• Polymer(Korea)
• /
• v.26 no.6
• /
• pp.718-727
• /
• 2002

In this work, an Ar+ beam was irradiated on carbon fiber surfaces to improve the interfacial shear strength (IFSS) of the resulting composites using an ion assisted reaction (IAR) method h single fiber pull-out test was executed to investigate the basic characteristics of the single Carbon fiber/matrix interface. Based on Greszczuk's geometrical model, the debonding force for pull-out of the fiber from the resins was discussed with the applied ion beam energy as a result, it was known that an ion beam treatment produced the functional groups on fiber surface and etching lines along the fiber axis direction, resulting in increasing the adhesion forces between fibers and matrix, which caused the improvement of the IFSS in a composite system. And, it was also found that the maximum IFSS was shown at 0.8 keV ion beam energy in this system.

• The Journal of the Korea Contents Association
• /
• v.10 no.11
• /
• pp.228-234
• /
• 2010

Ni-Cr and Co-Cr alloy uncontained Be element for using as dental porcelain alloy were analyzed the mechanical properties through bonding strength and fracture test after the bonding with porcelain. The bonding strengths between alloy and ceramic were measured through the shear bond strength test. Consequently, the T-3 group contained Be element that had shear strength of 41.13(${\pm}5.11$)MPa was showed the highest shear strength than the other groups. The second highest group was a verabond contained Be element that had shear strength of 40.72(${\pm}5.98$)MPa. The results of the other groups according to the shear strength were Wirobond(38.40(${\pm}9.66$)MPa) belonged to Co-Cr alloy, and Verabond 2V(32.77(${\pm}4.31$)MPa), Bellabond N(28.63(${\pm}6.39$)MPa), Bellabond plus(24.97(${\pm}6.13$)MPa), Argeloy N.P. Star(22.69(${\pm}3.41$)MPa) uncontained Be element, respectively. The morphological aspects of the fracture surface between alloys and ceramic were observed that all groups were caused mixed failure as conformation attached ceramic fragments to metallic surface by fracture process.

• Journal of Adhesion and Interface
• /
• v.7 no.2
• /
• pp.26-31
• /
• 2006

In order to effectively improve interfacial adhesion strength between polypropylene (PP) and jute fiber, we particularly incorporated maleic anhydride grafted PP (MAPP) into the matrix through the environment-friendly process without an additional method of process and had better mechanical performances by providing the alignment into the natural fiber than those of the conventional fabrication technology such as an extrusion or injection molding. We also proposed hot pressing method which applied relatively low shear to the composites and confirmed the chemical bonds among the functional groups of MAPP and jute using FT-IR approach. The concentration of MAPP for maximum tensile strength and modulus was optimized at 3 wt%. Flexural properties had no noticeable tendency to increase with MAPP contents compared to tensile strength, which could probably be explained by the degree in wetting of PP/MAPP matrix.

• Polymer(Korea)
• /
• v.24 no.4
• /
• pp.499-504
• /
• 2000

The effect of anodic oxidation on high strength PAN-based carbon fibers has been studied in terms of surface functionality and surface energetics of the fiber surfaces, resulting in improving the mechanical properties of composites. According to FT-IR and XPS measurements, it reveals that the oxygen functional groups on fiber surfaces induced by an anodic oxidation largely influence the surface energetics of fibers or the mechanical interfacial properties of composites, such as the interlaminar shear strength (ILSS) of composites. According to the contact angle measurements based on the wicking rate of a test liquid, it is observed that anodic oxidation does lead to an increase in surface free energy of the carbon fibers, mainly due to the increase of its specific (or polar) component. From the surface energetic point of view, it is found that good wetting plays an important role in improving the degree of adhesion at interfaces between fiber and epoxy resin matrix of the resulting composites. Also, a direct linear relationship is shown between 01s/01s ratio and ILSS or between specific component and ILSS of the composites for this system.

• Composites Research
• /
• v.26 no.5
• /
• pp.315-321
• /
• 2013

In this work, pitch-carbonized glass fibers were prepared for reinforcement of composites. The influence of acid functionalization of the fibers on the morphological, mechanical, and thermal properties of fiber-reinforced epoxy matrix composites was investigated. The acid functionalization of the fibers led to 10 and 150% increases in the mechanical and thermal properties, respectively, as compared to carbon fiber-reinforced composites. This can be attributed to the superior orientation of fiber structures and good interfacial interactions between fillers and epoxy matrix, resulting in enhanced degree of dispersion and formation of thermally conductive paths in the functionalized composites.

• Polymer(Korea)
• /
• v.38 no.2
• /
• pp.240-249
• /
• 2014

Multi-walled carbon nanotube (MWNT) reinforced poly(ethylene terephthalate) (PET) composites are studied. To increase the interfacial interactions between PET and MWNTs, the MWNTs are functionalized with bishydroxy-ethylene-terephthalate (BHET). The functionalized MWNTs are melt blended into PET matrix using a twin screw extruder. The amount of MWNTs loaded in PET matrix ranges from 0.5 to 2.0 wt%. After compounding and spinning, the filaments are post-drawn and annealed. To verify the chemical modifications of carbon nanotubes, Raman, $^1H$ NMR, XPS, TGA and FE-SEM are used. The nanocomposites are also analyzed with DSC, TGA, and UTM. These tests show that crystallization temperature and thermal degradation temperature increase due to the functionalized MWNTs. Also, tensile test shows that yield strength and toughness increase more than 30% with addition of only 1 wt% of MWNTs. These results show that the introduction of BHET onto the MWNTs is a very effective way in manufacturing MWNT/PET composite.

• Polymer(Korea)
• /
• v.24 no.5
• /
• pp.721-727
• /
• 2000

The electrolytic plating of a metallic nickel on carbon fiber surfaces was carried out to improve mechanical interfacial properties of carbon fiber/epoxy resin composites. The surface characteristics of carbon fibers and the mechanical interfacial properties of final composites were characterized by X-ray photoelectron spectroscopy (XPS) and interlaminar shear strength (ILSS), respectively. It was found that the electrolytic Ni-plating conditions significantly affected the degree of adhesion at interfaces between carbon fibers and epoxy resin matrix in a composite system. Especially, the increase of O,$_{1s}$/$C_{1s}$ ratio, production of NiO groups, and formation of metallic nickel on the nickel-plated carbon fiber surfaces led to an increase of the ILSS of the composites. Also, the ILSS of the composites was greatly correlated with the $O_{1s}$/$C_{1s}$ ratio of the carbon fibers treated in this work.is work.

• Polymer(Korea)
• /
• v.36 no.5
• /
• pp.573-578
• /
• 2012

In general, most physical properties of wood/polyvinyl chloride (PVC) composites are lower than those of corresponding neat PVC resin because of poor interfacial adhesion between the hydrophilic wood flour and hydrophobic PVC. Therefore, in this study, we treated wood flour with three aminosilanes to improve wood/PVC interfacial adhesion strength, and eco-friendly wood/PVC/nanoclay composites were prepared by melt blending the aminosilane-treated wood flour, a heavy metal free PVC compound, and a type of nanoclay. The effects of treating wood flour with the aminosilanes and adding the nanoclay on the mechanical properties of the composites were investigated. Mechanical properties of the composites were investigated by universal testing machine (UTM), izod impact tester, dynamic mechanical analyzer (DMA), and thermomechanical analyzer (TMA). The tensile properties of the composites with the aminosilane-treated wood flour were considerably higher than those of the composites with neat wood flour. Furthermore, a small amount of the nanoclay improved mechanical properties of the composites. The performance of the wood/PVC composites was considerably improved by using the aminosilane-treated wood flour and the nanoclay.

• Composites Research
• /
• v.12 no.2
• /
• pp.91-100
• /
• 1999

The manufacture of high strength polyethylene(HSPE) tape yarns has been accomplished by a solid state processing(SSP) method as the compaction of ultra-high molecular weight polyethylene(UHMWPE) powders and drawing of the compacted film under the melting point without any organic solvents. In this study, the characteristics of HSPE tape yarns produced by SSP which is desirable for production cost and environmental aspect were analyzed. As the results, tensile strengths of HSPE tape yarns increased with increasing the draw ratio and the fracture morphology of highly drawn HSPE tape yarns showed more fibrillar shape than the low drawn one. Interfacial shear strengths of HSPE tape yarns with vinylester resin increased by $O_2$ plasma treatment and maximum interfacial shear strength was obtained in the plasma treatment condition of 100W and 5min. In addition, mechanical properties of HSPE tape yarn reinforced composites were investigated and compared with those of the gel spun HSPE fiber reinforced composites.

• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.709-709
• /
• 1995

원거리 플라즈마 화학증착법을 이용하여 저온에서 이산화규소박막을 제조하였다. 본 연구 에서는 공정변수인 기판의 온도, 반응기체의 조성 및 분압과 플라즈마 전력에 따른 산화막의 재료적인 물성을 평가하였다. XPS결과에서 산화막은 양론비(O/Si=2)보다 약간 적어 실리콘이 많이 함유된 막으로 나타났다. 이 경우 굴절율과 ESR분석에 의해 미결합된 실리콘의 양이 증가함을 알 수 있었다. SIMS분석에 의해 미량의 질소성분이 계면에 존재하는 것과 실리콘 미결함을 관찰하였다. FT-IR로부터 막내 수소량을 정량화하였으며 결합각 분포는 200℃이상에서 열산화막과 비슷한 값을 얻었다. 하지만 열산화막에 비해 높은 식각율을 보여 계면 스트레스에 의해 막내의 결합력이 약해진 것으로 생각된다.