전자들이 Au/$TiO_2$ 사에의 schottky 장벽을 통과하여 $TiO_2$의 전도대 전자들의 밀도가 증가하여, charge carrier generating rate을 높여 소자의 광변환 효율의 향상을 증명하였다. 이에 본 연구에서는, $TiO_2$보다 높은 전자 이동도(mobility)와 직선통로(direct path way)의 장점을 갖고 있는 ZnO nanorod에서의 charge carrier generating rate을 높일 수 있도록, 비교적 가격이 저렴한 Ag nanoparticle을 코팅하였다. ZnO nanorod 제작은 낮은 온도에서 간단하게 성장시킬 수 있는 hydrothermal 방법을 이용하였다. 기판위에 RF magnetron 스퍼터를 이용하여 AZO seed layer를 증착한 후, zinc nitrate $Zn(NO_3)_2{\cdot}6H_2O$과 hexamethylentetramines (HMT)으로 혼합된 용액을 사용해 ZnO nanorods를 성장시켰다. 이 후, Ag를 형성할 수 있도록 열증기증착법을 이용하여 코팅하였다. Ag의 증착시간에 따른 ZnO nanorods에서의 코팅된 구조와 형태를 관찰하기 위해 field emission scanning electron microscopy (FE-SEM)을 이용하여 측정하였으며, 결정성을 조사하기 위해 X-ray diffraction (XRD)을 이용하여 분석하였다. 또한 입사된 빛에 의해, 여기된 ZnO 전도대 전자들이 다시 재결합을 통해 방출되는 photoluminescence 양을 scanning PL 장비를 통해 측정하여 Ag가 코팅된 ZnO nanorod의 광특성을 분석하였다.

• Journal of Radiation Industry
• /
• v.6 no.1
• /
• pp.55-59
• /
• 2012

Polyacrylonitrile (PAN)-based carbon fibers have been widely used due to their unique chemical, electrical, and mechanical properties. Electron beam irradiation has been extensively employed as means of altering properties of polymeric materials. Electron beam irradiation can induce chemical reactions in materials without any catalyst. Electron beam irradiation may be useful in accelerating the thermal compression stabilization of PAN nanofibers. To investigate the irradiation effect on PAN fibers, PAN nanofibers were irradiated by electron beam at 1,000~5,000 kGy. Irradiated and non-irradiated PAN nanofibers were heated at 180 and $220^{\circ}C$ without applying pressure for 15 min. Then 1 metric ton has been applied for 5 min. SEM images have been found that the fiber kept its morphological behavior after the hot pressing up to electron beam irradiated 1,000 kGy. DSC thermograms showed that the peak temperatures of the exothermic reactions were found to decrease with increasing electron beam irradiation doses and temperature. FT-IR spectra have been found to decrease $C{\equiv}N$ stretch band with increasing the electron beam irradiation dose. These results indicate that the modification of PAN via reactions such as cyclization is significantly enhanced by electron beam irradiation and thermal compression technique.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2009.05a
• /
• pp.671-674
• /
• 2009

We design a low-power and low-area asynchronous EEPROM of 256 bits used in a passive UHF RFID tag chip. For a low-power solution, we use a supply voltage of 1.8V and design a Dickson charge pump using N-type Schottky diodes with a low-voltage characteristic. And we use an asynchronous interface and a separate I/O method for a low-area solution of the peripheral circuit of the designed EEPROM. And we design a Dickson charge pump using N-type Schottky diodes to reduce an area of DC-DC converter. The layout area of the designed EEPROM of 256 bits with an array of 16 rows and 16 columns using $0.18{\mu}m$ EEPROM process is $311.66{\times}490.59{\mu}m^2$.