• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.1
• /
• pp.96-100
• /
• 2009

The properties of recycled fine aggregates which had different source concrete were examined by mortar test. With higher strength of source concrete, specific gravity of recycled fine aggregate was higher and absorption of recycled fine aggregate was lower due to reduction of the volume of adhered cement paste. The compressive strength and flexible strength of mortar with recycled fine aggregate were affected by the interface boundary of new mortar and the strength of adhered mortar. Strength development of mortar with recycled fine aggregate reduced because recycled fine aggregate become a porous material with the smaller strength of source concrete. The drying shrinkage of mortar was about$800{\sim}2000{\mu}m/m$. It was about 1.5 times than that of mortar with natural fine aggregate. Relative dynamic modulus of elasticity was a similar level with that of mortar with natural fine aggregate.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.383-388
• /
• 2019

The present study evaluated experimentally the effects of the type and content of plastic fine aggregates on cement mortar in order to utilize waste platics as raw materials of concrete. The two kinds of plastics, LLDPE and HDPE were used, and the mixing rate of plastic fine aggregates was increased 0, 25, 50, 75, 100%. The mortar of LLDPE fine aggregate and HDPE fine aggregate showed similar tendency in flow and material separation resistance, density and water absorption, compressive strength and flexural strength by age. The flowability of mortar mixed with plastic fine aggregates was increased up to 50% but decreased at 75% or more. The material separation resistance of mortar with plastic fine aggregates was also dramatically decreased. On the other hand, due to the low density of plastics, the density of mortar decreased with the mixing of plastic fine aggregates. Due to the low adhesion between plastic fine aggregates and cement, the compressive strength by age was decreased in proportion to the mixing ratio of plastic aggregate, but the flexural strength of each age decreased with maintaining a certain level at 50% or more of plastic fine aggregate content.

• Journal of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.531-539
• /
• 2015

Properties of normal-strength mortar containing coarsely-crushed coal bottom ash considering standard particle size distribution of fine aggregate were investigated. Mortar containing raw bottom ash was applied as a reference. By crushing the bottom ash with a particle size larger than fine binder but smaller than fine aggregates, i.e., coarse-crushing, water absorption and specific gravity of the particles could be controlled as similar levels to those of natural fine aggregates. Workability and strength of the mortar were not changed and even increased when the coarsely-crushed bottom ash was added considering standard particle size distribution in Standard Specification for Concrete, while those were decreased when raw bottom ash was added without any treatment. When a replacement ratio of coarsely-crushed bottom ash was less than 30 vol.%, there were no significant decrease in dynamic modulus of elasticity and dry shrinkage of the mortar.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.5
• /
• pp.217-225
• /
• 1998

분쇄한 FRP(Fiver-Reinforced Plastics) 폐기물을 사용한 폴리머 모르타르의 물성에 고나하여 조사하였다. 분쇄한 FRP 폐기물을 시멘트 모르타르의 세골재로 재활용하기 위하여 세골재에 대하여 0~50wt% 치환.사용하였고, FRP 폐기물의 사용으로 나타나는 강도 저하현상을 보완하기 위하여 3종류 폴리머 혼화제의 첨가량을 변화시켜 각종 공시체를 제작하였다. 폴리머 혼화제로서는 styrene-bytadiene rubber(SBR) 라텍스, polyacrylic ester(PAE) 에멀젼 및 ethylene-vinyl acetate(EVA)에멀젼을 사용하였다. 분쇄한 FRP 폐기물을 사용한 시멘트 모르타르에 폴리머 혼화제를 첨가하여 만든 폴리머 시멘트 모르타르는 폴리머 혼화제를 첨가하지 않은 모르타르보다 압축 및 휨강도가 크게 증가하였다. 폴리머 시멘트비 10wt%에서 세골재 대용으로 분쇄한 FRP 폐기물의 적정 치환량은 20wt%로 나타났다. 8$0^{\circ}C$에서 가열양생하여 제조한 폴리머 시멘트 모르타르는 폴리머 시멘트비 10wt%이하에서 표준양생한 모르타르보다 강도가 저하되었다. 폴리머 시멘트 포르타르의 흡수율은 폴리머 시멘트비가 증가함에 따라 크게 감소하였다.

• Cement
• /
• s.190
• /
• pp.32-38
• /
• 2011

콘크리트에서 알칼리골재반응은 내구성에 악 영향을 주는 일종의 암이라고 표현할 수 있다. 잠복기간이 길고, 균열이 나타나는 시기도 매우 오래 걸리기 때문이다. 이러한 현상이 1940 년대 알려지면서, 미국 ASTM에는 1950년에 모르타르봉 시험방법이, 1952년에 화학법이 각각 시험방법 규격으로 제정되었다. 국내에서는 한국도로교통연구원을 비롯한 전문연구기관 등에서 화학법 및 모르타르봉 방법으로 연구한 결과, 화학법에서는 일부 골재가 반응성이 있는 것으로 보고 되었으나, 모르타르봉 방법에서는 대상 골재에서 유해가능성이 낮은 것으로 보고되었다. 또한, 그동안은 구조물에서 알칼리골재반응에 의한 피해사례도 보고되지 않았고, 골재의 품질도 양호한 것으로 알려져 왔다. 그러나, 최근들어 서해안 고속도로 일부 구간에서 알칼리골재반응에 의한 포장노면에 균열 및 스폴링 등 심각한 피해사례가 보고되면서 국내에서도 관심이 높아지기 시작하였다. 특히 일본에서는 제 63회 시멘트기술대회 (2009년 5월 22일)에서 팽창기구의 재검토에 대한 이야기가 패널토의에서 제기되었고, 일부 시험방법의 이야기도 나왔다. 그동안의 골재는 현재의 규격만으로도 설명이 가능했는데, 최근의 골재들은 설명이 잘 안 되는 경우가 종종 있다는 이야기다. 이런 이야기들은 일본 지인들과 기술교류를 하면서 많은 이야기를 나누었고, 또한 우연히 문헌들을 독해하던 중 이런 이야기들을 경험한 문헌인 일본 태평양시벤트에서 발간되는 CEM'S 자료를 찾았기에 발췌 정리한 것이다.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.95-102
• /
• 2011

Vicker's hardness and pore size distribution of mortar adhered to the recycled coarse aggregate were tested according to the strength level of original concrete of recycled coarse aggregate to find the change of mortar adhered to the recycled coarse aggregate in cement paste. The strength levels of original concrete of recycled coarse aggregate were 25.5MPa, 41.7MPa and 60.1MPa and the aggregates were used at the state of saturated surface dry condition and oven dry condition. The results of this experimentation indicated that the mean value of Vicker's hardness was increased according to age and strength of original concrete of recycled aggregate. Porosity of $100nm{\sim}10{\mu}m$ size was reduced and porosity of 6nm~100nm size was increased in cement paste.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.327-334
• /
• 2022

In this study, in order to evaluate the characteristics of mortar and concrete using wood chip cogeneration plant flooring as fine aggregate, mortar characteristics according to wood chip aggregate replacement rate and water-cement ratio as a substitute for crushed sand, and concrete characteristics according to wood chip aggregate replacement rate were compared and evaluated. The cement mortar flow according to the wood chip aggregate replacement rate showed a tendency to increase as the wood chip aggregate replacement rate increased, and the compressive strength and flexural strength increased as the wood chip aggregate replacement rate increased. The slump and air content of concrete increased as the aggregate replacement rate increased, and the compressive strength and tensile splitting strength of concrete tended to increase as the wood chip aggregate replacement rate increased. Accordingly, the possibility of using the flooring by the cogeneration plant as a fine aggregate for concrete was confirmed.

• Proceedings of the Korean Society of Disaster Information Conference
• /
• 2015.11a
• /
• pp.132-133
• /
• 2015

이 논문은 세라믹 비드를 일반 모르타르의 잔골재로 대체하여 사용했을 경우 모르타르의 압축강도에 변화를 확인하고자 수행하였다. 잔골재를 대체할 세라믹 비드의 입도분포를 확인하였고, 세라믹 비드의 잔골재 대체율을 10%, 20%, 30%로 설정하고 2가지 종류의 세라믹 비드를 이용하여 시험체를 제작하여 7일, 14일 28일의 압축강도를 측정하였다.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.6
• /
• pp.479-485
• /
• 2016

This paper presents an experimental study conducted to investigate the effect of recycled fine aggregate (RFA) on the mechanical properties and chloride diffusion behavior of mortar. The test results revealed that the addition of RFA plays an important role in the mechanical properties and pore structures of the investigated mortar specimens as well as chloride diffusion behavior. The mechanical properties such as compressive strength and flexural strength of recycled fine aggregate mortar (RFAM) were gradually decreased as RFA replacement ratio increase. The pore structure of RFAM was examined by permeability tests. The RFAM showed a increment in the permeability according to replacement ratio increase of RFA. But the chloride diffusion coefficient of RFAM was almost same up to 50% replacement ratio of RFA due to a chloride binding phenomenon of RFAM which may compensate the higher permeability of RFAM.

• Journal of the Korea Concrete Institute
• /
• v.13 no.6
• /
• pp.561-567
• /
• 2001

It is reported that a lot of sludge powder is produced during the process of manufacturing crushed fine aggregate in mines. However, there is a limitation on the its use that most of them are disposed and wasted, which cause environmental pollution. Therefore, in this paper, tests are carried out in order to recycle sludge powder as filler for cement mortar products. Kinds of aggregates and mix proportion of mortar are varied under various contents of sludge powder. According to test results, it is found that cement mortar products using sludge powder as substitution of fine aggregate about 10% have better qualities than those without sludge powder.