• Membrane Journal
• /
• v.27 no.2
• /
• pp.154-166
• /
• 2017

Polymeric films for gas barrier applications such as food packaging and electronic devices have attracted great interest due to their cheap, light and easy processability among gas barrier materials. Especially in electronic devices, extremely low gas permeance is necessary for maintaining the device performance. However, current polymeric barrier films still suffer from relatively high gas permeance than other materials. Therefore, there have been strong needs to enhance the gas barrier performance of polymeric barrier films while keep their own advantages. Recently, graphene is highlighted as a 2D-layered material for gas barrier applications. However, owing to the poor workability and difficulty to produce in engineering scale, graphene oxide (GO) is on the rise. GO consists of oxygen-containing functional groups on surface with intrinsic 2D-layered structure and high aspect ratio, and it can be well-dispersed in aqueous polar solvents like water, resulting in scalable mass production. Here, we prepared GO incorporated polyimide (PI) nanocomposites. PI is widely used barrier polymer with high mechanical strength and thermal and chemical stability. We demonstrated that PI/GO nanocomposites could perform as a gas barrier. Furthermore, surfactants (Triton X-100 (TX) and Sodium deoxycholate (SDC)) are introduced to enhance the gas barrier performance by improving the degree of dispersion of GO in PI matrix. As a result, TX enhanced the gas barrier performance of PI/GO nanocomposites which is similar to predicted value. This finding will provide new insight to polymer nanocomposites for gas barrier applications.

• Korean Chemical Engineering Research
• /
• v.47 no.4
• /
• pp.476-480
• /
• 2009

A polymer composite electrolyte of a blend of poly(methyl methacrylate)(PMMA) and poly(ethylene oxide) (PEO) as a host polymer, the ethylene carbonate as a solvent, and $LiClO_4$ as a salt was studied. The crystallinity of the polymer electrolytes was evaluated using differential scanning calorimeter(DSC). The ionic conductivity of the polymer electrolytes was measured by frequency response analyzer(FRA) method. The effect of PEO/PMMA blend ratios on the ionic conduction in these electrolytes was investigated. The electrolyte films showed a phase separation due to immiscibility of the PMMA with the PEO. The PMMA-rich phase and the PEO-rich phase were produced during a film casting. The ionic conductivity of blend electrolyte was dependent on the content of PMMA and showed the highest value at 20 wt.%. However, when PMMA content exceeds 20 wt.%, the ionic conductivity was decreased due to the slow ionic transport through the PMMA-rich phase.

• Polymer(Korea)
• /
• v.29 no.4
• /
• pp.413-417
• /
• 2005

Orientations of liquid crystal molecules on a surface of a film of photoreactive polyvinylcinnamate were investigated in order to apply as an alignment layer of LCD. When the polyvinylcinnamate film was exposed to linearly polarized W light, optical anisotropy was induced in the film through a selective photoreaction. Liquid crystal molecules on a surface of the film was aligned along the oriented polymer chain direction through intermolecular interactions. Thermal and light stability of the photoaligned LC cell were studied by investigating LC alignment changes after the alignment layer was treated with heat and W light. When the film was exposed with linearly polarized UV several times, the LC alignment was induced only along the final UV exposure direction.

• Polymer(Korea)
• /
• v.24 no.1
• /
• pp.90-96
• /
• 2000

Organic electroluminescent (EL) device was fabricated with Alq$_3$ as an emitting material and PDPMA ultra thin film prepared by Langmuir-Boldgett technique as a polymer hole transport layer. A stable condensed PDPMA monolayer was obtained using arachidic acid as a surface active material. The thickness and absorbance of PDPMA LB film increased line-arly with the layer numbers. The organic multilayered device consisted of ITO/PDPMA LB film (19 layers)/Alq$_3$/Al emitted green light with brightness of 2500 cd/m$^2$ at a DC 14 V Especially, the drive voltage of EL device having PDPMA LB film of 15 layers exhibited the value as low as 4 V. The effects of thickness control and molecular orientation in the PDPMA LB film on EL performance were discussed.

• The Korean Journal of Rheology
• /
• v.10 no.2
• /
• pp.98-105
• /
• 1998

가공공정중 변형을 수반하게 되는 고분자제품은 대부분 고분자사슬의 배향을 갖게 된다. 이렇나 사슬배향은 제품의 기계적, 광학적, 그리고 전기적 특성에 매우 중요한 영향을 미치는 것으로 알려져있다. 지금까지 고분자사슬의 배향상태를 나타내기 위한 여러방법은 모두 배향의 중심축을이 알려져 있다는 가정하에 전개되었다, 그러나 복잡한 배향모드를 갖 는 고분자가공의 경우에 배향중심측이 실험축과 일치하지 않는 경우가 많다 따라서 본연구 에서는 일반적인 고분자의배향상태를 나타내는 방법에 대해 알아보고 실제 고분자 가공공정 에 적용을 위해 실험적으로 배향의 대칭축을 찾을 수 있는 접근방법을 제시하고자 하였다. 그 결과 결정성 고분자의 배향상태를 광각 x-선 회절 data를 이용한2차배향 tensor를 통해 배향 타원체를 구성할수있었다. 이를PETdustls 필름과 HDPE사출성형물에 적용해 본 결과 이들의 2차 배향 tensor가 타원체를 잘 구성함을 알수 있었다. 또한 주어진 고분자의 결정 면들에 관계없이 고유한 중심축을 지니고 있음을 확인할수 있었다. 이를 통해 복잡한 배향 모드를 갖는 경우에 본연구에서 제안한 x-타원체를 통해 결정의 배향중심축을 효과적으로 찾을수 있음을 알수 있었다.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2012.03a
• /
• pp.63-63
• /
• 2012

전자제품 패키지에 요구되는 쿠션성과 정전방전 기능을 갖는 폴리우레탄 발포 필름의 제조기술을 확립하게 되면 IT산업용에 적용 가능한 필름제품이 개발되어 ESD(정전방전, Electrostatic Dissipation) 성능을 발휘하게 됨으로서 정전기 쇼크에 의한 각종 전자제품의 오작동이나 파손 방지가 가능하게 되어 포장재, 자동차 전자제품의 하우징 등으로 사용될 수 있게 된다. 전도성 고분자인 Polyaniline (PANI)은 다른 여러 고분자와 비교하여 볼 때 다른 유형의 전도성 고분자보다 합성하기가 쉽고 높은 전기전도도를 보임은 물론 열적 및 대기 안정성이 우수하며 가격이 저렴한 장점을 가지고 있다. 본연구는 CNT 나노기술을 응용한 IT산업용 적층간지용 ESD PU발포필름의 제조 가공기술 및 상품화 개발을 수행하고자 방수, 투습방수성을 가지는 유연재료인 폴리우레탄(PU)의 1액형 PU와 DMF에 PANI의 함량을 5, 10, 15, 20, 25, 30wt%로 변화시켜 제조한 PANI/DMF 분산용액과 IPA/MWNT 3wt% 분산용액의 혼용비에 변화를 주어 $120^{\circ}C$에서 2분 건조시켜 그라운드 필름을 제조하였다. 그리고 2액형 PU와 IPA/MWNT 3wt% 분산용액과 발포제를 사용하여 발포온도 $150^{\circ}C$에서 5분간 건조시켜 발포필름을 제조하였으며 이들의 전기적 특성과 역학적 특성을 조사하였다. 제조된 필름의 전기전도성은 전기저항측정기 KEITHLEY 8009를 사용하여 부피저항과, 표면저항을 각각 측정하여 확인하였으며, 필름의 마찰 대전압은 E.S.T-7 마찰 대전압 시험기를 이용하여 표면 마찰 대전압을 측정하여 확인하고, 필름의 물리적 특성은 인장시험기를 이용하여 breaking stress, breaking strain을 측정하였다. 필름단면의 CNT 발포특성은 주사전자현미경(SEM)을 사용하여 측정하여 발포특성과 물성과의 연관성을 확인하였다. 그 결과 필름의 전기적 특성은 PANI가 30% 함량일 때 전반적으로 낮은 저항값이 측정되었으며, 마찰대전압을 측정한 결과 대부분의 시료가 0에 가까운 낮은 값을 가졌다. 필름의 물리적 인장특성은 PANI가 10wt%의 함량일 때 가장 높은 절단강도를 가졌으며 분산용액의 혼용비에 따른 경향성은 나타나지 않았다. 필름의 단면형상을 확인하여 발포특성을 분석한 결과 PANI의 함량에 따라 발포 cell의 크기는 뚜렷한 경향성을 보이지 않았으나 30wt%의 PANI/DMF 분산용액 20part(gr)와 3wt% IPA/MWNT 분산용액 40part(gr)로 제조한 시료의 cell이 가장 균일하고 고르게 발포되었으며, 3.90E+06ohm으로 가장 낮은 표면저항 값으로 측정되어 가장 좋은 전기전도성을 가짐을 확인하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.05a
• /
• pp.99-115
• /
• 2000

• Proceedings of the Korean Institute of Industrial Safety Conference
• /
• 2004.10a
• /
• pp.450-454
• /
• 2004

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.167-167
• /
• 2012

• The monthly packaging world
• /
• s.74
• /
• pp.157-160
• /
• 1999