Properties of Mortar Adhered to the Recycled Coarse Aggregate in Cement Paste

시멘트풀 속에서의 순환굵은골재 부착모르타르의 성상변화에 관한 연구

Vicker's hardness and pore size distribution of mortar adhered to the recycled coarse aggregate were tested according to the strength level of original concrete of recycled coarse aggregate to find the change of mortar adhered to the recycled coarse aggregate in cement paste. The strength levels of original concrete of recycled coarse aggregate were 25.5MPa, 41.7MPa and 60.1MPa and the aggregates were used at the state of saturated surface dry condition and oven dry condition. The results of this experimentation indicated that the mean value of Vicker's hardness was increased according to age and strength of original concrete of recycled aggregate. Porosity of $100nm{\sim}10{\mu}m$ size was reduced and porosity of 6nm~100nm size was increased in cement paste.

순환굵은골재 콘크리트에서 혼합전의 순환굵은골재에 부착되어 있었던 모르타르의 성상변화를 조사하기 위한 방법으로, 시멘트풀 속에 순환굵은골재를 투입하여 경화시킨 다음 순환굵은골재에 부착된 모르타르의 비캇경도와 공극분포를 검토하였다. 이때 순환굵은골재는 모재콘크리트의 압축강도를 3수준(25.5MPa, 41.7MPa, 60.1MPa)으로 변화시켜 제조한 것을 파쇄시킨 다음 표면건조포화상태 및 절대건조상태에서 사용되었다. 실험결과 순환굵은골재에 부착된 모르타르의 비캇경도는 순환굵은골재의 모재콘크리트의 강도가 클수록 크며, 재령이 증가할수록 크게 되는 것으로 나타났다. 또한, 시멘트풀 속에서 부착모르타르의 공극분포는 $100nm{\sim}10{\mu}m$ 크기의 공극이 감소되며, 6nm~100nm 크기의 작은 공극이 증가하는 것으로 나타났다.