Abstract
Organic electroluminescent (EL) device was fabricated with Alq$_3$ as an emitting material and PDPMA ultra thin film prepared by Langmuir-Boldgett technique as a polymer hole transport layer. A stable condensed PDPMA monolayer was obtained using arachidic acid as a surface active material. The thickness and absorbance of PDPMA LB film increased line-arly with the layer numbers. The organic multilayered device consisted of ITO/PDPMA LB film (19 layers)/Alq$_3$/Al emitted green light with brightness of 2500 cd/m$^2$ at a DC 14 V Especially, the drive voltage of EL device having PDPMA LB film of 15 layers exhibited the value as low as 4 V. The effects of thickness control and molecular orientation in the PDPMA LB film on EL performance were discussed.
고분자 정공 전달체로 LB 기법에 의해 제조한 PDPMA 초박막과 발광층으로 Alq$_3$를 사용하여 유기 발광소자를 제작하였다. 표면활성제로 arachidic acid를 사용하여 안정한 PDPMA 단분자막을 얻을 수 있었다. PDPMA LB 필름의 두께와 320nm의 최대 흡광도는 층수의 증가에 따라 거의 선형적으로 증가하였다. ITO/PDPMA LB 필름(19층)/Alq$_3$/Al으로 구성된 유기 적층형 소자는 DC 14V에서 2500 cd/m$^2$의 높은 휘도를 갖는 녹색 빛을 발광하였다. 특히 PDPMA LB 필름의 층이 15로 이루어진 발광소자의 구동전압은 4V의 매우 낮은 값을 나타내었다. PDPMA LB 필름의 두께 조절 및 분자 배향에 따른 EL 성능에 미치는 영향에 관하여도 검토하였다.