Carbon fibers were coated with carboxy modified poly(hydroxy ether)(C-PHE, water dispersed), water soluble polymers poly(hydroxy ether ethanol amine)(PHEA) or water insoluble poly(hydroxy ether)(PHE). Interfacial shear strength of polymer coated carbon fibers was measured by micro-droplet tests with vinyl ester resin, and approximately 30 samples were tested. The interfacial adhesion of poly-mers to carbon fibers was also evaluated, and diffusion behavior of polymer films in vinyl ester resin was investigated. The carbon fibers after testing and diffusion samples were analysed by SEM in order to understand adhesion mechanism. Interfacial shear strength of carbon fibers was enhanced by the coating of PHE and C-PHE which have good or marginal solubility in vinyl ester resin, respectively, but not by the coating of PHEA possibly due to the poor solubility in vinyl ester resin.

• Journal of the Korea Concrete Institute
• /
• v.28 no.4
• /
• pp.407-417
• /
• 2016

In this study, concrete composite beams were tested under two-point loading to evaluate horizontal shear strength. The test variables were a type of composite members (PC+RC, PSC+RC, SFRC+RC), area ratio of high-strength (60MPa) to low-strength concrete (24 MPa), and transverse reinforcement ratio. The test results showed that the contribution of transverse reinforcements and interface conditions had influence on horizontal shear strength. Existing and previous test results were classified according to test methods and the interface conditions and were compared with the predictions of current design codes. On the basis of test results, an improved design method was proposed.

• Journal of Adhesion and Interface
• /
• v.14 no.2
• /
• pp.75-81
• /
• 2013

Epoxy matrix based composites were fabricated by adding SiC nano fillers. The interfacial properties of composites were varied with different shapes of SiC nano fillers. To investigate the shape effects on the interfacial properties, beta and whisker type SiC nano fillers were used for this evaluation. The dispersion states of nano SiC-epoxy nanocomposites were evaluated by capacitance measurements. FE-SEM was used to observe the fracture surface of different structures of SiC-epoxy nanocomposites and to investigate for reinforcement effect. Interfacial properties between carbon fiber and SiC-epoxy nanocomposites were also evaluated by ILSS (interlaminar shear strength) and IFSS (interfacial shear strength) tests. The interfacial adhesion of beta type nanocomposites was better than whisker type.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.45-45
• /
• 2009

원가 측면에서 유리한 저항점용접(Resistance Spot Welding)이 차체 용접에 80%이상으로 가장 많이 적용되고 있다. 첨단고강도강(Advanced High Strength Steel)의 저항점용접성 및 용접부 특성에 미치는 공정 변수의 영향에 대한 연구결과는 많으나, 합금원소의 영향에 대해서는 전무하다. 특히, Si는 DP(Dual Phase)강에 첨가 시 균일한 마르텐사이트의 분포를 촉진하는 원소로 저항 점용접성 및 용접부 특성에 영향을 미칠 것으로 예상되며, 이에 대한 연구는 보고된바 없다. 본 연구에서는 냉연 DP강의 저항 점용접시 중요한 인자 중 하나인 너깃경과 전단인장강도에 미치는 Si함유량의 영향을 검토하였다. 사용된 강재 및 용접기는 1.2mm 두께의 Si함유량(0, 0.5, 1.0, 1.5wt%)이 다른 인장강도 780~1000MPa급 냉연 DP강과 단상 AC용접기를 사용하였다. 용접조건은 ISO 18278-2규격에 따라 가압력 4kA, 초기가압시간 40cycle, 유지시간 17cycle로 고정하고, 용접전류만 변화하여 용접을 실시하였다. 너깃경은 용접부 단면을 컷팅 후 폴리싱 하여, 광학현미경과 Image Pro plus를 이용하여 측정했으며, 인장시편규격은 JIS Z 3137를 이용하였다. Si함유량이 증가에 따라 스패터 발생 전류는 감소했고, 너깃경은 직선적으로 증가했다. Si함유량 증가에 따른 너깃경 증가 이유는 저항(R) 측정결과, Si함유량 증가에 따라 모재의 저항이 높아져, 따라서 입열량($Q=I^2Rt$)이 많아지기 때문으로 판단되었다. 인정전단강도는 Si함유량 증가에 따라 직선적으로 증가했다. 이러한 이유는 Si함유량 증가에 따라 너깃경이 증가되기 때문으로 판단되었고, 너깃경과 인장전단강도 사이에 직선적 관계(PL(kN)=$3.2N_{dia.}$-0.81, $R^2$=0.93)를 가지고 있었다. 파단양상은 Si함유량에 상관없이 5.4kA이하에서는 계면파단이 일어났고, 6.0kA이상에서는 풀 아웃 파단이 일어났다. 계면파단주원인은 용접부 가장자리에 지름이 약 $5{\mu}m$이하의 예리한 노치가 존재하여 노치응력집중과 HAZ계면 근처에 미접합부가 존재하기 때문으로 판단되었다. 6.0kA이상에서는 예리한 노치가 없었고, HAZ부가 완전히 접합되어 있기 때문에 풀 아웃 파단이 일어난 것으로 판단되었다. 따라서, Si함유량 증가에 따라 적정용접전류 구간은 감소했고, 너깃경은 직선적으로 증가했다. 또한, Si함유량 증가에 따라 인장전간강도는 증가 했으며, 너깃경과 인장전단강도 사이에 직선적 관계를 가지고 있었다. 파단 양상은 Si함유량에 상관없이 5.2kA이하에서는 계면파단이, 6.0kA이상에서는 풀 아웃 파단이 일어났다.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.3
• /
• pp.237-245
• /
• 2016

Structural performance and durability of ultra high performance concrete could demonstrate optimal performance when unity was kept. Accordingly, it is necessary to involve the characteristics and quantitative surface treatment at the same time in order to retain oneness of Ultra-High-Performance Concrete(UHPC) according to construction joint occurrence. Therefore, this study derives a reasonable surface treatment method in a material's point of view through the shear adhesion performance evaluation according to the construction joints surface processing method as a part for securing the adhesion performance of the construction joints when casting UHPC. 180 MPa of required average strength was used for mix of UHPC and surface treatment method was set to totally 7 level that MN, GR-10-0, GR-20-0, GR-30-0, SH-30-5, SH-30-10. After the specimen were manufactured to a size of $150{\times}150{\times}150mm$, Direct shear test was performed to evaluate the shear adhesion strength. As a result, it was confirmed that the adhesion performance was improved when executing a surface treatment for the construction joint interface and standard of failure mode of specimen was over Type C. Also, It was considered that interface of cross section and depth of concavo-convex should be concerned.

• The Journal of the Korea Contents Association
• /
• v.10 no.11
• /
• pp.228-234
• /
• 2010

Ni-Cr and Co-Cr alloy uncontained Be element for using as dental porcelain alloy were analyzed the mechanical properties through bonding strength and fracture test after the bonding with porcelain. The bonding strengths between alloy and ceramic were measured through the shear bond strength test. Consequently, the T-3 group contained Be element that had shear strength of 41.13(${\pm}5.11$)MPa was showed the highest shear strength than the other groups. The second highest group was a verabond contained Be element that had shear strength of 40.72(${\pm}5.98$)MPa. The results of the other groups according to the shear strength were Wirobond(38.40(${\pm}9.66$)MPa) belonged to Co-Cr alloy, and Verabond 2V(32.77(${\pm}4.31$)MPa), Bellabond N(28.63(${\pm}6.39$)MPa), Bellabond plus(24.97(${\pm}6.13$)MPa), Argeloy N.P. Star(22.69(${\pm}3.41$)MPa) uncontained Be element, respectively. The morphological aspects of the fracture surface between alloys and ceramic were observed that all groups were caused mixed failure as conformation attached ceramic fragments to metallic surface by fracture process.

• Journal of the Korea Concrete Institute
• /
• v.24 no.1
• /
• pp.25-35
• /
• 2012

For a member subjected to direct shear forces, forces are transferred across interface concrete area and resisted by shear transfer capacity. Shear-friction equations in recent concrete structural design provisions are derived from experimental test results where shear-friction capacity is defined as a function of steel reinforcement area contained in the interface. This empirical equation gave too conservative values for concrete members with large amounts of reinforcement. This paper presents a method to evaluate shear transfer strengths and to define ultimate conditions which result in crushing of concrete struts after yielding of longitudinal reinforcement perpendicular to the interface concrete. This method is based on the bi-axial stress field theory where different constitutive laws are applied in various means to gain accurate shear strengths by considering softening effects of concrete struts based on the modified compression-field theory and the softened truss model. The validity of the proposed method is examined by applying to some selected test specimens in literatures and results are compared with recent design code provisions. A general agreement is observed between predicted and measured values at ultimate loading stages in initially uncracked normal-strength concrete test.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.381-389
• /
• 2000

Metal matrix composite(MMCs) have been rapidly becoming one of the strongest candidates for structural materials for high temperature application. It is well recognized that MMCs always experience at least one large cool-down from processing temperature before my significant applied service loading. Due to the large difference in thermal expansion coefficient between the fiber and matrix, large thermal residual stresses generally develop in composites. It was reported from many previous studies that the effects of thermal residual stress on mechanical properties and fracture behavior were much more complex and dramatic than conventional engineering materials. Therefore it is crucial to evaluate the effect of heat treatment which changes the characteristic of distribution of thermal residual stress in MMCs. Single fiber composite(SFC) test based on the balance in a micromechanical model is a quite convenient method to evaluate interfacial shear strength(IFSS) and the failure mode of composite. In this study the effect of heat treatment on IFSS and the microscopic failure mechanism of MMC is investigated by combining acoustic emission(AE) technique with SFC test. The characteristic of AE signal, IFSS and microscopic failure mechanism due to heat treatment condition is discussed.

• Journal of Adhesion and Interface
• /
• v.10 no.4
• /
• pp.162-168
• /
• 2009

As a preliminary study of optimum composite properties under cryogenic temperature, the comparison of interfacial properties of carbon or glass fibers reinforced epoxy composites was evaluated at ambient and intermediate low temperature, i.e., 25 and $-10^{\circ}C$ by using micromechanical techniques. Under tensile and compressive loading conditions, their mechanical modulus at low temperature was higher than that atambient temperature. Interfacial shear strength (IFSS) at ambient and low temperatures was compared to each other, depending on epoxy matrix toughness and apparent modulus at the interface. The IFSS was much higher at low temperature than that at room temperature because of the increased epoxy matrix modulus. Statistical distributions of tensile strengths of glass and carbon fibers were evaluated for different temperature ranges, which is dependent upon fiber's inherent flaws and rigidity.

• Journal of the Korea Concrete Institute
• /
• v.27 no.3
• /
• pp.299-309
• /
• 2015

Ultra High Performance Fiber Reinforced Concrete (UHPFRC) is distinguished from the normal concrete by outstanding compressive and tensile strength. Cracked normal concrete resists shear by aggregate interlocking while clamped by transverse reinforcement, which is called as shear friction theory. Cracked UHPFRC is expected to have a different shear transfer mechanism due to rather smooth crack face and post-cracking behavior under tensile force. Twenty-four push-off specimens with transverse reinforcement are tested for four different fiber volume ratio and three different ratio of reinforcement along the shear plane. The shear friction strength for monolithic concrete are suggested by limit analysis of plasticity and verified by test results. Plastic analysis gives a conservative, but reasonable estimate. The suggested shear friction factor and effectiveness factor of UHPFRC can be applied for interface shear transfer design of high-strength concrete and fiber reinforced concrete with post-cracking tensile strength.